STRESS CORROSION CRACK INITIATION BEHAVIOR FOR THE X70 PIPELINE STEEL BENEATH A DISBONDED COATING |
WANG Zhiying 2, WANG Jianqiu 1, HAN En–hou 1, KE Wei 1, YAN Maocheng 1, ZHANG Junwei 2, LIU Chuwei 2 |
1. State Key Lab for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
2. School of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan 114051 |
|
Cite this article:
WANG Zhiying WANG Jianqiu HAN En–hou KE Wei YAN Maocheng ZHANG Junwei LIU Chuwei . STRESS CORROSION CRACK INITIATION BEHAVIOR FOR THE X70 PIPELINE STEEL BENEATH A DISBONDED COATING. Acta Metall Sin, 2012, 48(10): 1267-1272.
|
Abstract Stress corrosion cracking (SCC) has become one of the main threats for pipelines safe. The crack initiation is the first step for pipeline SCC. The disbonded coating affects the SCC initiation behavior. In the present paper, the effect of cathodic protection potential on SCC initiation for X70 pipeline steel in the NS4 solution beneath a disbonded coating is studied by a cyclic loading test. The SCC initiation situation was observed at the different distances beneath a disbonded coating area by SEM. The results show that the SCC initiation degree lightens with the increase of distance from the disbonded coating area under the condition of –850 mV cathodic protection potential. When the cathodic protection potential increases to –1000 mV, the SCC initiation degree slightly increases with the increase of distance from the disbonded position. But compared with that under the –850 mV, the crack initiation degree under –1000 mV is lower at the corresponding position. It is shown that the coating disbondment reduces the cathodic protection effect, and in order to obtain the same cathodic protection effect the cathodic protection potential should be appropriately moved in an negative way
|
Received: 04 May 2012
|
|
Fund: Supported by National Natural Science Foundation of China (No.51025104) and PhD Starting Funds of Liaoning Provincial Science and Technology Department (No.20101048) |
[1] Yan M C, Wang J Q, Han E H. Corros Sci, 2008; 50: 1331[2] Vuillemin B, Oltra R, Cottis R. Electrochim Acta, 2007; 52: 570[3] Sridhar N, Dunn D S, Seth M. Corrosion, 2001; 57: 598[4] Jack T R, Van Boven G, Wilmott M J, Utherby R L S,Worthingham R G. Mater Perform, 1994; 33(8): 17[5] Charles E A, Parkins R N. Corrosion, 1995; 51: 518[6] Beavers J A, Thompson N G. Mater Perform, 1997; 36(4): 13[7] Li Z F, Mao X H, Gan F X. J Chin Soc Corros Prot, 2000; 20: 3383(李正复, 毛旭辉, 甘复兴. 中国腐蚀与防护学报, 2000; 20: 338)[8] Li Z F, Mao X H, Gan F X. J Chin Soc Corros Prot, 2000; 20: 129(李正复, 毛旭辉, 甘复兴. 中国腐蚀与防护学报, 2000; 20: 129)[9] Chen X, Li X G, Du C W, Liang P. J Chin Soc Corros Prot, 2010; 30: 35(陈旭, 李晓刚, 杜翠薇, 梁平. 中国腐蚀与防护学报, 2010; 30: 35)[10] Song Y Q, Du C W, Zhang X, Li X G. Acta Metall Sin, 2009; 45: 1130(宋义全, 杜翠薇, 张新, 李晓刚. 金属学报, 2009; 45: 1130)[11] Guo H, Du C W, Li X G, Zhang X. Corros Sci Prot Technol, 2008; 20: 336(郭昊, 杜翠薇, 李晓刚, 张新. 腐蚀科学与防护技术, 2008; 20: 336)[12] Chen X, Li X G, Du C W, Liang P. Acta Metall Sin, 2008; 44: 1431(陈旭, 李晓刚, 杜翠薇, 梁平. 金属学报, 2008; 44: 1431)[13] Song Y Q, Du C W, Zhang X, Li X G. Acta Metall Sin, 2006; 42: 305(宋义全, 杜翠薇, 张 新, 李晓刚. 金属学报, 2006; 42: 305)[14] Chen X, Du CW, Li X G, Huang Y Z. J Appl Electrochem, 2009; 39: 697[15] Li Z F, Gan F X, Mao X H. Corros Sci, 2002; 44: 689[16] Yan M C. Postdoc Report, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 2007(闫茂成. 中国科学院金属研究所博士后出站报告, 沈阳, 2007)[17] Parkins R N. Corrosion’ 2000, Houston, Texas: NACE, 2000: Paper No. 00363(CD)[18] Liu X, Yang W. Mater Mech Eng, 2002; 26(1): 5(刘杏, 杨武. 机械工程材料, 2002; 26(1): 5)[19] Charles E A, Parkins R N. Corrosion, 1995; 51: 518[20] Yan M C, Wang J Q, Ke W, Han E H. J Chin Soc Corros Prot, 2007; 27: 257(闫茂成, 王俭秋, 柯伟, 韩恩厚. 中国腐蚀与防护学报, 2007; 27: 257)[21] Gu B, Luo J L, Mao X. Corrosion, 1999; 55: 96[22] Qiao L J, Luo J L, Mao X. Corrosion, 1998; 54: 115[23] Szb´c S, Bakos I. Corros Rew, 2006; 24: 39[24] Niu L, Cheng Y F. Appl Surf Sci, 2007; 258: 8626[25] Cheng Y F. Electrochim Acta, 2007; 52: 2661 |