定向凝固NiAl-Cr(Mo)-Hf(Ho)共晶合金的组织与性能
肖旋1;谢亿2;郭建亭3
1. 沈阳理工大学材料科学与工程学院; 沈阳 110168
2. 湖南省电力公司试验研究院; 长沙 410007
3. 中国科学院金属研究所; 沈阳 110016
MICROSTRUCTURES AND MECHANICAL PROPERTIES OF DIRECTIONALLY SOLIDIFIED NiAl–Cr(Mo)–Hf(Ho) EUTECTIC ALLOY
XIAO Xuan 1; XIE Yi 2; GUO Jianting 3
1. School of Materials Science and Engineering; Shenyang Ligong University; Shenyang 110168
2. Hunan Electric Power Test and Research Institute; Changsha 410007
3. Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110016
引用本文:

肖璇 谢亿 郭建亭. 定向凝固NiAl-Cr(Mo)-Hf(Ho)共晶合金的组织与性能[J]. 金属学报, 2010, 46(6): 701-707.
, , . MICROSTRUCTURES AND MECHANICAL PROPERTIES OF DIRECTIONALLY SOLIDIFIED NiAl–Cr(Mo)–Hf(Ho) EUTECTIC ALLOY[J]. Acta Metall Sin, 2010, 46(6): 701-707.

全文: PDF(3711 KB)  
摘要: 

通过液态金属冷却技术制备了名义成分为Ni-30.4Al-34Cr-4.3Mo-0.1Hf-0.05Ho(原子分数, \%)的定向合金. 定向凝固工艺消除了普通铸造合金中的初生Cr(Mo)相, 获得了共晶组织. 随抽拉速率从8 mm/min提高到15 mm/min, 合金中的共晶胞尺寸从115 μm减小到85 μm, 共晶胞间距变窄, 胞间混乱区减少. 与普通铸造相比,定向凝固工艺能提高该共晶合金的室温、高温拉伸强度, 高温拉伸塑性以及室温断裂韧度,并且定向合金的上述力学性能随抽拉速率增大而增大.

关键词 NiAl合金 定向凝固工艺 显微组织 力学性能    
Abstract

The alloy with nominal composition of Ni-30.4Al-34Cr-4.3Mo-0.1Hf-0.05Ho (atomic fraction, %) has been directionally solidified at two withdrawal rates by liquid metal (Sn) cooling (LMC) process. Compared to the as-cast alloy, directional solidification process eliminates primary Cr(Mo) phase. With increasing withdrawal rate from 8 to 15 mm/min, the diameter of NiAl/Cr(Mo) eutectic cell decreases from 115 to 85 μm. In addition, the intercellular spaces and disordered regions become less. In virtue of the disappearance of primary Cr(Mo) phase, the mechanical properties of directionally solidified alloys are better than those of as--cast alloy and are further improved with increasing withdrawal rate.

Key wordsNiAl alloy    directional solidification    microstructure    mechanical property
收稿日期: 2009-10-10     
作者简介: 肖璇, 女, 1966年生, 副教授

[1] Noebe R D, Bowman R R, Nathal N V. Int Mater Rev, 1993; 38: 193
[2] Miracle D B. Acta Metall Mater, 1993; 41: 649
[3] Johnson D R, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 493
[4] Yang J M, Jeng S M, Bain K, Amato R A. Acta Metall Mater, 1997; 45: 295
[5] Johnson D R, Chen X F, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 99
[6] Walter J L, Cline H E. Metall Trans, 1970; 1: 1221
[7] Cline H E, Walter J L. Metall Trans, 1970; 1: 2907
[8] Cline H E, Walter J L, Lifshine E, Russell R R. Metall Trans, 1971; 2: 189
[9] Chen X F, Johnson D R, Noebe R D, Oliver B F. J Mater Res, 1995; 10: 1159
[10] Raj S V, Locci I E. Intermetallics, 2001; 9: 217
[11] Whittenberger J D, Raj S V, Locci I E, Salem J A. Intermetallics, 1999; 7: 1159
[12] Raj S V, Locci I E, Salem J A, Pawlik R J. Metall Mater Trans, 2002; 33A: 597
[13] Jachson K H, Hunt J D. Trans Metall Soc AIME, 1966; 236: 1129
[14] Whittenberger J D, Locci I E, Darolia R, Bowman R R. Mater Sci Eng, 1999; A268: 165
[15] Takeyama M, Liu C T. J Mater Res, 1990; 5: 1189
[16] Guo J T, Cui C Y, Qi Y H, Ye H Q. J Alloys Compd, 2002; 343: 142
[17] Guo J T, Huai K W, Gao Q, Ren W L, Li G S. Intermetallics , 2007; 15: 727
[18] Ren W L, Guo J T, Li G S, Zhou J. Mater Lett, 2003; 57: 1374

[1] 张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿. K439B铸造高温合金800℃长期时效组织与性能演变[J]. 金属学报, 2023, 59(9): 1253-1264.
[2] 卢楠楠, 郭以沫, 杨树林, 梁静静, 周亦胄, 孙晓峰, 李金国. 激光增材修复单晶高温合金的热裂纹形成机制[J]. 金属学报, 2023, 59(9): 1243-1252.
[3] 郑亮, 张强, 李周, 张国庆. /降氧过程对高温合金粉末表面特性和合金性能的影响:粉末存储到脱气处理[J]. 金属学报, 2023, 59(9): 1265-1278.
[4] 宫声凯, 刘原, 耿粒伦, 茹毅, 赵文月, 裴延玲, 李树索. 涂层/高温合金界面行为及调控研究进展[J]. 金属学报, 2023, 59(9): 1097-1108.
[5] 张健, 王莉, 谢光, 王栋, 申健, 卢玉章, 黄亚奇, 李亚微. 镍基单晶高温合金的研发进展[J]. 金属学报, 2023, 59(9): 1109-1124.
[6] 陈礼清, 李兴, 赵阳, 王帅, 冯阳. 结构功能一体化高锰减振钢研究发展概况[J]. 金属学报, 2023, 59(8): 1015-1026.
[7] 李景仁, 谢东升, 张栋栋, 谢红波, 潘虎成, 任玉平, 秦高梧. 新型低合金化高强Mg-0.2Ce-0.2Ca合金挤压过程中的组织演变机理[J]. 金属学报, 2023, 59(8): 1087-1096.
[8] 丁桦, 张宇, 蔡明晖, 唐正友. 奥氏体基Fe-Mn-Al-C轻质钢的研究进展[J]. 金属学报, 2023, 59(8): 1027-1041.
[9] 孙蓉蓉, 姚美意, 王皓瑜, 张文怀, 胡丽娟, 仇云龙, 林晓冬, 谢耀平, 杨健, 董建新, 成国光. Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为[J]. 金属学报, 2023, 59(7): 915-925.
[10] 袁江淮, 王振玉, 马冠水, 周广学, 程晓英, 汪爱英. Cr2AlC涂层相结构演变对力学性能的影响[J]. 金属学报, 2023, 59(7): 961-968.
[11] 吴东江, 刘德华, 张子傲, 张逸伦, 牛方勇, 马广义. 电弧增材制造2024铝合金的微观组织与力学性能[J]. 金属学报, 2023, 59(6): 767-776.
[12] 侯娟, 代斌斌, 闵师领, 刘慧, 蒋梦蕾, 杨帆. 尺寸设计对选区激光熔化304L不锈钢显微组织与性能的影响[J]. 金属学报, 2023, 59(5): 623-635.
[13] 张东阳, 张钧, 李述军, 任德春, 马英杰, 杨锐. 热处理对选区激光熔化Ti55531合金多孔材料力学性能的影响[J]. 金属学报, 2023, 59(5): 647-656.
[14] 刘满平, 薛周磊, 彭振, 陈昱林, 丁立鹏, 贾志宏. 后时效对超细晶6061铝合金微观结构与力学性能的影响[J]. 金属学报, 2023, 59(5): 657-667.
[15] 李殿中, 王培. 金属材料的组织定制[J]. 金属学报, 2023, 59(4): 447-456.