金属学报  2011, Vol. 47 Issue (7): 917-920    DOI: 10.3724/SP.J.1037.2011.00156

论文 本期目录 | 过刊浏览 |

CLAM钢在600 ℃长期时效过程中的组织与性能变化

杨春光1), 严伟1), 王威1),  单以银1), 杨柯1), 吴宜灿2)

1) 中国科学院金属研究所, 沈阳 110016 2) 中国科学院等离子体物理研究所, 合肥 230031

CHANGES OF MICROSTRUCTURE AND MECHANICAL PROPERTY OF THE CLAM STEEL AFTER LONG TERM AGING AT 600 ℃

YANG Chunguang1), YAN Wei1), WANG Wei1), SHAN Yiyin1), YANG Ke1), WU Yican2)

1) Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 2) Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031

杨春光 严伟 王威 单以银 杨柯 吴宜灿. CLAM钢在600 ℃长期时效过程中的组织与性能变化[J]. 金属学报, 2011, 47(7): 917-920.
. CHANGES OF MICROSTRUCTURE AND MECHANICAL PROPERTY OF THE CLAM STEEL AFTER LONG TERM AGING AT 600 ℃[J]. Acta Metall Sin, 2011, 47(7): 917-920.

摘要 参考文献 相关文章 Metrics 全文: PDF(806 KB)   摘要: 研究了CLAM钢在600 ℃时效1100 和3000 h后的显微组织与力学性能变化. 结果表明, 随着时效时间的延长, CLAM钢中析出相的数量逐渐增多, 尺寸增大. 时效1100 h时, CLAM钢的强度略有提高; 时效至3000 h时, CLAM钢强度又有所降低. 与原始热处理态相比, 时效1100 h后CLAM钢的韧脆转变温度升高, 但时效时间延长到3000 h时, 韧脆转变温度又降低到原始热处理态水平. 根据钢中析出相在时效过程中的析出和粗化行为, 解释了CLAM钢时效不同时间后强度、冲击韧性和韧脆转变温度的变化, 同时还指出钢中较低的W含量可以有效延缓钢中Laves相的析出. 关键词 ： CLAM钢,  时效,  力学性能,  第二相     Abstract：China low activation martensitic (CLAM) steel is a new reduced activation ferritic/martensitic steel developed in China to use for blanket/first-wall structures of the D-T fusion reactor. The microstructures and mechanical properties of the CLAM steel after aging at 600 ℃ for 1100  and 3000 h were investigated by SEM and TEM. The results showed that the prior austenite grain size did not increase with increasing aging time, while the precipitates at grain boundaries and inside grains were increased. The strength of CLAM steel was slightly increased after aging for 1100 h. When the aging time was prolonged to 3000 h, the strength of CLAM steel was decreased due to coarsening of precipitates. The ductile-brittle transition temperature (DBTT) was increased after aging for 1100 h. However, when the aging time increased to 3000 h, the DBTT lowered to the as heat-treated level. The changes of strength, toughness and DBTT after aging were interpreted from the view points of precipitation and coarsening behaviors of precipitates. It was also noticed that the low W content in the CLAM steel can effectively postpone the formation of Laves phase. Key words： CLAM steel    aging    mechanical property    second phase 收稿日期: 2011-03-23      基金资助: 国家重点基础研究发展计划项目2008CB717802, 国家科技重大专项项目2009GB109002和中国科学院知识创新工程重要方向项目KJCX2-YW-N35资助 作者简介: 杨春光, 男, 1982年生, 博士 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 单以银 44.8K 链接本文: https://www.ams.org.cn/CN/10.3724/SP.J.1037.2011.00156      或      https://www.ams.org.cn/CN/Y2011/V47/I7/917 [1] Bloom E E. J Nucl Mater, 1998; 258–263: 7 [2] Tamura M, Hayakawa H, Tanmura M, Hishnuma A, Kondo T. J Nucl Mater, 1986; 141–143: 1067 [3] Yamanouchi N, Tamura M, Hayakawa H, Hishinuma A, Kondo T. J Nucl Mater, 1992; 191–194: 822 [4] Jitsukawa S, Tamura M, van der Schaaf B, Klueh R L, Alamo A, Petersen C, Schirra M, Spaetig P, Odette G R, Tavassoli A A, Shiba K, Kohyama A, Kimura A. J Nucl Mater, 2002; 307–311: 179 [5] Kimura A, Kasada R, Kohyama A, Tanigawa H, Hirose T, Shiba K, Jitsukawa S, Ohtsuka S, Ukai S, Sokolov M A, Klueh R L, Yamamoto T, Odette G R. J Nucl Mater, 2007; 367–370: 60 [6] Klueh R L, Alexander D J, Kenik E A. J Nucl Mater, 1995; 227: 11 [7] Huang Q Y, Li J G, Chen Y X. J Nucl Mater, 2004; 329–333: 268 [8] Fern´andez P, Lancha A M, Lape˜na J, Hern´andez–Mayoral M. Fusion Eng Des, 2001; 58–59: 787 [9] Hu P, Yan W, Sha W, Wang W, Guo Z L, Shan Y Y, Yang K. Front Mater Sci China, 2009; 3: 434 [10] Abe F, Noda T, Okada M. J Nucl Mater, 1992; 195: 51 [11] Li Q. Metall Mater Trans, 2006; 37A: 89 [12] Bhandarkar M D, Bhat M S, Parker E R, Zackey V F. Metall Trans, 1976; 7A: 753 [1] 张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿. K439B铸造高温合金800℃长期时效组织与性能演变[J]. 金属学报, 2023, 59(9): 1253-1264. [2] 宫声凯, 刘原, 耿粒伦, 茹毅, 赵文月, 裴延玲, 李树索. 涂层/高温合金界面行为及调控研究进展[J]. 金属学报, 2023, 59(9): 1097-1108. [3] 张健, 王莉, 谢光, 王栋, 申健, 卢玉章, 黄亚奇, 李亚微. 镍基单晶高温合金的研发进展[J]. 金属学报, 2023, 59(9): 1109-1124. [4] 郑亮, 张强, 李周, 张国庆. 增/降氧过程对高温合金粉末表面特性和合金性能的影响：粉末存储到脱气处理[J]. 金属学报, 2023, 59(9): 1265-1278. [5] 李景仁, 谢东升, 张栋栋, 谢红波, 潘虎成, 任玉平, 秦高梧. 新型低合金化高强Mg-0.2Ce-0.2Ca合金挤压过程中的组织演变机理[J]. 金属学报, 2023, 59(8): 1087-1096. [6] 陈礼清, 李兴, 赵阳, 王帅, 冯阳. 结构功能一体化高锰减振钢研究发展概况[J]. 金属学报, 2023, 59(8): 1015-1026. [7] 丁桦, 张宇, 蔡明晖, 唐正友. 奥氏体基Fe-Mn-Al-C轻质钢的研究进展[J]. 金属学报, 2023, 59(8): 1027-1041. [8] 袁江淮, 王振玉, 马冠水, 周广学, 程晓英, 汪爱英. Cr2AlC涂层相结构演变对力学性能的影响[J]. 金属学报, 2023, 59(7): 961-968. [9] 吴东江, 刘德华, 张子傲, 张逸伦, 牛方勇, 马广义. 电弧增材制造2024铝合金的微观组织与力学性能[J]. 金属学报, 2023, 59(6): 767-776. [10] 梁凯, 姚志浩, 谢锡善, 姚凯俊, 董建新. 新型耐热合金SP2215组织与性能的关联性[J]. 金属学报, 2023, 59(6): 797-811. [11] 张东阳, 张钧, 李述军, 任德春, 马英杰, 杨锐. 热处理对选区激光熔化Ti55531合金多孔材料力学性能的影响[J]. 金属学报, 2023, 59(5): 647-656. [12] 侯娟, 代斌斌, 闵师领, 刘慧, 蒋梦蕾, 杨帆. 尺寸设计对选区激光熔化304L不锈钢显微组织与性能的影响[J]. 金属学报, 2023, 59(5): 623-635. [13] 刘满平, 薛周磊, 彭振, 陈昱林, 丁立鹏, 贾志宏. 后时效对超细晶6061铝合金微观结构与力学性能的影响[J]. 金属学报, 2023, 59(5): 657-667. [14] 王长胜, 付华栋, 张洪涛, 谢建新. 冷轧变形对高性能Cu-Ni-Si合金组织性能与析出行为的影响[J]. 金属学报, 2023, 59(5): 585-598. [15] 王滨, 牛梦超, 王威, 姜涛, 栾军华, 杨柯. 含Cu马氏体时效不锈钢的组织与强韧性[J]. 金属学报, 2023, 59(5): 636-646. Viewed Full text Abstract Cited   Shared      Discussed