熔体保温温度对<span>W<sub>f</sub>/Zr基金属玻璃复合材料室温力学性能的影响</span>

doi:10.3724/SP.J.1037.2013.00541

金属学报

2013, Vol. 49

Issue (11): 1481-1486 DOI: 10.3724/SP.J.1037.2013.00541

论文

本期目录 | 过刊浏览

熔体保温温度对W_f/Zr基金属玻璃复合材料室温力学性能的影响

高度,陈光,范沧

南京理工大学材料评价与设计教育部工程研究中心, 南京 210094

INFLUENCE OF MELT HOLDING TEMPERATURES ON MECHANICAL PROPERTIES AT ROOM TEMPERATURE OF W_f/Zr－BASED METALLIC GLASS COMPOSITES

GAO Du, CHEN Guang, FAN Cang

Engineering Research Center of Materials Behavior and Design,Ministry of Education, Nanjing University of Science and Technology, Nanjing 210094

引用本文:

高度,陈光,范沧. 熔体保温温度对W_f/Zr基金属玻璃复合材料室温力学性能的影响[J]. 金属学报, 2013, 49(11): 1481-1486.
GAO Du, CHEN Guang, FAN Cang. INFLUENCE OF MELT HOLDING TEMPERATURES ON MECHANICAL PROPERTIES AT ROOM TEMPERATURE OF W_f/Zr－BASED METALLIC GLASS COMPOSITES[J]. Acta Metall Sin, 2013, 49(11): 1481-1486.

全文: PDF(1506 KB)

摘要:

系统研究了熔体保温温度对渗流铸造快淬法制备的W_f/Zr基金属玻璃复合材料的影响.室温力学性能测试结果表明, W_f/Zr基金属玻璃复合材料在制备过程中存在一个最佳熔体保温温度.偏离该保温温度, 复合材料的室温压缩塑性发生恶化.光学显微组织和能谱分析结果表明其原因在于, 在不同的熔体保温温度,基体内产生不同数量的各种析出相. 在最佳熔体保温温度810℃下,制备出了室温压缩塑性达到19.6%的、W_f体积分数为75%的复合材料.

关键词 ：金属玻璃复合材料, W纤维, 析出相, 保温温度, 压缩塑性

Abstract：

The effect of the molten temperatures on the preparation of the W_f/Zr－based metallic glass composites by infiltration casting rapid quenching technique was well studied. The results of the mechanical properties at ambient temperature indicate that the composite has an optimum melt holding temperature in the preparation process. Lower or higher than the optimum temperature, the compressive plasticity of the composite deteriorated. The optical microstructure and EDS analyses indicate that the reason for the deterioration of the compressive plasticity was the resulted microstructures, which contains different precipitates with different molten temperatures. At the optimum preparation condition, a W_f/Zr--based metallic glass composite with 75% volume fraction of tungsten fiber was successfully produced with significantly improved compressive plasticity of 19.6%.

Key words： metallic glass composite W fiber, precipitate melt holding temperature compression plasticity

收稿日期: 2013-09-02

基金资助:

国家自然科学基金项目50971057和51371099资助

作者简介: 高度, 男, 1983年生, 博士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	高度
	陈光
	范沧
44.8K

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2013.00541 或 https://www.ams.org.cn/CN/Y2013/V49/I11/1481

[1] Johnson W L. MRS Bull, 1999; 24: 42

[2] Inoue A. Acta Mater, 2000; 48: 279

[3] Ashby M F, Greer A L. Scr Mater, 2006; 54: 321

[4] Schuh C A, Hufnagel T C, Ramamurty U. Acta Mater, 2007; 55: 4067

[5] Greer A L. Mater Today, 2009; 12: 14

[6] Zhang Z F, Eckert J, Schultz L. Acta Mater, 2003; 51: 1167

[7] Eckert J, Das J, Pauly S, Duhamel C. J Mater Res, 2007; 22: 285

[8] Wu F F, Zhang Z F, Mao S X, Peker A, Eckert J. Phys Rev, 2007; 75B: 134201

[9] Wang Z H, Chen G, Jiang F, Du Y L, Chen G L. Rare Met Mater Eng, 2006; 35: 1568

(王志华, 陈光, 姜斐, 杜宇雷, 陈国良. 稀有金属材料与工程, 2006; 35: 1568)

[10] Conner R D, Dandliker R B, Johnson W L. Acta Mater, 1998; 46: 6089

[11] Dandliker R B, Conner R D, Johnson W L. J Mater Res, 1998; 13: 2896

[12] Kim C P, Busch R, Masuhr A, Choi--Yim H, Johnson W L. Appl Phys Lett, 2001;79: 1456

[13] Bian Z, Pan M X, Zhang Y, Wang W H. Appl Phys Lett, 2002; 81: 4739

[14] Qiu K Q, Wang A M, Zhang H F, Ding B Z, Hu Z H. Intermetallics, 2002; 10: 1283

[15] Wang G, Chen D M, Shen J, Stachurski Z H, Qin Q H, Sun J F, Zhou B D.J Non－Cryst Solids, 2006; 352: 3872

[16] Wadhwa P, Heinrich J, Busch R. J Alloys Compd, 2007; 434--435: 259

[17] Zhang H, Zhang Z F, Wang Z G, Zhang H F. Mater Sci Eng, 2008; A483--484: 164

[18] Zhang X C, Chen X H, Zhang Y, Chen G L. Rare Met Mater Eng, 2008; 37: 786

(张兴超, 陈晓华, 张勇, 陈国良. 稀有金属材料与工程, 2008; 37: 786)

[19] Lee K, Son C Y, Lee S B, Lee S K, Lee S. Mater Sci Eng, 2010; A527: 941

[20] Deng S T, Diao H, Chen Y L, Yan C, Zhang H F, Wang A M, Hu Z H. Scr Mater, 2011; 64: 85

[21] Choi－Yim H, Johnson W L. Appl Phys Lett, 1997; 71: 3808

[22] Kato H, Inoue A. Mater Trans JIM, 1997; 38: 793

[23] Choi－Yim H, Busch R, K\"{oster U, Johnson W L. Acta Mater, 1999; 47: 2455

[24] Choi－Yim H, Conner R D, Szuecs F, Johnson W L. Scr Mater, 2001; 45: 1039

[25] Choi－Yim H, Schroers J, Johnson W L. Appl Phys Lett, 2002; 80: 1906

[26] Li H, Subhash G, Kecskes L J, Dowing R J. Mater Sci Eng, 2005; A403: 134

[27] Chen G, Bei H, Cao Y, Gali A, Liu C T, George E P. Appl Phys Lett, 2009; 95: 081908

[28] Cheng J L, Chen G, Xu F, Du Y L, Li Y S, Liu C T. Intermetallics, 2010; 18: 2425

[29] Hays C C, Kim C P, Johnson W L. Phys Rev Lett, 2000; 84: 2901

[30] Szuecs F, Kim C P, Johnson W L. Acta Mater, 2001; 49: 1507

[31] Sun G Y, Chen G, Liu C T, Chen G L. Scr Mater, 2006; 55: 375

[32] Hofmann D C, Suh J Y, Wiest A, Duan G, Lind M L, Demetriou M D, Johnson W L. Nature, 2008; 451: 1085

[33] Fan C, Li C F, Inoue A, Haas V. Phys Rev, 2000; 61B: R3761

[34] Leonhard A, Xing L Q, Heilmaier M, Gebert A, Eckert J, Schultz L.Nanostruct Mater, 1998; 10: 805

[35] Stawovy M T, Aning A O. Mater Sci Eng, 1998; A256: 138

[36] Lee M H, Kim J--H, Park J S, Kim J C, Kim W T, Kim D H. Scr Mater, 2004; 50: 1367

[37] Yu P, Kim K B, Das J, Baier F, Xu W, Eckert J. Scr Mater, 2006; 54: 1445

[38] Zhang Z H, Han B Q, Witkin D, Ajdelsztajn L, Laverna E J. Scr Mater, 2006; 54: 869

[39] Conner R D, Dandliker R B, Scruggs V, Johnson W L. Int J Impact Eng, 2000; 24: 435

[40] Zhou X, Kou H C, Wang J, Li J S, Zhou L. Intermetallics, 2012; 28: 45

[41] Fan C, Liu C T, Chen G, Chen D, Yang X, Liaw P K, Yan H G. Intermetallics, 2013; 38: 19

[42] Schroers J, Busch R, Masuhr A, Johnson W L. Appl Phys Lett, 1999; 74: 2806

[43] Dandliker R B. PhD Dissertation, California Institute of Technology, Pasadena, 1998

[44] Qiu K Q, Wang A M, Zhang H F, Qiao D C, Ding B Z, Hu Z H. Acta Metall Sin, 2002; 38: 1091

(邱克强, 王爱民, 张海峰, 乔东春, 丁炳哲, 胡壮麒.金属学报, 2002; 38: 1091)

[45] Qiu K Q. PhD Dissertation, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2002

(邱克强. 中国科学院金属研究所博士学位论文, 沈阳, 2002)

[46] Zhang H, Zhang Z F, Wang Z G, Qiu K Q, Zhang H F, Zang Q S, Hu Z Q. Mater Sci Eng, 2006; A418: 146

[47] Wang M L, Chen G L, Hui X, Zhang Y, Bai Z Y. Intermetallics, 2007; 15: 1309

[48] Wang M L, Hui X D, Kou H C, Chen G L. Rare Met Mater Eng, 2005; 34: 1102

(王美玲, 惠希东, 寇宏超, 陈国良. 稀有金属材料与工程, 2005; 34: 1102)

[1]	梁凯, 姚志浩, 谢锡善, 姚凯俊, 董建新. 新型耐热合金SP2215组织与性能的关联性[J]. 金属学报, 2023, 59(6): 797-811.
[2]	陈凯旋, 李宗烜, 王自东, Demange Gilles, 陈晓华, 张佳伟, 吴雪华, Zapolsky Helena. Cu-2.0Fe合金等温处理过程中富Fe析出相的形态演变[J]. 金属学报, 2023, 59(12): 1665-1674.
[3]	芮祥, 李艳芬, 张家榕, 王旗涛, 严伟, 单以银. 新型纳米复合强化9Cr-ODS钢的设计、组织与力学性能[J]. 金属学报, 2023, 59(12): 1590-1602.
[4]	马国楠, 朱士泽, 王东, 肖伯律, 马宗义. SiC颗粒增强Al-Zn-Mg-Cu复合材料的时效行为和力学性能[J]. 金属学报, 2023, 59(12): 1655-1664.
[5]	李小琳, 刘林锡, 李雅婷, 杨佳伟, 邓想涛, 王海丰. 单一 MX 型析出相强化马氏体耐热钢力学性能及蠕变行为[J]. 金属学报, 2022, 58(9): 1199-1207.
[6]	陈果, 王新波, 张仁晓, 马成悦, 杨海峰, 周利, 赵运强. 搅拌头转速对2507双相不锈钢搅拌摩擦加工组织及性能的影响[J]. 金属学报, 2021, 57(6): 725-735.
[7]	高一涵, 刘刚, 孙军. 耐热铝基合金研究进展：微观组织设计与析出策略[J]. 金属学报, 2021, 57(2): 129-149.
[8]	刘峰, 王天乐. 基于热力学和动力学协同的析出相模拟[J]. 金属学报, 2021, 57(1): 55-70.
[9]	郭倩颖, 李彦默, 陈斌, 丁然, 余黎明, 刘永长. 高温时效处理对S31042耐热钢组织和蠕变性能的影响[J]. 金属学报, 2021, 57(1): 82-94.
[10]	韩宝帅, 魏立军, 徐严谨, 马晓光, 刘雅菲, 侯红亮. 预变形对超高强Al-Zn-Mg-Cu合金时效组织与力学性能的影响[J]. 金属学报, 2020, 56(7): 1007-1014.
[11]	梁孟超, 陈良, 赵国群. 人工时效对2A12铝板力学性能和强化相的影响[J]. 金属学报, 2020, 56(5): 736-744.
[12]	刘振宝,梁剑雄,苏杰,王晓辉,孙永庆,王长军,杨志勇. 高强度不锈钢的研究及发展现状[J]. 金属学报, 2020, 56(4): 549-557.
[13]	张正延,柴锋,罗小兵,陈刚,杨才福,苏航. 调质态含Cu高强钢的强化机理及钢中Cu的析出行为[J]. 金属学报, 2019, 55(6): 783-791.
[14]	杜娟, 程晓行, 杨天南, 陈龙庆, Mompiou Frédéric, 张文征. 奥氏体析出相激发形核的原位TEM研究[J]. 金属学报, 2019, 55(4): 511-520.
[15]	朱上,李志辉,闫丽珍,李锡武,张永安,熊柏青. Zn添加对预时效态Al-Mg-Si-Cu合金自然时效和烘烤硬化性的影响[J]. 金属学报, 2019, 55(11): 1395-1406.

Viewed

Full text

Abstract

Cited

Shared

Discussed