金属学报  2012, Vol. 48 Issue (3): 357-362    DOI: 10.3724/SP.J.1037.2011.00587
  论文 本期目录 | 过刊浏览 |
AZ31镁合金单轴压缩中孪生行为研究
黄洪涛1), 刘伟1), A. Godfrey1),  唐瑞鹤1), 刘庆2)
1) 清华大学材料科学与工程系, 北京 100084
2) 重庆大学材料科学与工程学院, 重庆 400044
STUDY OF TWIN BEHAVIOR DURING UNIAXIAL COMPRESSION OF AZ31 MAGNESIUM ALLOY
HUANG Hongtao1), LIU Wei1), A. Godfrey1), TANG Ruihe1), LIU Qing2)
1) Department of Materials Science and Engineering, Tsinghua University, Beijing 100084
2) School of Materials Science and Engineering, Chongqing University, Chongqing 400044
全文: PDF(3249 KB)  
摘要: 本文采用EBSD技术研究了室温下AZ31镁合金单轴压缩实验中不均匀变形对孪生行为的影响. 死区、易变形区、自由变形区处孪生分数统计结果表明, 当应变小于8%时, 3处孪生分数不相等, 应变增加到8\%时, 3处孪生分数均达到90\%左右, 孪生基本完全, 不均匀变形在低应变下对3处孪生分数影响很大, 而在高应变下影响很小. 对2\%应变下3处孪生变体选择机制进行分析, 发现80%以上开动的孪生变体都是对应第一大和第二大Schmid因子变体, 表明3处孪生变体激活均满足Schmid定律. 由于应力状态不同, 自由变形区同时开动两个变体的晶粒百分数大于死区和易变形区.
关键词 AZ31拉伸孪生孪生分数变体选择    
Abstract:The effect of inhomogeneous deformation on twinning behavior during uniaxial compression of AZ31 magnesium alloy at room temperature was investigated with electron backscattered diffraction (EBSD technique. The evolution of twin area fraction in three locations, typical of a dead zone, an easy zone and a free zone with strain was analyzed. The results show that the twin area fractions at the locations in dead zone, easy zone and free zone are different at compression strains less than 8\%. As compression strain reaches 8%, the area fraction of extension twins at these three locations is almost the same, and is about 90\%. Inhomogeneous deformation exerts much effect on the twin area fraction at the locations in the three zones at low strains while exerts little effect at high strains. Twin variant selection in the three zones at 2% strain was also analyzed. The results show that the twin variant activation is governed by the Schmid factor criterion in all the three zones. However, the percentage of grains with two twin variant types in free zone is higher than that in dead zone and easy zone, due to the different stress states in this location.
Key wordsAZ31    extension twinning    twin area fraction    variant selection
收稿日期: 2011-09-17     
ZTFLH: 

TG146.2

 
基金资助:

国家重点基础研究发展计划资助项目2007CB613703

通讯作者: 刘伟     E-mail: liuw@mail.tsinghua.edu.cn
Corresponding author: LIU Wei     E-mail: liuw@mail.tsinghua.edu.cn
作者简介: 黄洪涛, 男, 1983年生, 博士生

引用本文:

黄洪涛 刘伟 A. Godfrey 唐瑞鹤 刘庆. AZ31镁合金单轴压缩中孪生行为研究[J]. 金属学报, 2012, 48(3): 357-362.
HUANG Hong-Shou, LIU Wei, TANG Rui-He, LIU Qiang. STUDY OF TWIN BEHAVIOR DURING UNIAXIAL COMPRESSION OF AZ31 MAGNESIUM ALLOY. Acta Metall Sin, 2012, 48(3): 357-362.

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2011.00587      或      https://www.ams.org.cn/CN/Y2012/V48/I3/357

[1] Agnew S R, Duygulu O. Int J Plast, 2005; 21: 1161

[2] Liu Q. Acta Metall Sin, 2010; 46: 1458

(刘庆. 金属学报, 2010; 46: 1458)

[3] Jain A, Agnew S R. Mater Sci Eng, 2007; A462: 29

[4] Chapuis A, Driver J H. Acta Mater, 2011; 59: 1986

[5] Barnett M R. Mater Sci Eng, 2007; A464: 1

[6] Barnett M R. Mater Sci Eng, 2007; A464: 8

[7] Martin E, Capolungo L, Jiang L, Jonas J J. Acta Mater, 2010; 58: 3970

[8] Barnett M R, Keshavarz Z, Beer A G, Ma X. Acta Mater, 2008; 56: 5

[9] Barnett M R. Scr Mater, 2008; 59: 696

[10] Meyers M A, Vohringer O, Lubarda V A. Acta Mater, 2001; 49: 4025

[11] Barnett M R, Keshavarz Z, Beer A G, Atwell D. Acta Mater, 2004; 52: 5093

[12] Jiang L, Jonas J J, Luo A A, Sachdev A K, Godet S. Mater Sci Eng, 2007; A445–446: 302

[13] Jiang L, Jonas J J, Luo A A, Sachdev A K, Godet S. Scr Mater, 2006; 54: 771

[14] Knezevic M, Levinson A, Harris R, Mishra R K, Doherty R D, Kalidindi S R. Acta Mater, 2010; 58: 6230

[15] Koike J, Sato Y, Ando D. Mater Trans, 2008; 49: 2792

[16] Yang X Y, Zhang L. Acta Metall Sin, 2009; 45: 1303

(杨续跃, 张雷. 金属学报, 2009; 45: 1303)

[17] Wang Y N, Huang J C. Acta Mater, 2007; 55: 897

[18] Jiang J, Godfrey A, Liu Q. Mater Sci Technol, 2005; 21: 1417

[19] Gharghouri M A, Weatherly G C, Embury J D, Root J. Philos Mag, 1999; 79A: 1671

[20] Godet S, Jiang L, Luo A A, Jonas J J. Scr Mater, 2006; 55: 1055

[21] Jiang J, Godfrey A, Liu W, Liu Q. Scr Mater, 2008; 58: 122

[22] Park S H, Hong S G, Lee C S. Scr Mater, 2010; 62: 202

[23] Hong S G, Park S H, Lee C S. Acta Mater, 2010; 58: 5873

[24] Venugopal S, Mannan S L, Prasad Y V R K. J Mater Proc Technol, 1997; 65: 107

[25] Nave M D, Barnett M R. Scr Mater, 2004; 51: 881

[26] Brown D W, Agnew S R, Bourke M A M, Holden T M, Vogel S C, Tome C N. Mater Sci Eng, 2005; A399: 1
[1] 韩林原, 李旋, 储成林, 白晶, 薛烽. 流场环境中AZ31镁合金的腐蚀行为研究[J]. 金属学报, 2017, 53(10): 1347-1356.
[2] 闫亚琼,罗晋如,张济山,庄林忠. 强织构AZ31镁合金板材深低温轧制过程中微观组织演变及力学性能控制研究[J]. 金属学报, 2017, 53(1): 107-113.
[3] 王丽娜,杨平,毛卫民. 高锰TRIP钢高速拉伸时的马氏体转变行为分析*[J]. 金属学报, 2016, 52(9): 1045-1052.
[4] 张金虎,徐东生,王云志,杨锐. 位错对Ti-6Al-4V合金α相形核及微织构形成的影响*[J]. 金属学报, 2016, 52(8): 905-915.
[5] 汪炳叔,邓丽萍,CHAPUIS Adrien,郭宁,李强. AZ31镁合金在平面应变压缩过程中的孪生行为研究*[J]. 金属学报, 2015, 51(12): 1441-1448.
[6] 黄洪涛,Godfrey Andrew,刘伟,付宝勤,刘庆. 多向压缩中AZ31镁合金变形行为的EBSD跟踪研究[J]. 金属学报, 2013, 49(8): 932-938.
[7] 娄超,张喜燕,汪润红,段高林,刘庆. 退孪生行为以及{1012},孪晶片层结构对镁合金力学性能的影响[J]. 金属学报, 2013, 49(3): 291-296.
[8] 黄洪涛 Godfrey Andrew 刘伟 唐瑞鹤 刘庆. 样品取向对AZ31镁合金静态再结晶行为的影响[J]. 金属学报, 2012, 48(8): 915-921.
[9] 孙朝阳 栾京东 刘赓 李瑞 张清东. AZ31镁合金热变形流动应力预测模型[J]. 金属学报, 2012, 48(7): 853-860.
[10] 罗晋如,刘庆,刘伟,Godfrey Andrew. 轧制温度对AZ31镁合金轧制板材中的{1011}-{1012}双孪生行为的影响[J]. 金属学报, 2012, 48(6): 717-724.
[11] 王西霞,郭晖, 王鼎, 白银, 杨善武, 贺信莱. Fe-C-Mn-Si钢中奥氏体共格孪晶界对贝氏体铁素体变体选择的影响[J]. 金属学报, 2012, 48(4): 385-392.
[12] 刘娟 李居强 崔振山 阮立群. 新的单参数动态再结晶动力学建模及晶粒尺寸预测[J]. 金属学报, 2012, 48(12): 1510-1519.
[13] 熊缨 程利霞. 挤压AZ31B镁合金多轴疲劳寿命预测[J]. 金属学报, 2012, 48(12): 1446-1452.
[14] 罗晋如 刘庆 刘伟 Godfrey Andrew. AZ31镁合金板轧制过程中的{10-11}-{10-12}双孪生对板材显微组织、织构、力学性能的影响[J]. 金属学报, 2011, 47(12): 1567-1574.
[15] 王东 刘杰 肖伯律 马宗义. 铝合金/镁合金搅拌摩擦焊接界面处Mg/Al反应及接头力学性能[J]. 金属学报, 2010, 46(5): 589-594.