金属学报  2008, Vol. 44 Issue (1): 29-33

论文 本期目录 | 过刊浏览 |

准同型相界附近PLZT铁电陶瓷相变的原位Raman谱观测

刘怡萱;程璇;张颖

厦门大学

Phase Transitions of PLZT Ceramics near MPB Observed by In-situ Raman Spectroscopy

;CHENG Xuan;

厦门大学

刘怡萱; 程璇; 张颖 . 准同型相界附近PLZT铁电陶瓷相变的原位Raman谱观测[J]. 金属学报, 2008, 44(1): 29-33 .
, , . Phase Transitions of PLZT Ceramics near MPB Observed by In-situ Raman Spectroscopy[J]. Acta Metall Sin, 2008, 44(1): 29-33 .

摘要 参考文献 相关文章 Metrics 全文: PDF(227 KB)   摘要: 对Zr与Ti的原子比约为52/48, 掺杂了少量La、Mn和 Nb的PLZT铁电陶瓷进行了不同 温度下的原位Raman谱观测, 对所获得的谱图进行温度分布修正, 再利用阻尼-谐振-振荡器模型的光谱响应函数及Gauss 分布函数对所得结果进行分峰拟合, 得到了各Raman峰的波数和峰强随温 度的变化规律. 结果表明, 准同型相界附近的PLZT铁电陶瓷在 47—600 ℃升温过程中, 于240和360 ℃分别发生两次相变, 表明 样品中可能存在混合相；通过比较未极化和极化样品的Raman 谱峰的变化结果, 分析了预极化处理对相变的影响. 关键词 ： 准同型相界,  铁电陶瓷,  相变     Abstract：In-situ Raman spectroscopy was employed to investigate PLZT ceramics (atomic ratio Zr/Ti=52/48, doped with small amount of La, Mn and Nb) at different temperatures. The observed Raman spectra were modified by the Bose population factor, and curve-fitted by the damped-harmonic-oscillator model and Gauss distribution function. Accordingly, the variations of Raman shifts and intensities of soft modes with temperatures were obtained. It confirmed that two types of phase transitions near morphotropic phase boundary (MPB) occurred at 240℃ and 360℃, respectively, when the temperatures increased from 47 to 600℃, indicating possible presence of mixed phases in PLZT ceramics. The effects of pre-polarization on phase transition are briefly discussed based on a comparison between the changes in Raman shift and intensity of soft mode observed with the unpoled powders and poled bulk specimens. Key words： morphotropic phase boundary    ferroelectric ceramics    phase transition    in-situ Raman spectroscopy 收稿日期: 2007-05-28      ZTFLH:  TB321   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 刘怡萱 程璇 张颖 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2008/V44/I1/29 [1]Zhong H S,Li Q,Zhao S X,Song F B,Li C H.Bull Chin Ceram Soc,2004;23(3):41 (钟海胜，李强，赵世玺，宋锋兵，李春红．硅酸盐通报，2004；23(3)：41) [2]Isupov V A,Stolypin Y E.J Phys Soc Jpn,1971;28:87 [3]Zhao J Q,Yue Z X,Wang W Q,Yang G,Gui Z L,Li L T.Funct Mater,2006;37:1129 (赵坚强，岳振星，王伟强，杨刚，桂治轮，李龙土．功能材料，2006；37：1129) [4]Noheda B,Gonzalo J A,Cross L E,Guo R,Park S E,Cox D E,Shirane G.Phys Rev,2000;61B:8687 [5]Noheda B,Cox D E,Shirane G,Guo R,Jones B,Cross L E.Phys Rev,2000;63B:014103 [6]Bouzid A,Bourim E M,Gabbay M,Fantozzi G.J Eur Ceram Soc,2005;25:3213 [7]Guarany C A,Pelaio L H Z,Araújo E B,Yukimitu K, Moraes J C S,Eiras J A.J Phys:Condens Matter,2003; 15:4851 [8]Rossetti G A,Zhang W,Khachaturyan A G.Appl Phys Lett,2006;88:072912 [9]Rouquette J,Haines J,Bornand V,Pintard M,Ph P, Sauvajol J L.Phys Rev,2006;73B:224118 [10]Guo R,Cross L E,Park S E,Noheda B,Cox D E,Shirane G.Phys Rev Lett,2000;84:5423 [11]Zhao X,Qu W,He H,Vittayakorn N,Tan X.J Am Ceram Soc,2006;89:202 [12]Tang X G,Liu Q X,Wang J,Chen-Wang L H.Prog Phys, 2006;26:500 (唐新佳，刘秋香，王杰，陈王丽华．物理学进展，2006；26：500) [13]Lee J K,Yi J Y,Hong K S,Park S E,Millan J.J Appl Phys,2002;91:4474 [14]Burns G,Scott B A.Phys Rev Lett,1970;25:167 [15]Svitelskiy O,Toulouse J,Yong G,Ye Z-G.Phys Rev,2003; 68B:104107 [16]Carabatos Nedelec C,Becker P.J Raman Spectrosc,1997; 28:663 [17]Angel S M,Carrabba M,Cooney T F.Spectrochim Acta, 1995;51A:1779 [18]Sun Q C,Lu C M,Xu M X.Rare Met Mater Eng,2006; 35:1101 (孙清池，陆翠敏，徐明霞．稀有金属材料与工程，2006；35：1101)N [1] 白佳铭, 刘建涛, 贾建, 张义文. 高W高Ta型粉末高温合金的蠕变性能及溶质原子偏聚[J]. 金属学报, 2023, 59(9): 1230-1242. [2] 冯艾寒, 陈强, 王剑, 王皞, 曲寿江, 陈道伦. 低密度Ti2AlNb基合金热轧板微观组织的热稳定性[J]. 金属学报, 2023, 59(6): 777-786. [3] 张开元, 董文超, 赵栋, 李世键, 陆善平. 固态相变对Fe-Co-Ni超高强度钢长臂梁构件焊接-淬火过程应力和变形的影响[J]. 金属学报, 2023, 59(12): 1633-1643. [4] 王重阳, 韩世伟, 谢峰, 胡龙, 邓德安. 固态相变和软化效应对超高强钢焊接残余应力的影响[J]. 金属学报, 2023, 59(12): 1613-1623. [5] 姜江, 郝世杰, 姜大强, 郭方敏, 任洋, 崔立山. NiTi-Nb原位复合材料的准线性超弹性变形[J]. 金属学报, 2023, 59(11): 1419-1427. [6] 李小兵, 潜坤, 舒磊, 张孟殊, 张金虎, 陈波, 刘奎. W含量对Ti-42Al-5Mn-xW合金相转变行为的影响[J]. 金属学报, 2023, 59(10): 1401-1410. [7] 李赛, 杨泽南, 张弛, 杨志刚. 珠光体-奥氏体相变中扩散通道的相场法研究[J]. 金属学报, 2023, 59(10): 1376-1388. [8] 孙毅, 郑沁园, 胡宝佳, 王平, 郑成武, 李殿中. 3Mn-0.2C中锰钢形变诱导铁素体动态相变机理[J]. 金属学报, 2022, 58(5): 649-659. [9] 李伟, 贾兴祺, 金学军. 高强韧QPT工艺的先进钢组织调控和强韧化研究进展[J]. 金属学报, 2022, 58(4): 444-456. [10] 原家华, 张秋红, 王金亮, 王灵禺, 王晨充, 徐伟. 磁场与晶粒尺寸协同作用对马氏体形核及变体选择的影响[J]. 金属学报, 2022, 58(12): 1570-1580. [11] 杨平, 王金华, 马丹丹, 庞树芳, 崔凤娥. 成分对真空脱锰法相变控制高硅电工钢{100}织构的影响[J]. 金属学报, 2022, 58(10): 1261-1270. [12] 胡标, 张华清, 张金, 杨明军, 杜勇, 赵冬冬. 界面热力学与晶界相图的研究进展[J]. 金属学报, 2021, 57(9): 1199-1214. [13] 冯苗苗, 张红伟, 邵景霞, 李铁, 雷洪, 王强. 耦合热力学相变路径预测Fe-C包晶合金宏观偏析[J]. 金属学报, 2021, 57(8): 1057-1072. [14] 李学达, 李春雨, 曹宁, 林学强, 孙建波. 高强管线钢焊接临界再热粗晶区中逆转奥氏体的逆相变晶体学[J]. 金属学报, 2021, 57(8): 967-976. [15] 王金亮, 王晨充, 黄明浩, 胡军, 徐伟. 低应变预变形对变温马氏体相变行为的影响规律及作用机制[J]. 金属学报, 2021, 57(5): 575-585. Viewed Full text Abstract Cited   Shared      Discussed