定向凝固NiAl合金的微观组织和高温力学性能Ⅱ.高温力学性能和界面 |
崔传勇 郭建亭 |
中国科学院金属研究所;沈阳 110015 |
|
引用本文:
崔传勇; 郭建亭 . 定向凝固NiAl合金的微观组织和高温力学性能Ⅱ.高温力学性能和界面[J]. 金属学报, 2000, 36(11): 1144-1148 .
[1] Whittenberger J D, Viswanadham R K, Mannan S K, Kumar K S. J Mater Res, 1989; 4: 1164 [2] Whittenberger J D, Noebe R D. Metall Mater Trans, 1996;A27: 2628 [3] Whittenberger J D, Luton M J. J Mater Res, 1995; 10:1171 [4] Jiang D T, Guo J T. Mater Sci Eng, 1998; A255: 154 [5] Jiang D T, Guo J T, Li G S, Shi C X. Acta Metall Sin,1998; 34: 1143 (姜东涛,郭建亭,李谷松,师昌绪.金属学报,1998;34:1143) [6] Cui C Y, Guo J T. Acta Metall Sin, 1999; 35: 477 (崔传勇,郭建亭.金属学报,1999;35:477) [7]Cui C Y.M S Thesis Institute of Metal Research,The Chinese Academy of Sciences, 1999 (崔传勇.中国科学院金属研究所硕士学位论文,1999) [8] Chen X F, Johnson D R, Noebe R D, Oliver B F. J MaterRes, 1995; 10: 1159 [9] Locci I E, Dickerson R M, Grag A, Noebe R D, Whittenberger J D, Nathal M V, Darolia R. J Mater Res, 1996;11: 3024 [10] Xing Z P, Dai J Y, Guo J T, An G Y, Hu Z Q. Scr MetallMater, 1994; 31: 1141 [11] Jiang D T, Guo J T. Mated Lett, 1998; 36(7): 33 [12] Whittenberger J D, Locci I E, Darolia R, Bowman R.Mater Sci Eng, 1999; A268: 165 [13] Chen R S, Guo J T, Zhou J Y. Mater Lett, 2000; 42(1):75 [14] Johnson D R, Chen X F, Oliver B F, Noebe R D, Whittenberger J D. Intermetallics, 1995; 3: 99 [15] Oh-Ishi K, Horita Z, Nemoto M. Mater Sci Eng, 1997;A239/240: 472 |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|