| 还原性气氛中HCl和H2S导致Fe-Cr合金在700 ℃的加速失效 |
| 潘太军;鲁伟明;曾潮流;牛 焱 |
| 中国科学院金属研究所 |
|
| Accelerated Degradation of Three Iron-based Alloys Induced by the Presence of HCl and H2S in Reducing Atmospheres at 700oC |
| pan taijun |
| 中国科学院金属研究所 |
引用本文:
潘太军; 鲁伟明; 曾潮流; 牛焱 . 还原性气氛中HCl和H2S导致Fe-Cr合金在700 ℃的加速失效[J]. 金属学报, 2007, 43(12): 1261-1267 .
,
,
,
.
Accelerated Degradation of Three Iron-based Alloys Induced by the Presence of HCl and H2S in Reducing Atmospheres at 700oC[J]. Acta Metall Sin, 2007, 43(12): 1261-1267 .
[1]Meadowcroft D B.Mater Sci Eng,1989;A121:669
[2]Miller P D,Krouse H H.Corrosion,1971;27:31
[3]Vaughan D A,Krouse H H,Boyd W K.Mater Perform, 1975;14:16
[4]Zahs A,Spiegel M,Grabke H J.Corros Sci,2000;42: 1093
[5]Grabke H J,Reese E,Spiegel M.Corros Sci,1995;37: 1023
[6]Spiegel M,Warnecke R.Corrosion,2001,Paper No.01182
[7]Stringer J.High Temp Technol,1985;3:119
[8]Wood G C,Hodgkiess T,Whittle D P.Corros Sci,1966; 6:129
[9]Yearian H J,Randell E C,Longo T A.Corrosion,1956; 12:515t.
[10]Zhang K,Niu Y,Al-Omary M,Wu W T.Oxid Met,2004; 62:323
[11]Zheng X J,Rapp R A.Oxid Met,1997;48:553
[12]Prescott R,Stott F H,Elliott P.Corros Sci,1989;29:465
[13]Krausse H H,Vaughan D A,Miller P D.Trans ASME J Eng Power,1973;95A:45
[14]Haycock E W.J Electrochem Soc,1959;106:764
[15]Gesmundo F,Roos C,Oquab D,Viani F.High Temp Mater Processes,1998;17:145
[16]Mrowec S,Przybylski K.High Temp Mater Processes, 1984;6:1
[17]Pan T J,Al-Omary M,Zeng C L,Wu W T,Niu Y.High Temp Mater Processes,2005;24:3
[18]Pan T J,Gesmundo F,Niu Y.Corros Sci,2007;49:1362 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|