金属学报  2012, Vol. 48 Issue (3): 343-350    DOI: 10.3724/SP.J.1037.2011.00517
  论文 本期目录 | 过刊浏览 |
时效对7055铝合金厚板淬透性的影响
刘胜胆, 李承波, 邓运来, 张新明
中南大学材料科学与工程学院教育部有色金属重点实验室, 长沙 410083
INFLUENCE OF AGING ON THE HARDENABILITY OF 7055 ALUMINUM ALLOY THICK PLATE
LIU Shengdan, LI Chengbo, DENG Yunlai, ZHANG Xinming
Key Laboratory of Nonferrous Metals, Ministry of Education, School of Materials Science and Engineering, Central South University, Changsha 410083
全文: PDF(3505 KB)  
摘要: 采用末端淬火实验、光学显微镜、扫描电子显微镜、透射电子显微镜和差示扫描量热法, 研究了时效制度对7055铝合金厚板淬透性的影响. 结果表明: 人工时效前进行长时间的自然时效可提高板材的淬透性, 自然时效和人工时效的淬透深度分别约为78和45 mm, 而自然+人工时效的淬透层深度可达100 mm. 冷却速率减小时, 析出了粗大的$\eta$平衡相, 溶质和空位浓度降低, 时效后的 η'沉淀强化相数量减少, 尺寸增加, 因此硬度降低. 人工时效前的长时间自然时效有利于慢速冷却处形成稳定的 GP区, 最终得到数量更多、分布更均匀弥散、尺寸更细小的$\eta^{\prime}$ 沉淀强化相, 硬度升高, 提高了淬透性.
关键词 7055铝合金厚板淬透性时效    
Abstract:The influence of aging on the hardenability of 7055 aluminum alloy thick plate was investigated by means of end-quench test, optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). The results show that the hardenability can be improved by long time natural aging before artificial aging. The hardened depth is about 78 mm after natural aging and only about 45 mm after artificial aging, but increased to be about 100 mm after natural and artificial aging. During slow quenching, the coarse η equilibrium phase forms, and the solute concentration and vacancy concentration are decreased, which lead to larger and fewer η' hardening precipitates, thus lower hardness after aging. The long time natural aging before artificial aging is favorable for formation of stable GP zones at slowly-cooled locations, and consequently more amount of dispersed and fine η'  hardening precipitates, which give rise to higher hardness and simultaneously better hardenability.
Key words7055 aluminum alloy thick plate    hardenability    aging
收稿日期: 2011-08-10     
ZTFLH: 

TG146.21

 
基金资助:

国家重点基础研究发展计划项目2012CB619501和中南大学自由探索计划项目201012200238资助

通讯作者: 刘胜胆     E-mail: csuliusd@163.com
Corresponding author: LIU Shengdan     E-mail: csuliusd@163.com
作者简介: 刘胜胆, 男, 1980年生, 副教授

引用本文:

刘胜胆 李承波 邓运来 张新明. 时效对7055铝合金厚板淬透性的影响[J]. 金属学报, 2012, 48(3): 343-350.
LIU Qing-Tan, LI Zhang-Bei, DENG Yun-Lai, ZHANG Xin-Meng. INFLUENCE OF AGING ON THE HARDENABILITY OF 7055 ALUMINUM ALLOY THICK PLATE. Acta Metall Sin, 2012, 48(3): 343-350.

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2011.00517      或      https://www.ams.org.cn/CN/Y2012/V48/I3/343

[1] Liu S D, Liu W J, Zhang Y, Zhang X M, Deng Y L. J Alloys Compd, 2010; 507: 53

[2] Robinson J S, Cudd R L, Tanner D A. J Mater Process Technol, 2001; 119: 261

[3] Lim S T, Yun S J, Nam S W. Mater Sci Eng, 2004; A371: 82

[4] Liu S D, Zhong Q M, Zhang Y, Zhang X M. Mater Des, 2010; 31: 3116

[5] Zhang X M, Deng Y L, Zhang Y. Chin Pat, 200710034410.8, 2007

(张新明, 邓运来, 张 勇. 中国专利, 200710034410.8, 2007)

[6] Robson J D, Prangnell P B. Mater Sci Technol, 2002; 18: 607

[7] Liu S D, Zhang X M, You J H, Huang Z B, Zhang C, Zhang X Y. Trans Nonferrous Met Soc China, 2006; 16: 2034

刘胜胆, 张新明, 游江海, 黄振宝, 张翀, 张小艳. 中国有色金属学报, 2006; 16: 2034)

[8] Liu S D, Zhang X M, Chen M A. Trans Nonferrous Met Soc China, 2007; 17: 787

[9] Viana F, Pinto A M P, Santos H M C, Lopes A B. J Mater Process Technol, 1999; 92–93: 54

[10] Park J K, Ardell A J. Mater Sci Eng, 1989; A114: 197

[11] Chen J Z. PhD Thesis, Harbin Institute of Technology, 2008

(陈军洲. 哈尔滨工业大学博士学位论文, 2008)

[12] Hansen V, Stiller K, Waterloo G. Mater Sci Forum, 2002; 396–402: 815

[13] Chinh N O, Lendvi J, Ping D H. J Alloys Compd, 2004; 378: 52

[14] Porter D A, Easterling K E. Phase Transformation in Metals and Alloys. Oxford: Alden Press, 1981: 265

[15] Liu S D, Zhang X M, Chen M A. Mater Charact, 2008; 59: 53
[1] 耿遥祥, 樊世敏, 简江林, 徐澍, 张志杰, 鞠洪博, 喻利花, 许俊华. 选区激光熔化专用AlSiMg合金成分设计及力学性能[J]. 金属学报, 2020, 56(6): 821-830.
[2] 梁孟超, 陈良, 赵国群. 人工时效对2A12铝板力学性能和强化相的影响[J]. 金属学报, 2020, 56(5): 736-744.
[3] 张乐,王威,M. Babar Shahzad,单以银,杨柯. 新型多层金属复合材料的制备与性能[J]. 金属学报, 2020, 56(3): 351-360.
[4] 谭超林,周克崧,马文有,曾德长. 激光增材制造成型马氏体时效钢研究进展[J]. 金属学报, 2020, 56(1): 36-52.
[5] 秦海龙,张瑞尧,毕中南,杜洪标,张金辉. GH4169合金圆盘时效过程残余应力的演化规律研究[J]. 金属学报, 2019, 55(8): 997-1007.
[6] 蔡超,李煬,李劲风,张昭,张鉴清. 2A97 Al-Li合金薄板时效析出与电位及晶间腐蚀的相关性研究[J]. 金属学报, 2019, 55(8): 958-966.
[7] 黄太文,卢晶,许瑶,王栋,张健,张家晨,张军,刘林. ReTa对抗热腐蚀单晶高温合金900 ℃长期时效组织稳定性的影响[J]. 金属学报, 2019, 55(11): 1427-1436.
[8] 朱上,李志辉,闫丽珍,李锡武,张永安,熊柏青. Zn添加对预时效态Al-Mg-Si-Cu合金自然时效和烘烤硬化性的影响[J]. 金属学报, 2019, 55(11): 1395-1406.
[9] 石章智, 张敏, 黄雪飞, 刘雪峰, 张文征. 可时效强化Mg-Sn基合金的研究进展[J]. 金属学报, 2019, 55(10): 1231-1242.
[10] 向雪梅, 赖玉香, 刘春辉, 陈江华. 微合金化元素Sn对Al-Mg-Si合金高温时效强化相析出路径的改变[J]. 金属学报, 2018, 54(9): 1273-1280.
[11] 宋元元, 赵明久, 戎利建. Fe-Ni基合金时效过程中γ'相析出的原子探针层析技术研究[J]. 金属学报, 2018, 54(9): 1236-1244.
[12] 李彦默, 刘晨曦, 余黎明, 李会军, 王祖敏, 刘永长, 李文亚. 高温时效对S31042钢线性摩擦焊接头组织和力学性能的影响[J]. 金属学报, 2018, 54(7): 981-990.
[13] 张宇, 王清, 董红刚, 董闯, 张洪宇, 孙晓峰. 基于团簇模型设计的镍基单晶高温合金(Ni, Co)-Al-(Ta, Ti)-(Cr, Mo, W)及其在900 ℃下1000 h的长期时效行为[J]. 金属学报, 2018, 54(4): 591-602.
[14] 李冬冬, 钱立和, 刘帅, 孟江英, 张福成. Mn含量对Fe-Mn-C孪生诱发塑性钢拉伸变形行为的影响[J]. 金属学报, 2018, 54(12): 1777-1784.
[15] 杨柯, 牛梦超, 田家龙, 王威. 新一代飞机起落架用马氏体时效不锈钢的研究[J]. 金属学报, 2018, 54(11): 1567-1585.