金属学报  2010, Vol. 46 Issue (2): 251-256    DOI: 10.3724/SP.J.1037.2009.00470
  论文 本期目录 | 过刊浏览 |
X80管线钢在NaHCO3溶液中的阳极电化学行为
周建龙1; 李晓刚1; 杜翠薇1; 李云玲1;  李涛1; 潘莹2
1.北京科技大学腐蚀与防护中心; 北京 100083
2.武汉材料保护研究所; 武汉 430030
ANODIC ELECTROCHEMICAL BEHAVIOR OF X80 PIPELINE STEEL IN NaHCO3 SOLUTION
ZHOU Jianlong1; LI Xiaogang1; DU Cuiwei1; LI Yunling1; LI Tao1;PAN Ying2
1.Corrosion and Protection Center; University of Science and Technology Beijing; Beijing 100083
2.Wuhan Research Institute of Materials Protection; Wuhan 430030
引用本文:

周建龙 李晓刚 杜翠薇 李云玲 李涛 潘莹. X80管线钢在NaHCO3溶液中的阳极电化学行为[J]. 金属学报, 2010, 46(2): 251-256.
. ANODIC ELECTROCHEMICAL BEHAVIOR OF X80 PIPELINE STEEL IN NaHCO3 SOLUTION[J]. Acta Metall Sin, 2010, 46(2): 251-256.

全文: PDF(1328 KB)  
摘要: 

采用动电位极化曲线、动电位电化学阻抗谱(DEIS)和SEM研究了X80管线钢在NaHCO3溶液中的阳极电化学行为. 结果表明: 随着HCO3-浓度增加, X80管线钢腐蚀速率呈现先增加、后减小的趋势, X80管线钢“钝化”的临界HCO3-浓度为0.009 mol/L. 随着HCO3-浓度增加, 极化曲线阳极电流峰发生变化, 当HCO3-浓度低于0.009 mol/L时, 无阳极电流峰; 当浓度在0.009-0.05 mol/L时, 有一个阳极电流峰;当浓度增加到0.1 mol/L时, 出现两个明显的阳极电流峰, 且第1峰与第2峰的峰值电流比随浓度的增大而逐渐增大. DEIS结果与动电位极化曲线完全对应,二者相结合可以很好地研究在不同电位下NaHCO3溶液中X80管线钢的腐蚀行为,同时对其腐蚀产物 和腐蚀机理进行了分析.

关键词 X80管线钢 动电位极化曲线 动电位电化学阻抗谱(DEIS)    
Abstract

X80 steel has the potential to be widely used for building the gas transmission pipelines because of its high–intensity and high–toughness. Its corrosion performance is a key problem for the life expectancy, especially in soil environment. The anodic electrochemical behavior of X80 pipeline steel in NaHCO3 solution was studied using potentiodynamic polarization curve, dynamic electrochemical impedance spectroscopy (DEIS) as well as SEM observation. The results show that the shape of the polarization curves changes with HCO3- concentration. The corrosion rate of X80 pipeline steel first increases and then decreases with the increase of HCO3- concentration. 0.009 mol/L is the critical concentration of HCO3- for forming the'passive' film of the X80 pipeline steel. There is no anodic current peak in the solution when HCO3- concentration is below 0.009 mol/L, and one anodic current peak below 0.05 mol/L and two anodic current peaks above 0.1 mol/L. The results of the DEIS measurements are in complete agreement with the potentiodynamic polarization curve. The corrosion products chane with polarization potential and two equivalent circuits are used to explain the experimental spectra of X80 pipeline steel in the whole corrosion process. Therefore, the combination of dynamic polarization cure and DEIS methods can be well used to investigate the corrosion behavior of X80 pipeline steel in aHCO3 solution at various potentials. In addition, different corrosion products forming at various potentials and the corrosion mechanisms of X80 pipeline steel are briefly analyzed.

Key wordsX80 pipeline steel    potentiodynamic polarization curve;dynamic electrochemical impedance spectroscopy
收稿日期: 2009-07-13     
基金资助:

国家科技部基础条件平台建设资助项目2005DKA10400

作者简介: 周建龙, 男, 1977年生, 博士生

[1] Li D G, Feng Y R, Bai Z Q, Zhu J W, Zheng M S. Appl Surf Sci, 2008; 254: 2837
[2] Liang P, Li X G, Du C W, Chen X. Mater Des, 2009; 30: 1712
[3] Li D G, Feng Y R, Bai Z Q, Zhu J W, Zheng M S. Electrochim Acta, 2007; 52: 7877
[4] Du C W, Li X G, Chen X, Liang P, Guo H. Acta Metall Sin (Engl Lett), 2008; 21: 235
[5] Li M C, Cheng Y F. Electrochim Acta, 2008; 53: 2831
[6] Liu Z Y, Li X G, Du C W, Zhai G L, Cheng Y F. Corros Sci, 2008; 50: 2251
[7] Mao X, Liu X, Revie R W. Corrosion, 1994; 50: 651
[8] Zeng Y M, Luo J L, Norton P R. Electrochim Acta, 2004; 49: 703
[9] Fraunhofer J A V. Corros Sci, 1970; 10: 245
[10] Armstrong R D, Coates A C. J Electroanal Chem Interfacial Electrochem, 1974; 50: 303
[11] Lu Z P, Huang C B, Huang D L, Yang W. Corros Sci, 2006; 48: 3049
[12] Darowicki K, Krakowiak S, ´Slepski P. Electrochim Acta, 2004; 49: 2909
[13] Nagarajan S, Karthega M, Rajendran N. J Appl Electrochem , 2007; 37: 195
[14] Arutunow A, Darowicki K. Electrochim Acta, 2008; 53: 4387
[15] El–Naggar M M. J Appl Electrochem, 2004; 34: 911
[16] Zhao J M, Zuo Y. Electrochemistry, 2005; 11: 27

[1] 陈芳,李亚东,杨剑,唐晓,李焰. X80钢焊接接头在模拟天然气凝析液中的腐蚀行为[J]. 金属学报, 2020, 56(2): 137-147.
[2] 张体明, 赵卫民, 蒋伟, 王永霖, 杨敏. X80钢焊接残余应力耦合接头组织不均匀下氢扩散的数值模拟[J]. 金属学报, 2019, 55(2): 258-266.
[3] 万红霞,宋东东,刘智勇,杜翠薇,李晓刚. 交流电对X80钢在近中性环境中腐蚀行为的影响[J]. 金属学报, 2017, 53(5): 575-582.
[4] 刘智勇,李宗书,湛小琳,皇甫文珠,杜翠薇,李晓刚. X80钢在鹰潭土壤模拟溶液中应力腐蚀裂纹扩展行为机理*[J]. 金属学报, 2016, 52(8): 965-972.
[5] 王家贞,王俭秋,韩恩厚. 800合金在300 ℃ NaOH和ETA溶液中的腐蚀行为*[J]. 金属学报, 2016, 52(5): 599-606.
[6] 张体明,王勇,赵卫民,唐秀艳,杜天海,杨敏. 高压煤制气环境下X80钢及热影响区的氢渗透参数研究[J]. 金属学报, 2015, 51(9): 1101-1110.
[7] 刘玉,李焰,李强. 阴极极化对X80管线钢在模拟深海条件下氢脆敏感性的影响[J]. 金属学报, 2013, 49(9): 1089-1097.
[8] 范林,刘智勇,杜翠薇,李晓刚. X80管线钢高pH应力腐蚀开裂机制与电位的关系[J]. 金属学报, 2013, 49(6): 689-698.
[9] 王新华,李秀刚,李强,黄福祥,李海波,杨建. X80管线钢板中条串状CaO-Al2O3系非金属夹杂物的控制[J]. 金属学报, 2013, 49(5): 553-561.
[10] 刘智勇 王长朋 杜翠薇 李晓刚. 外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响[J]. 金属学报, 2011, 47(11): 1434-1439.
[11] 邓伟 高秀华 秦小梅 高鑫 赵德文 杜林秀. 冷却速率对变形与未变形X80管线钢组织的影响[J]. 金属学报, 2010, 46(8): 959-966.
[12] 陈旭 吴明 何川 肖军. 外加电位对X80钢及其焊缝在库尔勒土壤 模拟溶液中SCC行为的影响[J]. 金属学报, 2010, 46(8): 951-958.
[13] 邓伟 高秀华 秦小梅 赵德文 杜林秀 王国栋. X80管线钢的冲击断裂行为[J]. 金属学报, 2010, 46(5): 533-540.
[14] 万先松 师玉英 马军 李海庆 宫骏 孙超. 电弧离子镀CrN涂层盐雾腐蚀行为[J]. 金属学报, 2010, 46(5): 600-606.
[15] 缪成亮 尚成嘉 王学敏 张龙飞 Mani Subramanian. 高Nb X80管线钢焊接热影响区显微组织与韧性[J]. 金属学报, 2010, 46(5): 541-546.