Effect of Aging Treatment on Mechanical Property and H2S Resistant Behavior of Acicular Ferrite Pipeline Steels |
ZHAO Mingchun; SHAN Yiyin; YANG Ke |
Institute of Metal Research; The Chinese Academy of Sciences; Shenyang 110016 |
|
Cite this article:
ZHAO Mingchun; SHAN Yiyin; YANG Ke. Effect of Aging Treatment on Mechanical Property and H2S Resistant Behavior of Acicular Ferrite Pipeline Steels. Acta Metall Sin, 2004, 40(9): 948-954 .
|
Abstract Hot-rolled acicular ferrite pipeline steel plate
can be further strengthened by aging treatment. After an
aging treatment at 600 ℃ for 10 h, the acicular ferrite pipeline steel
plate is strengthened to the level of X 100 while its impact toughness
does not obviously decrease. At the same time, its H2S
cracking resistant ability is also improved obviously. All
these can be attributed to the additional precipitation
of micro-alloyed carbonitrides, the transformation of
martensite/austenite (M/A) islands to tempering martensite
and the improvement of the uniformity in acicular ferrite
microstructure during aging treatment.
|
Received: 25 September 2003
|
|
[1] Kaneko T, Ikeda A. Trans Iron Steel Inst Jpn, 1988; 28: 575 [2] Margot-Marette H, Bardou G, Charbonnier J C. Corros Sci, 1987; 27: 1009 [3] Yong Q L, Ma M T, Wu B R. Microalloy Steel-Physical, Mechanic and Metallurgy. Beijing: China Machine Industry Press,1989: 84(雍岐龙,马鸣图,吴宝榕.微合金钢--物理和力学冶金.北京:机械工业出版社, 1989:84) [4] Echaniz G, Morales C, Perez T. In: Corrosion/98, Houston, Texas: NACE, 1998: 120 [5] Watkins M, Ayer R. In: Corrosion/95, Houston, Texas: NAGE, 1995: 50 [6] Ikeda A, Kowaka M. Chem Econ Eng Rev, 1978; 10: 1 [7] Lopez H F, Bharadwaj R, Albarran J L, Martinez L. Met-all Mater Trans, 1999; 30A: 2419 [8] Zhao M C, Tang B, Shan Y Y, Yang K. Metall Mater Trans, 2003; 34A: 1089 [9] Zhao M C. PhD Dissertation, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang, 2003(赵明纯.中国科学院金属研究所博士学位论文,沈阳,2003) [10] NACE Standard TM0177-96, Laboratory Testing of Metals for Resistance to Specific Forms of Environmental Cracking in H2S Environments, 1996, NACE [11] Smith Y E, Coldren A P, Cryderman R L. Toward An- proved Ductility and Toughness. Tokyo: Climax Molybdenum Company Ltd., 1972:119 [12] Lutz M, translated by Zhao H. Optimum of Mechanical Property on Strip Steel During Control Rolling and Control Cooling. Beijing: Metallurgical Industry Press, 1996: 41(Lutz M著,赵辉译.带钢轧制过程中材料性能的优化.北京:冶金工业出版社, 1996:41) [13] Yoshie A, Fujioka M, Watanabe Y, Nishioka K, MorikawaH. ISIJ Int, 1992; 32: 395 [14] Dong Z Q, Zhou S C. Metal Material and Heat Treatment.Changsha: Central South University of Technology Press,1989; 202(邓至谦,周善初.金属材料及热处理.长沙:中南工业大学出版社,1989:202) [15] Li H L, Guo S W, Feng Y R, Huo C Y, Chai H F. An Illustrative Collection of Micro structure Micrographs. Beijing: Petroleum Industry Press, 2001: 11(李鹤林,郭生武,冯耀荣,霍春勇,柴惠芬.高强度微合金管线钢显微组织分析与鉴别图谱.北京:石油工业出版社,2001:111 [16] Liu Y X. Heat Treatment for Metals. Beijing: China Machine Industry Press, 1981: 61(刘云旭.金属热处理原理.北京:机械工业出版社,1981:61) [17] Cui Z Q. Metallurgy and Heat Treatment. Beijing: China Machine Industry Press, 1997: 258(崔忠圻.金属学与热处理(铸造、焊接专业用).北京:机械工业出版社,1997:258) |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|