Acta Metall Sin  2016, Vol. 52 Issue (4): 426-436    DOI: 10.11900/0412.1961.2015.00379
Orginal Article Current Issue | Archive | Adv Search |
FRECKLE FORMATION DURING DIRECTIONALSOLIDIFICATION OF COMPLEX CASTINGSOF SUPERALLOYS
Dexin MA1,2()
1 Material R&D Center, Dongfang Turbine Co., LTD, Deyang 618000, China
2 State Key Laboratory of Long-Life High Temperature Materials, Deyang 618000, China
Cite this article: 

Dexin MA. FRECKLE FORMATION DURING DIRECTIONALSOLIDIFICATION OF COMPLEX CASTINGSOF SUPERALLOYS. Acta Metall Sin, 2016, 52(4): 426-436.

Download:  HTML  PDF(1300KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  

Freckles are a detrimental grain defect formed during directional and single crystal solidification of superalloy components leading to a high rejection rate. Based on the experimental and theoretical studies over the past forty years, the occurrence of freckles is generally believed to be mainly dependent on the alloy chemistry and process parameters, while the geometrical factor of castings was hardly taken into account. In the present work, a series of superalloy castings with complex geometry were directionally solidified in a production-scale Bridgman furnace. Some new features of freckle appearance have been observed, indicating new aspects of freckle formation. The freckles are preferably formed on the edges instead of on the plane surfaces of the castings. Correspondingly, freckles were found exclusively on the casting surface having positive curvature, whereas no freckles formed on the surface with negative one. The casting portions having inward sloping surfaces are very freckle prone, while those with outward sloping surfaces are absolutely freckle free. Therefore, as an independent factor the geometrical feature of the castings can more effectively affect the freckle formation than the local thermal conditions. It was also observed that freckles could occur not only on the external surfaces, but also inside the castings where a core was inserted, because both the shell and the core wall can provide very high permeability for freckling convection in the mushy zone. Based on this wall effect, all the important phenomena observed in the present work, such as the edge effect, the step effect, the sloping effect and the curvature effect on freckle formation in complex castings of superalloys, can be reasonably explained.

Key words:  superalloy      freckle      directional solidification      casting     
Received:  13 July 2015     

URL: 

https://www.ams.org.cn/EN/10.11900/0412.1961.2015.00379     OR     https://www.ams.org.cn/EN/Y2016/V52/I4/426

Fig.1  Low (left) and high (right) magnified images of freckle chains formed on the edges of the castings with quadrate (a) and rectangular (b) cross sections
Fig.2  Morphologies of a directionally solidified turbine blade (a) and freckles formed on blade edge (b, c)
Fig.3  Morphologies of a single crystal turbine blade (a) and freckles observed on blade edge surface (b) and transverse section (c)
Fig.4  Surface photos of a decanted blade, showing the solidification front and the positions of freckle formation(a) convex side A with serious freckles(b) concave side B without freckles(c) leading edge C with a freckle chain(d) trailing edge D with a freckle chain(e) top view of the decanted blade
Fig.5  Surface (a) and longitudinal section (b) of a sample with abruptly increasing diameter, showing the suppressing effect on the freckle growth
Fig.6  Surface of a cylindrical sample (a) and a turbine blade (b) with abruptly decreasing casing size, showing the promoting effect on the freckle formation
Fig.7  Samples with successional abrupt increase (a) and decrease (b) in diameter, showing freckle free and serious freckle structure respectively (Fig.7c shows the longitudinal section of Fig.7b)
Fig.8  Morphologies of the castings having outward (a) and inward (b) sloping surface, showing freckle free and serious freckle structure, as also observed in the longitudinal section of Fig.8b (c)
Fig.9  Surface (a) and longitudinal (b) morphologies of combined casting geometries shown in Fig.8a and 8b, revealing its influence on the freckle formation
Fig.10  Cross sectional morphologies of cylindrical samples without (a) and with ceramic core (b), showing the external freckles (A1 and A2) as well as the internal freckle (A3)
Fig.11  Al-Si alloy sample decanted during directional solidification (a) [23], schematic of the decanting depth Lout and Lin (b) and distribution of permeability P in mushy zone (c) (Lin—internal decanting depth, Lout—external decanting depth, Pin—internal permeability, Pout—external permeability, δ—depth of wall effect)
Fig.12  Schematic of the wall effect zones and their overlap in a polygonal casting section
Fig.13  Schematics of freckling convection in the casting sections with stepwise increasing (a) and decreasing (b) size
Fig.14  Schematics of freckling convection on the outward (a) and inward (b) sloping surface
[1] Giamei A F, Kear B H.Metall Trans, 1970; 1: 2185
[2] Copley S M, Giamei A F, Johnson S M, Hornbecker M F.Metall Trans, 1970; 1: 2193
[3] Tin S, Pollock T M. J Mater Sci, 2004; 39: 7199
[4] Pollock T M, Murphy W H.Metall Mater Trans, 1996; 27A: 1081
[5] Auburtin P, Wang T, Cockcroft S L, Mitchell A.Metall Mater Trans, 2000; 31B: 801
[6] Auburtin P, Cockcroft S L, Mitchell A, Wang T.In: Pollock T M, Kissinger R D, Bowman R R eds., Superalloy 2000, Warrendale, PA: TMS, 2000: 255
[7] Tin S.PhD Dissertation, University of Michigan, 2001
[8] Hobbs R A, Tin S, Rae C M F.Metall Mater Trans, 2005; 36A: 2761
[9] Schadt R, Wagner I, Preuhs J, Sahm P R.In: Pollock T M, Kissinger R D, Bowman R R eds., Superalloy 2000, Warrendale, PA: TMS, 2000: 211
[10] Tin S, Pollock T M, King W T.In: Pollock T M, Kissinger R D, Bowman R R eds., Superalloy 2000, Warrendale, PA: TMS, 2000: 201
[11] Felicelli S D, Heinrichand J C, Poirier D R.Metall Trans, 1991; 22B: 847
[12] Schneider M C, Beckermann C.Metall Mater Trans, 1995; 16A: 2373
[13] Schneider M C, Beckermann C.ISIJ Int, 1995; 35: 665
[14] Felicelli S D, Poirior D R, Heinrich J C.J Cryst Growth, 1997; 177: 145
[15] Schneider M C, Gu J P, Beckermann C, Katterner U R.Metall Mater Trans, 1998; 29B: 847
[16] Frueh C, Poirior D R, Felicelli S D.Mater Sci Eng, 2002; A328: 245
[17] Medina M, Terrail Y D, Durand F, Fautrelle Y.Metall Mater Trans, 2004; 35B: 743
[18] Jain J, Kumar A, Dutta P.J Phys, 2007; 40D: 1150
[19] Katz R F, Worster M G.J Comput Phys, 2008; 227: 9823
[20] Yuan L, Lee P D.ISIJ Int, 2010; 50: 1814
[21] Ma D X, Wu Q, Bührig-Polaczek A.Metall Mater Trans, 2012; 43B: 344
[22] Ma D X, Bührig-Polaczek A.Metall Mater Trans, 2014; 45A: 1435
[23] Ma D X, Sahm P R.Aluminium, 1996; 72: 905
[24] Ma D X, Bührig-Polaczek A.Metall Mater Trans, 2012; 43B: 671
[1] LI Jiarong, DONG Jianmin, HAN Mei, LIU Shizhong. Effects of Sand Blasting on Surface Integrity and High Cycle Fatigue Properties of DD6 Single Crystal Superalloy[J]. 金属学报, 2023, 59(9): 1201-1208.
[2] BI Zhongnan, QIN Hailong, LIU Pei, SHI Songyi, XIE Jinli, ZHANG Ji. Research Progress Regarding Quantitative Characterization and Control Technology of Residual Stress in Superalloy Forgings[J]. 金属学报, 2023, 59(9): 1144-1158.
[3] ZHENG Liang, ZHANG Qiang, LI Zhou, ZHANG Guoqing. Effects of Oxygen Increasing/Decreasing Processes on Surface Characteristics of Superalloy Powders and Properties of Their Bulk Alloy Counterparts: Powders Storage and Degassing[J]. 金属学报, 2023, 59(9): 1265-1278.
[4] MA Dexin, ZHAO Yunxing, XU Weitai, WANG Fu. Effect of Gravity on Directionally Solidified Structure of Superalloys[J]. 金属学报, 2023, 59(9): 1279-1290.
[5] CHEN Jia, GUO Min, YANG Min, LIU Lin, ZHANG Jun. Effects of W Concentration on Creep Microstructure and Property of Novel Co-Based Superalloys[J]. 金属学报, 2023, 59(9): 1209-1220.
[6] GONG Shengkai, LIU Yuan, GENG Lilun, RU Yi, ZHAO Wenyue, PEI Yanling, LI Shusuo. Advances in the Regulation and Interfacial Behavior of Coatings/Superalloys[J]. 金属学报, 2023, 59(9): 1097-1108.
[7] ZHAO Peng, XIE Guang, DUAN Huichao, ZHANG Jian, DU Kui. Recrystallization During Thermo-Mechanical Fatigue of Two High-Generation Ni-Based Single Crystal Superalloys[J]. 金属学报, 2023, 59(9): 1221-1229.
[8] BAI Jiaming, LIU Jiantao, JIA Jian, ZHANG Yiwen. Creep Properties and Solute Atomic Segregation of High-W and High-Ta Type Powder Metallurgy Superalloy[J]. 金属学报, 2023, 59(9): 1230-1242.
[9] ZHANG Jian, WANG Li, XIE Guang, WANG Dong, SHEN Jian, LU Yuzhang, HUANG Yaqi, LI Yawei. Recent Progress in Research and Development of Nickel-Based Single Crystal Superalloys[J]. 金属学报, 2023, 59(9): 1109-1124.
[10] LU Nannan, GUO Yimo, YANG Shulin, LIANG Jingjing, ZHOU Yizhou, SUN Xiaofeng, LI Jinguo. Formation Mechanisms of Hot Cracks in Laser Additive Repairing Single Crystal Superalloys[J]. 金属学报, 2023, 59(9): 1243-1252.
[11] JIANG He, NAI Qiliang, XU Chao, ZHAO Xiao, YAO Zhihao, DONG Jianxin. Sensitive Temperature and Reason of Rapid Fatigue Crack Propagation in Nickel-Based Superalloy[J]. 金属学报, 2023, 59(9): 1190-1200.
[12] WANG Lei, LIU Mengya, LIU Yang, SONG Xiu, MENG Fanqiang. Research Progress on Surface Impact Strengthening Mechanisms and Application of Nickel-Based Superalloys[J]. 金属学报, 2023, 59(9): 1173-1189.
[13] FENG Qiang, LU Song, LI Wendao, ZHANG Xiaorui, LI Longfei, ZOU Min, ZHUANG Xiaoli. Recent Progress in Alloy Design and Creep Mechanism of γ'-Strengthened Co-Based Superalloys[J]. 金属学报, 2023, 59(9): 1125-1143.
[14] MU Yahang, ZHANG Xue, CHEN Ziming, SUN Xiaofeng, LIANG Jingjing, LI Jinguo, ZHOU Yizhou. Modeling of Crack Susceptibility of Ni-Based Superalloy for Additive Manufacturing via Thermodynamic Calculation and Machine Learning[J]. 金属学报, 2023, 59(8): 1075-1086.
[15] LIU Xingjun, WEI Zhenbang, LU Yong, HAN Jiajia, SHI Rongpei, WANG Cuiping. Progress on the Diffusion Kinetics of Novel Co-based and Nb-Si-based Superalloys[J]. 金属学报, 2023, 59(8): 969-985.
No Suggested Reading articles found!