金属学报  2012, Vol. 48 Issue (6): 725-732    DOI: 10.3724/SP.J.1037.2012.00025
  论文 本期目录 | 过刊浏览 |
复合添加Y和Nd对Mg-Li合金显微组织及室温压缩织构的影响
崔崇亮,朱天龙,冷哲,巫瑞智,张景怀,张密林
哈尔滨工程大学材料科学与化学工程学院, 超轻材料与表面技术教育部重点实验室,哈尔滨 150001
EFFECTS OF COMBINED ADDITION OF Y AND Nd ON MICROSTRUCTURE AND TEXTURE AFTER COMPRESSION OF Mg-Li ALLOY AT ROOM TEMPERATURE
CUI Chongliang,ZHU Tianlong,LENG Zhe,WU Ruizhi,ZHANG Jinghuai,ZHANG Milin
Key Laboratory of Superlight Materials and Surface Technology, Ministry of Education, College of Materials Science and Chemical Engineering, Harbin Engineering University, Harbin 150001
引用本文:

崔崇亮,朱天龙,冷哲,巫瑞智,张景怀,张密林. 复合添加Y和Nd对Mg-Li合金显微组织及室温压缩织构的影响[J]. 金属学报, 2012, 48(6): 725-732.
, , , , . EFFECTS OF COMBINED ADDITION OF Y AND Nd ON MICROSTRUCTURE AND TEXTURE AFTER COMPRESSION OF Mg-Li ALLOY AT ROOM TEMPERATURE[J]. Acta Metall Sin, 2012, 48(6): 725-732.

全文: PDF(9262 KB)  
摘要: 采用OM, SEM, XRD, EBSD及电子万能试验机, 对比研究了Mg-5Li-3Al-2Zn和Mg-5Li-3Al-2Zn-1.2Y-0.8Nd铸态合金的显微组织、力学性能以及室温单向压缩后的织构演变. 研究发现, 复合添加Y和Nd 2种稀土元素后, 合金中絮丝状AlLi相明显减少, 晶粒得到显著细化, 平均尺寸在30 μm左右. 2种合金的塑性表现良好, 加入少量稀土的合金室温压缩的变形量可达到27%. 复合添加的稀土元素大幅度降低了Mg晶格的c/a值, 显著弱化了合金的基面织构,激活了锥面滑移系的同时, 也使得室温下少见的柱面滑移被激活.
关键词 YNdMg-Li合金室温压缩织构    
Abstract:Due to the super light-weight property, Mg-Li alloys are very promising in the fields of aerospace and military defense. Up to now, many studies about hot deformation behavior of Mg-Li alloys have been reported. However, there are little researches on their room-temperature deformation behavior. Therefore, the plastic deformation mechanism of Mg-Li alloys needs further investigated. It is known that addition of RE to Mg alloys could cause solid solution strengthening, fine grain strengthening and secondary phase strengthening. Nevertheless, reports refer to the effect of RE on the texture of Mg-Li alloys. This work was devoted to study the microstructure, mechanical properties and the evolution of texture after compression at room-temperature of the as-cast Mg-5Li-3Al-2Zn and Mg-5Li-3Al-2Zn-1.2Y-0.8Nd alloys with OM, SEM, XRD, ODF and EBSD techniques as well as material testing machine. The results show that with the addition of Y and Nd, most of the filamentous AlLi intermetallic compounds are suppressed and substituted by other two intermetallics Al2Y and Al11Nd3. Meanwhile, the grains are refined with the average size of\linebreak 30 μm. ODF analysis indicates that for Mg-5Li-3Al-2Zn alloy, when the strain is 0.17 the C-axis of most grains is roughly 75° form ND, while in Mg-5Li-3Al-2Zn-1.2Y-0.8Nd, when the strain is 0.10 the strong prismatic texture appeares, which means that the <1010> of most grains parallel to ND. Both of the two alloys exhibit high plasticity when tested at room-temperature, while the compression deformation of the alloy containing Y and Nd can reach up to 27%. The combined addition of Y and Nd significantly reduces the c/a of the magnesium lattice, weakes basal texture, activates the pyramidal slip system and, especially, activates the prismatic slip system which seldom occurs at room-temperature in magnesium alloys.
Key wordsY    Nd    Mg-Li alloy    compression at room temperature    texture
收稿日期: 2012-01-11     
ZTFLH: 

TG146.2

 
基金资助:

国家自然科学基金项目51001034, 中央高校基本科研业务费专项资金项目HEUCF201210004以及吉林大学汽车材料教育部重点实验室开放基金项目资助

作者简介: 崔崇亮, 男, 1984年生, 博士生
[1] Wu R Z, Qu Z K, Zhang M L.  Rev Adv Mater Sci, 2010; 24: 14

[2] Liang C P, Gong H R.  J Alloys Compd, 2010; 489: 130

[3] Sasaki T T, Yamamoto K, Honma T.  Scr Mater, 2008; 59: 1111

[4] Wang T, Zhang M L, Niu Z Y, Liu B.  J Rare Earths, 2006; 24: 797

[5] Zhang M L, Meng X R, Wu R Z, Cui C L, Wu L B.  Kovove Mater,2010; 211: 216

[6] Liu X H, G J Du, R Z Wu, Z Y Niu, M L Zhang.  J Alloys Compd,2011; 509: 9558

[7] Li J Q, Qu Z K, Wu R Z, Zhang M L.  Mater Sci Eng, 2011; A528: 3915

[8] Wu L B, Cui C L, Wu R Z, Zhang M L.  Mater Sci Eng, 2011; A528: 2174

[9] Drozd Z, Trojanova Z, Kudela S.  J Alloys Compd, 2004; 378: 192

[10] Mishra R K, Gupta A K, Rao P R, Sachdev A K, Kumar A M, Luo A A. Scr Mater, 2008; 59: 562

[11] Luo J R, Liu Q, Liu W, Godfrey A.  Acta Metall Sin, 2011; 12: 1567

     (罗晋如, 刘庆, 刘伟, Godfrey Andrew. 金属学报, 2011; 12: 1567)

[12] Liu T, Zhang W, Wu S D.  Mater Sci Eng, 2003; A360: 345

[13] Li L, Zhou T T, Li H X, Chen C Q, Wu Q L, Zhang Q Q. Mater Sci Forum, 2007; 546-549: 347

[14] Xiang Q, Wu R Z, Zhang M L.  J Alloys Compd, 2009; 477: 832

[15] Mukai T, Yamanoi M, Watanabe H.  Scr Mater, 2001; 45: 89

[16] Meng X R, Wu R Z, Zhang M L, Wu L B, Cui C L.  J Alloys Compd,2009; 486: 722

[17] Ando S, Tonda H.  Mater Sci Forum, 2000; 350: 43

[18] Agnew S R, Yoo M H, Tome C N.  Acta Metall, 2001; 49: 4277

[19] Stanford N, Atwell D, Barnett M R.  Acta Metall, 2010; 58: 6773

[20] Liu T, Wang Y D, Wu S D.  Scr Mater, 2004; 51: 1057

[21] Dong H W, Wang L D, Wu Y M, Wang L M.  J Alloys Compd,2010; 506: 468

[22] Takuda H, Kikuchi S, Yoshida N, Okahara H.  Mater Trans,2003; 44: 2266

[23] Song Y, Shan D, Chen R, Han E H.  Corros Sci, 2009; 51: 1087

[24] Wei S Q, Zhang M L, Han W, Yan Y D, Zhang B.  Acta Metall Sin,2011; 47: 173

     (魏树权, 张密林, 韩伟, 颜永得, 张斌. 金属学报, 2011; 47: 173)

[25] Ye K, Chen Y, Zhang M L, Han W, Yan Y D, Wei S Q.  Chem Lett,2010; 28: 128

[26] Bohlen J, Yi S, Letzig D, Kainer K U.  Mater Sci Eng,2010; A527: 7092

[27] Hantzsche K, Bohlen J, Wendt J, Kainer K U, Yi S B,Letzig D.  Scr Mater, 2010; 63: 725

[28] Cui C L, Wu L B, Wu R Z, Zhang J H, Zhang M L. J Alloys Compd, 2011; 509: 9045

[29] Koike J.  Mater Sci Forum, 2003; 189: 419

[30] Li T Q, Liu Y B, Cao Z Y, Wu R Z, Zhang M L, Cheng L R,Jiang D M.  J Alloys Compd, 2011; 509: 7607

[31] Guo X T, Liu P J, Zeng D B.  J Chin Rare Earths, 2003; 21: 672

     (郭旭涛, 李培杰, 曾大本. 中国稀土学报, 2003; 21: 672)

[32] Chino Y, Kado M, Mabuchi M.  Mater Sci Eng, 2008; A494: 343

[33] Li Z J, Jin Q L, Jiang Y H, Zhou R.  Acta Metall Sin, 2009; 45: 924

     (李再久, 金青林, 蒋业华, 周荣. 金属学报, 2009; 45: 924)
[1] 常松涛, 张芳, 沙玉辉, 左良. 偏析干预下体心立方金属再结晶织构竞争[J]. 金属学报, 2023, 59(8): 1065-1074.
[2] 孙蓉蓉, 姚美意, 王皓瑜, 张文怀, 胡丽娟, 仇云龙, 林晓冬, 谢耀平, 杨健, 董建新, 成国光. Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为[J]. 金属学报, 2023, 59(7): 915-925.
[3] 张德印, 郝旭, 贾宝瑞, 吴昊阳, 秦明礼, 曲选辉. Y2O3 含量对燃烧合成Fe-Y2O3 纳米复合粉末性能的影响[J]. 金属学报, 2023, 59(6): 757-766.
[4] 李民, 王继杰, 李昊泽, 邢炜伟, 刘德壮, 李奥迪, 马颖澈. Y对无取向6.5%Si钢凝固组织、中温压缩变形和软化机制的影响[J]. 金属学报, 2023, 59(3): 399-412.
[5] 娄峰, 刘轲, 刘金学, 董含武, 李淑波, 杜文博. 轧制态Mg-xZn-0.5Er合金板材组织及室温成形性能[J]. 金属学报, 2023, 59(11): 1439-1447.
[6] 宋庆忠, 潜坤, 舒磊, 陈波, 马颖澈, 刘奎. 镍基高温合金K417G与氧化物耐火材料的界面反应[J]. 金属学报, 2022, 58(7): 868-882.
[7] 姜伟宁, 武晓龙, 杨平, 顾新福, 解清阁. 热轧硅钢表层动态再结晶区形成规律及剪切织构特征[J]. 金属学报, 2022, 58(12): 1545-1556.
[8] 杨平, 王金华, 马丹丹, 庞树芳, 崔凤娥. 成分对真空脱锰法相变控制高硅电工钢{100}织构的影响[J]. 金属学报, 2022, 58(10): 1261-1270.
[9] 丁宁, 王云峰, 刘轲, 朱训明, 李淑波, 杜文博. 高应变速率多向锻造Mg-8Gd-1Er-0.5Zr合金的微观组织、织构及力学性能[J]. 金属学报, 2021, 57(8): 1000-1008.
[10] 颜孟奇, 陈立全, 杨平, 黄利军, 佟健博, 李焕峰, 郭鹏达. 热变形参数对TC18钛合金β相组织及织构演变规律的影响[J]. 金属学报, 2021, 57(7): 880-890.
[11] 曹富荣, 丁鑫, 项超, 尚会会. Mg-4.4Li-2.5Zn-0.46Al-0.74Y合金高温变形流动应力、组织演变与本构分析[J]. 金属学报, 2021, 57(7): 860-870.
[12] 赵婉辰, 郑晨, 肖斌, 刘行, 刘璐, 余童昕, 刘艳洁, 董自强, 刘轶, 周策, 吴洪盛, 路宝坤. 基于Bayesian采样主动机器学习模型的6061铝合金成分精细优化[J]. 金属学报, 2021, 57(6): 797-810.
[13] 刘冠熙, 黄光宏, 罗学昆, 申造宇, 何利民, 李建平, 牟仁德. 表面喷丸处理对NiCrAlYSi涂层恒温氧化行为的影响[J]. 金属学报, 2021, 57(5): 684-692.
[14] 吴玉程, 高志强, 徐光青, 刘家琴, 轩海成, 刘友好, 衣晓飞, 陈静武, 韩培德. 烧结NdFeB永磁材料腐蚀与防护的研究现状及挑战[J]. 金属学报, 2021, 57(2): 171-181.
[15] 左良, 李宗宾, 闫海乐, 杨波, 赵骧. 多晶Ni-Mn-X相变合金的织构化与功能行为[J]. 金属学报, 2021, 57(11): 1396-1415.