Acta Metall Sin  2010, Vol. 46 Issue (1): 19-26    DOI:
论文 Current Issue | Archive | Adv Search |
DYNAMIC RECRYSTALLIZATION OF FERRITE IN A MEDIUM-CARBON STEEL WITH TEMPERED MARTENSITE STRUCTURE DURING HOT DEFORMATION
LI Longfei1); XIA Yangqing1); SUN Zuqing1); YANG Wangyue2)
1 The State Key Laboratory for Advanced Metals and Materials; University of Science $\&$ Technology Beijing; Beijing 100083 2 School of Materials Science and Engineering; University of Science & Technology Beijing; Beijing 100083
Cite this article: 

LI Longfei, XIA Yangqing, SUN Zuqing, YANG Wangyue. DYNAMIC RECRYSTALLIZATION OF FERRITE IN A MEDIUM-CARBON STEEL WITH TEMPERED MARTENSITE STRUCTURE DURING HOT DEFORMATION. Acta Metall Sin, 2010, 46(1): 19-26.

Download:  PDF(1797KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  

For plain carbon steels, the microduplex (α+θ) structure consisting of ultrafine ferrite matrix and dispersed cementite particles demonstrates a good balance between strength and ductility as compared with a normal microstructure, e.g. ferrite plus pearlite in hypoeutectoid steels or pearlite in eutectoid steels etc.. Various thermo-mechanical treatments have been developed to obtain such microduplex (α+θ) structure. It is commonly considered that the formation of fine equiaxed ferrite grains during thermo-mechanical treatments involving hot (warm) deformation could be attributed to dynamic recrystallization (DRX) of ferrite. However, the mechanism of DRX of ferrite during the formation of the microduplex (α+θ) structure as well as the effect of cementite particles on DRX of ferrite are still not well understood. In the present work, DRX of ferrite in a medium-carbon steel with different tempered martensites was investigated by hot uniaxial compression tests at 0.01 s-1 and 700 ℃, and the effect of cementite particles with different initial states was analyzed. The results indicate that during hot deformation the coarsening of cementite particles and DRX of ferrite took place, leading to the formation of the microduplex (α+θ) structure. In comparison with static tempering, the diffusions of Fe atoms and C atoms were enhanced by hot deformation and thus the coarsening kinetics of cementite particles was accelerated by 2-3 orders of magnitude. During hot deformation the sizes of cementite particles at the boundaries of ferrite grains increased and the amount of cementite particles in ferrite grains decreased. The former is beneficial to the particle stimulated nucleation under coordinated effects of several particles, and the later can reduce the drag effect of cementite particles on the migration of grain boundaries, both of them are advantageous to DRX of ferrite. With the decrease in the size of cementite particles in the initial microstructures, the critical strain for DRX of ferrite increased, but the resultant microduplex ($\alpha+\theta$) structure is fine, and more uniform.

Key words:  medium-carbon steel      tempered martensite      ferrite      cementite particle      dynamic recrystallization     
Received:  08 June 2009     
ZTFLH:  TG142.1  
Fund: 

Supported by National Natural Science Foundation of China (No.50701004)

Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2010/V46/I1/19

[1] Ma E. Scr Mater, 2003; 49: 663

[2] Ohmori A, Torizuka S, Nagai K. ISIJ Int, 2004; 44: 1063

[3] Tsuji N, Ueji R, Minamino Y, Saito Y. Scr Mater, 2002; 46: 305

[4] Torizuka S, Ohmori A, Murty S V S N, Nagai K. Scr Mater, 2006; 54: 563

[5] Zhao M C, Hanamura T, Qiu H, Nagai K, Yang K. Scr Mater, 2006; 54: 1395

[6] Storojeva L, Ponge D, Kaspar R, Raabe R. Acta Mater, 2004; 52: 2209

[7] Li L F, Yang W Y, Sun Z Q. Metall Mater Trans, 2008; 39A: 624

[8] Poorganji B, Miyamoto G, Maki T, Furuhara T. Scr Mater, 2008; 59: 279

[9] Li Q, Wang T S, Jing T F, Gao Y W, Zhou J F, Yu J K, Li H B. Mater Sci Eng, 2009; A515: 38

[10] Wang M, Li L F, Yang W Y, Sun Z Q. Acta Metall Sin, 2007; 43: 1009

(王猛, 李龙飞, 杨王玥, 孙祖庆. 金属学报, 2007; 43: 1009)

[11] Wang M, Li L F, Yang W Y, Sun Z Q. J Univ Sci Technol Beijing, 2008; 30: 993

(王猛, 李龙飞, 杨王玥, 孙祖庆. 北京科技大学学报, 2008; 30: 993)

[12] Tsuchiyama T, Miyamoto Y, Takaki S. ISIJ Int, 2001; 41: 1047

[13] Kramer J J, Pound G M, Mehl R F. Acta Metall, 1958; 6: 763

[14] Stuart H, Ridley N. J Iron Steel Inst, 1966; 204: 711

[15] Swartz J C. Trans Metall Soc AIME, 1969; 245: 1083

[16] Smith R P. Trans Metall Soc AIME, 1962; 224: 105

[17] Li C Y, Blakely J M, Feingold A H. Acta Metall, 1966; 14: 1397

[18] Chattopadhyay S, Sellars C M. Acta Metall, 1982; 30: 157

[19] Fridberg J, Torndahl L E, Hillert M. Jernkont Ann, 1969; 153: 263

[1] LI Fulin, FU Rui, BAI Yunrui, MENG Lingchao, TAN Haibing, ZHONG Yan, TIAN Wei, DU Jinhui, TIAN Zhiling. Effects of Initial Grain Size and Strengthening Phase on Thermal Deformation and Recrystallization Behavior of GH4096 Superalloy[J]. 金属学报, 2023, 59(7): 855-870.
[2] WANG Zhoutou, YUAN Qing, ZHANG Qingxiao, LIU Sheng, XU Guang. Microstructure and Mechanical Properties of a Cold Rolled Gradient Medium-Carbon Martensitic Steel[J]. 金属学报, 2023, 59(6): 821-828.
[3] ZHAO Yafeng, LIU Sujie, CHEN Yun, MA Hui, MA Guangcai, GUO Yi. Critical Inclusion Size and Void Growth in Dual-Phase Ferrite-Bainite Steel During Ductile Fracture[J]. 金属学报, 2023, 59(5): 611-622.
[4] CHENG Yuanyao, ZHAO Gang, XU Deming, MAO Xinping, LI Guangqiang. Effect of Austenitizing Temperature on Microstructures and Mechanical Properties of Si-Mn Hot-Rolled Plate After Quenching and Partitioning Treatment[J]. 金属学报, 2023, 59(3): 413-423.
[5] LOU Feng, LIU Ke, LIU Jinxue, DONG Hanwu, LI Shubo, DU Wenbo. Microstructures and Formability of the As-Rolled Mg- xZn-0.5Er Alloy Sheets at Room Temperature[J]. 金属学报, 2023, 59(11): 1439-1447.
[6] HOU Xuru, ZHAO Lin, REN Shubin, PENG Yun, MA Chengyong, TIAN Zhiling. Effect of Heat Input on Microstructure and Mechanical Properties of Marine High Strength Steel Fabricated by Wire Arc Additive Manufacturing[J]. 金属学报, 2023, 59(10): 1311-1323.
[7] WU Caihong, FENG Di, ZANG Qianhao, FAN Shichun, ZHANG Hao, LEE Yunsoo. Microstructure Evolution and Recrystallization Behavior During Hot Deformation of Spray Formed AlSiCuMg Alloy[J]. 金属学报, 2022, 58(7): 932-942.
[8] SUN Yi, ZHENG Qinyuan, HU Baojia, WANG Ping, ZHENG Chengwu, LI Dianzhong. Mechanism of Dynamic Strain-Induced Ferrite Transformation in a 3Mn-0.2C Medium Mn Steel[J]. 金属学报, 2022, 58(5): 649-659.
[9] REN Shaofei, ZHANG Jianyang, ZHANG Xinfang, SUN Mingyue, XU Bin, CUI Chuanyong. Evolution of Interfacial Microstructure of Ni-Co Base Superalloy During Plastic Deformation Bonding and Its Bonding Mechanism[J]. 金属学报, 2022, 58(2): 129-140.
[10] PENG Jun, JIN Xinyan, ZHONG Yong, WANG Li. Influence of Substrate Surface Structure on the Galvanizability of Fe-16Mn-0.7C-1.5Al TWIP Steel Sheet[J]. 金属学报, 2022, 58(12): 1600-1610.
[11] JIANG Weining, WU Xiaolong, YANG Ping, GU Xinfu, XIE Qingge. Formation of Dynamic Recrystallization Zone and Characteristics of Shear Texture in Surface Layer of Hot-Rolled Silicon Steel[J]. 金属学报, 2022, 58(12): 1545-1556.
[12] NI Ke, YANG Yinhui, CAO Jianchun, WANG Liuhang, LIU Zehui, QIAN Hao. Softening Behavior of 18.7Cr-1.0Ni-5.8Mn-0.2N Low Nickel-Type Duplex Stainless Steel During Hot Compression Deformation Under Large Strain[J]. 金属学报, 2021, 57(2): 224-236.
[13] CHEN Wenxiong, HU Baojia, JIA Chunni, ZHENG Chengwu, LI Dianzhong. Post-Dynamic Softening of Austenite in a Ni-30%Fe Model Alloy After Hot Deformation[J]. 金属学报, 2020, 56(6): 874-884.
[14] ZHANG Yang, SHAO Jianbo, CHEN Tao, LIU Chuming, CHEN Zhiyong. Deformation Mechanism and Dynamic Recrystallization of Mg-5.6Gd-0.8Zn Alloy During Multi-Directional Forging[J]. 金属学报, 2020, 56(5): 723-735.
[15] WU Huajian, CHENG Renshan, LI Jingren, XIE Dongsheng, SONG Kai, PAN Hucheng, QIN Gaowu. Effect of Al Content on Microstructure and Mechanical Properties of Mg-Sn-Ca Alloy[J]. 金属学报, 2020, 56(10): 1423-1432.
No Suggested Reading articles found!