金属学报  2011, Vol. 47 Issue (1): 53-60    DOI: 10.3724/SP.J.1037.2010.00369

论文 本期目录 | 过刊浏览 |

Al-Cu-Mg-Ag耐热铝合金高温蠕变行为

刘晓艳1), 潘清林1, 2), 陆智伦1), 曹素芳1), 何运斌1), 李文斌1)

1) 中南大学材料科学与工程学院, 长沙 410083 2) 中南大学有色金属材料科学与工程教育部重点实验室, 长沙 410083

CREEP BEHAVIOR OF Al-Cu-Mg-Ag HEAT-RESISTANT ALLOY AT ELEVATED TEMPERATURE

LIU Xiaoyan1),  PAN Qinglin1, 2),  LU Zhilun1), CAO Sufang1),  HE Yunbin1),  LI Wenbin1)

1) School of Materials Science and Engineering, Central South University, Changsha 410083 2) The Key Laboratory of Nonferrous Materials Science and Engineering of Ministry of Education, Central South University, Changsha 410083

刘晓艳 潘清林 陆智伦 曹素芳 何运斌 李文斌. Al-Cu-Mg-Ag耐热铝合金高温蠕变行为[J]. 金属学报, 2011, 47(1): 53-60.
, , , , , . CREEP BEHAVIOR OF Al-Cu-Mg-Ag HEAT-RESISTANT ALLOY AT ELEVATED TEMPERATURE[J]. Acta Metall Sin, 2011, 47(1): 53-60.

摘要 参考文献 相关文章 Metrics 全文: PDF(1275 KB)   摘要: 在100-210℃和150-300 MPa的条件下, 研究了Al-5.3Cu-0.8Mg-0.5Ag-0.3Mn-0.15Zr耐热铝合金的蠕变行为, 探讨了时效状态对合金高温性能的影响. 结果表明: 在相同蠕变条件下, 欠时效态合金的稳态蠕变速率远远低于峰时效态合金. 在210℃/200 MPa下, 欠时效态合金的蠕变断裂时间为75 h, 而峰时效态合金的蠕变断裂时间仅为21 h. 蠕变过程中, 合金中的析出相长大. 峰时效态合金中析出相尺寸的增大速率高于欠时效态合金. 欠时效态合金中还发生了动态析出, 这些细小的析出相在蠕变过程中阻碍了位错的运动, 使得合金蠕变速率降低. 在100-150℃下合金的稳态蠕变速率保持在较低水平. 当温度升高到180℃时, 合金的稳态蠕变速率急剧增大. 合金稳态蠕变速率随着蠕变温度的升高和应力的提高均有增大趋势, 3者之间的关系可用一本构方程来表示, 其表观激活能为102 kJ/mol. 关键词 ： Al-Cu-Mg-Ag合金,  蠕变,  欠时效态,  稳态蠕变速率     Abstract：The creep behaviors of heat--resistant alloy Al-5.3Cu-0.8Mg-0.5Ag-0.3Mn-0.15Zr (Al-Cu-Mg-Ag) were studied in a temperature range of 100-210℃ and a load range of 150-300 MPa, and the effect of aging on the properties of Al-Cu-Mg-Ag alloy at elevated temperatures was also investigated. The results show that the steady creep rate of the under-aged alloy is much lower than that of the peak--aged alloy at the same creep conditions. The creep fracture time is 75 h for the under-aged Al-Cu-Mg-Ag alloy at 210℃/200 MPa, while that for the peak-aged alloy is only 21 h. The precipitates grow gradually during the creep process and the growth rate in the peak-aged alloy is higher than that in the under-aged alloy. Dynamic precipitation happened in the under-aged alloy. The fine precipitates inhibite the motion of the dislocations during the creep, which leads to lower creep deformation rate compared to the peak-aged alloy. The steady creep rates of the under-aged Al-Cu-Mg-Ag alloy at 100-150℃ keep a relatively lower level, but increases to a high level when the creep temperature increased to 180℃. The steady creep rate increased with increasing temperature or stress, which can be described by a constitutive equation with an apparent activation energy of 102 kJ/mol. Key words： Al-Cu-Mg-Ag alloy    creep    under-aged    steady creep rate 收稿日期: 2010-07-23      ZTFLH:  TG 146.21   基金资助: 中南大学优秀博士学位论文扶植基金资助项目2008yb012 作者简介: 刘晓艳, 女, 1980年生, 博士生 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 刘晓艳 潘清林 陆智伦 曹素芳 何运斌 李文斌 44.8K 链接本文: https://www.ams.org.cn/CN/10.3724/SP.J.1037.2010.00369      或      https://www.ams.org.cn/CN/Y2011/V47/I1/53 [1] Sukumaran K, Ravikumar K K, Pillai S G K, Rajan T P D, Ravi M, Pillai R M, Pai B C. Mater Sci Eng, 2008; A490: 235 [2] Naga R P, Srinivasa R K, Reddy G M, Kamaraj M, Prasad R K. Mater Sci Eng, 2007; A464: 192 [3] Wang J, Yi D, Su X, Yin F. Mater Charact, 2008; 59: 965 [4] Yu K, Li W, Li S, Zhao J. Mater Sci Eng, 2004; A368: 88 [5] Chang C H, Lee S L, Lin J C, Yeh M S, Jeng R R. Mater Chem Phys, 2005; 91: 454 [6] Xiao D H, Wang J N, Ding D Y, Chen S P. J Alloys Compd, 2002; 343: 77 [7] Bakavos D, Prangnell P B, Bes B, Eberl F. Mater Sci Eng, 2008; A491: 214 [8] Somi R A. Mater Des, 2008; 29: 763 [9] Lumley R N, Morton A J, Polmear I J. Acta Mater, 2002; 50: 3597 [10] Yan J L, Sun Y S, Xue F, Tao W J. Acta Metall Sin, 2008; 44: 1354 (晏井利, 孙扬善, 薛烽, 陶卫建. 金属学报, 2008; 44: 1354) [11] Spigarelli S, Evangelista E, Cucchieri S. Mater Sci Eng, 2004; A387–389: 702 [12] Qi Y H, Guo J T, Cui C Y. Acta Metall Sin, 2001; 37: 957 (齐义辉, 郭建亭, 崔传勇. 金属学报, 2001; 37: 957) [13] Kermanidis A T, Zervaki A D, Haidemenopoulos G N, Pantelakis Sp G. Mater Des, 2010; 31: 42 [14] Das G, Das M, Ghosh S, Dubey P, Ray A K. Mater Sci Eng, 2010; A527: 1590 [15] Xia Q K, Liu Z Y, Li Y T. Trans Nonferrous Met Soc China, 2008; 18: 789 [16] Seeger A T. Naturforschung, 1956; 9: 758 [17] Sha G Y, Han E H, Yu T, Xu Y B, Liu L, Gao G Z. Acta Metall Sin, 2003; 39: 1025 (沙桂英, 韩恩厚, 于 涛, 徐永波, 刘 路, 高国忠. 金属学报, 2003; 39: 1025) [18] Li B Q, Wawner F E. Acta Mater, 1998; 46: 5483 [19] Mukherjee A K, Bird J E, Dorn J E. Trans ASM, 1969; 62: 155 [1] 陈佳, 郭敏, 杨敏, 刘林, 张军. 新型钴基高温合金中W元素对蠕变组织和性能的影响[J]. 金属学报, 2023, 59(9): 1209-1220. [2] 白佳铭, 刘建涛, 贾建, 张义文. 高W高Ta型粉末高温合金的蠕变性能及溶质原子偏聚[J]. 金属学报, 2023, 59(9): 1230-1242. [3] 冯强, 路松, 李文道, 张晓瑞, 李龙飞, 邹敏, 庄晓黎. γ' 相强化钴基高温合金成分设计与蠕变机理研究进展[J]. 金属学报, 2023, 59(9): 1125-1143. [4] 李小琳, 刘林锡, 李雅婷, 杨佳伟, 邓想涛, 王海丰. 单一 MX 型析出相强化马氏体耐热钢力学性能及蠕变行为[J]. 金属学报, 2022, 58(9): 1199-1207. [5] 高川, 邓运来, 王冯权, 郭晓斌. 蠕变时效对欠时效7075铝合金力学性能的影响[J]. 金属学报, 2022, 58(6): 746-759. [6] 彭子超, 刘培元, 王旭青, 罗学军, 刘健, 邹金文. 不同服役条件下FGH96合金的蠕变特征[J]. 金属学报, 2022, 58(5): 673-682. [7] 杨志昆, 王浩, 张义文, 胡本芙. Ta含量对镍基粉末高温合金高温蠕变变形行为和性能的影响[J]. 金属学报, 2021, 57(8): 1027-1038. [8] 张倪侦, 马昕迪, 耿川, 穆永坤, 孙康, 贾延东, 黄波, 王刚. Ag元素添加对Cu-Zr-Al基金属玻璃纳米压痕行为的影响[J]. 金属学报, 2021, 57(4): 567-574. [9] 徐静辉, 李龙飞, 刘心刚, 李辉, 冯强. 热力耦合对一种第四代镍基单晶高温合金1100℃蠕变组织演变的影响[J]. 金属学报, 2021, 57(2): 205-214. [10] 郭倩颖, 李彦默, 陈斌, 丁然, 余黎明, 刘永长. 高温时效处理对S31042耐热钢组织和蠕变性能的影响[J]. 金属学报, 2021, 57(1): 82-94. [11] 刘天, 罗锐, 程晓农, 郑琦, 陈乐利, 王茜. 形成Al2O3表层的奥氏体不锈钢加速蠕变实验研究[J]. 金属学报, 2020, 56(11): 1452-1462. [12] 吴静,刘永长,李冲,伍宇婷,夏兴川,李会军. 高Fe、Cr含量多相Ni3Al基高温合金组织与性能研究进展[J]. 金属学报, 2020, 56(1): 21-35. [13] 胡斌,李树索,裴延玲,宫声凯,徐惠彬. <111>取向小角偏离对一种镍基单晶高温合金蠕变性能的影响[J]. 金属学报, 2019, 55(9): 1204-1210. [14] 唐文书,肖俊峰,李永君,张炯,高斯峰,南晴. 再热恢复处理对蠕变损伤定向凝固高温合金γ′相的影响[J]. 金属学报, 2019, 55(5): 601-610. [15] 逯世杰, 王虎, 戴培元, 邓德安. 蠕变对焊后热处理残余应力预测精度和计算效率的影响[J]. 金属学报, 2019, 55(12): 1581-1592. Viewed Full text Abstract Cited   Shared      Discussed