(NiTi)50-0.5xNbx形状记忆合金的阻尼性能及力学性能

金属学报

2009, Vol. 45

Issue (1): 18-24

论文

本期目录 | 过刊浏览

(NiTi)_50-0.5xNb_x形状记忆合金的阻尼性能及力学性能

肖甫¹;赵新青¹;徐惠彬¹;姜海昌²;戎利建²

1 北京航空航天大学材料科学与工程学院; 北京 100083
2 中国科学院金属研究所; 沈阳 110016

DAMPING CAPACITY AND MECHANICAL PROPERTY OF
NiTiNb SHAPE MEMORY ALLOYS

XIAO Fu¹; ZHAO Xinqing¹; XU Huibin¹;JIANG Haichang²; RONG Lijian²

1 School of Materials Science and Engineering; Beijing University of Aeronautics and Astronautics; Beijing 100083
2 Institute of Metal Research; Chinese Academy of Sciences; Shenyang 110016

引用本文:

肖甫赵新青徐惠彬姜海昌戎利建. (NiTi)_50-0.5xNb_x形状记忆合金的阻尼性能及力学性能[J]. 金属学报, 2009, 45(1): 18-24.
. DAMPING CAPACITY AND MECHANICAL PROPERTY OF
NiTiNb SHAPE MEMORY ALLOYS[J]. Acta Metall Sin, 2009, 45(1): 18-24.

全文: PDF(1075 KB)

摘要:

通过加入Nb制备了具有双相组织的(NiTi)_50-0.5xNb_x (x=5, 10, 15, 20)形状记忆合金,合金兼具高阻尼性能和高屈服强度. 随着Nb含量x的增大, 合金中(NiTi+β-Nb)共晶组织比例含量增加, 合金轧制样品在马氏体状态自协作屈服强度随之升高, 在x=15时达到最高(289 MPa); 同时, 合金轧制样品保持高阻尼性能, 本征阻尼性能tanδ>0.01, 并随x增大而升高. 根据形状记忆合金阻尼理论以及NiTiNb形状记忆合金的阻尼性能随温度的变化规律, 探讨了β---Nb和NiTi相界面阻尼对合金阻尼性能的影响.

关键词 ： NiTiNb形状记忆合金, 马氏体相变, 阻尼性能, 屈服强度

Abstract：

Two-phase NiTi base alloys (NiTi)_50-0.5xNb_x (x=5, 10, 15, 20) with both high damping capacity and high yield strength have been prepared by addition of Nb. With increasing Nb content, the fraction of eutectic (NiTi+β--Nb) increases, and yield strength in martensite state rises. When x=15, the yield strength reaches the highest value of 289 MPa. And the alloys also exhibit high damping capacity, tanδ>0.01. According to the damping mechanism for the shape memory alloys, the relationship between the damping properties and temperatures of NiTiNb alloys was explained, and phase boundary damping from the β-Nb and NiTi phases was discussed.

Key words： NiTiNb shape memory alloy martensite phase transformation damping capacity yield strength

收稿日期: 2008-05-21

ZTFLH:

TG113.22

基金资助:

国家高技术研究发展计划项目2006AA03Z102和航空自然科学基金项目2006ZF51069资助

作者简介: 肖甫, 男, 1981年生, 博士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	赵新青
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2009/V45/I1/18

[1] Otsuka K, Ren X. Prog Mater Sci, 2005; 50: 511
[2] Van Humbeeck J. J Alloys Compd, 2003; 355: 58
[3] Cai W, Lu X L, Zhao L C. Mater Sci Eng, 2005; A394: 78
[4] Wu S K, Lin H C. J Alloys Compd, 2003; 355: 72
[5] Cai W, Meng X L, Zhao L C. Curr Opin Solid State Mater Sci, 2005; 9: 296
[6] Xiao F, Ma G J, Zhao X Q, Xu H B, Jiang H C, Rong L J. Proc SPIE, 2007; 6423: 64232L
[7] Rajagopalan S, Little A L, Bourke M A M, Vaidyanathan R. Appl Phys Lett, 2005; 86: 081901
[8] Schaller R. J Alloys Compd, 2003; 355: 131
[9] Piao M, Miyazaki S, Otsuka K, Nishida N. Mater Trans JIM, 1992; 33: 337
[10] Piao M, Miyazaki S, Otsuka K. Mater Trans JIM, 1992; 33: 346
[11] Zhao X Q, Yan X M, Yang Y Z, Xu H B. Mater Sci Eng, 2006; A575: 438
[12] He X M, Rong L J, Yan D S, Li Y Y. Mater Sci Eng, 2004; A371: 193
[13] Bidaux J E, Schaller R, Benoit W. Acta Metall, 1989; 37: 803
[14] San Juan J, No M L. J Alloys Compd, 2003; 355: 65
[15] P´er´ez–Saez R B, Recarte V, No M L, San Juan J. Phys Rev, 1998; 57B: 5684
[16] San Juan J, No M L. Mater Sci Eng, 2006; A442: 429
[17] Ritchie I G, Pan Z L. Metall Trans, 1991; 22A: 607
[18] Xiao F, Zhao X Q, Xu H B, Jiang H C, Rong L J. Chin J Aeronaut, 2009; 22: in press
[19] Melton K N, Mercier O. Acta Metall, 1981; 29: 393

[1]	姜江, 郝世杰, 姜大强, 郭方敏, 任洋, 崔立山. NiTi-Nb原位复合材料的准线性超弹性变形[J]. 金属学报, 2023, 59(11): 1419-1427.
[2]	李伟, 贾兴祺, 金学军. 高强韧QPT工艺的先进钢组织调控和强韧化研究进展[J]. 金属学报, 2022, 58(4): 444-456.
[3]	沈国慧, 胡斌, 杨占兵, 罗海文. 回火温度对含 δ 铁素体高铝中锰钢力学性能和显微组织的影响[J]. 金属学报, 2022, 58(2): 165-174.
[4]	原家华, 张秋红, 王金亮, 王灵禺, 王晨充, 徐伟. 磁场与晶粒尺寸协同作用对马氏体形核及变体选择的影响[J]. 金属学报, 2022, 58(12): 1570-1580.
[5]	王金亮, 王晨充, 黄明浩, 胡军, 徐伟. 低应变预变形对变温马氏体相变行为的影响规律及作用机制[J]. 金属学报, 2021, 57(5): 575-585.
[6]	王玉, 胡斌, 刘星毅, 张浩, 张灏云, 官志强, 罗海文. 退火温度对含Nb高锰钢力学和阻尼性能的影响[J]. 金属学报, 2021, 57(12): 1588-1594.
[7]	左良, 李宗宾, 闫海乐, 杨波, 赵骧. 多晶Ni-Mn-X相变合金的织构化与功能行为[J]. 金属学报, 2021, 57(11): 1396-1415.
[8]	肖飞, 陈宏, 金学军. 形状记忆合金弹热制冷效应的研究现状[J]. 金属学报, 2021, 57(1): 29-41.
[9]	王世宏, 李健, 柴锋, 罗小兵, 杨才福, 苏航. 固溶温度对Fe-19Mn合金的γ→ε相变和阻尼性能的影响[J]. 金属学报, 2020, 56(9): 1217-1226.
[10]	王世宏,李健,葛昕,柴锋,罗小兵,杨才福,苏航. γ/ε双相Fe-19Mn合金在拉伸变形过程中的组织演变和加工硬化行为[J]. 金属学报, 2020, 56(3): 311-320.
[11]	郑晓航, 宁睿, 段佳彤, 蔡伟. Ti₇₀_-_xTa₁₅Zr₁₅Fe_x (x=0.3、0.6、1.0)形状记忆合金薄膜的马氏体相变与阻尼行为[J]. 金属学报, 2020, 56(12): 1690-1696.
[12]	陈雷, 郝硕, 梅瑞雪, 贾伟, 李文权, 郭宝峰. 节约型双相不锈钢TRIP效应致塑性增量及其固溶温度依赖性[J]. 金属学报, 2019, 55(11): 1359-1366.
[13]	崔立山, 姜大强. 基于应变匹配的高性能金属纳米复合材料研究进展[J]. 金属学报, 2019, 55(1): 45-58.
[14]	姚彦桃, 陈礼清, 王文广. 原位反应浸渗法制备(B₄C+Ti)混杂增强Mg及AZ91D复合材料及其阻尼性能[J]. 金属学报, 2019, 55(1): 141-148.
[15]	魏铖, 柯常波, 马海涛, 张新平. 基于序参量梯度的改进相场模型及对大尺度体系马氏体相变的模拟研究[J]. 金属学报, 2018, 54(8): 1204-1214.

Viewed

Full text

Abstract

Cited

Shared

Discussed