实用型数值回归法在三元铝合金互扩散系数计算中的应用* |
刘远荣,陈伟民,汤颖,杜勇,张利军( ) |
中南大学粉末冶金国家重点实验室, 长沙 410083 |
|
APPLICATION OF PRAGMATIC NUMERICAL INVERSE METHOD IN COMPUTATION OF INTERDIFFUSION COEFFICIENTS IN Al TERNARY ALLOYS |
Yuanrong LIU,Weimin CHEN,Ying TANG,Yong DU,Lijun ZHANG( ) |
State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, China |
引用本文:
刘远荣,陈伟民,汤颖,杜勇,张利军. 实用型数值回归法在三元铝合金互扩散系数计算中的应用*[J]. 金属学报, 2016, 52(8): 1009-1016.
Yuanrong LIU,
Weimin CHEN,
Ying TANG,
Yong DU,
Lijun ZHANG.
APPLICATION OF PRAGMATIC NUMERICAL INVERSE METHOD IN COMPUTATION OF INTERDIFFUSION COEFFICIENTS IN Al TERNARY ALLOYS[J]. Acta Metall Sin, 2016, 52(8): 1009-1016.
[1] | Zhang X M, Liu S D.Mater China, 2013; 32(1): 39 | [1] | (张新明, 刘胜胆. 中国材料进展, 2013; 32(1): 39) | [2] | Zhang X M, Deng Y L, Zhang Y.Acta Metall Sin, 2015; 51: 257 | [2] | (张新明, 邓运来, 张勇. 金属学报, 2015; 51: 257) | [3] | Cao D J, Ta N, Du Y, Zhang L J.Mater China, 2015; 34(1): 50 | [3] | (曹东甲, 塔娜, 杜勇, 张利军.中国材料进展, 2015; 34(1): 50) | [4] | Wei M, Tang Y, Zhang L J, Sun W H, Du Y.Metall Mater Trans, 2015; 46A: 3182 | [5] | Zhang L J, Stratmann M, Du Y, Sundman B, Steinbach I.Acta Mater, 2015; 88: 156 | [6] | Du Y, Liu S, Zhang L, Xu H, Zhao D, Wang A, Zhou L.Calphad, 2011; 35: 427 | [7] | Du Y, Zhang L, Cui S, Zhao D, Liu D, Zhang W, Sun W, Jie W.Sci China Technol Sci, 2012; 55: 306 | [8] | Liu M, Zhang L J, Chen W M, Xin J H, Du Y, Xu H H.Calphad, 2013; 41: 108 | [9] | Chen J, Zhang C, Wang J, Chen W M, Tang Y, Zhang L J, Du Y.Calphad, 2015; 50: 118 | [10] | Li J, Chen W, Liu D, Sun W, Zhang L, Du Y, Xu H.J Phase Equilib Diffusion, 2013; 34: 484 | [11] | Li J, Liu T, Chen W, Wang S, Zhang L, Du Y, Xu H.J Min Metall B-Metall, 2014; 50: 93 | [12] | Kirkaldy J S, Lane J E, Masson G R.Can J Phys, 1963; 41: 2174 | [13] | Kirkaldy J S, Young D J.Diffusion in the Condensed State. London: Institute of Metals, 1987: 41 | [14] | Zhang L, Liu D, Zhang W, Wang S, Tang Y, Ta N, Wei M, Du Y.In: Marthinsen K, Holmedal B, Li Y eds., Material Science Forum, Zurich: Trans Tech Publications, 2014: 611 | [15] | Kaufman L, ?gren J.Scr Mater, 2014; 70: 3 | [16] | Olson G B, Kuehmann C J.Scr Mater, 2014; 70: 25 | [17] | Dayananda M A, Sohn Y H.Metall Mater Trans, 1999; 30A: 535 | [18] | Zhang D, Morral J E, Brody H D.Mater Sci Eng, 2007; A447: 217 | [19] | Jaques A V, LaCombe J C.J Phase Equilib Diff, 2012; 33: 181 | [20] | Paul A.Philos Mag, 2015; 93: 2297 | [21] | Cheng K, Chen W, Liu D, Zhang L, Du Y.Scr Mater, 2014; 76: 5 | [22] | Chen W M, Zhang L J, Du Y, Tang C Y, Huang B Y. Scr Mater, 2014; 90-91: 53 | [23] | Xu H X, Chen W M, Zhang L J, Du Y, Tang C Y.J Alloy Compd, 2015; 644: 687 | [24] | Liu M. Master Thesis Central South University Changsha, 2014 | [24] | (柳萌. 中南大学硕士学位论文, 长沙, 2014) | [25] | Andersson J O, ?gren J.J Appl Phys, 1992; 72: 1350 | [26] | Manning J R.Metall Trans, 1970; 1B: 499 | [27] | Dayananda M A.Metall Trans, 1983; 14A: 1851 | [28] | Léchelle J, Noyau S, Aufore L, Arredondo A, Audubert F.Diffu Fundam Org, 2012; 17(2): 1 |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|