金属学报  1998, Vol. 34 Issue (3): 255-262

论文 本期目录 | 过刊浏览 |

Ti-47Al-2Mn-2Nb-0.8TiB_2合金韧脆转变温度及其应变速率敏感性

王瑜;林栋梁;刘俊亮;C.C.Law

上海交通大学材料科学系国家教委高温材料及高温测试开放实验室;上海;200030;上海交通大学材料科学系国家教委高温材料及高温测试开放实验室;上海;200030;上海交通大学材料科学系国家教委高温材料及高温测试开放实验室;上海;200030;Materials&MechanicsEngineering;UnitedTechnologiesCoporation-Pratt;CT06108;USA

BRITTLE-TO-DUCTILE TRANSITION TEMPERATURE AND ITS STRAIN RAf E SENSITIVITY IN Ti-47Al-2Mn-2Nb-0.8TiB_2

WANG Yu; LIN Dongliang;T. L. LIN; LIU Junliang; C. C. LAW (The Public Laboratory of State Education Commission for High Temperature Materials and High Temperature Tests; Department of Materials Science;Shanghai Jiaotong University; Shanghai 200030)(Materials & Mechanics Engineering; United Technologies Coporation-Pratt & Whitney; East Hartford;CT 06108; USA)

王瑜;林栋梁;刘俊亮;C.C.Law. Ti-47Al-2Mn-2Nb-0.8TiB_2合金韧脆转变温度及其应变速率敏感性[J]. 金属学报, 1998, 34(3): 255-262.
, , , . BRITTLE-TO-DUCTILE TRANSITION TEMPERATURE AND ITS STRAIN RAf E SENSITIVITY IN Ti-47Al-2Mn-2Nb-0.8TiB_2[J]. Acta Metall Sin, 1998, 34(3): 255-262.

摘要 参考文献 相关文章 Metrics 全文: PDF(3010 KB)   摘要: 采用拉伸试验，研究厂不同应变速率（10－5-10－1S-1）下温度对台体积分数为0．8％的TiB2、具有近全片层组织的Ti—47Al—2Mn－2Nb金属间化合物的屈服强度和延伸率的影响，得到合金韧脆转变温度随应变速率升高而升高的变化关系，确定这种含TiB2的TiAL合金的韧脆转变激活能为256kJ／mol这一数值低于无TiB2的合金的韧脆转变激活能（324kJ／mol），接近TiAl合金中原子自扩散激活能结合断口分析和理论计算结果，表明这种含TiB2的TiAl合金韧脆转变过程可能受位错攀移机制控制. 关键词 ： TIAl,  金属间化合物,  韧脆转变,  应变速率     Abstract：The effect of strain rate on the tensile yield strength and elongation of titanium aluminide has been studied. The alloy has a composition of Ti-47Al-2Mn-2Nb-0.8TiB2 (atomic fraction, %; volume fraction, %, only for TiB2) and near lamellar dricrostructure. It manifests brittle-to-ductile transition (BDT) at elevated temperature and its brittle-to-ductile transition temperature (TBDT) is positively sensitive to the strain rate. The addition of boron lowers the TBDT considerably, and the corresponding activation energy of BDT decreases to 256 kJ/mol, which is less than that of the alloy without boron (TiB2), but approximates the self-diffusion activation energy of atoms in the TiAl alloy. From additional fractography analysis and theoretical estimation, it is suggested that the BDT course of 7 titanium aluminide with the addition of boron (TiB2) is controlled by dislocation climbing. Key words： titanium aluminide    intermetullics    BDT    strain rate 收稿日期: 1998-03-18      基金资助:国家自然科学基金!59331011;;上海交通大学与美国United Technologies Coporation－Pratt ＆ Whitney公司合作研究项目 服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 王瑜 林栋梁 刘俊亮 C.C.Law 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I3/255 1 Kim Y-W. JOM, 1994; 46: 30 2 Huang S C, Hall E L. Metall Trans,1991; 22A: 47 3 Kumpfert J, Kim Y W, Dimiduk D M. Mater Sci Eny, 1995; A192/193: 465 4 王瑜, 林栋梁, 刘俊亮, Law C C. 金属学报, 1997; 33: 1021(Wang Yu, Lin dongliang, Liu Junliang, Law C C. Acta Metall Sin, 1997; 33: 1021) 5 Westwood A R C. Metall Trans, 1988; 19: 749 6 Zener C, Hollomon J. J Appl Phys, 1944; 15: 22 7 Kroll S, Mehrer H, Stolwijk N, Herzig C, Rosenkraus R, Frommeyer G. Z Mettallk, 1992; 83: 591 8 Sprengel W, Oikawa N, Nakajima H. Intermetallics, 1996; 4: 185 9 Nabarro F R N. Philos Mag 1967; 16: 231 10 Schafrik R E. Metall Trans, 1977; 8A: 1003 11 Kad B K, Fraser H L. Philos Mag, 1994; 69: 689 12 Guillard S, Rack H J. Mater Sci Eng, 1994; A183: 181 13 Godfrey A B, Loretto M H. Intermetottics, 1996; 4: 47 14 Kim Y W. In: Kim Y W, Wagner R, Yamaguchi M eds., Gamma Titanium Aboinidea, Warrendale,Pennsylvania: TMS, 1995: 637 15 Pu Z, Wu K-H. Scr Maten 1996; 34: 169M [1] 韩卫忠, 卢岩, 张雨衡. 体心立方金属韧脆转变机制研究进展[J]. 金属学报, 2023, 59(3): 335-348. [2] 王迪, 贺莉丽, 王栋, 王莉, 张思倩, 董加胜, 陈立佳, 张健. Pt-Al涂层对DD413合金高温拉伸性能的影响[J]. 金属学报, 2023, 59(3): 424-434. [3] 王凯, 晋玺, 焦志明, 乔珺威. CrFeNi中熵合金在宽温域拉伸条件下的力学行为与变形本构方程[J]. 金属学报, 2023, 59(2): 277-288. [4] 常立涛. 压水堆主回路高温水中奥氏体不锈钢加工表面的腐蚀与应力腐蚀裂纹萌生：研究进展及展望[J]. 金属学报, 2023, 59(2): 191-204. [5] 王虎, 赵琳, 彭云, 蔡啸涛, 田志凌. 激光熔化沉积TiB2 增强TiAl基合金涂层的组织及力学性能[J]. 金属学报, 2023, 59(2): 226-236. [6] 李小兵, 潜坤, 舒磊, 张孟殊, 张金虎, 陈波, 刘奎. W含量对Ti-42Al-5Mn-xW合金相转变行为的影响[J]. 金属学报, 2023, 59(10): 1401-1410. [7] 王楠, 陈永楠, 赵秦阳, 武刚, 张震, 罗金恒. 应变速率对X80管线钢铁素体/贝氏体应变分配行为的影响[J]. 金属学报, 2023, 59(10): 1299-1310. [8] 沈莹莹, 张国兴, 贾清, 王玉敏, 崔玉友, 杨锐. SiCf/TiAl复合材料界面反应及热稳定性[J]. 金属学报, 2022, 58(9): 1150-1158. [9] 刘仁慈, 王鹏, 曹如心, 倪明杰, 刘冬, 崔玉友, 杨锐. 700℃热暴露对 β 凝固 γ-TiAl合金表面组织及形貌的影响[J]. 金属学报, 2022, 58(8): 1003-1012. [10] 陈玉勇, 叶园, 孙剑飞. TiAl合金板材轧制研究现状[J]. 金属学报, 2022, 58(8): 965-978. [11] 丁宗业, 胡侨丹, 卢温泉, 李建国. 基于同步辐射X射线成像液/固复层界面氢气泡的形核、生长演变与运动行为的原位研究[J]. 金属学报, 2022, 58(4): 567-580. [12] 周丽君, 位松, 郭敬东, 孙方远, 王新伟, 唐大伟. 基于飞秒激光时域热反射法的微尺度Cu-Sn金属间化合物热导率研究[J]. 金属学报, 2022, 58(12): 1645-1654. [13] 李天瑞, 刘国怀, 于少霞, 王文娟, 张风奕, 彭全义, 王昭东. 直接包套轧制铸态Ti-46Al-8Nb合金的组织特征及热变形机制[J]. 金属学报, 2020, 56(8): 1091-1102. [14] 刘先锋, 刘冬, 刘仁慈, 崔玉友, 杨锐. Ti-43.5Al-4Nb-1Mo-0.1B合金的包套热挤压组织与拉伸性能[J]. 金属学报, 2020, 56(7): 979-987. [15] 王希,刘仁慈,曹如心,贾清,崔玉友,杨锐. 冷却速率对β凝固γ-TiAl合金硼化物和室温拉伸性能的影响[J]. 金属学报, 2020, 56(2): 203-211. Viewed Full text Abstract Cited   Shared      Discussed