AA3104铝合金均匀化过程中的(Fe, Mn)Al6相向α-Al12(Fe, Mn)3Si相转变研究

doi:10.3724/SP.J.1037.2011.00689

金属学报

2012, Vol. 48

Issue (3): 351-356 DOI: 10.3724/SP.J.1037.2011.00689

论文

本期目录 | 过刊浏览

AA3104铝合金均匀化过程中的(Fe, Mn)Al₆相向α-Al₁₂(Fe, Mn)₃Si相转变研究

张永皞, 张志清, Robert E. Sanders, 刘庆

重庆大学材料科学与工程学院, 重庆 400044

STUDY OF THE PHASE TRANSFORMATION FROM (Fe, Mn)Al₆ TO α-Al₁₂(Fe, Mn)₃Si IN AA3104 ALUMINUM ALLOY DURING HOMOGENIZATION

ZHANG Yonghao, ZHANG Zhiqing, Robert E. SANDERS, LIU Qing

College of Materials Science and Engineering, Chongqing University, Chongqing 400044

引用本文:

张永皞张志清 Robert E. Sanders 刘庆. AA3104铝合金均匀化过程中的(Fe, Mn)Al₆相向α-Al₁₂(Fe, Mn)₃Si相转变研究[J]. 金属学报, 2012, 48(3): 351-356.
, , , . STUDY OF THE PHASE TRANSFORMATION FROM (Fe, Mn)Al₆ TO α-Al₁₂(Fe, Mn)₃Si IN AA3104 ALUMINUM ALLOY DURING HOMOGENIZATION[J]. Acta Metall Sin, 2012, 48(3): 351-356.

全文: PDF(2332 KB)

摘要: 采用SEM背散射电子(BSE)技术以及能谱(EDS)等手段定量研究了加热温度和保温时间对AA3104铝合金中(Fe, Mn)Al₆相向α-Al₁₂(Fe, Mn)₃Si相转变作用规律, 通过连续截面方法对600 ℃保温条件下不同阶段的共晶相(即 (Fe, Mn)Al₆相及α-Al₁₂(Fe, Mn)₃Si相)形貌进行三维重构, 从三维角度揭示了转化各阶段共晶相的三维形态. 对转变过程中标志性的铝点进行了定量表征, 结果表明在转化的不同阶段, 对应的铝点形貌特征也不尽相同, 在均匀化进行到一定阶段后, 大量铝点通过扩散而消失, 导致α相体积明显减小. 分析了转化后α相的微观形貌特征, 认为转化后存在的脆弱“双相”界面以及α相内部“疏松多孔”的状态, 将有助于其在轧制过程中的破碎.

关键词 ： AA3104铝合金, 均匀化, 共晶相, 相转变

Abstract：The effect of heating temperature and holding time on the phase transformation from (Fe, Mn)Al₆ to α-Al₁₂(Fe, Mn)₃Si in AA3104 aluminum alloy during homogenization was studied by BSE and EDS in SEM. The 3D morphology of the eutectic phases heated at 600 ℃ for different holding times was reconstructed by a novel serial sectioning method. Evolution of the microstructure could be revealed in 3D for the first time. Al spots were observed within the α-Al₁₂(Fe, Mn)₃Si phase and counted during different transformation stages. Large number of Al spots disappeared by diffusing into the neighboring matrix after extended heating times, while the volume of the α phase was also decreased at the same time. The microstructure of the α phase after transformation was analyzed, showing ‘duplex interfaces’created by partly transformed particles. The dense holes within α phase particles are believed to promote particle break up during hot rolling of the omogenized material.

Key words： AA3104 aluminum alloy omogenization utectic phase hase transformation

收稿日期: 2011-11-07

ZTFLH:

TG146.2

基金资助:

中央高校基本科研业务费资助项目CDJRC10130008

作者简介: 张永皞, 男, 1982年生, 博士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张永皞
	张志清
	Robert E. Sanders
	刘庆
44.8K

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2011.00689 或 https://www.ams.org.cn/CN/Y2012/V48/I3/351

[1] Engler O, Kong X W, Yang P. Scr Mater, 1997; 37: 1665

[2] Humphreys F J. Acta Metall, 1977; 25: 1323

[3] Vatne H E, Engler O, Nes E. Mater Sci Technol, 1997; 13: 3

[4] Yang P, Engler O. Acta Metall Sin, 1998; 34: 785

(杨平, Engler O. 金属学报, 1998; 34: 785)

[5] Alexander D T L, Greer A L. Philos Mag, 2004; 84: 3051

[6] Hamerton R, Cama H, Meredith M W. Mater Sci Forum, 000; 331–337: 143

[7] Alexander D T L, Greer A L. Mater Sci Technol, 2005; 1: 955

[8] Gandhi C. Master Dissertation, Vancouver: The University f British Columbia, 1999

[9] Li Y J, Arnberg L. Mater Sci Eng, 2003; A347: 130

[10] Moulin N, Parra–Denis E, Jeulin D, Ducottet C, Bigot A, Boller E, Maire E, Barat C, Kl¨ocker H. Adv Eng Mater, 2010; 12: 20

[11] Skjerpe P. Metall Mater Trans, 1987; 18A: 189

[12] Li Y J, Johansen A, Benum S, Simensen C J, Dons A L, Hakonsen A, Arnberg L. Aluminium, 2004; 80: 578

[13] Sun D L, Kang S B, Koo H S. Mater Chem Phys, 2000; 63: 37

[14] Alexander D T L, Greer A L. Acta Mater, 2002; 50: 2571

[15] Alexander D T L, Greer A L. Philos Mag, 2004; 84: 3071

[16] Fiala J C. J Microsc, 2005; 218: 52

[17] Li Y J, Arnberg L. Acta Mater, 2003; 51: 3415

[18] Sun D L, Kang S B, Koo H S. Chinese J Nonferr Met, 1999; 9: 556

(孙东立, 姜石峰, 高兴锡. 中国有色金属学报, 1999; 9: 556)

[19] Dehmas M, Weisbecker P, Geandier G, Archambault P, Aeby–Gautier E. J Alloys Compd, 2005; 400: 116

[20] Li Y J, Arnberg L. Acta Mater, 2004; 52: 2945

[1]	张少华, 谢光, 董加胜, 楼琅洪. 单晶高温合金共晶溶解行为的差热分析[J]. 金属学报, 2021, 57(12): 1559-1566.
[2]	向雪梅, 江河, 董建新, 姚志浩. 难变形高温合金GH4975的铸态组织及均匀化[J]. 金属学报, 2020, 56(7): 988-996.
[3]	王涛,万志鹏,李钊,李佩桓,李鑫旭,韦康,张勇. 热处理工艺对GH4720Li合金细晶铸锭组织与热加工性能的影响[J]. 金属学报, 2020, 56(2): 182-192.
[4]	王宝刚, 易红亮, 王国栋, 骆智超, 黄明欣. 原位生成铁基复合材料中TiB₂的三维形貌重构[J]. 金属学报, 2019, 55(1): 133-140.
[5]	王光东, 田妮, 何长树, 赵刚, 左良. DC铸造Al-12Si-0.65Mg-xMn合金中第二相的形成[J]. 金属学报, 2018, 54(7): 1059-1067.
[6]	孙朝阳,郭祥如,郭宁,杨竞,黄杰. 耦合孪生的TWIP钢多晶体塑性变形行为研究^*[J]. 金属学报, 2015, 51(12): 1507-1515.
[7]	董建新,李林翰,李浩宇,张麦仓,姚志浩. 高温合金铸锭均匀化程度对开坯热变形的再结晶影响[J]. 金属学报, 2015, 51(10): 1207-1218.
[8]	田素贵,王欣,谢君,刘臣,郭忠革,刘姣,孙文儒. GH4169G合金热处理期间的相转变特征与机理分析[J]. 金属学报, 2013, 49(7): 845-852.
[9]	曹零勇，郭明星，崔华，蔡元华，张巧霞，胡晓倩，张济山. *Al-Mg-Si系合金均匀化过程中β→α相转变动力学研究*[J]. 金属学报, 2013, 29(4): 428-434.
[10]	张月来,段德莉,赵宇航,侯思焓,李曙. 泡沫NiCrAl电热合金的制备及其电学性能[J]. 金属学报, 2013, 49(2): 214-220.
[11]	吴泽恩,胡锐,张铁邦,周欢,寇宏超,李金山. 间隙原子O对高Nb－TiAl合金显微组织与相转变的影响[J]. 金属学报, 2013, 49(11): 1381-1386.
[12]	潘晓林汪波孙文儒涂赣峰郭守仁胡壮麒. 均匀化处理对GH742合金热变形行为的影响[J]. 金属学报, 2012, 48(11): 1403-1408.
[13]	林双平黄晖文胜平聂祚仁. 含Er 5083合金均匀化退火过程中Al₃Er相的TEM观察[J]. 金属学报, 2009, 45(8): 978-982.
[14]	刘建涛; 林鑫; 吕晓卫; 陈静; 黄卫东 . Ti-Ti2AlNb功能梯度材料的激光立体成形研究[J]. 金属学报, 2008, 44(8): 1006-1012 .
[15]	吕海燕; 李双明; 钟宏; 刘林; 傅恒志 . 激光快速熔凝Cu-75%Sn过包晶合金中ε相向包晶η相的转变[J]. 金属学报, 2008, 44(7): 843-847 .

Viewed

Full text

Abstract

Cited

Shared

Discussed