金属学报  2009, Vol. 45 Issue (2): 151-155    
  论文 本期目录 | 过刊浏览 |
过共析钢温变形过程中的组织演变 I. 铁素体的等轴化及Al的影响
陈伟1;李龙飞1;杨王玥2;孙祖庆1;何建平1
1. 北京科技大学新金属材料国家重点实验室; 北京 100083
2. 北京科技大学材料科学与工程学院; 北京 100083
MICROSTRUCTURE EVOLUTION OF HYPEREUTECTOID STEELS DURING WARM DEFORMATION I. Formation of Equiaxial Ferrite and Effects of Al
CHEN Wei 1; LI Longfei 1; YANG Wangyue 2; SUN Zuqing 1; HE Jianping 1
1. State Key Laboratory for Advanced Metals and Materials; University of Science and Technology Beijing; Beijing 100083
2. School of Materials Science and Engineering; University of Science and Technology Beijing; Beijing 100083
引用本文:

陈伟 李龙飞 杨王玥 孙祖庆 何建平. 过共析钢温变形过程中的组织演变 I. 铁素体的等轴化及Al的影响[J]. 金属学报, 2009, 45(2): 151-155.
, , , , . MICROSTRUCTURE EVOLUTION OF HYPEREUTECTOID STEELS DURING WARM DEFORMATION I. Formation of Equiaxial Ferrite and Effects of Al[J]. Acta Metall Sin, 2009, 45(2): 151-155.

全文: PDF(2631 KB)  
摘要: 

利用Gleeble 1500热模拟试验机进行单轴热压缩实验, 结合SEM, TEM和EBSD等方法研究了过共析钢温变形过程中的组织演变规律, 重点讨论了铁素体的等轴化演变过程, 同时考察了合金元素Al的影响. 结果表明: 过共析钢温变形经历片层渗碳体的熔断球化、铁素体的等轴化以及渗碳体的溶解再析出等过程. 温变形初期, 片层状渗碳体缺陷处局部熔断的同时其近邻铁素体内产生大量位错, 并通过动态回复过程形成亚晶; 继续变形过程中, 由于渗碳体粒子钉扎, 亚晶发生转动, 导致大角度晶界的形成, 即铁素体通过连续动态再结晶过程实现等轴化.Al的加入细化了铁素体晶粒尺寸, 提高了等轴状铁素体晶粒大角度晶界的比例.

关键词 过共析钢 温变形 等轴铁素体 渗碳体 Al    
Abstract

The microstructure evolution of hypereutectoid steels during warm deformation was investigated by uniaxial hot compression simulation experiment and by means of SEM, TEM and EBSD, especially for the formation of equiaxial ferrite grains and the effects of Al on the formation of equiaxial ferrite grains. The results indicate that the microstructure evolution of hypereutectoid steel during warm deformation involves the spheroidization of lamellar cementite, the equiaxial process of ferrite and the re–precipitation of cementite particles. At the beginning of warm deformation, lots of dislocations are introduced into ferrite, and subgrain boundaries are formed by dynamic recovery of ferrite. With the strain increasing, subgrains rotate due to the pinning effect of cementite particles, leading to the formation of high angle grain boundaries, i.e., the formation of equiaxial ferrite grains is actualized by the dynamic continuous recrystallization of ferrite. By the addition of Al, the coarsening of cementite is hindered, the sizes of cementite particles and ferrite grains are refined and the fraction of high angle grain boundary is increased.

Key wordshypereuectoid steel    warm deformation    equiaxial ferrite    cementite    Al
收稿日期: 2008-06-06     
ZTFLH: 

TG142.1

 
基金资助:

国家自然科学基金项目50471092, 教育部博士点专项基金项目20050008017和新金属材料国家重点实验室自主课题资助

作者简介: 陈伟, 男, 1979 年生, 博士生

[1] Sherby O D,Walser B, Young C M, Cady E M. Scr Metall, 1975; 9: 569
[2] Sherby O D, Oyama T, Kum D W, Walser B, Wadsworth J. J Met, 1985; 37(6): 50
[3] Oyama T, Sherby O D, Wadsworth J, Walser B. Scr Metall , 1984; 18: 799
[4] Furuhara T, Mizoguchi T, Maki T. ISIJ Int, 2005; 45: 392
[5] Lesuer D R, Syn C K, Goldberg A, Wadsworth J, Sherby O D. JOM, 1993; 45(8): 40
[6] Syn C K, Lesuer D R, Goldberg A, Tsai H C, Sherby O D. Mater Sci Forum, 2007; 539–543: 4844
[7] Lesuer D R, Syn C K, Whittenberger J D, Sherby O D. Metall Mater Trans, 1999; 30A: 1559
[8] Frommeyer G, Jimenez J A. Metall Mater Trans, 2005; 36A: 295
[9] Tsuzaki K, Sato E, Furimoto S, Furuhara T, Maki T. Scr Mater, 1999; 40: 675
[10] Chattopadhyay S, Sellars C M. Acta Metall, 1982; 30: 157
[11] Robbins J L, Shepard O C, Sherby O D. J Iron Steel Inst, 1964; 202: 804
[12] Harrigan M J, Sherby O D. Mater Sci Eng, 1971; 7: 177
[13] Paqueton H, Pinau A. J Iron Steel Inst, 1971; 209: 991
[14] Kaspar R, Kapellner W, Lang C. Steel Res, 1988; 59: 492
[15] Chen W, Li L F, Yang W Y, Sun Z Q. Acta Metall Sin, 2008; 44: 626
(陈伟, 李龙飞, 杨王玥, 孙祖庆. 金属学报,2008; 44: 626)
[16] Chen W, Li L F, Yang W Y, Sun Z Q. Chin J Mater Res, 2008; 22: 374
(陈伟, 李龙飞, 杨王玥 , 孙祖庆. 材料研究学报, 2008; 22: 374)

[17] Chen G A, Yang W Y, Sun Z Q. Acta Metall Sin, 2007;43: 27
(陈国安, 杨王玥, 孙祖庆. 金属学报, 2007; 43: 27)
[18] Huang Q S, Li L F, Yang W Y, Sun Z Q. Acta Metall Sin, 2007; 43: 724

(黄青松, 李龙飞, 杨王玥, 孙祖庆. 金属学报, 2007; 43: 724)
[19] Bever M B, Holt D L, Tichener A L. Prog Mater Sci, 1973;17: 5
[20] Chattopadhyay S, Sellars C M. Metallography, 1977; 10:89
[21] Song R, Ponge D, Raabe D. Scr Mater, 2005; 52: 1075
[22] Song R, Ponge D, Raabe D, Kaspar R. Acta Mater, 2005;53: 845
[23] Humphreys F J. Acta Metall, 1979; 27: 1801

[1] 丁桦, 张宇, 蔡明晖, 唐正友. 奥氏体基Fe-Mn-Al-C轻质钢的研究进展[J]. 金属学报, 2023, 59(8): 1027-1041.
[2] 王宗谱, 王卫国, Rohrer Gregory S, 陈松, 洪丽华, 林燕, 冯小铮, 任帅, 周邦新. 不同温度轧制Al-Zn-Mg-Cu合金再结晶后的{111}/{111}近奇异晶界[J]. 金属学报, 2023, 59(7): 947-960.
[3] 孙蓉蓉, 姚美意, 王皓瑜, 张文怀, 胡丽娟, 仇云龙, 林晓冬, 谢耀平, 杨健, 董建新, 成国光. Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为[J]. 金属学报, 2023, 59(7): 915-925.
[4] 袁江淮, 王振玉, 马冠水, 周广学, 程晓英, 汪爱英. Cr2AlC涂层相结构演变对力学性能的影响[J]. 金属学报, 2023, 59(7): 961-968.
[5] 冯艾寒, 陈强, 王剑, 王皞, 曲寿江, 陈道伦. 低密度Ti2AlNb基合金热轧板微观组织的热稳定性[J]. 金属学报, 2023, 59(6): 777-786.
[6] 吴东江, 刘德华, 张子傲, 张逸伦, 牛方勇, 马广义. 电弧增材制造2024铝合金的微观组织与力学性能[J]. 金属学报, 2023, 59(6): 767-776.
[7] 王福容, 张永梅, 柏国宁, 郭庆伟, 赵宇宏. Al掺杂Mg/Mg2Sn合金界面的第一性原理计算[J]. 金属学报, 2023, 59(6): 812-820.
[8] 刘满平, 薛周磊, 彭振, 陈昱林, 丁立鹏, 贾志宏. 后时效对超细晶6061铝合金微观结构与力学性能的影响[J]. 金属学报, 2023, 59(5): 657-667.
[9] 王迪, 贺莉丽, 王栋, 王莉, 张思倩, 董加胜, 陈立佳, 张健. Pt-Al涂层对DD413合金高温拉伸性能的影响[J]. 金属学报, 2023, 59(3): 424-434.
[10] 李斗, 徐长江, 李旭光, 李双明, 钟宏. La掺杂PCeyFe3CoSb12 热电材料及涂层的热电性能[J]. 金属学报, 2023, 59(2): 237-247.
[11] 王虎, 赵琳, 彭云, 蔡啸涛, 田志凌. 激光熔化沉积TiB2 增强TiAl基合金涂层的组织及力学性能[J]. 金属学报, 2023, 59(2): 226-236.
[12] 朱智浩, 陈志鹏, 刘田雨, 张爽, 董闯, 王清. 基于不同 α / β 团簇式比例的Ti-Al-V合金的铸态组织和力学性能[J]. 金属学报, 2023, 59(12): 1581-1589.
[13] 巩向鹏, 伍翠兰, 罗世芳, 沈若涵, 鄢俊. 自然时效对Al-2.95Cu-1.55Li-0.57Mg-0.18Zr合金160℃人工时效的影响[J]. 金属学报, 2023, 59(11): 1428-1438.
[14] 张丽丽, 吉宗威, 赵九洲, 何杰, 江鸿翔. 亚共晶Al-Si合金中微量元素La变质共晶Si的关键影响因素[J]. 金属学报, 2023, 59(11): 1541-1546.
[15] 胡敏, 周生玉, 国京元, 胡明昊, 李冲, 李会军, 王祖敏, 刘永长. 多相Ni3Al基高温合金微区氧化行为[J]. 金属学报, 2023, 59(10): 1346-1354.