定向凝固NiAl合金的微观组织和高温力学性能Ⅰ.微观组织和韧脆转变温度 |
郭建亭 崔传勇 |
中国科学院金属研究所;沈阳 110015 |
|
引用本文:
郭建亭; 崔传勇 . 定向凝固NiAl合金的微观组织和高温力学性能Ⅰ.微观组织和韧脆转变温度[J]. 金属学报, 2000, 36(11): 1139-1143 .
[1] Cline H E, Walter J L, Lifshin E, Russell R R. MetallTrans, 1971; 2: 189 [2] Cline H E, Walter J L. Metall Trans, 1970; 1: 2907 [3] Johnson D R, Chen X F, Oliver F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 99 [4] Yang J M, Jeng S M, Bain K, Amato R A. Acta Mater,1997; 45: 295 [5] Oh-Ishi K, Horita Z, Nemoto M. Mater Sci Eng, 1997;A239/240: 472 [6] Darolia R, Walston W S. In: Nathal M V, Darolia R, LiuC T, Martin P L, Miracle D B, Wagner R, YamaguchiM eds, Structural Intermetallics 1997, Pennsylvania: TheMinerals, Metals & Materials Society, 1997: 585 [7] Noebe R D, Bowman R R, Nathal M V. Int Mater Rev,1993; 38: 193 [8] Ball A, Smallman R E. Acta Metall Mater 1966; 14: 1349 [9] Noebe R D, Cullers C L, Bowman R R. J Mater Res, 1992;7: 605 [10] Schulson E M, Rarker D R. Scr Metall, 1983; 17: 519 [11] Raj S V, Noebe R D, Bowman R R. Scr Metall, 1989; 23:2049 [12] Ebrahimi F Hoyle T G. Acta Mater, 1997; 45: 4193 [13] Miracle D. Acta Metall Mater 1991; 39: 1457 [14] Chen R S, Guo J T, Zhou W L, Zhou J Y. Intermetallics,2000; 8: 663 [15] Chen Y X, Cui C Y, He L L, Guo J T, Li D X. Acta MetallSin, 1999; 35: 897(陈玉喜,崔传勇,贺连龙,郭建亭,李斗星.金属学报,1999;35:897) [16] Cui C Y, Chen Y X, Guo J T, Li D X, Ye H Q. MaterLett, 2000; 43(4): 303 [17] Locci I E, Dickerson R M, Grag A, Noebe R D, Whittenberger J D, Nathal M V, Darolia R. J Mater Res, 1996;11: 3024 [18] Ebrahimi F, Hoyle T G. Acta Mater 1997; 45: 4193 [19] Pascoe R T, Newey L W A. Met Sci J, 1968; 2: 138 [20] Stroh A N. Adv Phys, 1957; 6: 418 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|