EFFECTS OF WITHDRAWAL RATE ON MICROSTRUCTURE AND STRESS RUPTURE PROPERTIES OF A Ni3Al–BASED SINGLE CRYSTAL SUPERALLOY IC6SX |
JIANG Liwu 1; LI Shusuo 1; QIU Zicheng 2; HAN Yafang 1;3 |
1. School of Materials Science and Engineering; Beihang University; Beijing 100083
2. Xinyi Machinery Factory; China Aviation Industry Corporation I; Guiyang 561114
3. Beijing Institute of Aeronautical Materials; Beijing 100095 |
|
Cite this article:
JIANG Liwu LI Shusuo QIU Zicheng HAN Yafang . EFFECTS OF WITHDRAWAL RATE ON MICROSTRUCTURE AND STRESS RUPTURE PROPERTIES OF A Ni3Al–BASED SINGLE CRYSTAL SUPERALLOY IC6SX. Acta Metall Sin, 2009, 45(5): 547-552.
|
Abstract As high–temperature structural materials, Ni3Al possesses excellent comprehensive properties, such as good strength at high temperature, low density, excellent ductility, superior oxidation resistance and so on. A high performance Ni3Al–based alloys IC6 has been developed by authors and successfully applied for aero–engine vanes. It has been found that the high temperature mechanical properties of the single crystal IC6 alloy are superior to both equiaxial crystal and directional columnar IC6 alloys. A lot of research work for IC6 alloys has been carried out on the equiaxial crystal and directional columnar IC6 alloys during the last two decades. In order to further improve the mechanical properties and meet the requirement of turbine blade materials, the single crystal Ni3Al–based alloy IC6SX has been developed and the research work on single crystal processing has been carried out recently. In the present investigation, the influence of withdrawal rate on the microstructure and stress rupture properties of a Ni3Al–based single crystal superalloy IC6SX were studied. The single crystal specimens were prepared by screw selection crystal method. The microstructure analysis by SEM and OM reveals that the microstructure of specimens is dendrite structure, and the primary dendrite arm spacing decreases from 480 μm to 390 μm with withdrawal rate increasing from 1.5 mm/min to 6.0 mm/min. Different with the common Ni–based superalloys, the size of the γ' phase in the dendritic core is larger than that in the interdendritic area. As withdrawal rate increases the size of the γ' phase decreases. The average size of the γ' phase in the dendritic core decreases from 3 μm to 1.3 μm and the average size of the γ' phase in the interdendritic area decreases from 1.6 μm to 0.8 μm with withdrawal rate increasing. Meanwhile, the shape of γ' phase tends to regular, and more primary eutectic γ' phase precipitates form in the interdendrite region. The volume fractions of primary eutectic γ' phase precipitates are 0.07\%, 0.18\%, 0.36\% and 0.77\%, respectively at the withdrawal rates 1.5, 3.0, 4.5 and 6.0 mm/min. It has been found that the stress rupture properties are affected by primary dendrite arm spacing and size of γ' phase significantly, i.e., the rupture lives of as-cast specimens increase with increasing withdrawal rate, which may be attributed to the refining microstructure. The above results can be used to optimize the process design for both single crystal specimen preparation and component fabrication of the present alloy IC6SX and may be used as a reference for other Ni--based single crystal alloys.
|
Received: 21 October 2008
|
|
[1] Zhang Y G, Han Y F, Chen G L, Guo J T, Wan X J, Feng D. Structural Intermetallics. Beijing: National Defence Industry Press, 2001: 560
(张永刚, 韩雅芳, 陈国良, 郭建亭, 万晓景, 冯 涤. 金属间化合物结构材料. 北京: 国防工业出版社, 2001: 560)
[2] Wilson B C, Cutler E R, Fuchs G E. Mater Sci Eng, 2008; A479: 356
[3] Liu W W, Tang D Z. J Mater Eng, 2006; 1: 16
(刘维维, 唐定中. 材料工程, 2006; 1: 16)
[4] Li J G, Wang Z, Jin T, Zhao N R, Sun X F, Guan H R, Hu Z Q. Mater Mech Eng, 2002; 3: 17
(李金国, 王 震, 金 涛, 赵乃仁, 孙晓峰, 管恒荣, 胡壮麒. 机械工程材料, 2002; 3: 17))
[5] Raj S V, Locci I E. Intermetallics, 2001; 9: 217
[6] Wu Q, Si N C, Guo Y, Li D Y. Chin J Nonferrous Met, 2007; 7: 1101
(吴 强, 司乃潮, 郭 毅, 李达云. 中国有色金属学报, 2007; 7: 1101)
[7] Wang K F, Guo J J, Li C Y, Mi G F, Fu H Z. Foundry, 2007; 56: 1186
(王狂飞, 郭景杰, 历长云, 米国发, 傅恒志. 铸造, 2007; 56: 1186)
[8] Карсев Б Е, translated by Gui Z L, Zhang X H, Xia M R, Sun L. Casting Turbine Blade Manufacturing Engineering . Beijing: Beijing Institute of Aeronautical Materials,
1998: 195
(Карсев Б Е著, 桂忠楼, 张鑫华, 夏明仁, 孙 \ \ 理译. 铸造涡轮叶片制造工程. 北京: 北京航空材料研究院, 1998: 195)
[9] Pan J S, Tong J M, Tian M B. Foundation of Material Science. Beijing: Tsinghua University Press, 1998: 503
(潘金生, 仝健民, 田民波. 材料科学基础. 北京: 清华大学出版社, 1998: 503)
[10] Beattie H J, Hagel W C. Trans AIME, 1965; 233: 277 |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|