2.25Cr-1Mo-0.25V钢焊缝中第二相高温回火转变

陶鹏¹;张弛¹;杨志刚¹;武田裕之²

1 清华大学材料科学与工程系先进材料教育部重点实验室; 北京 100084
2 (株)神户制钢所材料研究所材质制御研究室; 兵库651-2271; 日本

EVOLUTION OF SECOND PHASE IN 2.25Cr-1Mo-0.25V STEEL WELD METAL DURING HIGH TEMPERATURE TEMPERING

TAO Peng¹; ZHANG Chi¹; YANG Zhigang¹;TAKEDA Hiroyuki²

1 Key Laboratory for Advanced Materials of Ministry of Education; Department of Materials Science and Engineering; Tsinghua University; Beijing 100084
2 Materials Design Section; Materials Research Laboratory; Kobe Steel Ltd.; Hyogo 651-2271; Japan

引用本文:

陶鹏张弛杨志刚武田裕之. 2.25Cr-1Mo-0.25V钢焊缝中第二相高温回火转变[J]. 金属学报, 2009, 45(1): 51-57.
, , . EVOLUTION OF SECOND PHASE IN 2.25Cr-1Mo-0.25V STEEL WELD METAL DURING HIGH TEMPERATURE TEMPERING[J]. Acta Metall Sin, 2009, 45(1): 51-57.

全文: PDF(2146 KB)

摘要:

利用TEM和EDX技术, 研究了2.25Cr-1Mo-0.25V钢焊缝中第二相在700 ℃下保温一系列时间段的转变. 结果表明, 焊后空冷焊缝中的第二相为M₃C, 回火过程中第二相主要组成为M₃C+M₇C₃+M₂₃C₆. 长时间回火后M₃C发生球化并消失, 初期析出的低w_Cr/w_Fe(Cr与Fe的质量比)的M₇C₃是亚稳相, M₂₃C₆只能在较低的回火参数范围内存在, 后期形成了w_Crw_Fe更高的M₇C₃稳定的第二相. M₃C多呈球状,M₇C₃和M₂₃C₆多为长条状和块状.

关键词 ：焊缝, 第二相, 碳化物, 回火, 低合金钢2.25Cr--1Mo--0.25V

Abstract：

The evolution of the second phase in 2.25Cr–1Mo–0.25V steel weld metal during holding at 700 ℃ for a series of durations was studied by TEM and EDX. The precipitates in the as– welded specimen are M₃C carbides, and during tempering M₇C₃ and M₂₃C₆ carbides appeared. After long term tempering M₃C carbides spheroidized and disappeared. In the early tempering stage M₇C₃ carbide with low wCr/wFe is metastable phase. M23C6 carbide can exist only under low tempering parameter, and M₇C₃ carbide with high w_Cr/w_Fe formed in the late stage is the stable phase. M₃C carbides are often sphere–liked, M₇C₃ and M₂₃C₆ carbides are rod–shaped and lump–shaped.

Key words： weld metal second phase carbide tempering low alloy steel 2.25Cr--1Mo--0.25V

收稿日期: 2008-06-04

ZTFLH:

TG146.1

作者简介: 陶鹏, 男, 1985年生, 硕士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陶鹏
	张弛
	杨志刚
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2009/V45/I1/51

[1] Bhadeshia H K D H. Bainite in Steels. 2nd Ed., London: The Institute of Materials, 2001: 323
[2] Davis J R. Metals Handbook. Vol.1, 10th Ed., Materials Park, OH: ASM International, 1990: 617
[3] Klueh R L, Swindeman R W. Metall Trans, 1986; 17A: 1027
[4] Miranda R M, Fortes M A. Mater Sci Eng, 1989; A108: 1
[5] Cheruvu N S. Metall Trans, 1989; 20A: 87
[6] Thomson R C, Badeshia H. Mater Sci Technol, 1994; 10: 193
[7] Fujita N, Bhadeshia H K D H. ISIJ Int, 2002; 42: 760
[8] Baker R G, Nutting J. J Iron Steel Inst, 1959; 192: 257
[9] Tsai M C, Chiou C S, Yang J R. J Mater Sci, 2003; 38: 2373
[10] Tsai M C, Yang J R. Mater Sci Eng, 2003; A340: 15
[11] Janovec J, Svoboda M, Kroupa A, Vyrostkova A. J Mater Sci, 2006; 41: 3425
[12] Sourmail T. Mater Sci Technol, 2001; 17: 1
[13] Inouoe A, Masumoto T. Metall Trans, 1980; 11A: 739
[14] Lane J R, Grant N J. Trans ASM, 1952; 44: 113
[15] Sims C T. J Met, 1969; 21: 27
[16] V´yrostkov´a A, Kroupa A, Janovec J, Janovec J. Acta Mater, 1998; 46: 31
[17] Kroupa A, V´yrostkov´a A, Svoboda M, Janovec J. Acta Mater, 1998; 46: 39
[18] Janovec J, Svoboda M, Vyrostkova A, Kroupa A. Mater Sci Eng, 2005; A402: 288

[1]	刘继浩, 周健, 武会宾, 马党参, 徐辉霞, 马志俊. 喷射成形M3高速钢偏析成因及凝固机理[J]. 金属学报, 2023, 59(5): 599-610.
[2]	娄峰, 刘轲, 刘金学, 董含武, 李淑波, 杜文博. 轧制态Mg-xZn-0.5Er合金板材组织及室温成形性能[J]. 金属学报, 2023, 59(11): 1439-1447.
[3]	李闪闪, 陈云, 巩桐兆, 陈星秋, 傅排先, 李殿中. 冷速对高碳铬轴承钢液析碳化物凝固析出机制的影响[J]. 金属学报, 2022, 58(8): 1024-1034.
[4]	沈国慧, 胡斌, 杨占兵, 罗海文. 回火温度对含 δ 铁素体高铝中锰钢力学性能和显微组织的影响[J]. 金属学报, 2022, 58(2): 165-174.
[5]	周成, 赵坦, 叶其斌, 田勇, 王昭东, 高秀华. 回火温度对1000 MPa级NiCrMoV低碳合金钢微观组织和低温韧性的影响[J]. 金属学报, 2022, 58(12): 1557-1569.
[6]	骆文泽, 胡龙, 邓德安. SUS316不锈钢马鞍形管-管接头的残余应力数值模拟及高效计算方法开发[J]. 金属学报, 2022, 58(10): 1334-1348.
[7]	王占花, 惠卫军, 谢志奇, 张永健, 赵晓丽. 回火对钒钛微合金化Mn-Cr系贝氏体型非调质钢组织和性能的影响[J]. 金属学报, 2020, 56(11): 1441-1451.
[8]	武华健, 程仁山, 李景仁, 谢东升, 宋锴, 潘虎成, 秦高梧. Al含量对Mg-Sn-Ca合金微观组织与力学性能的影响[J]. 金属学报, 2020, 56(10): 1423-1432.
[9]	杨柯,梁烨,严伟,单以银. (9~12)%Cr马氏体耐热钢中微量B元素的择优分布行为及其对微观组织与力学性能的影响[J]. 金属学报, 2020, 56(1): 53-65.
[10]	李嘉荣,谢洪吉,韩梅,刘世忠. 第二代单晶高温合金高周疲劳行为研究[J]. 金属学报, 2019, 55(9): 1195-1203.
[11]	董福涛,薛飞,田亚强,陈连生,杜林秀,刘相华. 退火温度对TWIP钢组织性能和氢致脆性的影响[J]. 金属学报, 2019, 55(6): 792-800.
[12]	冯汉臣,闵学刚,魏大圣,周立初,崔世云,方峰. 低温回火对超大形变冷拔珠光体钢丝显微组织和力学性能的影响[J]. 金属学报, 2019, 55(5): 585-592.
[13]	黄宇, 成国光, 李世健, 代卫星. Ce微合金化H13钢中一次碳化物的析出机理及热稳定性研究[J]. 金属学报, 2019, 55(12): 1487-1494.
[14]	曾荣昌, 崔蓝月, 柯伟. 医用镁合金：成分、组织及腐蚀[J]. 金属学报, 2018, 54(9): 1215-1235.
[15]	刘金辉, 宋影伟, 单大勇, 韩恩厚. 铸态和锻造态Mg-5Y-7Gd-1Nd-0.5Zr合金腐蚀行为对比研究[J]. 金属学报, 2018, 54(8): 1141-1149.

Viewed

Full text

Abstract

Cited

Shared

Discussed