金属学报  2020, Vol. 56 Issue (7): 1047-1056    DOI: 10.11900/0412.1961.2019.00344
  本期目录 | 过刊浏览 |
铝电解槽中局部阴极电流增大对电解质-铝液两相流场的影响
王富强1,2, 刘伟2, 王兆文1()
1.东北大学冶金学院 沈阳 110819
2.沈阳铝镁设计研究院有限公司 沈阳 110001
Effect of Local Cathode Current Increasing on Bath-Metal Two-Phase Flow Field in Aluminum Reduction Cells
WANG Fuqiang1,2, LIU Wei2, WANG Zhaowen1()
1. School of Metallurgy, Northeastern University, Shenyang 110819, China
2. Shenyang Aluminum and Magnesium Engineering and Research Institute Co. , Ltd. , Shenyang 110001, China
引用本文:

王富强, 刘伟, 王兆文. 铝电解槽中局部阴极电流增大对电解质-铝液两相流场的影响[J]. 金属学报, 2020, 56(7): 1047-1056.
Fuqiang WANG, Wei LIU, Zhaowen WANG. Effect of Local Cathode Current Increasing on Bath-Metal Two-Phase Flow Field in Aluminum Reduction Cells[J]. Acta Metall Sin, 2020, 56(7): 1047-1056.

全文: PDF(2520 KB)   HTML
摘要: 

采用数值模拟方法建立了三维非稳态电解质-铝液两相流500 kA全槽模型,并通过铝液流速和电解质/铝液的界面变形测试数据验证了模型的准确性。在此基础上模拟并定量评估了6种实际电解生产中存在的局部阴极电流增大60%对铝液流场和界面变形产生的影响程度。结果表明,局部阴极电流增大并不能改变全槽的铝液流场和界面变形的整体趋势,只是局部位置的铝液流速和界面变形幅度略有差异,其中A2A3阴极电流增大有利于抑制B侧中部的界面隆起,极距平均改善幅度为3.0%。分别通过增大电解槽两端部,中部和A、B两侧的部分阴极电流比例对比分析了两相流场变化规律。结果表明,适当增加电解槽两端部的阴极电流有利于抑制界面变形,尤其是A1~A4和A21~A34阴极电流增加28%可将界面隆起最大值降低2.4 mm,B7~B18的极距平均拉高9.5%。该研究为母线优化和改善电解槽磁流体稳定性提供了一条新思路。

关键词 铝电解槽两相流场局部阴极电流增大界面变形数值模拟优化    
Abstract

The stability of the magnetohydrodynamics (MHD) of aluminum reduction cell is determined by the bath-metal two-phase flow field. So, konwing how to optimize the metal flow field and restrain the bath/metal interface deformation is the key to maintain the stable and efficient operation of cell. Many previous works on the bath-metal flow field are based on the static electromagnetic force stirring the melt, however, it should be have some deviation from the actual cell state. A three dimensional bath-metal two-phase quasi-steady flow model (based on transient electromagnetic force) for full 500 kA aluminum reduction cell was built by means of numerical simulation in this work, and validated by metal velocity and bath/metal interface deformation measurement in industrial cells. The effects of 60% increase of local cathode current on melt flow distribution and interface deformation were simulated and evaluated according to abnormal 6 cases in realistic electrolytic process. It was found that the increase of local cathode current has little effects on the general pattern of flow field and interface deformation in cell, but the amplitude of local metal velocity and interface deformation would be changed in certain extent. The increase of local cathode current in A2~A3 could decrease the interface height in middle cell of downstream side (side B), with anode cathode distance (ACD) increasing by 3.0%. But the other 5 cases could deteriorate the low ACD zone further in side B, especially the increase of local cathode current in A10A11, with average ACD decreasing by 4.6% in B12~B20. The solution is to cut cathode flexes partially in abnormal position to decrease the effect on the bath-metal two-phase flow. According to the evaluation results, it is found that the uneven distribution of cathode current may be helpful to decrease the interface deformation and improve the MHD stability of cell. Based on this finding, the bath-metal two-phase flow field was changed by increasing the proportion of cathode current at the two ends of cell, the middle part of cell and side A and side B respectively, and then was analyzed in this work. The simulation results show that it is beneficial to restrain the interface deformation by increasing the cathode current at both ends of cell properly, and it is also helpful to solve the cooling problem at cell ends. In particular, when the cathode currents at A1~A4 and A21~A24 increase by 28%, the distribution trend of melt flow field remains unchanged basically, and the maximum of metal velocity under A19~A20 increases by 10%, and the maximum of interface height decreases by 2.4 mm, and the average of ACD under B7~B18 increases by 9.5%. It provides a valuable reference for optimizing the busbar design and improving the cell MHD stability.

Key wordsaluminum reduction cell    two-phase flow field    local cathode current increase    interface deformation    numerical simulation    optimization
收稿日期: 2019-10-15     
ZTFLH:  TF821,O441.4  
基金资助:国家自然科学基金项目(51434005);国家自然科学基金项目(51529401)
作者简介: 王富强,男,1981年生,教授级高级工程师,博士生
Material

Density

kg·m-3

Viscosity

Pa·s

Conductivity

S·m-1

Bath2.13×1032.51×10-30.23×103
Metal2.30×1031.18×10-34.17×106
表1  物性参数
图1  电解质-铝液两相流物理模型
图2  正常槽况下铝液流速分布模拟结果
Range / mRatio / %
-0.05~-0.040.3
-0.04~-0.032.0
-0.03~-0.027.0
-0.02~-0.0121.8
-0.01~08.4
0~0.0123.9
0.01~0.0223.8
0.02~0.0312.8
0.03~0.040.1
表2  正常槽况下界面变形范围分布
图3  正常槽况下电解质/铝液界面变形模拟结果
图4  铝液流速测点位置及流速方向
图5  铝液流速模拟值与测试值对比
图6  界面变形的模拟值与测试值对比
CaseLocationMetal velocity / (m·s-1)Interface deformation / m
Max.Aver.Min.Max.
1A2A30.2150.064-0.0460.031
2A6A70.1840.068-0.0450.032
3A10A110.1840.072-0.0530.032
4A14A150.1790.071-0.0540.031
5A18A190.1990.067-0.0440.031
6A22A230.2060.067-0.0470.031
表3  6种不同槽况下两相流场的模拟结果对比
图7  局部阴极电流增大后的两相流场模拟结果
图8  A侧和B侧极距(ACD)变化幅度
CaseLocationCurrent increaseMetal velocity / (m·s-1)Interface deformation / m
%Max.Aver.Min.Max.
11AB: 1~4, 21~24100.2010.065-0.0450.030
12AB: 1~4, 21~24200.2090.064-0.0530.029
13AB: 5~2050.1770.067-0.0440.032
14B: 1~4, 21~24140.1910.067-0.0490.031
15B: 1~4, 21~24280.1960.067-0.0560.030
16B: 1~4, 21~24420.1970.067-0.0610.030
17A: 1~4, 21~24140.1970.065-0.0440.029
18A: 1~4, 21~24280.2070.063-0.0410.029
19A: 1~4, 21~24420.2150.061-0.0410.030
表4  9种对比槽况下两相流场的模拟结果汇总
图9  Case 11~case 19的B侧极距变化幅度
图10  Case 11、case 12和case 17~case 19的两相流场模拟结果
[1] Liu Y X, Li J, et al. Modern Aluminum Electrolysis [M]. Beijing: Metallurgical Industry Press, 2008: 338
[1] (刘业翔, 李 劼等. 现代铝电解 [M]. 北京: 冶金工业出版社, 2008: 338)
[2] Urata N, Arita Y, Ikeuchi H. Magnetic field and flow pattern of liquid aluminum in the reduction cells [A]. Light Metals [C]. Warrendale: Metallurgical Society of AIME, 1975: 233
[3] Mori K, Shiota K, Urata N, et al. Surface oscillation of liquid metal in aluminum reduction cells [A]. Light Metals [C]. Warrendale: Metallurgical Society of AIME, 1976: 77
[4] Arita Y, Ikeuchi H. Numerical calculation of bath and metal convection patterns and their interface profile in Al reduction cells [A]. Light Metals [C]. Warrendale: Metallurgical Society of AIME, 1981: 357
[5] Tarapore E D. Magnetic fields in aluminum reduction cells and their influence on metal pad circulation [A]. Light Metals [C]. Warrendale: Metallurgical Society of AIME, 1979: 541
[6] Ai D K. The hydrodynamics of the hall-héroult cell an overview [A]. Light Metals [C]. Warrendale: Metallurgical Society of AIME, 1985: 593
[7] Moreau R, Evans J W. An analysis of the hydrodynamics of aluminum reduction cells [J]. J. Electrochem. Soc., 1984, 131: 2251
[8] Moreau R J, Ziegler D. The moreau-evans hydrodynamic model applied to actual hall-héroult cells [J]. Metall. Trans., 1988, 19B: 737
[9] Zikanov O, Thess A, Davidson P A, et al. A new approach to numerical simulation of melt flows and interface instability in hall-héroult cells [J]. Metall. Mater. Trans., 2000, 31B: 1541
[10] Potočnik V, Laroche F. Comparison of measured and calculated metal pad velocities for different prebake cell designs [A]. Light Metals [C]. Warrendale: TMS, 2001: 419
[11] Severo D S, Gusberti V, Schneider A F, et al. Comparison of various methods for modeling the metal-bath interface [A]. Light Metals [C]. Warrendale: TMS, 2008: 413
[12] Bojarevics V, Sira S. MHD stability for irregular and disturbed aluminium reduction cells [A]. Light Metals [C]. Warrendale: TMS, 2014: 685
[13] Dupuis M, Bojarevics V. Influence of the cathode surface geometry on the metal pad current density [A]. Light Metals [C]. Warrendale: TMS, 2014: 479
[14] Severo D S, Schneider A F, Pinto E C V, et al. Modeling magneto-hydrodynamics of aluminum electrolysis cells with ANSYS and CFX [A]. Light Metals [C]. Warrendale: TMS, 2005: 475
[15] Zhou P, Zhou N J, Mei C, et al. Numerical calculation and industrial measurements of metal pad velocities in hall-héroult cells [J]. Trans. Nonferrous Met. Soc. China, 2003, 13: 208
[16] Li M, Zhou J M, Wang C H. Coupled simulation of multiple physical fields in a 300 kA aluminum electrolysis cell [J]. Chin. J. Process Eng., 2007, 7: 354
[16] (李 茂, 周孑民, 王长宏. 300 kA铝电解槽电、磁、流多物理场耦合仿真 [J]. 过程工程学报, 2007, 7: 354)
[17] Zhou J M, Li M, Jiang S J. Two-phase simulation and its interface tracking of fluid flow in aluminum electrolysis cell [J]. J. Cent. South Univ. (Sci. Technol.), 2007, 38: 267
[17] (周孑民, 李 茂, 蒋胜矩. 铝电解槽磁流体的两相模拟及其界面追踪 [J]. 中南大学学报(自然科学版), 2007, 38: 267)
[18] Liu W, Li J, Lai Y Q, et al. Development and application of electro-magneto-flow mathematic model of aluminum reduction cells [J]. Chin. J. Nonferrous Met., 2008, 18: 909
[18] (刘 伟, 李 劼, 赖延清等. 铝电解槽电磁流场的数学建模与应用 [J]. 中国有色金属学报, 2008, 18: 909)
[19] Xu Y J. A study of multi-physical fields coupled modeling and structure optimization of large-scale energy-saving aluminum reduction cells [D]. Changsha: Central South University, 2010
[19] (徐宇杰. 铝电解槽内熔体运动数学建模及应用研究 [D]. 长沙: 中南大学, 2010)
[20] He Z, Li B K, Wang F, et al. Impact of the novel cathode convex on the electrolyte/aluminum interface wave in a reduction cell [J]. J. Northeastern Univ. (Nat. Sci.), 2011, 32: 704
[20] (贺 铸, 李宝宽, 王 芳等. 电解槽内异型凸台对电解质/铝液界面波动的影响 [J]. 东北大学学报(自然科学版), 2011, 32: 704)
[21] He Z, Xia T, Xiong W, et al. Mathematical models for the novel cathode convexes in a reduction cell [J]. J. Metall., 2013, 2013: 196891
[22] Hua J S, Droste C, Einarsrud K E, et al. Revised benchmark problem for modeling of metal flow and metal heaving in reduction cells [A]. Light Metals [C]. Warrendale: TMS, 2014: 691
[23] Wang Q, Li B K, He Z, et al. Simulation of magnetohydrodynamic multiphase flow phenomena and interface fluctuation in aluminum electrolytic cell with innovative cathode [J]. Metall. Mater. Trans., 2014, 45B: 272
[24] Zhan S Q. Numerical simulation and application of multiphase flow dynamics behavior in melts of aluminum reduction cells [D]. Changsha: Central South University, 2015
[24] (詹水清. 铝电解槽熔体内多相流体动力学行为的数值模拟及应用研究 [D]. 长沙: 中南大学, 2015)
[25] Hua J S, Rudshaug M, Droste C, et al. Modelling of metal flow and metal pad heaving in a realistic reference aluminum reduction cell [A]. Light Metals [C]. Warrendale: TMS, 2016: 339
[26] Hua J S, Rudshaug M, Droste C, et al. Numerical simulation of multiphase magnetohydrodynamic flow and deformation of electrolyte-metal interface in aluminum electrolysis cells [J]. Metall. Mater. Trans., 2018, 49B: 1246
[27] Liu W, Zhou D F, Liu Y F, et al. Simulation and measurements on the flow field of 600 kA aluminum reduction pot [A]. Light Metals [C]. Warrendale: TMS, 2015: 479
[28] Dupuis M, Pagé M. Modeling gravity wave in 3D with openfoam in an aluminum reduction cell with regular and irregular cathode surfaces [A]. Light Metals [C]. Warrendale: TMS, 2016: 909
[29] Feng Y Q, Schwarz M P, Yang W, et al. Two-phase CFD model of the bubble-driven flow in the molten electrolyte layer of a hall-héroult aluminum cell [J]. Metall. Mater. Trans., 2015, 46B: 1959
[30] Mei C. Simulation and Optimization of Nonferrous Metallurgy Furnace [M]. Beijing: Metallurgical Industry Press, 2001: 74
[30] (梅 炽. 有色冶金炉窑仿真与优化 [M]. 北京: 冶金工业出版社, 2001: 74)
[31] Bradley B F, Dewing E W, Rogers J N. Metal pad velocity measurements by the iron rod method [A]. Light Metals [C]. Warrendale: Metallurgical Society of AIME, 1984: 541
[1] 毕中南, 秦海龙, 刘沛, 史松宜, 谢锦丽, 张继. 高温合金锻件残余应力量化表征及控制技术研究进展[J]. 金属学报, 2023, 59(9): 1144-1158.
[2] 王重阳, 韩世伟, 谢峰, 胡龙, 邓德安. 固态相变和软化效应对超高强钢焊接残余应力的影响[J]. 金属学报, 2023, 59(12): 1613-1623.
[3] 张开元, 董文超, 赵栋, 李世键, 陆善平. 固态相变对Fe-Co-Ni超高强度钢长臂梁构件焊接-淬火过程应力和变形的影响[J]. 金属学报, 2023, 59(12): 1633-1643.
[4] 周小宾, 赵占山, 汪万行, 徐建国, 岳强. 渣-金界面气泡夹带行为数值物理模拟[J]. 金属学报, 2023, 59(11): 1523-1532.
[5] 高建宝, 李志诚, 刘佳, 张金良, 宋波, 张利军. 计算辅助高性能增材制造铝合金开发的研究现状与展望[J]. 金属学报, 2023, 59(1): 87-105.
[6] 夏大海, 邓成满, 陈子光, 李天书, 胡文彬. 金属材料局部腐蚀损伤过程的近场动力学模拟:进展与挑战[J]. 金属学报, 2022, 58(9): 1093-1107.
[7] 胡龙, 王义峰, 李索, 张超华, 邓德安. 基于SH-CCT图的Q345钢焊接接头组织与硬度预测方法研究[J]. 金属学报, 2021, 57(8): 1073-1086.
[8] 赵婉辰, 郑晨, 肖斌, 刘行, 刘璐, 余童昕, 刘艳洁, 董自强, 刘轶, 周策, 吴洪盛, 路宝坤. 基于Bayesian采样主动机器学习模型的6061铝合金成分精细优化[J]. 金属学报, 2021, 57(6): 797-810.
[9] 李子晗, 忻建文, 肖笑, 王欢, 华学明, 吴东升. 热导型等离子弧焊电弧物理特性和熔池动态行为[J]. 金属学报, 2021, 57(5): 693-702.
[10] 杨勇, 赫全锋. 高熵合金中的晶格畸变[J]. 金属学报, 2021, 57(4): 385-392.
[11] 孙晓峰, 宋巍, 梁静静, 李金国, 周亦胄. 激光增材制造高温合金材料与工艺研究进展[J]. 金属学报, 2021, 57(11): 1471-1483.
[12] 盛鹰, 贾彬, 王汝恒, 陈国平. 一种原子尺度应变定义方法及其在识别微观缺陷演化中的应用[J]. 金属学报, 2020, 56(8): 1144-1154.
[13] 杨杰, 王雷. 核电站DMWJ中材料拘束的影响与优化[J]. 金属学报, 2020, 56(6): 840-848.
[14] 刘继召, 黄鹤飞, 朱振博, 刘阿文, 李燕. 氙离子辐照后Hastelloy N合金的纳米硬度及其数值模拟[J]. 金属学报, 2020, 56(5): 753-759.
[15] 王波,沈诗怡,阮琰炜,程淑勇,彭望君,张捷宇. 冶金过程中的气液两相流模拟[J]. 金属学报, 2020, 56(4): 619-632.