Investigation of Corrosion Behavior of Welded Joint of X70 Pipeline Steel for Deep Sea

doi:10.11900/0412.1961.2017.00149

Acta Metall Sin

2018, Vol. 54

Issue (4): 527-536 DOI: 10.11900/0412.1961.2017.00149

Orginal Article

Current Issue | Archive | Adv Search

Investigation of Corrosion Behavior of Welded Joint of X70 Pipeline Steel for Deep Sea

Ge MA, Xiurong ZUO(

), Liang HONG, Yinglun JI, Junyuan DONG, Huihui WANG

Key Laboratory of Material Physics, Ministry of Education, Zhengzhou University, Zhengzhou 450052, China

Cite this article:

Ge MA, Xiurong ZUO, Liang HONG, Yinglun JI, Junyuan DONG, Huihui WANG. Investigation of Corrosion Behavior of Welded Joint of X70 Pipeline Steel for Deep Sea. Acta Metall Sin, 2018, 54(4): 527-536.

Download:

HTML

PDF(6540KB)
Export: BibTeX | EndNote (RIS)

Abstract

X70 pipeline steel with thick specifications (40.5 mm) for 3500 m deep sea reached the international advanced level in the wall thickness and service depth. Due to the high heat input during the welding process, the corrosion resistance of inside welding and outside welding would vary depending on the microstructure differences. The corrosion resistance of the welded joints of X70 pipeline for deep sea was studied by the immersion test, the weight loss test, the electrochemical test in this work. The components of the passive film were analyzed by XRD and the microstructure was observed by SEM. The results show that the corrosion resistance of the weld metal is the best. The corrosion resistance of the heat affected zone follows. The corrosion resistance of the base metal is the worst. And for the same area, the corrosion resistance of the inside welding is better than that of the outside welding. The formation of dense Fe₃O₄ passivation film can effectively slow down the progress of the reaction, and the corrosion products of Fe₂O₃, FeOOH and Fe(OH)₃ which are loose in the outer layer, have no protective effect on the matrix. The microstructure of the weld metal with the best corrosion resistance is mostly the intragranular nucleation ferrite and martensite-austenite (M-A) constituent is fine and uniform. The microstructure gradient of the heat affected zone is the largest, the M-A constituent is coarse and the corrosion resistance is inferior to the weld metal. The base metal consists of ferrite and bainite, the bainite is island-like distribution and the corrosion resistance is the worst. Microstructure of the inside welding is more refined, owing to the influence of outside welding thermal cycle, and the volume fraction of M-A constituent in inside welding is higher than that of the outside welding, so the corrosion resistance is better than that of the outside welding.

Key words: X70 pipeline pitting inclusion microstructure M-A constituent

Received: 25 April 2017

ZTFLH:

TG172.6

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Ge MA
	Xiurong ZUO
	Liang HONG
	Yinglun JI
	Junyuan DONG
	Huihui WANG

URL:

https://www.ams.org.cn/EN/10.11900/0412.1961.2017.00149 OR https://www.ams.org.cn/EN/Y2018/V54/I4/527

Fig.1 Diagram (a) and macroscopic morphology (b) of X70 pipeline steel (BM—base metal, HAZ—heat affected zone, WM—weld metal, WMin—inside weld metal, HAZin—inside heat affected zone, BMin—inside base metal, WMout—outside weld metal, HAZout—outside heat affected zone, BMout—outside base metal)

Table 1 Chemical compositions of base metal and weld metal in X70 pipeline steel (mass fraction / %)

Fig.2 Macro morphologies of welded joints after immersion 2 h in 3.5%NaCl solution

(a) untreated (b) polished

Fig.3 OM images of welded joints after immersion 2 h in 3.5%NaCl solution (d—diameter)

(a) WMin (b) HAZin (c) BMin (d) WMout (e) HAZout (f) BMout

Fig.4 Statistical results of pitting corrosion of welded joints after immersion 2 h in 3.5%NaCl solution

(a) number of pits per unit area (b) proportion of pits in a certain diameter range

Fig.5 Results of weight loss test of welded joints in 3.5%NaCl solution

(a) average mass change curve (b) average corrosion rate curve

Fig.6 XRD spectra of passive film of welded joints after immersion 96 h in 3.5%NaCl solution

Fig.7 Open circuit potentials of each region of welded joints

Fig.8 Potentiodynamic polarization curves in each region of welded joints (E—potential, i—current density)

(a) outside welding (b) inside welding

Table 2 Self corrosion potential (E_corr) and self corrosion current density (i_corr) in different regions of welded joints

Fig.9 Different morphologies (a, b) and corresponding EDS analyses (c, d) of oxide inclusions of Ti (a, c) and composite oxide inclusions (b, d) in welded joints after immersion 96 h in 3.5%NaCl solution

Fig.10 SEM images of welded joints in different regions (AF—acicular ferrite, LB—lath bainite, GB—granular bainite, PF—polygonal ferrite, M-A—martensite-austenite)

(a) WM (b) coarse grain heat affected zone (CGHAZ) (c) fine grain HAZ (FGHAZ) (d) intercritical HAZ (ICHAZ) (e) BM

Fig.11 OM images of M-A constituents in each area of the outside welding

(a) WM (b) CGHAZ (c) FGHAZ (d) IGHAZ (e) BM

Fig.12 M-A constituent size distributions of per unit area of welded joints

(a) outside welding (b) inside welding

[1]	Li S S, Liu M, Zuo X R, et al.Prospect of development and application of pipeline steel for deep water[J]. Hot Work. Technol., 2013, 42(18): 23(李树森, 刘敏, 左秀荣等. 深海管线用钢开发及应用前景[J]. 热加工工艺, 2013, 42(18): 23)
[2]	Rihan R O.Galvanic corrosion of electric resistance welded X52 steel in CO2-containing solution[J]. Anti-Corros. Method. Mater., 2014, 61: 431
[3]	Zhao W, Zou Y, Matsuda K, et al.Corrosion behavior of reheated CGHAZ of X80 pipeline steel in H2S-containing environments[J]. Mater. Des., 2016, 99: 44
[4]	Alizadeh M, Bordbar S.The influence of microstructure on the protective properties of the corrosion product layer generated on the welded API X70 steel in chloride solution[J]. Corros. Sci., 2013, 70: 170
[5]	Huang M, Zhang M X, Wang Y, et al.Electrochemical behaviour of X80 pipeline steel with alumina coating[J]. Surf. Eng., 2015, 31: 295
[6]	Kuang D, Cheng Y F.Study of cathodic protection shielding under coating disbondment on pipelines[J]. Corros. Sci., 2015, 99: 249
[7]	Zhao P X, Zuo X R, Chen K, et al.Corrosion behavior of X80 pipeline steel with strain-based design[J]. Trans. Mater. Heat Treat., 2013, 34(suppl.2): 221(赵鹏翔, 左秀荣, 陈康等. X80大变形管线钢的腐蚀行为[J]. 材料热处理学报, 2013, 34(增刊 2): 221)
[8]	Wang Y P, Zuo X R, Li J L.Corrosion resistance of the welded joint of submarine pipeline steel with ferrite plus bainite dual-phase microstructure[J]. Steel Res. Int., 2015, 86: 1260
[9]	Cai G J, Li C S.Effects of Ce on inclusions and corrosion resistance of low-nickel austenite stainless steel[J]. Mater. Corros., 2015, 66: 1445
[10]	Liu C, Guo Y B, Wang D G, et al.Effects of alternating stray current on corrosion behavior of X80 pipeline steel[J]. Corros. Prot., 2015, 36: 213(刘骋, 郭岩宝, 王德国等. 交流杂散电流对X80管线钢腐蚀行为的影响[J]. 腐蚀与防护, 2015, 36: 213)
[11]	Xie Y, Li Y, Sun T, et al.Study on the protection of Q235 steel by in situ grown pure γ-FeOOH and α-FeOOH rust film[J]. Chin. Sci. Bull., 2008, 53: 2848(谢颖, 李瑛, 孙挺等. 原位生长的纯γ-FeOOH和α-FeOOH锈膜对Q235钢保护性能的研究[J]. 科学通报, 2008, 53: 2848)
[12]	Zhu J Y, Xu L N, Feng Z C, et al.Galvanic corrosion of a welded joint in 3Cr low alloy pipeline steel[J]. Corros. Sci., 2016, 111: 391
[13]	Shim J H, Cho Y W, Chung S H, et al.Nucleation of intragranular ferrite at Ti2O3 particle in low carbon steel[J]. Acta Mater., 1999, 47: 2751
[14]	Grigorovich K V, Shibaeva T V, Arsenkin A M.Effect of a pipe-steel killing technology on the composition and number of nonmetallic inclusions[J]. Russ. Metall., 2011, 2011: 927
[15]	Zheng S Q, Chen C F, Chen L Q.Influence of S contents on the hydrogen blistering and hydrogen induced cracking of A350LF2 steel[J]. Mater. Sci. Appl., 2011, 2: 917
[16]	Cheng Y Y, Chen Z Z, Niu Y J, et al. Influence of inclusions on strength and toughness of X70 pipeline steel Girth Weld [J]. Appl. Mech. Mater., 2012, 182-183: 1554
[17]	Lang F J, Huang X Q, Pang T, et al. Effect of inclusion on pitting corrosion of X80 pipeline steel [J]. Adv. Mater. Res., 2015, 1120-1121: 999
[18]	Wang J Q, Atrens A, Cousens D R, et al.Measurement of grain boundary composition for X52 pipeline steel[J]. Acta Mater., 1998, 46: 5677
[19]	Zhu Z X, Kuzmikova L, Li H J, et al.Effect of inter-critically reheating temperature on microstructure and properties of simulated inter-critically reheated coarse grained heat affected zone in X70 steel[J]. Mater. Sci. Eng., 2014, A605: 8
[20]	Alé R M, Rebello J M A, Charlier J. A metallographic technique for detecting martensite-austenite constituents in the weld heat-affected zone of a micro-alloyed steel[J]. Mater. Charact., 1996, 37: 89
[21]	Hrivnak I, Matsuda F, Li Z L, et al.Investigation of metallography and behavior of M-A constituent in Weld HAZ of HSLA steels (Materials, Metallurgy & Weldability)[J]. Trans. JWRI, 1992, 21: 241
[22]	Pardal J M, da Silva M R, Bastos I N, et al. Influence of tempering treatment on microstructure and pitting corrosion resistance of a new super ferritic-martensitic-austenitic stainless steels with 17%Cr[J]. Corros. Eng., Sci. Technol., 2016, 51: 337
[23]	Wang L W, Du C W, Liu Z Y, et al.Influence of carbon on stress corrosion cracking of high strength pipeline steel[J]. Corros. Sci., 2013, 76: 486
[24]	Masumoto T.Studies on electrolytic extraction of carbides in iron and steels[J]. Tetsu Hagané, 1969, 55: 1347(増本健. 鉄鋼中の炭化物の電解抽出条件の検討[J]. 鉄と鋼, 1969, 55: 1347)
[25]	Tsai W T, Chen J R.Galvanic corrosion between the constituent phases in duplex stainless steel[J]. Corros. Sci., 2007, 49: 3659

[1]	ZHANG Leilei, CHEN Jingyang, TANG Xin, XIAO Chengbo, ZHANG Mingjun, YANG Qing. Evolution of Microstructures and Mechanical Properties of K439B Superalloy During Long-Term Aging at 800^oC[J]. 金属学报, 2023, 59(9): 1253-1264.
[2]	LU Nannan, GUO Yimo, YANG Shulin, LIANG Jingjing, ZHOU Yizhou, SUN Xiaofeng, LI Jinguo. Formation Mechanisms of Hot Cracks in Laser Additive Repairing Single Crystal Superalloys[J]. 金属学报, 2023, 59(9): 1243-1252.
[3]	WANG Lei, LIU Mengya, LIU Yang, SONG Xiu, MENG Fanqiang. Research Progress on Surface Impact Strengthening Mechanisms and Application of Nickel-Based Superalloys[J]. 金属学报, 2023, 59(9): 1173-1189.
[4]	GONG Shengkai, LIU Yuan, GENG Lilun, RU Yi, ZHAO Wenyue, PEI Yanling, LI Shusuo. Advances in the Regulation and Interfacial Behavior of Coatings/Superalloys[J]. 金属学报, 2023, 59(9): 1097-1108.
[5]	LI Jingren, XIE Dongsheng, ZHANG Dongdong, XIE Hongbo, PAN Hucheng, REN Yuping, QIN Gaowu. Microstructure Evolution Mechanism of New Low-Alloyed High-Strength Mg-0.2Ce-0.2Ca Alloy During Extrusion[J]. 金属学报, 2023, 59(8): 1087-1096.
[6]	CHEN Liqing, LI Xing, ZHAO Yang, WANG Shuai, FENG Yang. Overview of Research and Development of High-Manganese Damping Steel with Integrated Structure and Function[J]. 金属学报, 2023, 59(8): 1015-1026.
[7]	LIU Xingjun, WEI Zhenbang, LU Yong, HAN Jiajia, SHI Rongpei, WANG Cuiping. Progress on the Diffusion Kinetics of Novel Co-based and Nb-Si-based Superalloys[J]. 金属学报, 2023, 59(8): 969-985.
[8]	ZHANG Qiliang, WANG Yuchao, LI Guangda, LI Xianjun, HUANG Yi, XU Yunze. Erosion-Corrosion Performance of EH36 Steel Under Sand Impacts of Different Particle Sizes[J]. 金属学报, 2023, 59(7): 893-904.
[9]	CHEN Runnong, LI Zhaodong, CAO Yanguang, ZHANG Qifu, LI Xiaogang. Initial Corrosion Behavior and Local Corrosion Origin of 9%Cr Alloy Steel in Cl^－Containing Environment[J]. 金属学报, 2023, 59(7): 926-938.
[10]	SUN Rongrong, YAO Meiyi, WANG Haoyu, ZHANG Wenhuai, HU Lijuan, QIU Yunlong, LIN Xiaodong, XIE Yaoping, YANG Jian, DONG Jianxin, CHENG Guoguang. High-Temperature Steam Oxidation Behavior of Fe22Cr5Al3Mo-xY Alloy Under Simulated LOCA Condition[J]. 金属学报, 2023, 59(7): 915-925.
[11]	ZHANG Deyin, HAO Xu, JIA Baorui, WU Haoyang, QIN Mingli, QU Xuanhui. Effects of Y₂O₃ Content on Properties of Fe-Y₂O₃ Nanocomposite Powders Synthesized by a Combustion-Based Route[J]. 金属学报, 2023, 59(6): 757-766.
[12]	WANG Fa, JIANG He, DONG Jianxin. Evolution Behavior of Complex Precipitation Phases in Highly Alloyed GH4151 Superalloy[J]. 金属学报, 2023, 59(6): 787-796.
[13]	WU Dongjiang, LIU Dehua, ZHANG Ziao, ZHANG Yilun, NIU Fangyong, MA Guangyi. Microstructure and Mechanical Properties of 2024 Aluminum Alloy Prepared by Wire Arc Additive Manufacturing[J]. 金属学报, 2023, 59(6): 767-776.
[14]	FENG Aihan, CHEN Qiang, WANG Jian, WANG Hao, QU Shoujiang, CHEN Daolun. Thermal Stability of Microstructures in Low-Density Ti₂AlNb-Based Alloy Hot Rolled Plate[J]. 金属学报, 2023, 59(6): 777-786.
[15]	GUO Fu, DU Yihui, JI Xiaoliang, WANG Yishu. Recent Progress on Thermo-Mechanical Reliability of Sn-Based Alloys and Composite Solder for Microelectronic Interconnection[J]. 金属学报, 2023, 59(6): 744-756.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed