奥氏体不锈钢钎焊界面裂纹形成机制研究 |
张青科,裴夤崟,龙伟民 |
郑州机械研究所新型钎焊材料与技术国家重点实验室, 郑州 450001 |
|
INVESTIGATIONS ON FORMATION MECHANISMS OF BRAZING CRACKS AT THE AUSTENITIC STAINLESS STEEL/FILLER METAL BRAZING JOINT INTERFACES |
ZHANG Qingke, PEI Yinyin, LONG Weimin |
State Key Laboratory of Advanced Brazing Filler Metals and Technology, Zhengzhou Research Institute of Mechanical Engineering, Zhengzhou 450001 |
引用本文:
张青科,裴夤崟,龙伟民. 奥氏体不锈钢钎焊界面裂纹形成机制研究[J]. 金属学报, 2013, 49(10): 1177-1184.
ZHANG Qingke,
PEI Yinyin,
LONG Weimin.
INVESTIGATIONS ON FORMATION MECHANISMS OF BRAZING CRACKS AT THE AUSTENITIC STAINLESS STEEL/FILLER METAL BRAZING JOINT INTERFACES[J]. Acta Metall Sin, 2013, 49(10): 1177-1184.
[1] Han E H. Acta Metall Sin, 2011; 47: 769
(韩恩厚. 金属学报, 2011; 47: 769)
[2] Han E H, Wang J Q, Wu X Q, Ke W. Acta Metall Sin, 2010; 46: 1379
(韩恩厚, 王俭秋, 吴欣强, 柯伟. 金属学报, 2010; 46: 1379)
[3] Sanyasi R, Ali Y A-K. Weld J, 2010; 89(2): 46
[4] Shankar V, Gill T P S, Mannan S L, Sundaresan S. Sci Technol Weld Join, 2000; 5(2): 91
[5] Shankar V, Gill T P S, Mannan S L, Sundaresan S. Sadhana, 2003; 28: 359
[6] Shankar V, Gill T P S, Mannan S L, Terrance A L E, Sundaresan S. Metall Mater Trans, 2000;31A: 3109
[7] Shankar V, Gill T P S, Mannan S L, Sundaresan S. Mater Sci Eng, 2003; A343: 170
[8] Shinoda T,~Miyake H, Matsuzaka T, Matsumoto T,~Kanai H. Mater Sci Technol, 1992; 8: 913
[9] Zhang L T, Wang J Q. Acta Metall Sin, 2013; 49: 911
(张利涛, 王俭秋. 金属学报, 2013; 49: 911)
[10] Lin S B, Song J L, Yang C L, Ma G C. Acta Metall Sin, 2009; 45: 1211
(林三宝, 宋建岭, 杨春利, 马广超. 金属学报, 2009; 45: 1211)
[11] Qin G L, Su Y H, Wang S J. Acta Metall Sin, 2012; 48: 1018
(秦国梁, 苏玉虎, 王术军. 金属学报, 2012; 48: 1018)
[12] Jiang W C, Gong J M, Chen H, Tu S D. Acta Metall Sin, 2008; 44: 105
(蒋文春, 巩建鸣, 陈虎, 涂善东. 金属学报, 2008; 44: 105)
[13] Savage W F, Nippes E F. Weld J, 1978; 57(5): 145
[14] Ji J, Jing X G, Zhang W Y. Trans China Weld Inst, 2004; 25(3): 124
(季杰, 井绪贵, 张文钺. 焊接学报, 2004; 25(3): 124)
[15] Lee H W, Sung J H. Sci Technol Weld Join, 2005; 10(2): 145
[16] Holbert Jr R K, Dobbins A G, Bennett Jr R K. Weld J, 1987; 66(8): 38
[17] Radhakrishnan V M. Sci Technol Weld Join, 2000; 5(1): 40
[18] Li L, Messler Jr R W. Weld J, 1999; 78(12): 387
[19] Nelson T W, Lippold J C, Lin W, Baeslack W A III. Weld J, 1997; 76(5): 110
[20] Zacharia T. Weld J, 1995; 74(1): 164
[21] Neidel A, Riesenbeck S. J Fail Anal Preven, 2011; 11: 473
[22] Ogawa T, Tsunetomi E. Weld Res Sup, 1982; 3: 82
[23] Srinivasan G, Divya M, Albert S K, Bhaduri A K, Klenk A, Achar D R G.Weld World, 2010; 54(11-12): R322
[24] Berecz T, Majlinger K, Orbulov I N, Szabo P J. Mater Sci Forum, 2013; 729: 442
[25] Atabaki M M, Wati J N, Idris J. Weld J, 2013; 92(3): 57
[26] Liu W, Tian Y, Zhang X. Weld J, 1994; 73(9): 297 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|