The adhesive behaviour of NiCrAlY coatings with Cr-O-N diffusion barriers

;;;;;

中科院金属所

Cite this article:

;. The adhesive behaviour of NiCrAlY coatings with Cr-O-N diffusion barriers. Acta Metall Sin, 2008, 44(7): 876-882 .

Download:

PDF(3397KB)
Export: BibTeX | EndNote (RIS)

Abstract Cr-O-N films with different chemical composition were deposited using arc ion plating (AIP) between NiCrAlY coatings and the DSM11 substrate as diffusion barriers. The influences of the barriers and the roughness of the substrate on the adhesion of DSM11/Cr-O-N/NiCrAlY were investigated. In general, we observed that the NiCrAlY coating without diffusion barrier has the best adhesion. After including the Cr-O-N films, the adhesion decreased with the increasing oxygen flow rate and the adhesion of the wet blasting substrate is higher than the polishing substrate.

Key words: Cr-O-N diffusion barrier adhesion arc ion plating (AIP)

Received: 14 September 2007

ZTFLH:	TG111.5
	TG174.44

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y2008/V44/I7/876

[1]Rhys-Jones T N.Corros Sci,1989;29:623
[2]Morrai J E,Thompson M S.Surf Coat Technol,1990; 43/44:371
[3]Rairden J R.Thin Solid Films,1978;53:251
[4]Reichert K.Surf Eng,1999;15:163
[5]Cremer R,Witthaut M,Reichert K,Schierling M, Neuschiitz D.Surf Coat Technol,1998;108/109:48
[6]Knotek O,I(?)ffler F,Beele W.Surf Coat Technol,1993; 61:6
[7]Knotek O,Lugscheider E,L(?)ffler F,Beeler W.Surf Coat Technol,1994;68/69:22
[8]Wang Q M,Wu Y N,Ji A L,Ke P L,Sun C,Huang R F, Wen L S.Acta Metall Sin,2004;40:83 (王启民，武颖娜，纪爱玲，柯培玲，孙超，黄荣芳，闻立时．金属学报，2004；40：83)
[9]Li W Z,Yao Y,Wang Q M,Bao Z B,Gong J,Sun C, Jiang X.J Mater Res,2008;23:341
[10]Wang B,Song G H,Gong J,Sun C,Wen L S,Han Y F. Oxid Met,2001;56(1/2):1
[11]Liang Y J,Che Y C.Handbook of Thermodynamic Data for Inorganic Compounds.Shenyang:Northeastern Uni- versity Press,1993:49,51,122,123 (梁英教，车荫昌．无机物热力学数据手册．沈阳：东北大学出版社，1993：49，51，122，123)
[12]Chen H Y,Lu F H.J Vac Sci Technol,2003;21A:695
[13]Lu F H,Chen H Y,Hung C H.J Vac Sci Technol,2003; 21A:671
[14]Lu F H,Chen H Y.Thin Solid Films,2001;398:368

[1]	Chao XIA, Shi QIAN, Donghui WANG, Xuanyong LIU. Properties of Carbon Ion Implanted Biomedical Titanium[J]. 金属学报, 2017, 53(10): 1393-1401.
[2]	Jianxiong ZOU,Bo LIU,Liwei LIN,Ding REN,Guohua JIAO,Yuanfu LU,Kewei XU. Microstructure and Thermal Stability of MoC DopedRu-Based Alloy Films as Seedless Diffusion Barrier[J]. 金属学报, 2017, 53(1): 31-37.
[3]	Zujiang HUANG, Min ZHOU, Yang YANG, Quanzhi CHEN, Shiguang TANG, Weizhou LI. STUDY OF ANODIC ALUMINUM OXIDE FILM AS AN INTERLAYER TO SUPPRESS ELEMENT DIFFUSION[J]. 金属学报, 2016, 52(3): 341-348.
[4]	LIAN Feng, REN Hongmei, GUAN Shankun, ZHANG Huichen. INFLUENCE OF INTERFACE EFFECT ON ADHESION OF CHLORELLA ON TITANIUM ALLOY SURFACE[J]. 金属学报, 2014, 50(9): 1146-1152.
[5]	PENG Xiao, WANG Fuhui. HIGH TEMPERATURE CORROSION OF NANO-CRYSTALLINE METALLIC MATERIALS[J]. 金属学报, 2014, 50(2): 202-211.
[6]	ZHANG Lidong, WANG Fei, CHEN Shunli, WANG Yuan. FABRICATION AND THERMAL STABILITY OF AlCrTaTiNi/(AlCrTaTiNi)N BILAYER DIFFUSION BARRIER[J]. 金属学报, 2013, 49(12): 1611-1616.
[7]	. HIGH TEMPERATURE OXIDATION RESISTANCE AND MECHANICAL PROPERTIES OF NiCrAlY/Al--Al₂O₃ COATINGS ON AN ORTHORHOMBIC Ti₂AlNb ALLOY[J]. 金属学报, 2012, 48(5): 579-586.
[8]	LU Xuyang, YU Daqian, JIANG Sumeng, LIU Shanchuan, GONG Jun, SUN Chao. HOT CORROSION BEHAVIOR OF A (NiCoCrAlYSiB+AlSiY) COMPOSITE COATING[J]. 金属学报, 2012, 48(4): 461-468.
[9]	FAN Yongzhong ZHANG Shujuan TU Jinwei SUN Xia LIU Fang LI Mingsheng. INFLUENCE OF DOPING WITH Si AND Y ON STRUCTURE AND PROPERTIES OF (Ti, Al)N COATING[J]. 金属学报, 2012, 48(1): 99-106.
[10]	ZHANG Lu SHI Nanlin GONG Jun PEI Zhiliang GAO Lijun SUN Chao. PREPARATION OF COMPOSITE COATING (Al+Al₂O₃) ON SiC LONG FIBER[J]. 金属学报, 2011, 47(4): 497-501.
[11]	SHI Yongjuan REN Yibin ZHANG Bingchun YANG Ke. THE EFFECT OF PASSIVATION ON THE HAEMOCOMPATIBILITY OF 316L STAINLESS STEEL[J]. 金属学报, 2011, 47(12): 1575-1580.
[12]	LI Weizhou WANG Qimin GONG Jun SUN Chao JIANG Xin. ONE-STEP DEPOSITION AND INTERFACIAL ADHESIVE STRENGTH OF THE MULTILAYER SYSTEM WITH A DIFFUSION BARRIER[J]. 金属学报, 2010, 46(5): 561-568.
[13]	CAI Hui WANG Fei WANG Yaping SONG Xiaoping DING Bingjun. FABRICATION OF Cu/Si COMPOSITES ON SOL–GEL PRETREATED Si POWDERS[J]. 金属学报, 2009, 45(10): 1261-1266.
[14]	LI Jianguo; Hu Dongping; MEI Jun; LIU Shi; LI Yiyi. Enhancing Adhesion Between Diamond Film and WC--Co Substrate[J]. 金属学报, 2006, 42(7): 763-769 .
[15]	WANG Qimin; WU Yingna; KE Peiling; JI Ailing; SUN Chao; HUANG Rongfang; WEN Lishi. HOT CORROSION BEHAVIOR OF Ni--Co--Cr--Al--Y--Si--B COATING DEPOSITED BY AIP[J]. 金属学报, 2004, 40(4): 399-403 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed