一种TiAl合金的高温蠕变和疲劳行为及其寿命预测方法

于慧臣¹⁾,董成利¹⁾,焦泽辉¹⁾,孔凡涛²⁾,陈玉勇²⁾,苏勇君²⁾

1) 北京航空材料研究院航空材料检测与评价北京市重点实验室,先进高温结构材料国防科技重点实验室, 北京 100095
2) 哈尔滨工业大学金属精密热加工国防科技重点实验室, 哈尔滨 150001

HIGH TEMPERATURE CREEP AND FATIGUE BEHAVIOR AND LIFE PREDICTION METHOD OF A TiAl ALLOY

YU Huichen ¹⁾, DONG Chengli ¹⁾, JIAO Zehui¹⁾, KONG Fantao ²⁾, CHEN Yuyong ²⁾, SU Yongjun²⁾

1) Beijing Key Laboratory of Aeronautical Materials Testing and Evaluation, Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095
2) National Key Laboratory of Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001

引用本文:

于慧臣,董成利,焦泽辉,孔凡涛,陈玉勇,苏勇君. 一种TiAl合金的高温蠕变和疲劳行为及其寿命预测方法[J]. 金属学报, 2013, 49(11): 1311-1317.
YU Huichen, DONG Chengli, JIAO Zehui, KONG Fantao, CHEN Yuyong, SU Yongjun. HIGH TEMPERATURE CREEP AND FATIGUE BEHAVIOR AND LIFE PREDICTION METHOD OF A TiAl ALLOY[J]. Acta Metall Sin, 2013, 49(11): 1311-1317.

全文: PDF(804 KB)

摘要:

针对双态(duplex, DP)和全片层(fully lamellar, FL)不同组织形态的Ti－43Al－9V－Y金属间化合物合金,开展了高温蠕变(700℃)和高温低周疲劳(700和750℃)实验,研究其高温蠕变、疲劳变形行为和寿命预测方法.首先采用Omega法对2种组织形态TiAl合金的蠕变变形行为进行了数值模拟,并对其持久寿命进行了预测, 然后在Walker应变的基础上提出了新的寿命模型,对2种组织形态TiAl合金的疲劳寿命进行了预测. 研究结果表明:(1) 2种组织形态TiAl合金的高温蠕变实验曲线仅包含稳态和加速蠕变阶段, 而不包含初始蠕变阶段,且Omega法能够对2种组织形态TiAl合金的高温蠕变变形行为进行准确地表征;(2) 相同温度和应力水平下, FL组织形态TiAl合金的持久寿命比DP组织形态TiAl合金的长,且Omega法预测的持久寿命与相应的实验寿命吻合得很好;(3) 在相同温度和载荷条件下,DP组织形态TiAl合金的疲劳寿命比FL组织形态TiAl合金的长,且采用新提出的寿命模型能够对2种不同组织形态TiAl合金的疲劳寿命进行预测,预测的寿命全部位于实验寿命的±3倍分散带以内.

关键词 ：双态, 全片层, 蠕变, 低周疲劳, 寿命预测

Abstract：

Creep (at 700℃) and low cycle fatigue (at 700 and 750℃) tests of Ti－43Al－9V－Y alloy with duplex (DP) and fully lamellar (FL) microstructures are carried out to study the creep, fatigue deformation and life prediction. Firstly, Omega method is employed to characterize the creep deformation and to predict the rupture life. Secondly, the proposed fatigue life model based on walker strain is employed to predict the fatigue life for these two types of TiAl alloy. The results show that: (1) high temperature creep curves of the material of both DP and FL microstructure contain steady and accelerated creep stages other than initial creep stage, and Omega method is able to characterize the creep deformation of TiAl alloy with DP and FL microstructure; (2) the rupture time of the material of FL microstructure is longer than that of DP microstructure, and the predicted rupture time by Omega method agrees well with the test data; (3) the fatigue life of DP is longer than that of FL under the same test condition, and the predicted fatigue life is well located in the scatter band of 3 of the test fatigue life.

Key words： Duplex fully lamellar creep, low cycle fatigue life prediction

收稿日期: 2013-07-23

基金资助:

国家重点基础研究发展计划项目2011CB605506及国家自然科学基金项目51074058资助

作者简介: 于慧臣, 男, 1964年生, 博士, 研究员

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	于慧臣
	董成利
	焦泽辉
	孔凡涛
	陈玉勇
	苏勇君
44.8K

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2013.00434 或 https://www.ams.org.cn/CN/Y2013/V49/I11/1311

[1] Ding X F, Lin J P, Zhang L Q, Su Y Q, Chen G L. Acta Mater, 2012; 60: 498

[2] Henaff G, Gloanec AL. Intermetallics, 2005; 13: 543

[3] Lin J P, Xu X J, Wang Y L, Gao J F, Chen G L. Intermetallics, 2007; 15: 668

[4] Kong F T, Chen Y Y, Tian J, Chen Z Y. Mater Sci Technol, 2003; 11: 441

(孔凡涛, 陈玉勇, 田竞, 陈子勇. 材料科学与工艺, 2003; 11: 441)

[5] Wang Y H, Lin J P, He Y H. Intermetallics, 2008; 16: 215

[6] Chen G Q, Zhang B G, Liu W, Feng J C. Intermetallics, 2011; 19: 1857

[7] Zhu H L, Seo D Y, Maruyama K, Au P. Mater Sci Eng, 2008; A483－484: 533

[8] Chen Y Y, Niu H Z, Kong F T, Xiao S L. Intermetallics, 2011; 19: 1405

[9] Kassner M E, Perez－Prado M T. Prog Mater Sci, 2000; 45: 102

[10] Monkman F C, Grant N J. Proc ASTM, 1956; 56: 593

[11] Nagode A, Kosec L, Ule B. Eng Fail Anal, 2011; 18: 61

[12] Larson F R, Miller J. Trans ASME, 1952; 74: 765

[13] Orr R L, Sherby O D, Dorn J E. Trans ASM, 1954; 46: 113

[14] Manson S S, Brown W F. Proc ASTM, 1953; 53: 683

[15] Evans R, Wilshire B. Creep of Metals and Alloys. London: Institute of Metals, 1985: 1

[16] Prager M. J Pres Ves Technol, 2000; 122: 273

[17] Goodman J. Mechanics Applied to Engineering. London: Longmans, Green and Co., 1919: 631

[18] Smith J O. The Effect of Range of Stress on the Fatigue Strength of Metals.Bulletin No.334, Urbana, IL: Universityof Illinois, Engineering Experiment Station, 1942: 13

[19] Gerber H. Zeitschrift Bayerischen Architeckten Ingenieur－ Vereins, 1874; 3: 359

[20] Morrow J D. Fatigue Design Handbook－Advances in Engineering. Warrendate:Society of Automo－tive Engineers, 1968: 21

[21] Soderberg C R. Trans ASME, 1939; 52: 13

[22] Walker K. Effects of Environment and Complex Loading History on Fatigue Life.Philadelphia: American Society for Testing and Materials, 1970: 1

[23] Chen Y Y, Kong F T, Han J C, Chen Z Y, Tian J. Intermetallics, 2005; 13: 263

[24] Yeom J T, Kim J Y, Na Y S, Park N K. Met Mater Int, 2003; 9: 555

[25] Ye D Y, Wang Z L. Int J Fatigue, 2001; 23: 679

[26] Mediratta S R, Ramaswamy V, Rao P R. Int J Fatigue, 1988; 10: 13

[1]	白佳铭, 刘建涛, 贾建, 张义文. 高W高Ta型粉末高温合金的蠕变性能及溶质原子偏聚[J]. 金属学报, 2023, 59(9): 1230-1242.
[2]	陈佳, 郭敏, 杨敏, 刘林, 张军. 新型钴基高温合金中W元素对蠕变组织和性能的影响[J]. 金属学报, 2023, 59(9): 1209-1220.
[3]	冯强, 路松, 李文道, 张晓瑞, 李龙飞, 邹敏, 庄晓黎. γ' 相强化钴基高温合金成分设计与蠕变机理研究进展[J]. 金属学报, 2023, 59(9): 1125-1143.
[4]	李小琳, 刘林锡, 李雅婷, 杨佳伟, 邓想涛, 王海丰. 单一 MX 型析出相强化马氏体耐热钢力学性能及蠕变行为[J]. 金属学报, 2022, 58(9): 1199-1207.
[5]	周红伟, 高建兵, 沈加明, 赵伟, 白凤梅, 何宜柱. 高温低周疲劳下C-HRA-5奥氏体耐热钢中孪晶界演变[J]. 金属学报, 2022, 58(8): 1013-1023.
[6]	高川, 邓运来, 王冯权, 郭晓斌. 蠕变时效对欠时效7075铝合金力学性能的影响[J]. 金属学报, 2022, 58(6): 746-759.
[7]	彭子超, 刘培元, 王旭青, 罗学军, 刘健, 邹金文. 不同服役条件下FGH96合金的蠕变特征[J]. 金属学报, 2022, 58(5): 673-682.
[8]	杨志昆, 王浩, 张义文, 胡本芙. Ta含量对镍基粉末高温合金高温蠕变变形行为和性能的影响[J]. 金属学报, 2021, 57(8): 1027-1038.
[9]	张倪侦, 马昕迪, 耿川, 穆永坤, 孙康, 贾延东, 黄波, 王刚. Ag元素添加对Cu-Zr-Al基金属玻璃纳米压痕行为的影响[J]. 金属学报, 2021, 57(4): 567-574.
[10]	徐静辉, 李龙飞, 刘心刚, 李辉, 冯强. 热力耦合对一种第四代镍基单晶高温合金1100℃蠕变组织演变的影响[J]. 金属学报, 2021, 57(2): 205-214.
[11]	郭倩颖, 李彦默, 陈斌, 丁然, 余黎明, 刘永长. 高温时效处理对S31042耐热钢组织和蠕变性能的影响[J]. 金属学报, 2021, 57(1): 82-94.
[12]	周红伟, 白凤梅, 杨磊, 陈艳, 方俊飞, 张立强, 衣海龙, 何宜柱. 1100 MPa级高强钢的低周疲劳行为[J]. 金属学报, 2020, 56(7): 937-948.
[13]	张哲峰,邵琛玮,王斌,杨浩坤,董福元,刘睿,张振军,张鹏. 孪生诱发塑性钢拉伸与疲劳性能及变形机制[J]. 金属学报, 2020, 56(4): 476-486.
[14]	刘天, 罗锐, 程晓农, 郑琦, 陈乐利, 王茜. 形成Al₂O₃表层的奥氏体不锈钢加速蠕变实验研究[J]. 金属学报, 2020, 56(11): 1452-1462.
[15]	吴静,刘永长,李冲,伍宇婷,夏兴川,李会军. 高Fe、Cr含量多相Ni₃Al基高温合金组织与性能研究进展[J]. 金属学报, 2020, 56(1): 21-35.

Viewed

Full text

Abstract

Cited

Shared

Discussed