THERMAL FATIGUE BEHAVIORS OF THREE CAST NICKEL BASE SUPERALLOYS

doi:10.3724/SP.J.1037.2011.00066

Acta Metall Sin

2011, Vol. 47

Issue (9): 1129-1134 DOI: 10.3724/SP.J.1037.2011.00066

论文

Current Issue | Archive | Adv Search

THERMAL FATIGUE BEHAVIORS OF THREE CAST NICKEL BASE SUPERALLOYS

XIAO Xuan, XU Hui, QIN Xuezhi, GUO Yongan, GUO Jianting, ZHOU Lanzhang

1) School of Materials Science and Engineering, Shenyang Ligong University, Shenyang 110168
2) Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

Cite this article:

XIAO Xuan XU Hui QIN Xuezhi GUO Yongan GUO Jianting ZHOU Lanzhang. THERMAL FATIGUE BEHAVIORS OF THREE CAST NICKEL BASE SUPERALLOYS. Acta Metall Sin, 2011, 47(9): 1129-1134.

Download:

PDF(4636KB)
Export: BibTeX | EndNote (RIS)

Abstract Thermal fatigue (TF) behaviors of three Ni-based cast superalloys were investigated in the temperature ranges of 850, 900 and 950℃ to 20℃, respectively. OM and SEM were used to observe the microstructures and TF cracks of the tested specimens. The results demonstrated that the main style of crack initiation is the formation, gathering and interconnecting of oxidation cavities induced by thermal stress. Carbides, $\gamma$+$\gamma^{\prime}$ eutectics and grain boundaries can promote the initiation and propagation of TF cracks. The three alloys showed different mechanisms of TF crack propagation due to the distinct chemical compositions and microstructures. The TF cracks of equiaxial IN738 alloy propagate intergranularly, while those of the directional solidification (DS) DZ444 alloy propagate along interdendritical regions. The paths of TF crack propagation of DZ445 transfer from interdendrite to crystallographic orientation with increasing temperatures, i.e. (111)<110>, which is the easy slip system of face centered cubic alloy. The interaction of high-temperature oxidation and thermal stress is the main fractural mechanism in TF process. Some microstructural evolution at 950℃ accelerates the reduction of the TF property of three alloys.

Key words: Ni-based superalloy thermal fatigue high-temperature oxidation crystallographic orientation microstructural evolution

Received: 28 January 2011

Fund:

Supported by Higher Education Scientific Research Project of Liaoning Education Department (No.L2010473)

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	XIAO Xuan
	XU Hui
	QIN Hua-Zhi
	GUO Jian-Ting
	ZHOU Lan-Zhang

URL:

https://www.ams.org.cn/EN/10.3724/SP.J.1037.2011.00066 OR https://www.ams.org.cn/EN/Y2011/V47/I9/1129

[1]	ZHENG Liang, ZHANG Qiang, LI Zhou, ZHANG Guoqing. Effects of Oxygen Increasing/Decreasing Processes on Surface Characteristics of Superalloy Powders and Properties of Their Bulk Alloy Counterparts: Powders Storage and Degassing[J]. 金属学报, 2023, 59(9): 1265-1278.
[2]	MU Yahang, ZHANG Xue, CHEN Ziming, SUN Xiaofeng, LIANG Jingjing, LI Jinguo, ZHOU Yizhou. Modeling of Crack Susceptibility of Ni-Based Superalloy for Additive Manufacturing via Thermodynamic Calculation and Machine Learning[J]. 金属学报, 2023, 59(8): 1075-1086.
[3]	ZHANG Lu, YU Zhiwei, ZHANG Leicheng, JIANG Rong, SONG Yingdong. Thermo-Mechanical Fatigue Cycle Damage Mechanism and Numerical Simulation of GH4169 Superalloy[J]. 金属学报, 2023, 59(7): 871-883.
[4]	SHEN Zhao, WANG Zhipeng, HU Bo, LI Dejiang, ZENG Xiaoqin, DING Wenjiang. Research Progress on the Mechanisms Controlling High-Temperature Oxidation Resistance of Mg Alloys[J]. 金属学报, 2023, 59(3): 371-386.
[5]	LIU Laidi, DING Biao, REN Weili, ZHONG Yunbo, WANG Hui, WANG Qiuliang. Multilayer Structure of DZ445 Ni-Based Superalloy Formed by Long Time Oxidation at High Temperature[J]. 金属学报, 2023, 59(3): 387-398.
[6]	CONG Hongda, WANG Jinlong, WANG Cheng, NING Shen, GAO Ruoheng, DU Yao, CHEN Minghui, ZHU Shenglong, WANG Fuhui. A New Design Inorganic Silicate Composite Coating and Its Oxidation Behavior at High Temperature in Steam Atmosphere[J]. 金属学报, 2022, 58(8): 1083-1092.
[7]	ZHU Yuping, Naicheng SHENG, XIE Jun, WANG Zhenjiang, XUN Shuling, YU Jinjiang, LI Jinguo, YANG Lin, HOU Guichen, ZHOU Yizhou, SUN Xiaofeng. Precipitation Behavior of W-Rich Phases in a High W-Containing Ni-Based Superalloys K416B[J]. 金属学报, 2021, 57(2): 215-223.
[8]	ZHANG Xiaoli, FENG Li, YANG Yanhong, ZHOU Yizhou, LIU Guiqun. Influence of Secondary Orientation on Competitive Grain Growth of Nickel-Based Superalloys[J]. 金属学报, 2020, 56(7): 969-978.
[9]	WU Jing,LIU Yongchang,LI Chong,WU Yuting,XIA Xingchuan,LI Huijun. Recent Progress of Microstructure Evolution and Performance of Multiphase Ni3Al-Based Intermetallic Alloy with High Fe and Cr Contents[J]. 金属学报, 2020, 56(1): 21-35.
[10]	ZHANG Beijiang,HUANG Shuo,ZHANG Wenyun,TIAN Qiang,CHEN Shifu. Recent Development of Nickel-Based Disc Alloys andCorresponding Cast-Wrought Processing Techniques[J]. 金属学报, 2019, 55(9): 1095-1114.
[11]	Zhanxing CHEN,Hongsheng DING,Ruirun CHEN,Jingjie GUO,Hengzhi FU. Microstructural Evolution and Mechanism of Solidified TiAl Alloy Applied Electric Current Pulse[J]. 金属学报, 2019, 55(5): 611-618.
[12]	WANG Li,HE Yufeng,SHEN Jian,ZHENG Wei,LOU Langhong,ZHANG Jian. Effect of Secondary Orientation on Oxidation Anisotropy Around the Holes of Single Crystal Superalloy During Thermal Fatigue Tests[J]. 金属学报, 2019, 55(11): 1417-1426.
[13]	Weipeng REN, Qing LI, Qiang HUANG, Chengbo XIAO, Limin HE. Oxidation and Microstructure Evolution of CoAl Coating on Directionally Solidified Ni-Based Superalloys DZ466[J]. 金属学报, 2018, 54(4): 566-574.
[14]	Guangping ZHANG, Honglei CHEN, Xuemei LUO, Bin ZHANG. Progress in Thermal Fatigue of Micro/Nano-ScaleMetal Conductors[J]. 金属学报, 2018, 54(3): 357-366.
[15]	Hongxi LIU,Zhengxue LI,Xiaowei ZHANG,Jun TAN,Yehua JIANG. Effect of Heat Treatment on High-Temperature Oxidation Resistance of High Niobium Ti-Al Intermetallic Coating Fabricated by Laser In Situ Synthesis on Titanium Alloy[J]. 金属学报, 2017, 53(2): 201-210.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed