金属学报  2012, Vol. 48 Issue (5): 519-525    DOI: 10.3724/SP.J.1037.2011.00741

论文 本期目录 | 过刊浏览 |

5052铝合金板材磁脉冲动态拉伸塑性失稳分析

刘大海1,于海平2,李春峰2

1. 南昌航空大学航空制造工程学院, 南昌 330063 2. 哈尔滨工业大学材料科学与工程学院, 哈尔滨 150001

PLASTIC INSTABILITY ANALYSIS OF 5052 ALUMINUM SHEETS IN MAGNETIC DYNAMIC TENSION PROCESS

LIU Dahai1,YU Haiping2, LI Chunfeng2

1.School of Aeronautical Manufacturing Engineering, Nanchang Hangkong University, Nanchang 330063 2.School of Materials Science and Engineering, Harbin Institute of Technology,Harbin 150001

刘大海,于海平,李春峰. 5052铝合金板材磁脉冲动态拉伸塑性失稳分析[J]. 金属学报, 2012, 48(5): 519-525.
, , . PLASTIC INSTABILITY ANALYSIS OF 5052 ALUMINUM SHEETS IN MAGNETIC DYNAMIC TENSION PROCESS[J]. Acta Metall Sin, 2012, 48(5): 519-525.

摘要 参考文献 相关文章 Metrics 全文: PDF(4053 KB)   摘要: 为揭示磁脉冲成形的增塑机制, 采用理论分析与微观组织观察相结合的方法对5052铝合金板材磁脉冲动态拉伸过程中动态成形行为和塑性失稳机制进行了系统研究. 结果表明, 惯性力在动态成形中起主要作用,惯性力对试样的结构失稳具有抑制作用, 从而使试样的塑性提高并产生分散失稳;5052铝合金动态成形和准静态成形的成形性质相似, 不会产生特殊的组织结构,塑性变形机制均为位错滑移机制; 准静态成形过程以均匀单系位错滑移为主,断裂伴随着位错的缠结和攀移; 而动态成形过程中, 位错滑移趋于多系开动,在大面积区域出现明显的交滑移现象, 且滑移带较准静态成形时窄且密,位错组态更均匀; 动态成形的多系滑移和位错均化作用可在比准静态成形高的多的塑性应变水平下形成, 从而使材料表现出较高的塑性和强度. 关键词 ： 铝合金,  磁脉冲成形,  塑性失稳,  单向拉伸     Abstract：In order to reveal the hyperplasticity mechanism of electromagnetic forming (EMF), the plastic instability mechanisms and formation behaviors of 5052 aluminum alloy sheets in pulsed magnetic tension process were investigated by theoretical analysis and microanalysis. Results show that inertia force plays an important role in dynamic forming, which has the suppression effect on structural instability and thus improves the formability of sheet and spreads instability. The nature of dynamic formation is much similar with that of quasi--static formation and no special formation structures arise in dynamic process for 5052 aluminum alloy sheets. The formation mechanism of both processes is dislocation slip mechanism. For quasi--static formation, the dislocations show a uniform single--slip pattern, fracture combined with dislocation tangling and climbing. While for dynamic formation, dislocation system tends to more slips, large areas showing clear cross-slip structures. The dislocation bands are narrower and much denser than those shown in the quasi--static process, and a much more uniform dislocation configuration is also exhibited after pulsed magnetic loadings. The characteristics of multi--slips and uniform effect of dislocations under pulsed magnetic loading conditions will result in much higher plasticity and strength of materials. Key words： aluminum alloy    electromagnetic forming    plastic instability    uniaxial tension 收稿日期: 2011-11-30      基金资助: 国家自然科学基金资助项目51105190 作者简介: 刘大海, 男, 1981年生, 讲师, 博士 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 刘大海 于海平 李春峰 44.8K 链接本文: https://www.ams.org.cn/CN/10.3724/SP.J.1037.2011.00741      或      https://www.ams.org.cn/CN/Y2012/V48/I5/519 [1] Li C F.  High Energy Rate Forming. Beijing: National Defense Industry Press, 2001: 1     (李春峰. 高能率成形技术. 北京: 国防工业出版社, 2001: 1) [2] Psyk V, Risch D, Kinsey B L, Tekkaya A E, Kleiner M.  J Mater Process Technol, 2011; 5: 787 [3] Vohnout V J.  PhD Thesis, Ohio State University, Columbus, 1998 [4] Balanethiram V S, Daehn G S.  Scr Metall, 1992; 27: 1783 [5] Balanethiram V S, Daehn G S.  Scr Metall, 1994; 30: 515 [6] Balanethiram V S, Hu X Y, Daehn G S.  J Mater Process Technol,1994; 45: 595 [7] Hu X Y, Wagoner R H, Daehn G S, Ghosh S.  Metall Trans,1994; 25A: 2723 [8] Hu X Y, Daehn G S.  Acta Mater, 1996; 44: 1021 [9] Oliveira D A, Worswick M J.  J Phys IV France, 2003; 110: 293 [10] Oliveira D A, Worswick M J, Finn M, Newman D.  J Mater Process Technol, 2005; 170: 350 [11] Imbert J M, Winkler S L, Worswick M J, Oliveira D A.  J Eng Mater Technol, 2005; 27: 127 [12] Seth M.  PhD Thesis, Ohio State University, Columbus, 2006 [13] Thomas J D, Seth M, Daehn G S, Bradley J R, Triantafyllidis N. Acta Mater, 2007; 55: 2863 [14] Regazzoni G, Kocks U F, Follansbee P S.  Acta Mater, 1987; 35: 2865 [15] Follansbee P S, Kocks U F.  Acta Mater, 1988; 36: 81 [16] Gorham D A.  J De Phys III, 1991; 1: 411 [17] Dioh N N, Leevers P S, Williams J G.  Polymer, 1993; 34: 4230 [18] Meyers M A.  Dynamic Behavior of Materials. New York: Wiley, 1994 [19] Golovashchenko S F.  J Mater Eng Perform, 2007; 16: 314 [20] Hecker S S.  J Eng Mater Technol, 1975; 97H: 66 [21] Blazynsk T Z, translated by Li F Q, Wu B Q.  Explosive Welding,Forming and Compaction. Beijing: China Machine Press, 1983: 76      (Blazynsk T Z著, 李富勤, 吴柏青译. 爆炸焊接、成形与压制.北京: 机械工业出版社, 1983: 76)   [1] 王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新. 不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界[J]. 金属学报, 2023, 59(7): 947-960. [2] 夏大海, 计元元, 毛英畅, 邓成满, 祝钰, 胡文彬. 2024铝合金在模拟动态海水/大气界面环境中的局部腐蚀机制[J]. 金属学报, 2023, 59(2): 297-308. [3] 高建宝, 李志诚, 刘佳, 张金良, 宋波, 张利军. 计算辅助高性能增材制造铝合金开发的研究现状与展望[J]. 金属学报, 2023, 59(1): 87-105. [4] 马志民, 邓运来, 刘佳, 刘胜胆, 刘洪雷. 淬火速率对7136铝合金应力腐蚀开裂敏感性的影响[J]. 金属学报, 2022, 58(9): 1118-1128. [5] 宋文硕, 宋竹满, 罗雪梅, 张广平, 张滨. 粗糙表面高强铝合金导线疲劳寿命预测[J]. 金属学报, 2022, 58(8): 1035-1043. [6] 王春辉, 杨光昱, 阿热达克·阿力玛斯, 李晓刚, 介万奇. 砂型3DP打印参数对ZL205A合金铸造性能的影响[J]. 金属学报, 2022, 58(7): 921-931. [7] 田妮, 石旭, 刘威, 刘春城, 赵刚, 左良. 预拉伸变形对欠时效7N01铝合金板材疲劳断裂的影响[J]. 金属学报, 2022, 58(6): 760-770. [8] 高川, 邓运来, 王冯权, 郭晓斌. 蠕变时效对欠时效7075铝合金力学性能的影响[J]. 金属学报, 2022, 58(6): 746-759. [9] 苏凯新, 张继旺, 张艳斌, 闫涛, 李行, 纪东东. 微弧氧化6082-T6铝合金的高周疲劳性能及残余应力松弛机理[J]. 金属学报, 2022, 58(3): 334-344. [10] 王冠杰, 李开旗, 彭力宇, 张壹铭, 周健, 孙志梅. 高通量自动流程集成计算与数据管理智能平台及其在合金设计中的应用[J]. 金属学报, 2022, 58(1): 75-88. [11] 赵婉辰, 郑晨, 肖斌, 刘行, 刘璐, 余童昕, 刘艳洁, 董自强, 刘轶, 周策, 吴洪盛, 路宝坤. 基于Bayesian采样主动机器学习模型的6061铝合金成分精细优化[J]. 金属学报, 2021, 57(6): 797-810. [12] 孙佳孝, 杨可, 王秋雨, 季珊林, 包晔峰, 潘杰. 5356铝合金TIG电弧增材制造组织与力学性能[J]. 金属学报, 2021, 57(5): 665-674. [13] 陈军洲, 吕良星, 甄良, 戴圣龙. AA 7055铝合金时效析出强化模型[J]. 金属学报, 2021, 57(3): 353-362. [14] 刘刚, 张鹏, 杨冲, 张金钰, 孙军. 铝合金中的溶质原子团簇及其强韧化[J]. 金属学报, 2021, 57(11): 1484-1498. [15] 李吉臣, 冯迪, 夏卫生, 林高用, 张新明, 任敏文. 非等温时效对7B50铝合金组织及性能的影响[J]. 金属学报, 2020, 56(9): 1255-1264. Viewed Full text Abstract Cited   Shared      Discussed