金属学报  1998, Vol. 34 Issue (10): 1089-1094

论文 本期目录 | 过刊浏览 |

Fe-2Ce和Fe-5Ce合金在600-800℃空气中的氧化行为

曾潮流;王文;F.C.Rizzo;吴维

中国科学院金属腐蚀与防护研究所腐蚀与防护国家重点实验室;沈阳;110015;中国科学院金属腐蚀与防护研究所腐蚀与防护国家重点实验室;沈阳;110015;里约热内卢天主教大学;巴西里约热内卢;38008;中国科学院金属腐蚀与防护研究所腐蚀与防护国家重点实验室;沈阳;110015

THE OXIDATION OF Fe-2Ce and Fe-5Ce BINARY ALLOYS AT 600-800℃ IN AIR

ZENG Chaoliu; WANC Wen; F. C. Rizzo; WU Weitao(State Key Laboratory for Corrosion and Protection; Institute of Corrosion and Protection of Metals;The Chinese Academy of Sciences; Shenyang 110015)(Pontificia Universidade Catolica do Rio de Janeiro; Rio de Janeiro 38008; Brazil)Correspondent: ZENG Chaoliu; associate professor; Tel: (024)23915910; Fax: (024)23894149;E-mail: clzeng@icpm.syb.ac.cn

曾潮流;王文;F.C.Rizzo;吴维. Fe-2Ce和Fe-5Ce合金在600-800℃空气中的氧化行为[J]. 金属学报, 1998, 34(10): 1089-1094.
, , , . THE OXIDATION OF Fe-2Ce and Fe-5Ce BINARY ALLOYS AT 600-800℃ IN AIR[J]. Acta Metall Sin, 1998, 34(10): 1089-1094.

摘要 参考文献 相关文章 Metrics 全文: PDF(2006 KB)   摘要: 研究了二元Fe-2Ce和Fe-5Ce合金及纯Fe在600-800℃空气中的氧化行为．纯Fe在该温度范围的氧化均符合抛物线规律.Fe-5Ce合金在800℃氧化近似符合抛物线氧化规律，但在600和700℃则明显由两个抛物线阶段组成．Fe-2Ce合金在三个温度下近似抛循抛物线氧化规律．除Fe-5Ce合金在700℃氧化初期外,Fe-Ce合金在700和800℃的氧化速度比纯Fe低．但在600℃，Fe-Ce合金的氧化速度仍高于纯Fe．在700和800℃时，在Fe-Ce表面除形成三种Fe的氧化物外，还在氧化膜的内层形成双相氧化物CeFeO3．而在600℃时，仅形成Fe的氧化物和CeO2，并且FeO在Fe的氧化物中所占比例很小．此外，讨论了Ce在Fe-Ce合金氧化过程中的作用． 关键词 ： Fe,  Ce,  氧化     Abstract：The okidation of pure Fe and Fe-Ce alloys containing 2 and 5 Ce (atomicfraction,%) has been studied at 600-800℃ in air. The okidstion curves of pure Fe at 600, 700and 800 ℃ follow the parabolic rate law. The oxidation curve of the Fe-5Ce at 800 ℃ followsthe approximately parabolic rate law, but includes two distinct parabolic stages at 600 and 700℃. The Fe-2Ce goes through an appropriately parabolic oxidstion at the three temperatures.The Fe-2Ce and Fe-5Ce alloys are oxidized slower than pure Fe at 700 and 800 ℃ except inthe initial oxidation stage of the Fe-5Ce at 700℃, while go through a faster oxidation thanpure Fe at 600 ℃. Besides three Fe chides, double chide CeFeO3 also forms in the inner part ofthe scale. Nevertheless, only Fe oxides and CeO2 form in the case of the oxidation at 600 ℃Moreover, FeO only accounts for a small part of the total Fe oxides. Additionally, the effect ofCe in the oxidation of the Fe-Ce alloys has been discussed. Key words： Fe    Ce    oxidation 收稿日期: 1998-10-18      基金资助:国家自然科学基金!59571056 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 曾潮流 王文 F.C.Rizzo 吴维 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I10/1089 1 Wood G C, Stott F H. In: Aspp R A ed., High Teoprature Corrostion, Houston, TX: NACE, 1983 2 Whittle D P, Stringer J. Philos Trans R Soc London, 1980; 295A: 309 3 Nagai H, Ishikaw S, Amano N, Shoji K. Trans J Inst Met, 1985; 26: 753 4 Rhys-Hones T N, Grabke H J, Kudielka H. Wich Korro, 1987; 38: 65 5 Papaiacovou P Hussey R J, Mitchell D F, Graham M J. Corms Sci,1990; 4/5: 451 6 Niu Y, Gesmundo F, Wu W T, Zeng C L, Viani F. Acta Metall Sin (Engl Lett), 1996; 9:1 7 Niu Y, Gesmundo F, Zeng C L, Wu W T, Viani F. Oxid Met, 1997; 48: 243 8 Niu Y, Gesmundo F, Cedello P, Yan R Y, Viani F, Wu W T. Corros Sci, 1997; 39: 1093 9 Castello P, Fu G Y, Niu Y, Gesmundo F, Viani F. Oxid Met, 1998; 49: 71 10 Gesmundo F, Niu Y, Viani F. Orid Met, 1995; 43: 379 11 Gesmundo F, Viani F, Niu Y. Oxid Met, 1994; 42: 409 [1] 丁桦, 张宇, 蔡明晖, 唐正友. 奥氏体基Fe-Mn-Al-C轻质钢的研究进展[J]. 金属学报, 2023, 59(8): 1027-1041. [2] 常松涛, 张芳, 沙玉辉, 左良. 偏析干预下体心立方金属再结晶织构竞争[J]. 金属学报, 2023, 59(8): 1065-1074. [3] 司永礼, 薛金涛, 王幸福, 梁驹华, 史子木, 韩福生. Cr添加对孪生诱发塑性钢腐蚀行为的影响[J]. 金属学报, 2023, 59(7): 905-914. [4] 孙蓉蓉, 姚美意, 王皓瑜, 张文怀, 胡丽娟, 仇云龙, 林晓冬, 谢耀平, 杨健, 董建新, 成国光. Fe22Cr5Al3Mo-xY合金在模拟LOCA下的高温蒸汽氧化行为[J]. 金属学报, 2023, 59(7): 915-925. [5] 张德印, 郝旭, 贾宝瑞, 吴昊阳, 秦明礼, 曲选辉. Y2O3 含量对燃烧合成Fe-Y2O3 纳米复合粉末性能的影响[J]. 金属学报, 2023, 59(6): 757-766. [6] 黄鼎, 乔岩欣, 杨兰兰, 王金龙, 陈明辉, 朱圣龙, 王福会. 基体表面喷丸处理对纳米晶涂层循环氧化行为的影响[J]. 金属学报, 2023, 59(5): 668-678. [7] 沈朝, 王志鹏, 胡波, 李德江, 曾小勤, 丁文江. 镁合金抗高温氧化机理研究进展[J]. 金属学报, 2023, 59(3): 371-386. [8] 刘来娣, 丁彪, 任维丽, 钟云波, 王晖, 王秋良. DZ445镍基高温合金高温长时间氧化形成的多层膜结构[J]. 金属学报, 2023, 59(3): 387-398. [9] 李昕, 江河, 姚志浩, 董建新. O原子对高温合金基体Ni、Co和NiCr晶界作用的理论计算分析[J]. 金属学报, 2023, 59(2): 309-318. [10] 张开元, 董文超, 赵栋, 李世键, 陆善平. 固态相变对Fe-Co-Ni超高强度钢长臂梁构件焊接-淬火过程应力和变形的影响[J]. 金属学报, 2023, 59(12): 1633-1643. [11] 芮祥, 李艳芬, 张家榕, 王旗涛, 严伟, 单以银. 新型纳米复合强化9Cr-ODS钢的设计、组织与力学性能[J]. 金属学报, 2023, 59(12): 1590-1602. [12] 徐文国, 郝文江, 李应举, 赵庆彬, 卢炳聿, 郭和一, 刘天宇, 冯小辉, 杨院生. 微量Al、Ti对Inconel 690合金高温氧化行为的影响[J]. 金属学报, 2023, 59(12): 1547-1558. [13] 胡敏, 周生玉, 国京元, 胡明昊, 李冲, 李会军, 王祖敏, 刘永长. 多相Ni3Al基高温合金微区氧化行为[J]. 金属学报, 2023, 59(10): 1346-1354. [14] 金鑫焱, 储双杰, 彭俊, 胡广魁. 露点对连续退火0.2%C-1.5%Si-2.5%Mn高强钢选择性氧化及脱碳的影响[J]. 金属学报, 2023, 59(10): 1324-1334. [15] 丛鸿达, 王金龙, 王成, 宁珅, 高若恒, 杜瑶, 陈明辉, 朱圣龙, 王福会. 新型无机硅酸盐复合涂层制备及其在高温水蒸气环境的氧化行为[J]. 金属学报, 2022, 58(8): 1083-1092. Viewed Full text Abstract Cited   Shared      Discussed