金属学报  2009, Vol. 45 Issue (4): 390-395    
  论文 本期目录 | 过刊浏览 |
时效处理对极低碳针状铁素体钢组织和力学性能的影响
郭爱民1;2; 邹德辉1;2; 易伦雄3 ; 董汉雄1; 李平和1 ; 刘 凯4; 吴开明4
1. 武汉钢铁(集团)公司研究院; 武汉 430080
2. 武汉大学动力与机械学院; 武汉 430072
3. 中铁大桥勘测设计院; 武汉 430050
4.武汉科技大学冶金工业过程系统科学湖北省重点实验室; 武汉 430081
EFFECTS OF AGING ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF ULTRALOW CARBON ACICULAR FERRITE STEEL
GUO Aimin 1;2; ZOU Dehui1;2; YI Lunxiong3; DONG Hanxiong1; LI Pinghe1; LIU Kai4; WU Kaiming4
1.Institute of Research; Wuhan Iron and Steel (Group) Company;Wuhan 430080
2.School of Power and Mechanical Engineering; Wuhan University; Wuhan 430072
3.China Zhongtie Major Bridge Reconnaissance & Design Institute o. Ltd.; Wuhan 430050
4.Hubei Province Key Laboratory of Systems Science in Metallurgical Processing;Wuhan University of Science and Technology; Wuhan 430081
引用本文:

郭爱民 邹德辉 易伦雄 董汉雄 李平和 刘凯 吴开明. 时效处理对极低碳针状铁素体钢组织和力学性能的影响[J]. 金属学报, 2009, 45(4): 390-395.
, , , , , . EFFECTS OF AGING ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF ULTRALOW CARBON ACICULAR FERRITE STEEL[J]. Acta Metall Sin, 2009, 45(4): 390-395.

全文: PDF(3006 KB)  
摘要: 

利用光学显微镜、扫描电镜和透射电镜研究了变温时效对极低碳针状铁素体钢组织和性能的影响规律. 结果表明: 450---500 ℃时效处理时, 第二相析出较少, 组织无明显粗化,强度无明显变化; 550---650 ℃时效时, 强度快速上升, 主要是ε--Cu和Nb(C, N)第二相粒子的弥散析出所致; 650 ℃以上时效时, 发生过时效现象, 铁素体板条和第二相粒子粗化, 导致强度迅速下降; 时效温度达到750 ℃时进入两相区, 局部富C和合金元素富集区域先奥氏体化, 时效后冷却过程中形成了高碳的M/A组织, 使钢的韧性迅速恶化.

关键词 极低碳钢针状铁素体时效ε--Cu 沉淀    
Abstract

The effects of aging temperature on the microstructure and mechanical property of ultra–low–carbon acicular ferrite steel was studied by utilizing OM, SEM, TEM, tensile and impact tests. The strength of the specimen is not obviously changed due to little precipitating amount of the second phase and little coarsening of microstructure when aged from 450 to 500 ℃. The rapid increase in strength appears and is attributed to the dispersive precipitations of  ε–Cu and Nb(C, N) when aged from 550 to 650℃. When aged above 650 ℃, the abrupt decrease in strength appears and is caused by over–aging, i.e., the coalescence of ferrite plates and coarsening of precipitates. When aged at 750℃ (in two–phase field), the toughness decreases abruptly, which is related to the formation of martensite/austenite (M/A) ithigher carbon content during cooling.

Key wordsultra--low--carbon steel    acicular ferrite    aging     ε--Cu    precipitation
收稿日期: 2007-05-28     
ZTFLH: 

TG113

 
基金资助:

国家重点基础研究发展计划资助项目2004CB19102

作者简介: 郭爱民, 男, 1965年生, 教授级高级工程师

[1] Wu K M, Li Z G. In: Xie Q H, Xu L J, eds., Proceeding 2nd Baosteel Biennial Academic Conference, Shanghai: Shanghai Scientific and  echnological Literature Publishing House, 2006: 403
(吴开明, 李自刚. 见: 谢企华, 徐乐江主编, 第二届宝钢学术会议论文集, 上海: 上海科学技术文献出版社, 2006: 403)
[2] Wu K M, Li Z G. J Iron Steel Res, 2007; 19(10): 1
(吴开明, 李自刚. 钢铁研究学报, 2007; 19(10): 1)
[3] Wang H B, Kim Y G, Lee S, Kim Y M, Kim N J, Yoo J Y. Metal Mater Trans, 2005; 36A: 2107
[4] Xiao F R, Liao B, Shan Y Y, Qiao G Y, Zhong Y, Zhang C, Yang K. Mater Sci Eng, 2006; A431: 41
[5] Shin S Y, Hwang B, Kim S, Lee S. Mater Sci Eng, 2006; A429: 196
[6] Morrison W B. In: Liu G Q, Wang F M, Wang Z B, Zhang H T, eds., Proc of HSLA Steels 2000, Beijing: Metallurgical Industry Press, 2000: 11
[7] Wang X M, He X L, Yang S W, Shang C J. ISIJ Int, 2002; 42: 1553
[8] Yang S W, Wang X M, Shang C J, He X L. J Univ Tech Beijing (Engl Ed), 2001; 8: 214
[9] Lee J L. Acta Metall Mater, 1994; 42: 3291
[10] Yang J R, Huang C Y, Huang C F. J Mater Sci, 1995; 30: 5036
[11] Gregg J M, Bhadeshia H K D H. Acta Mater, 1997; 45: 739
[12] Barbaro F J, Krauklis P, Easterling K E. Mater Sci Technol, 1989; 5: 1057
[13] Ricks R A, Howell P R, Barritle G S. J Mater Sci, 1982;17: 732
[14] Madariaga I, Romero S L, Guti´errez I. Metall Mater Trans, 1998; 29A: 1003
[15] Guo A M, Li S R, Guo J, Li P H, Ding Q F, Wu K M, He X L. Mater Charact, 2008, 59: 134
[16] Wu K M, Li Z G, Guo A M, He X L, Zhang L Q, Fang A H, Cheng L. ISIJ Int, 2006; 46: 161
[17] Wu K M. Scr Mater, 2006; 54: 569
[18] Wu K M, Inagawa Y, Enomoto M. Mater Charact, 2004; 52: 121
[19] Itman A, Cardoso K R, Kestenbach H J. Iron Steel Vana dium Titanium, 1998; 19(2): 59
(Itman A, Cardoso K R, Kestenbach H J. 钢铁钒钛, 1998, 19(2): 59)
[20] Yong Q L, Ma M T, Wu B R. Microalloyed Steel—Physics and Mechanics Metallurgy. Beijing: China Machine Press, 1989: 501
(雍歧龙, 马鸣图, 吴宝榕. 微合金钢—物理和力学冶金. 北京: 机械工业出版社,, 1989: 501)

[1] 张雷雷, 陈晶阳, 汤鑫, 肖程波, 张明军, 杨卿. K439B铸造高温合金800℃长期时效组织与性能演变[J]. 金属学报, 2023, 59(9): 1253-1264.
[2] 梁凯, 姚志浩, 谢锡善, 姚凯俊, 董建新. 新型耐热合金SP2215组织与性能的关联性[J]. 金属学报, 2023, 59(6): 797-811.
[3] 王长胜, 付华栋, 张洪涛, 谢建新. 冷轧变形对高性能Cu-Ni-Si合金组织性能与析出行为的影响[J]. 金属学报, 2023, 59(5): 585-598.
[4] 刘满平, 薛周磊, 彭振, 陈昱林, 丁立鹏, 贾志宏. 后时效对超细晶6061铝合金微观结构与力学性能的影响[J]. 金属学报, 2023, 59(5): 657-667.
[5] 王滨, 牛梦超, 王威, 姜涛, 栾军华, 杨柯. Cu马氏体时效不锈钢的组织与强韧性[J]. 金属学报, 2023, 59(5): 636-646.
[6] 马国楠, 朱士泽, 王东, 肖伯律, 马宗义. SiC颗粒增强Al-Zn-Mg-Cu复合材料的时效行为和力学性能[J]. 金属学报, 2023, 59(12): 1655-1664.
[7] 巩向鹏, 伍翠兰, 罗世芳, 沈若涵, 鄢俊. 自然时效对Al-2.95Cu-1.55Li-0.57Mg-0.18Zr合金160℃人工时效的影响[J]. 金属学报, 2023, 59(11): 1428-1438.
[8] 侯旭儒, 赵琳, 任淑彬, 彭云, 马成勇, 田志凌. 热输入对电弧增材制造船用高强钢组织与力学性能的影响[J]. 金属学报, 2023, 59(10): 1311-1323.
[9] 耿遥祥, 唐浩, 许俊华, 张志杰, 喻利花, 鞠洪博, 江乐, 简江林. 选区激光熔化高强Al-(Mn, Mg)-(Sc, Zr)合金成形性及力学性能[J]. 金属学报, 2022, 58(8): 1044-1054.
[10] 田妮, 石旭, 刘威, 刘春城, 赵刚, 左良. 预拉伸变形对欠时效7N01铝合金板材疲劳断裂的影响[J]. 金属学报, 2022, 58(6): 760-770.
[11] 高川, 邓运来, 王冯权, 郭晓斌. 蠕变时效对欠时效7075铝合金力学性能的影响[J]. 金属学报, 2022, 58(6): 746-759.
[12] 任平, 陈兴品, 王存宇, 俞峰, 曹文全. 预变形和双级时效对Fe-30Mn-11Al-1.2C奥氏体低密度钢显微组织和力学性能的影响[J]. 金属学报, 2022, 58(6): 771-780.
[13] 袁波, 郭明星, 韩少杰, 张济山, 庄林忠. 添加3%ZnAl-Mg-Si-Cu合金非等温时效析出行为的影响[J]. 金属学报, 2022, 58(3): 345-354.
[14] 王硕, 王俊升. Al-Li合金中 δ′/θ′/δ复合沉淀相结构演化及稳定性的第一性原理探究[J]. 金属学报, 2022, 58(10): 1325-1333.
[15] 朱士泽, 王东, 王全兆, 肖伯律, 马宗义. Cu含量对SiC/Al-Mg-Si-Cu复合材料自然时效负面效应的影响[J]. 金属学报, 2021, 57(7): 928-936.