基于过冷奥氏体动态相变的热轧TRIP钢组织控制 II. 动态相变后冷却速率 |
尹云洋1;3;杨王玥1;李龙飞2;孙祖庆2;王西涛2 |
1. 北京科技大学材料科学与工程学院; 北京 100083
2. 北京科技大学新金属材料国家重点实验室; 北京 100083
3. 武汉钢铁(集团)公司研究院; 武汉 430080 |
|
MICROSTRUCTURE CONTROL OF HOT ROLLED TRIP STEEL BASED ON DYNAMIC TRANSFORMATION OF UNDERCOOLED AUSTENITE
II. Cooling Rate After Dynamic Transformation of Undercooled Austenite |
YIN Yunyang 1;3; YANG Wangyue 1; LI Longfei 2; SUN Zuqing 2; WANG Xitao 2 |
1. School of Materials Science and Engineering; University of Science & Technology Beijing; Beijing 100083
2. State Key Laboratory for Advanced Metals and Materials; University of Science & Technology Beijing; Beijing 100083
3. Research and Development Center; Wuhan Iron and Steel (Group) Corp.; Wuhan 430080 |
引用本文:
尹云洋 杨王玥 李龙飞 孙祖庆 王西涛. 基于过冷奥氏体动态相变的热轧TRIP钢组织控制 II. 动态相变后冷却速率[J]. 金属学报, 2010, 46(2): 161-166.
,
,
,
,
.
MICROSTRUCTURE CONTROL OF HOT ROLLED TRIP STEEL BASED ON DYNAMIC TRANSFORMATION OF UNDERCOOLED AUSTENITE
II. Cooling Rate After Dynamic Transformation of Undercooled Austenite[J]. Acta Metall Sin, 2010, 46(2): 161-166.
[1] Zackay V F, Parker E R, Fahr D, Bush R. Trans ASM, 1967; 60: 252
[2] Traint S, Pichler A, Hauzenberger K, Stiaszny P, Werner E. Steel Res, 2002; 73: 259
[3] Van der Zwaag S, Zhao L, Suzelotte O, Sietsma J. ISIJ Int, 2002; 42: 1565
[4] Sakuma Y, Matsumura O, Takechi H. Metall Trans, 1991; 22A: 489
[5] Koh H, Lee S, Park S, Choi S J, Kwon S J, Kim N J. Scr Mater, 1998; 38: 763
[6] Ryu H B, Speer J G, Wise J P. Metall Mater Trans, 2002; 33A: 2811
[7] Girault E, Mertens A, Jacques P, Houbaert Y, Verlinden B, ven Humbeeck J. Scr Mater, 2001; 44: 885
[8] Krizan D, de Cooman B C, Antonissen J. In: Baker M A ed., Int Conf on Advanced High Strength Sheet for Automotive Applications Proceedings, Winter Park, Colorado, 2004: 205
[9] Yin Y Y, Yang W Y, Li L F, Sun Z Q, Wang X T. Acta Metall Sin, 2008; 44: 1299
(尹云洋, 杨王玥,李龙飞, 孙祖庆, 王西涛. 金属学报, 2008; 44: 1299)
[10] Yin Y Y, Yang W Y, Li L F, Sun Z Q, Wang X T. Acta Metall Sin, 2008; 44: 686
(尹云洋, 杨王玥,李龙飞, 孙祖庆, 王西涛. 金属学报, 2008; 44: 686)
[11] Yin Y Y, Yang W Y, Li L F, Sun Z Q, Wang X T. Acta Metall Sin, 2010; 46: 155
(尹云洋, 杨王玥,李龙飞, 孙祖庆, 王西涛. 金属学报, 2010; 46: 155)
[12] Yang W Y, Qi J J, Zun Z Q, Yang P. Acta Metall Sin,2004; 40: 135
(杨王玥,齐俊杰, 孙祖庆, 杨平. 金属学报, 2004; 40: 135)
[13] Dong H, Sun X J. Curr Opin Solid State & Mater Sci, 2005; 9: 269
[14] Matsumura O, Sakuma Y, Takechi H. Trans ISIJ, 1987; 27: 570
[15] Hanlon D N, Sietma J, Van der Zwaag S. ISIJ Int, 2001; 41: 1028
[16] Liu Z Y, Yang Z G, Li Z D, Zhang C, Sheng G. Acta Metall Sin, 2008; 44: 703
(刘志远, 杨志刚, 李昭东, 张 弛, 盛广. 金属学报, 2008; 44: 703)
[17] Yu Y N. Fundamentals of Materials Science. Beijing: Higher Education Press, 2006: 720
(余永宁. 材料科学基础. 北京: 高等教育出版社, 2006: 720)
[18] Kim S K, Shin H C, Chung J H, Chang Y W. Inst Met Mater, 1998; 36: 151 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|