金属学报  2012, Vol. 48 Issue (8): 1011-1017    DOI: 10.3724/SP.J.1037.2012.00136
  论文 本期目录 | 过刊浏览 |
Hf含量对镍基粉末高温合金中γ'相形态的影响
张义文1,2,王福明1,胡本芙3
1. 北京科技大学冶金与生态工程学院, 北京 100083
2. 钢铁研究总院高温材料研究所, 北京 100081
3. 北京科技大学材料科学与工程学院, 北京 100083
EFFECT OF HAFNIUM CONTENT ON MORPHOLOGY EVOLUTION OF γ′ PRECIPITATES IN P/M Ni–BASED SUPERALLOY
ZHANG Yiwen 1,2, WANG Fuming 1, HU Benfu 3
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083
2. High Temperature Material Institute, Central Iron and Steel Research Institute, Beijing 100081
3. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083
全文: PDF(2472 KB)  
摘要: 研究了含Hf镍基粉末高温合金在长期时效处理过程中γ'相形态的演化过程.结果表明: 合金在高温长期处理过程中立方状γ'相发生分裂,呈现出二重平行状和八重小立方体组态, 八重小立方体组态作为择优形态不再发生分裂, 处于低能稳定状态. 不同Hf含量合金的错配度发生明显变化, γ'相的长大或粗化过程可以粗略地分为“界面控制”和“应变控制”2个阶段, γ'相间弹性相互作用能对合金中析出相的形态变化起着重要作用.
关键词 粉末高温合金 Ni3(Al, Ti) γ'相形态稳定性    
Abstract:The cubic γ′ particle morphology evolution was studied during long time aging process in a powder metallurgy (P/M) Ni–based superalloy with Hf addition. The results show that, during long time aging process, the cubic  γ′ particle splits into a doublet of plantes or an octet of cubes. The octet of cubes with low energy is a preferred shape, it splits no longer. The γ/γ′ lattice misfit varies with different Hf contents. The growth or coarsening process of  γ′ precipitate can be roughly divided into interface controlling and strain controlling stages, the  γ′ precipitate morphology is greatly influenced by the elastic interaction energy between  γ′ particles.
Key wordspowder metallurgy superalloy    Ni3(Al, Ti)     γ&prime    phase morphology stability
收稿日期: 2012-03-14     
ZTFLH: 

TG113.12

 
基金资助:

国家重点基础研究发展计划项目2010CB631204和中俄政府间科技合作项目CR14-20资助

通讯作者: 张义文     E-mail: yiwen64@126.com
作者简介: 张义文, 男, 1964年生, 教授级高工, 博士生

引用本文:

张义文 王福明 胡本芙. Hf含量对镍基粉末高温合金中γ'相形态的影响[J]. 金属学报, 2012, 48(8): 1011-1017.
ZHANG Xi-Wen, YU Fu-Meng, HU Ben-Fu. EFFECT OF HAFNIUM CONTENT ON MORPHOLOGY EVOLUTION OF γ′ PRECIPITATES IN P/M Ni–BASED SUPERALLOY. Acta Metall Sin, 2012, 48(8): 1011-1017.

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2012.00136      或      https://www.ams.org.cn/CN/Y2012/V48/I8/1011

[1] Maniar G N, Bridge J E. Metall Trans, 1971; 2: 95

[2] Muzyka D R. Met Eng Q, 1971; 11: 12

[3] Hu B F, Liu G Q, Wu K, Tian G F. Acta Metall Sin, 2012; 48: 257

(胡本芙, 刘国权, 吴 凯, 田高峰. 金属学报, 2012; 48: 257)

[4] Kotval P S, Venables J D, Calder R W. Metall Trans, 1972; 3: 453

[5] Duhl D N, Sullivan C P. J Met, 1971; 23: 38

[6] Dahl J M, Danesi W F, Dunn R G. Metall Trans, 1973; 4: 1087

[7] Maslenkov S B, Burova N N, Khangulov V V. Met Sci Heat Treat, 1980; 22: 283

[8] Miner R V. Metall Trans, 1977; 8A: 259

[9] Khachaturyan A G, Airapetyan V M. Phys Status Solidi, 1974; 26: 611

[10] Qiu Y Y. Acta Mater, 1996; 44: 4969

[11] Yoo Y S. Scr Mater, 2005; 53: 81

[12] Zhang Y W, Wang F M, Hu B F. Acta Metall Sin, 2012; 48: 187

(张义文, 王福明, 胡本芙. 金属学报, 2012; 48: 187)

[13] Lifshitz I M, Slyozov V V. J Phys Chem Solids, 1961; 19: 35

[14] Khachaturyan A G, Semenovskaya S V, Morris Jr J W. Acta Metall, 1988; 36: 1563

[15] Kaufman M J, Voorhees P W, Johnson W C, Biancaniello F S. Metall Mater Trans, 1989; 20A: 2171

[16] Grosdidier T, Hazotte A, Simon A. Mater Sci Eng, 1998; A256: 183

[17] Banerjee D, Banerjee R, Wang Y. Scr Mater, 1999; 41: 1023

[18] Qiu Y Y. J Alloys Compd, 1998; 270: 145

[19] Cha P R, Yeon D H, Chung S H. Scr Mater, 2005; 52: 1241

[20] Miyazaki T, Imamura H, Kozakai T. Mater Sci Eng, 1982; 54: 9

[21] Doi M, Miyazaki T, Wakatsuki T. Mater Sci Eng, 1984; 67: 247
[1] 张国庆,张义文,郑亮,彭子超. 航空发动机用粉末高温合金及制备技术研究进展[J]. 金属学报, 2019, 55(9): 1133-1144.
[2] 冯业飞,周晓明,邹金文,王超渊,田高峰,宋晓俊,曾维虎. 粉末高温合金中SiO2夹杂物与基体的界面反应机理及对其变形行为的影响[J]. 金属学报, 2019, 55(11): 1437-1447.
[3] 田甜, 郝志博, 贾崇林, 葛昌纯. 新型第三代粉末高温合金FGH100L的显微组织与力学性能[J]. 金属学报, 2019, 55(10): 1260-1272.
[4] 张明, 刘国权, 胡本芙. 镍基粉末高温合金热加工变形过程中显微组织不稳定性对热塑性的影响[J]. 金属学报, 2017, 53(11): 1469-1477.
[5] 张义文,胡本芙. 拓扑密堆μ相对含Hf的镍基粉末高温合金组织和性能的影响*[J]. 金属学报, 2016, 52(4): 445-454.
[6] 张义文,胡本芙. 镍基粉末高温合金中微量元素Hf的作用*[J]. 金属学报, 2015, 51(8): 967-975.
[7] 张义文,韩寿波,贾建,刘建涛,胡本芙. 微量元素Hf对镍基粉末高温合金FGH97显微组织的影响[J]. 金属学报, 2015, 51(10): 1219-1226.
[8] 马文斌,刘国权,胡本芙,贾成厂. 镍基粉末高温合金FGH96中原始粉末颗粒边界的形成机理[J]. 金属学报, 2013, 49(10): 1248-1254.
[9] 宁永权 姚泽坤. FGH4096粉末高温合金的再结晶形核机制[J]. 金属学报, 2012, 48(8): 1005-1010.
[10] 胡本芙 刘国权 吴凯 田高峰. 镍基粉末冶金高温合金中γ'相形态不稳定性研究[J]. 金属学报, 2012, 48(3): 257-263.
[11] 宁永权 姚泽坤 谢兴华 郭鸿镇 谭立军 陶宇. 热模锻造+直接时效粉末高温合金的强化机制[J]. 金属学报, 2010, 46(3): 324-328.
[12] 谢锡善; 张丽娜; 张麦仓; 董建新 . 镍基粉末高温合金中夹杂物的微观力学行为研究[J]. 金属学报, 2002, 38(6): 635-642 .
[13] 李晓; 董建新; 张丽娜; 张麦仓; 胡尧和; 谢锡善; 国为民 . 疲劳保载时间与固溶处理对PM René 95合金高温裂纹扩展速率的影响[J]. 金属学报, 2001, 37(10): 1059-1063 .
[14] 高庆;章守华;胡本芙;李慧英. 粉末Rene'95高温合金中项链组织的形成[J]. 金属学报, 1996, 32(10): 1019-1022.