金属学报  1998, Vol. 34 Issue (6): 591-596

论文 本期目录 | 过刊浏览 |

一种单晶镍基合金蠕变期间γ'相的定向粗化机制

田素贵;周惠华;张静华;杨洪才;徐永波;胡壮麒

中国科学院金属研究所材料疲劳与断裂国家重点实验室;东北大学材料科学与工程系;沈阳工业;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;东北大学材料科学与工程系;沈阳;110006;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015;中国科学院金属研究所材料疲劳与断裂国家重点实验室;沈阳;110015

A DIRECTIONAL COARSENING MECHANISM OF THE γ＇-PHASE DURING CREEP OF A SINGLE CRYSTAL NICKEL-BASE SUPERALLOY

TIAN Sugui ; ZHOU Huihua ; ZHANG Jinghua; YANG Hongcai ; XU Yongbo;HU Zhuangqi ( State Key Laboratory for Fatigue and Fracture of Materials; Institute of Metal Research; The Chinese Academyof Sciences; Shenyang 110015)( Department of Materials Science and Engineering; Northeastern University ; Shenyang 110006)( Department of Materials Science and Engineering; Shenyang Polytechnic University; Shenyang 110023)Correspondent: TIAN Sugui; associate professor Tel: (024)5927399

田素贵;周惠华;张静华;杨洪才;徐永波;胡壮麒. 一种单晶镍基合金蠕变期间γ'相的定向粗化机制[J]. 金属学报, 1998, 34(6): 591-596.
, , , , , . A DIRECTIONAL COARSENING MECHANISM OF THE γ＇-PHASE DURING CREEP OF A SINGLE CRYSTAL NICKEL-BASE SUPERALLOY[J]. Acta Metall Sin, 1998, 34(6): 591-596.

摘要 参考文献 相关文章 Metrics 全文: PDF(2039 KB)   摘要: 对[001]取向单晶镍基合金恒载拉伸蠕变不同阶段的组织形貌进行了SEM，TEM观察和EDAX成分分析，研究了γ＇相定向粗化过程及机理结果表明：蠕变初期，两相邻γ＇相呈侧平面对接方式，沿垂直于应力轴方向定向生长为类似筛网的核状组织，外加应力使γ＇／γ界面共格应变减少，应变能降低，释放的能量是促使合金元素定向扩散形成筏状γ＇结构的驱动力． 关键词 ： 单晶镍基合金,  蠕变,  定向粗化,  扩散驱动力     Abstract：The microstructures of a [001] single crystal nickel--base superalloy at differentstages of the constant loading tensile creep were observed by means of TEM and SEM, and thechemical compositions of γ and γ＇ phases were analyzed by EDAX in order to investigate theprocess and mechanism of the directional coarsening of γ＇ phase. The results showed that themesh--like rafts were formed along the direction normal to the stress axis in a mode of side--planelink in primary creep. The applied stress resulted in the decrease of the coherent strain and theenergy of the γ＇/γ interfaces. Thus, the energy released was supposed to be the driving force forthe directional diffusion of elements, leading to the formation of the γ＇ rafts. Key words： single crystal nickel-base superalloy    creep    directional coarsening    diffusion driving force 收稿日期: 1998-06-18      基金资助:国家自然科学基金!59571039 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 田素贵 周惠华 张静华 杨洪才 徐永波 胡壮麒 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I6/591 1Tien J K, Copley S M. Metoall Trans, 1971; 2: 215 2 Nathalal M L, Ebert L J. Scr, Metall 1983; 17: 1151 3 Mackay R A,Ebert L J .Scr,Metall 1983;17:1217 4 Pollock T M, Argon A S. Acto Metall Mater 1994; 42: 1859 5 Glatzel U, Feller-Knirpmeier M. Scr Metall 1989; 23: 1839 6 Socrate S, Parks D M. Acto Metall Mater 1993; 41: 2185 7 Muller L, Glatzel U, Feller-Kniepmeier M. Acta Metall Mater 1992; 40: 1321 8 彭志方, Glatzel U, Feller—Kniepmeier M.金属学报, 1995; 31: A531 (Peng Z F ,Glatzel U,Feller—Kniepmeier M.Acta Metall Sin 1995;31:A531) 9 秦高梧,郝士明.金属学报,1995;31:B485 (Qin G W, Hao S M. Acta Metall Sin 。, 1995; 31: B485) 10Svetlov I L, Golovko B A, Epishin A I, Abalakin N P. Scr Metall Mater 1992; 26: 1353 11Duval S, Chambleland S, Caron P, Blavette D. Acto Metall Mater 1994; 42: 185 12 Pcollock T M,Argon A S.In:Kassanger R D,Deye D J eds.Superalloys ,Warrendale Pa:A I M E,1988:285 13 Veron M, Brechet Y, Louchet P. In: Kassanger R D, Depe D J eds. Superalloys, Warrendale, Pa: A I M E, 1996:181 14 Nabarro F R N. Metall Mater Trans , 1996; 27A: 513 [1] 陈佳, 郭敏, 杨敏, 刘林, 张军. 新型钴基高温合金中W元素对蠕变组织和性能的影响[J]. 金属学报, 2023, 59(9): 1209-1220. [2] 冯强, 路松, 李文道, 张晓瑞, 李龙飞, 邹敏, 庄晓黎. γ' 相强化钴基高温合金成分设计与蠕变机理研究进展[J]. 金属学报, 2023, 59(9): 1125-1143. [3] 白佳铭, 刘建涛, 贾建, 张义文. 高W高Ta型粉末高温合金的蠕变性能及溶质原子偏聚[J]. 金属学报, 2023, 59(9): 1230-1242. [4] 李小琳, 刘林锡, 李雅婷, 杨佳伟, 邓想涛, 王海丰. 单一 MX 型析出相强化马氏体耐热钢力学性能及蠕变行为[J]. 金属学报, 2022, 58(9): 1199-1207. [5] 高川, 邓运来, 王冯权, 郭晓斌. 蠕变时效对欠时效7075铝合金力学性能的影响[J]. 金属学报, 2022, 58(6): 746-759. [6] 彭子超, 刘培元, 王旭青, 罗学军, 刘健, 邹金文. 不同服役条件下FGH96合金的蠕变特征[J]. 金属学报, 2022, 58(5): 673-682. [7] 杨志昆, 王浩, 张义文, 胡本芙. Ta含量对镍基粉末高温合金高温蠕变变形行为和性能的影响[J]. 金属学报, 2021, 57(8): 1027-1038. [8] 张倪侦, 马昕迪, 耿川, 穆永坤, 孙康, 贾延东, 黄波, 王刚. Ag元素添加对Cu-Zr-Al基金属玻璃纳米压痕行为的影响[J]. 金属学报, 2021, 57(4): 567-574. [9] 徐静辉, 李龙飞, 刘心刚, 李辉, 冯强. 热力耦合对一种第四代镍基单晶高温合金1100℃蠕变组织演变的影响[J]. 金属学报, 2021, 57(2): 205-214. [10] 郭倩颖, 李彦默, 陈斌, 丁然, 余黎明, 刘永长. 高温时效处理对S31042耐热钢组织和蠕变性能的影响[J]. 金属学报, 2021, 57(1): 82-94. [11] 刘天, 罗锐, 程晓农, 郑琦, 陈乐利, 王茜. 形成Al2O3表层的奥氏体不锈钢加速蠕变实验研究[J]. 金属学报, 2020, 56(11): 1452-1462. [12] 吴静,刘永长,李冲,伍宇婷,夏兴川,李会军. 高Fe、Cr含量多相Ni3Al基高温合金组织与性能研究进展[J]. 金属学报, 2020, 56(1): 21-35. [13] 胡斌,李树索,裴延玲,宫声凯,徐惠彬. <111>取向小角偏离对一种镍基单晶高温合金蠕变性能的影响[J]. 金属学报, 2019, 55(9): 1204-1210. [14] 唐文书,肖俊峰,李永君,张炯,高斯峰,南晴. 再热恢复处理对蠕变损伤定向凝固高温合金γ′相的影响[J]. 金属学报, 2019, 55(5): 601-610. [15] 逯世杰, 王虎, 戴培元, 邓德安. 蠕变对焊后热处理残余应力预测精度和计算效率的影响[J]. 金属学报, 2019, 55(12): 1581-1592. Viewed Full text Abstract Cited   Shared      Discussed