稀土元素La对GH4151合金凝固行为的影响

doi:10.11900/0412.1961.2025.00172

金属学报 DOI: 10.11900/0412.1961.2025.00172

本期目录 | 过刊浏览

稀土元素La对GH4151合金凝固行为的影响

王倩楠¹,张瑞¹,崔传勇¹,盖永超¹,吕少敏³,谢兴飞³,曲敬龙³,张廷安²,周亦胄¹

1 中国科学院金属研究所师昌绪先进材料创新中心沈阳 110016

2 东北大学材料科学与工程学院沈阳 110819

3 北京钢研高纳科技股份有限公司北京 100081

Effect of Lanthanum on the Solidification behavior of GH4151 Superalloy

WANG Qiannan ^1,2, ZHANG Rui ¹, CUI Chuanyong ¹, GAI Yongchao ¹, LYU Shaomin ³, XIE Xingfei ³, QU Jinglong ³, ZHANG Tingan ², ZHOU Yizhou ¹

1 Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

2 School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China

3 Beijing CISRI-GAONA Material and Technology Co. Ltd., Beijing 100081, China

引用本文:

王倩楠张瑞崔传勇李璞赵春玲盖永超吕少敏谢兴飞曲敬龙张廷安周亦胄. 稀土元素La对GH4151合金凝固行为的影响[J]. 金属学报, DOI: 10.11900/0412.1961.2025.00172.

全文: PDF(3886 KB)

摘要: 为揭示稀土元素对高温合金凝固行为及铸态组织的影响，促进稀土改性变形高温合金的研制，本工作以一种含高质量分数γ′相镍基变形高温合金，即GH4151合金为研究对象，调整稀土元素La的添加量，通过对未添加La元素以及不同La含量的合金铸态组织和均匀化组织进行观察，分析了La含量（0、0.01、0.1、1（wt.%质量百分比，下同））对铸态以及均匀化态合金的枝晶形貌、偏析情况、析出相特征的影响规律。结果发现，La含量从0.01 wt.%La增加到0.1 wt.%La后，GH4151合金的一次枝晶间距和二次枝晶间距逐渐减小，当La含量增加至1 wt.%，一次枝晶间距呈增加趋势。在0.1 wt.%La合金中发现存在富La析出相，且伴随O、S等元素的富集。添加La元素可显著影响合金中(γ+γ′)共晶、Laves相、MC碳化物η相在枝晶间的析出，降低GH4151合金中Ti、Nb元素在枝晶间的偏析程度。0.01 wt.%La合金(γ+γ′)共晶明显减少，η相比例增加，随La含量提高，(γ+γ′)共晶逐渐增加，MC碳化物和η相减少。通过调控微量元素La可明显降低相同均匀化条件处理后Ti、Nb、Mo的残余偏析指数，从而提高合金的均质性。

关键词 ： GH4151合金, 稀土, La元素, 凝固行为, 偏析程度

Abstract：The high alloying degree of GH4151 alloy gives rise to severe elemental segregation. Rare earth elements (REEs) have a great influence on the as-cast microstructure. In the present study, we delved into the evolution of the both the as-cast and homogenized microstructures of GH4151 alloy, modulating the content of the REE lanthanum (La) at varying concentrations (0, 0.01, 0.1, 1 wt.%, respectively). The results demonstrated that the inclusion of 0.01 wt.% La into GH4151 alloy led to a notable reduction in both primary and secondary dendrite spacings. Furthermore, in the 0.1 wt.% La alloy, a precipitate phase comprising La, O, and S was distinctly identified. Notably, the introduction of La significantly impacted the precipitation behavior of key phases such as (γ+γ′) eutectic, Laves phase, MC carbide, and η phase within the interdendritic regions, concomitantly mitigating the degree of segregation of Ti and Nb elements. Specifically, the (γ+γ′) eutectic content was conspicuously diminished in the 0.01 wt.% La alloy, whereas the proportion of η phase was increased. As the La content increased, the (γ+γ′) eutectic content gradually augmented, while the abundances of MC carbide and η phase diminished. Crucially, the modulation of trace La content facilitated a substantial reduction in the residual segregation indices of Ti, Nb, and Mo post homogenization, thereby enhancing the homogeneity of these major segregation elements. This improvement underscores the potential of REEs, particularly La, in refining the microstructure and mitigating segregation in GH4151 alloy.

Key words： GH4151 alloy rare earth La element solidification behavior degree of segregation

收稿日期: 2025-06-17

基金资助:国家科技重大专项项目;辽宁省科技重大专项;中国科学院青年创新促进会;中国科学院C类先导专项;新材料专项

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王倩楠
	张瑞
	崔传勇
	李璞
	赵春玲
	盖永超
	吕少敏
	谢兴飞
	曲敬龙
	张廷安
	周亦胄
44.8K

链接本文:

https://www.ams.org.cn/CN/Y0/V/I/0

[1]	杨波, 陈小亮, 史晓斌, 任伟, 高恒, 宋广生. 稀土Y掺杂V-Cr合金增塑机理及透氢性能[J]. 金属学报, 2025, 61(6): 887-899.
[2]	赵广迪, 李阳, 姚晓雨, 王亮, 李渭滨, 潘玉华, 李维娟, 王兆宇. B对Fe-Cr-B-C合金凝固行为、强韧性及耐磨性的影响[J]. 金属学报, 2025, 61(5): 699-716.
[3]	王叶青, 付珂, 赵永柱, 苏礼季, 陈正. Fe₇(CoNiMn)₈₀B₁₃ 共晶高熵合金的深过冷非平衡凝固行为及微观组织演变[J]. 金属学报, 2025, 61(1): 143-153.
[4]	朱桂杰, 王思清, 查敏, 李眉娟, 孙凯, 陈东风. 稀土元素Ce对挤压态Mg-0.3Al-0.2Ca-0.5Mn合金板材体织构及力学各向异性的影响[J]. 金属学报, 2024, 60(8): 1079-1090.
[5]	王浩宇, 吕熙睿, 陈琦, 熊瑛, 罗志新, 张洁, 王京阳. 高熵稀土单硅酸盐环境障涂层局域结构的原子对分布函数解析[J]. 金属学报, 2024, 60(8): 1130-1140.
[6]	刘仲武, 周帮, 廖雪峰, 何家毅. 全高丰度稀土(Ce, La, Y)-Fe-B永磁的研究现状和未来发展[J]. 金属学报, 2024, 60(5): 585-604.
[7]	王法, 江河, 董建新. 高合金化GH4151合金复杂析出相演变行为[J]. 金属学报, 2023, 59(6): 787-796.
[8]	王京阳, 孙鲁超, 罗颐秀, 田志林, 任孝旻, 张洁. 以抗CMAS腐蚀为目标的稀土硅酸盐环境障涂层高熵化设计与性能提升[J]. 金属学报, 2023, 59(4): 523-536.
[9]	杨天野, 崔丽, 贺定勇, 黄晖. 选区激光熔化AlSi10Mg-Er-Zr合金微观组织及力学性能强化[J]. 金属学报, 2022, 58(9): 1108-1117.
[10]	李民, 李昊泽, 王继杰, 马颖澈, 刘奎. 稀土Ce对薄带连铸无取向6.5%Si钢组织、高温拉伸性能和断裂模式的影响[J]. 金属学报, 2022, 58(5): 637-648.
[11]	刘洁, 徐乐, 史超, 杨少朋, 何肖飞, 王毛球, 时捷. 稀土Ce对非调质钢中硫化物特征及微观组织的影响[J]. 金属学报, 2022, 58(3): 365-374.
[12]	刘仲武, 何家毅. 钕铁硼永磁晶界扩散技术和理论发展的几个问题[J]. 金属学报, 2021, 57(9): 1155-1170.
[13]	陆斌, 陈芙蓉, 智建国, 耿如明. 应用稀土氧化物冶金技术改善高强钢焊接性能[J]. 金属学报, 2020, 56(9): 1206-1216.
[14]	朱健, 张志豪, 谢建新. 基于原位TEM拉伸的稀土H13钢塑性形变行为和断裂机制[J]. 金属学报, 2020, 56(12): 1592-1604.
[15]	黄宇, 成国光, 李世健, 代卫星. Ce微合金化H13钢中一次碳化物的析出机理及热稳定性研究[J]. 金属学报, 2019, 55(12): 1487-1494.

Viewed

Full text

Abstract

Cited

Shared

Discussed