金属学报  2014, Vol. 50 Issue (5): 524-530    DOI: 10.3724/SP.J.1037.2013.00681
  本期目录 | 过刊浏览 |
V-Ti微合金钢的组织性能及相间析出行为*
陈俊1, 吕梦阳2, 唐帅1(), 刘振宇1, 王国栋1
1 东北大学轧制技术及连轧自动化国家重点实验室, 沈阳 110819
2 东北大学材料与冶金学院, 沈阳 110819
MICROSTRUCTURE, MECHANICAL PROPERTIES AND INTERPHASE PRECIPITATION BEHAVIORS IN V-Ti MICROALLOYED STEEL
CHEN Jun1, LÜ Mengyang2, TANG Shuai1(), LIU Zhenyu1, WANG Guodong1
1 State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819
2 School of Materials and Metallurgy, Northeastern University, Shenyang 110819
引用本文:

陈俊, 吕梦阳, 唐帅, 刘振宇, 王国栋. V-Ti微合金钢的组织性能及相间析出行为*[J]. 金属学报, 2014, 50(5): 524-530.
Jun CHEN, Mengyang LÜ, Shuai TANG, Zhenyu LIU, Guodong WANG. MICROSTRUCTURE, MECHANICAL PROPERTIES AND INTERPHASE PRECIPITATION BEHAVIORS IN V-Ti MICROALLOYED STEEL[J]. Acta Metall Sin, 2014, 50(5): 524-530.

全文: PDF(8371 KB)   HTML
摘要: 

采用热模拟实验研究了等温温度对V-Ti微合金钢组织性能及相间析出行为的影响规律, 利用OM和TEM分析了不同等温温度下实验钢的组织特征. 结果表明, 不同等温温度下均可得到大量铁素体组织, 随等温温度的降低, 铁素体体积分数增加, 铁素体晶粒尺寸减小. 不同等温温度下均可观察到平面相间析出, 且降低等温温度可显著细化相间析出列间距和析出粒子尺寸. 纳米碳化物具有NaCl型晶体结构, 晶格常数约为0.436 nm, 同铁素体基体满足(100)carbide//(100)ferrite和[011]carbide//[001]ferrite的B-N关系. 在680 ℃下等温30 min, 沉淀强化量可达到360.6 MPa.

关键词 V-Ti微合金钢等温温度显微组织相间析出Vickers硬度    
Abstract

The microstructure, mechanical properties and precipitation behaviors in a low carbon V-Ti microalloyed steel were investigated using thermal simulation. The microstructural characteristics of tested steel were analyzed using OM and TEM. The results show that the larger volume fraction of ferrite can be obtained for different isothermal temperatures. The ferrite volume fraction is increased and ferrite grain size is reduced as the isothermal temperature is lowered. The planar interphase precipitation can be observed for different isothermal temperatures, and both sheet spacing and precipitates size are refined by lowering isothermal temperature. Moreover, the nanometer-sized carbides have a NaCl-type crystal structure with a lattice parameter of about 0.436 nm and they can obey one variant of Baker-Nutting (B-N) orientation relationship of (100)carbide//(100)ferrite and [011]carbide//[001]ferrite. The precipitation hardening for the specimen treated at 680 ℃ for 30 min can reach 360.6 MPa.

Key wordsV-Ti microalloyed steel    isothermal temperature    microstructure    interphase precipitation    Vickers-hardness
    
ZTFLH:  TG142.33  
基金资助:* 国家自然科学基金项目51204049和中央高校基本科研业务费专项资金项目N110607003资助
图1  
图2  
图3  
图4  
图5  
图6  
图7  
图8  
Temperature / ℃ Δs0 / MPa ΔsSS / MPa ΔsGB / MPa ΔsDis / MPa ΔsOrowan / MPa sy / MPa
750 53.9 76.2 163.6 168.5 239.3 585.8
720 53.9 76.2 174.3 168.5 277.9 628.4
700 53.9 76.2 178.8 168.5 287.5 641.5
680 53.9 76.2 194.2 168.5 360.6 721.6
  
[1] Chen J, Tang S, Liu Z Y, Wang G D. Acta Metall Sin, 2012; 48: 441
[1] (陈 俊, 唐 帅, 刘振宇, 王国栋. 金属学报, 2012; 48: 441)
[2] Guo J, Shang C J, Yang S W, Guo H, Wang X M, He X L. Mater Des, 2009; 30: 129
[3] Manohar P A, Chandra T, Killmore C R. ISIJ Int, 1996; 36: 1486
[4] Chen J, Chen X W, Tang S, Liu Z Y, Wang G D. Mater Sci Forum, 2013; 749: 243
[5] Cizek P, Wynne B P, Davies C H J, Muddle B C, Hodgson P D. Metall Mater Trans, 2002; 33A: 1331
[6] Funakawa Y, Shiozaki T, Tomita K, Yamamoto T, Maeda E. ISIJ Int, 2004; 44: 1945
[7] Yen H W, Chen P Y, Huang C Y, Yang J R. Acta Mater, 2011; 59: 6264
[8] Kestenbach H J, Campos S S, Morales E V. Mater Sci Technol, 2006; 22: 615
[9] Jang J H, Heo Y U, Lee C H, Bhadeshia H K D H, Suh D W. Mater Sci Technol, 2013; 29: 309
[10] Yen H W, Huang C Y, Yang J R. Scr Mater, 2009; 61: 616
[11] Chen C Y, Yen H W, Kao F H, Li W C, Huang C Y, Yang J R, Wang S H. Mater Sci Eng, 2009; A499: 162
[12] Okamoto R, Borgenstam A, Ågren J. Acta Mater, 2010; 58: 4783
[13] Mukherjee S, Timokhina I B, Zhu C, Ringer S P, Hodgson P D. Acta Mater, 2013; 61: 2521
[14] Sakuma T, Honeycombe R W K. Met Sci, 1984; 18: 449
[15] Dunlop G L, Carlsson C J, Frimodig G. Metall Trans, 1978; 9A: 261
[16] Freeman S, Honeycombe R W K. Met Sci, 1977; 11: 59
[17] Honeycombe R W K, Mehl Medalist R F. Metall Trans, 1976; 7A: 915
[18] Zhang Y J, Miyamoto G, Shinbo K, Furuhara T. Scr Mater, 2013; 69: 17
[19] Davenport A T, Berry F G, Honeycombe R W K. Met Sci, 1968; 2: 104
[20] Foreman A J E, Makin M J. Can J Phys, 1967; 45: 511.
[21] Pickering F B. Physical Metallurgy and the Design of Steels. London: Applied Science Publishing Ltd., 1978: 63
[22] Taylor K A. Scr Metall Mater, 1995; 32: 7
[23] Misra R D K, Nathani H, Hartmann J E, Siciliano F. Mater Sci Eng, 2005; A394: 339
[24] Brito R M, Kestenbach H J. J Mater Sci, 1981; 16: 1257
[25] Chen J, Lv M Y, Tang S, Liu Z Y, Wang G D. Mater Sci Eng, 2014; A594: 389
[1] 张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿. K439B铸造高温合金800℃长期时效组织与性能演变[J]. 金属学报, 2023, 59(9): 1253-1264.
[2] 卢楠楠, 郭以沫, 杨树林, 梁静静, 周亦胄, 孙晓峰, 李金国. 激光增材修复单晶高温合金的热裂纹形成机制[J]. 金属学报, 2023, 59(9): 1243-1252.
[3] 孙蓉蓉, 姚美意, 王皓瑜, 张文怀, 胡丽娟, 仇云龙, 林晓冬, 谢耀平, 杨健, 董建新, 成国光. Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为[J]. 金属学报, 2023, 59(7): 915-925.
[4] 吴东江, 刘德华, 张子傲, 张逸伦, 牛方勇, 马广义. 电弧增材制造2024铝合金的微观组织与力学性能[J]. 金属学报, 2023, 59(6): 767-776.
[5] 张东阳, 张钧, 李述军, 任德春, 马英杰, 杨锐. 热处理对选区激光熔化Ti55531合金多孔材料力学性能的影响[J]. 金属学报, 2023, 59(5): 647-656.
[6] 李殿中, 王培. 金属材料的组织定制[J]. 金属学报, 2023, 59(4): 447-456.
[7] 朱智浩, 陈志鹏, 刘田雨, 张爽, 董闯, 王清. 基于不同 α / β 团簇式比例的Ti-Al-V合金的铸态组织和力学性能[J]. 金属学报, 2023, 59(12): 1581-1589.
[8] 芮祥, 李艳芬, 张家榕, 王旗涛, 严伟, 单以银. 新型纳米复合强化9Cr-ODS钢的设计、组织与力学性能[J]. 金属学报, 2023, 59(12): 1590-1602.
[9] 彭立明, 邓庆琛, 吴玉娟, 付彭怀, 刘子翼, 武千业, 陈凯, 丁文江. 镁合金选区激光熔化增材制造技术研究现状与展望[J]. 金属学报, 2023, 59(1): 31-54.
[10] 葛进国, 卢照, 何思亮, 孙妍, 殷硕. 电弧熔丝增材制造2Cr13合金组织与性能各向异性行为[J]. 金属学报, 2023, 59(1): 157-168.
[11] 杨天野, 崔丽, 贺定勇, 黄晖. 选区激光熔化AlSi10Mg-Er-Zr合金微观组织及力学性能强化[J]. 金属学报, 2022, 58(9): 1108-1117.
[12] 李彦强, 赵九洲, 江鸿翔, 何杰. Pb-Al合金定向凝固组织形成过程[J]. 金属学报, 2022, 58(8): 1072-1082.
[13] 刘仁慈, 王鹏, 曹如心, 倪明杰, 刘冬, 崔玉友, 杨锐. 700℃热暴露对 β 凝固 γ-TiAl合金表面组织及形貌的影响[J]. 金属学报, 2022, 58(8): 1003-1012.
[14] 张鑫, 崔博, 孙斌, 赵旭, 张欣, 刘庆锁, 董治中. Y元素对Cu-Al-Ni高温形状记忆合金性能的影响[J]. 金属学报, 2022, 58(8): 1065-1071.
[15] 孙蓉蓉, 姚美意, 林晓冬, 张文怀, 仇云龙, 胡丽娟, 谢耀平, 杨健, 董建新, 成国光. 添加TiFe22Cr5Al3Mo合金在500℃过热蒸汽中腐蚀行为的影响[J]. 金属学报, 2022, 58(5): 610-622.