金属学报  2009, Vol. 45 Issue (1): 63-66    
  论文 本期目录 | 过刊浏览 |
粒子群算法对织构分析改进最大熵法的改进
王大鹏1;王大志2;武宝林1;左良3;王福3;梁志德3
1 沈阳航空工业学院材料科学与工程学院; 沈阳 110136
2 东北大学信息科学与工程学院; 沈阳 110004
3 东北大学材料与冶金学院; 沈阳 110004
IMPROVEMENT ON THE MODIFIED MAXIMUM ENTROPY METHOD FOR TEXTURE ANALYSIS BY PARTICLE SWARM OPTIMIZATION
WANG Dapeng1; WANG Dazhi2; WU Baolin1; ZUO Liang3; WANG Fu3; LIANG Zhide3
1 School of Materials Science and Engineering; Shenyang Institute of Aeronautical Engineering; Shenyang 110136
2 College of Information Science and Engineering; Northeastern University; Shenyang 110004
3 School of Materials and Metallurgy; Northeastern University; Shenyang 110004
引用本文:

王大鹏 王大志 武宝林 左良 王福 梁志德. 粒子群算法对织构分析改进最大熵法的改进[J]. 金属学报, 2009, 45(1): 63-66.
. IMPROVEMENT ON THE MODIFIED MAXIMUM ENTROPY METHOD FOR TEXTURE ANALYSIS BY PARTICLE SWARM OPTIMIZATION[J]. Acta Metall Sin, 2009, 45(1): 63-66.

全文: PDF(556 KB)  
摘要: 

将粒子群算法(PSO)成功地应用于改进最大熵法(MMEM), 使用两张或单张部分极图数据, 即可测算出多组具有宏观对称的冷轧纯铜片样品的完整晶粒取向分布(ODF). 这一改进保留了原MMEM的特长, 用较少的实验数据即可计算出样品的真ODF, 而又消除了原法在求解非线性方程组时需要选取特定初解的困难, 从而使MMEM更具普适性和实用性.

关键词 粒子群算法织构晶粒取向分布 改进最大熵法    
Abstract

The particle swarm optimization (PSO) was successfully applied for the modified maximum entropy method (MMEM) of the quantitative texture analysis. Using two incomplete pole figures or only one incomplete pole figure, the complete orientation distributions of pure copper samples can been obtained. Such an improvement has been verified to keep the merits of primary MMEM, i.e., the complete orientation distribution function (ODF) of samples can be calculated using lesser experimental data, furthermore, the difficulty to choose a set of purposely initial solutions has also been overcome when solving the nonlinear equation, which makes the MMEM more versatile and practicable.

Key wordsparticle swarm optimization    texture    orientation distribution function    modified maximum entropy method
收稿日期: 2008-04-23     
ZTFLH: 

TG335.19

 
基金资助:

国家自然科学基金项目50771067和沈阳航空工业学院博士研究基金项目BY2009-2953资助

作者简介: 王大鹏, 男, 1972年生, 副教授

[1] Liang Z D. Acta Metall Sin, 1997; 33: 133
(梁志德. 金属学报, 1997; 33: 133)
[2] Wang F, Xu J Z, Liang Z D. Textures Microstruct, 1992; 19: 55
[3] Kennedy J, Eberhart R. Proc IEEE Int Conf Neural Networks. Piscataway, NJ: IEEE Service Center, 1995: 1942
[4] Tang J G, Zhang X M, Deng Y L, Xuan Y, Chen Z Y. Mater Sci Forum, 2007; 546: 1009
[5] Wang D Z, Wang D P, Wang D W, Zuo L, Wang F, Liang Z D. Acta Metall Sin, 2008; 44: 183
(王大志, 王大鹏, 汪定伟, 左良, 王福, 梁志德. 金属学报, 2008; 44: 183)
[6] Wang Y D, Xu J Z, Liang Z D. Textures Microstruct, 1998; 26–27: 103
[7] Jiang J X,Wang F, Liu Y S, Liang Z D. In: Liang Z D, Zuo L, Chu Y Y, eds., Proc 11th Int Conf Textures of Materials, Part 1, Beijing: International Academic Publishers, 1996: 112
[8] Shi Y, Eberhart R. IEEE Int Conf Evolutionary Computation, Piscataway, NJ: IEEE Service Center, 1998: 69
[9] Trelea I. Inf Process Lett, 2003; 85: 317
[10] Liang Z D, Xu J Z, Wang F. Three Dimensional Orientation Analysis of Textured Materials–ODF Analysis. Shenyang: Northeastern University of Technology Press, 1986: 116
(梁志德, 徐家祯, 王福. 织构材料的三维取向分析术---ODF分析. 沈阳: 东北工学院出版社, 1986: 116)

[1] 常松涛, 张芳, 沙玉辉, 左良. 偏析干预下体心立方金属再结晶织构竞争[J]. 金属学报, 2023, 59(8): 1065-1074.
[2] 娄峰, 刘轲, 刘金学, 董含武, 李淑波, 杜文博. 轧制态Mg-xZn-0.5Er合金板材组织及室温成形性能[J]. 金属学报, 2023, 59(11): 1439-1447.
[3] 姜伟宁, 武晓龙, 杨平, 顾新福, 解清阁. 热轧硅钢表层动态再结晶区形成规律及剪切织构特征[J]. 金属学报, 2022, 58(12): 1545-1556.
[4] 杨平, 王金华, 马丹丹, 庞树芳, 崔凤娥. 成分对真空脱锰法相变控制高硅电工钢{100}织构的影响[J]. 金属学报, 2022, 58(10): 1261-1270.
[5] 丁宁, 王云峰, 刘轲, 朱训明, 李淑波, 杜文博. 高应变速率多向锻造Mg-8Gd-1Er-0.5Zr合金的微观组织、织构及力学性能[J]. 金属学报, 2021, 57(8): 1000-1008.
[6] 颜孟奇, 陈立全, 杨平, 黄利军, 佟健博, 李焕峰, 郭鹏达. 热变形参数对TC18钛合金β相组织及织构演变规律的影响[J]. 金属学报, 2021, 57(7): 880-890.
[7] 左良, 李宗宾, 闫海乐, 杨波, 赵骧. 多晶Ni-Mn-X相变合金的织构化与功能行为[J]. 金属学报, 2021, 57(11): 1396-1415.
[8] 许占一, 沙玉辉, 张芳, 章华兵, 李国保, 储双杰, 左良. 取向硅钢二次再结晶过程中的取向选择行为[J]. 金属学报, 2020, 56(8): 1067-1074.
[9] 于雷,罗海文. 部分再结晶退火对无取向硅钢的磁性能与力学性能的影响[J]. 金属学报, 2020, 56(3): 291-300.
[10] 程超,陈志勇,秦绪山,刘建荣,王清江. TA32钛合金厚板的微观组织、织构与力学性能[J]. 金属学报, 2020, 56(2): 193-202.
[11] 杜子杰, 李文渊, 刘建荣, 锁红波, 王清江. CMT增材制造TC4-DT合金组织均匀性与力学性能一致性研究[J]. 金属学报, 2020, 56(12): 1667-1680.
[12] 李鑫,董月成,淡振华,常辉,方志刚,郭艳华. 等通道角挤压制备超细晶纯Ti的腐蚀性能研究[J]. 金属学报, 2019, 55(8): 967-975.
[13] 邓丽萍,崔凯旋,汪炳叔,向红亮,李强. AZ31镁合金室温多道次压缩过程微观组织和织构演变的研究[J]. 金属学报, 2019, 55(8): 976-986.
[14] 刘征,刘建荣,赵子博,王磊,王清江,杨锐. 电子束快速成形制备TC4合金的组织和拉伸性能分析[J]. 金属学报, 2019, 55(6): 692-700.
[15] 刘后龙,马明玉,刘玲玲,魏亮亮,陈礼清. 热轧板退火工艺对19Cr2Mo1W铁素体不锈钢织构与成形性能的影响[J]. 金属学报, 2019, 55(5): 566-574.