THE PURIFICATION AND HYPERCOOLING OF Fe-B EUTECTIC ALLOY
西北工业大学凝固技术国家重点实验室
Cite this article: 

. THE PURIFICATION AND HYPERCOOLING OF Fe-B EUTECTIC ALLOY. Acta Metall Sin, 2008, 44(8): 956-960 .

Download:  PDF(753KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Adopting the molten glass denucleating technology combined with high frequency vacuum melting, and cycle superheating, the main factors affecting purifying of the bulk Fe-rich side Fe-B eutectic alloy melt were investigated. The optimized purification and parameters for high undercooling and hypercooling were given out. The hypercoolings of 324K~460K have been obtained successfully in bulk Fe83B17 eutectic alloy melts, and 485K in Fe80B20 hypereutectic alloy melts. So the primary nucleation undercoolings of (0.3~0.4) Tm were obtained in bulk Fe-B eutectic system alloy melts. The thermodynamic characters of hypercooling rapid solidification were also discussed by analyzing the cooling curves.
Key words:  Glass purifying      hypercooling      undercooling      Fe-B eutectic alloy      
Received:  29 November 2007     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y2008/V44/I8/956

[1]Herlach D M.Mater Sci Eng,1994;R12:177
[2]Wilde G,Grler G P,Willnecker R.Appl Phys Lett,1996; 69:2995
[3]Yang C L,Yang G C,Lu Y P,Chen J Q,Zhou Y H.Acta Metall Sin,2005;41:1053 (杨长林,杨根仓,卢一平,陈甲琪,周尧和.金属学报,2005;41:1053)
[4]Yang C L,Yang G C,Liu F,Chen Y Z,Liu N,Chen D, Zhou Y H.Physics,2006;373B:136
[5]Yang C L,Liu F,Yang G C,Chen Y,Liu N,Zhou Y H. Appl Phys,2007;86A:231
[6]Hu H Q.Principle of Metal Solidification.2nd ed,Beijing: China Machine Press,2000:256 (胡汉起.金属凝固原理.第2版,北京:机械工业出版社,2000:256)
[7]Kui H W,Greer A L,Turnbull D.Appl Phys Left,1984; 45:615
[8]Zhou Y H,Hu Z Q,Ji W Q.Solidification Technology. Beijing:China Machine Press,1998:45 (周尧和,胡壮麒,介万奇.凝固技术.北京:机械工业出版社,1998:451
[9]Wei B B.PhD Thesis,Northwestern Polytechnicai Uni- versity,Xi'an,1989 (魏炳波.西北工业大学博士学位论文,西安,1989)
[10]Powell G L F.TMS-AIME,1968;242:2133
[11]Kattamis T Z,Flemings M C.Trans TMS-AIME,1966; 236:1523
[12]Zhang Z Z.PhD Thesis,Northwestern Polytechnical Uni- versity,Xi'an,2000 (张振忠.西北工业大学博士学位论文,西安,2000)
[13]Perepezko J H.Mater Sci Eng,1997;A226-228:374
[14]Singh R N,Jaju R P,Ali I.Physics,2001;299B:108
[15]Pan S Q.New Glass.Shanghai:Tongji University Press, 1992:30 (潘守芹.新型玻璃.上海:同济大学出版社,1992:30)
[16]Battezzati L,Antonione C,Baricco M.J Alloys Compd, 1997;247:16
[1] XU Junfeng, ZHANG Baodong, Peter K Galenko. Model of Eutectic Transformation Involving Intermetallic Compound[J]. 金属学报, 2021, 57(10): 1320-1332.
[2] Kuanhui HU, Xinping MAO, Guifeng ZHOU, Jing LIU, Zhifen WANG. Effect of Si and Mn Contents on the Microstructure and Mechanical Properties of Ultra-High Strength Press Hardening Steel[J]. 金属学报, 2018, 54(8): 1105-1112.
[3] Yun LI, Lianjie LIU, Xinming LI, Jinfu LI. Solidification of Undercooled Co75B25 Alloy[J]. 金属学报, 2018, 54(8): 1165-1170.
[4] Dandan FAN, Junfeng XU, Yanan ZHONG, Zengyun JIAN. Effect of Superheated Temperature and Cooling Rate on the Solidification of Undercooled Ti Melt[J]. 金属学报, 2018, 54(6): 844-850.
[5] Zengyun JIAN, Tao XU, Junfeng XU, Man ZHU, Fang'e CHANG. Development of Solid-Liquid Interfacial Energyof Melt-Crystal[J]. 金属学报, 2018, 54(5): 766-772.
[6] Bin ZHAI, Kai ZHOU, Peng Lü, Haipeng WANG. Rapid Solidification of Ti-6Al-4V Alloy Micro-Droplets Under Free Fall Condition[J]. 金属学报, 2018, 54(5): 824-830.
[7] Jinfu LI, Yaohe ZHOU. Remelting of Primary Solid in Rapid Solidification of Deeply Undercooled Alloy Melts[J]. 金属学报, 2018, 54(5): 627-636.
[8] Jianglei ZHU, Qing WANG, Haipeng WANG. Thermophysical Properties and Atomic Distribution of Undercooled Liquid Cu[J]. 金属学报, 2017, 53(8): 1018-1024.
[9] Junhui YAN,Zengyun JIAN,Man ZHU,Fang'e CHANG,Junfeng XU. SOLIDIFICATION CHARACTERISTICS AND MICRO-STRUCTURE OF HIGH UNDERCOOLED Al-70%Si ALLOY[J]. 金属学报, 2016, 52(8): 931-937.
[10] CHEN Zheng, YANG Yanan, CHEN Qiang, XU Junfeng, TANG Yueyue, LIU Feng. RECALESCENCE EFFECT SIMULATION AND MICROSTRUCTURE EVOLUTION OF UNDERCOOLED Fe82B17Si1 ALLOY[J]. 金属学报, 2014, 50(7): 795-801.
[11] WEN Qiang, JIAN Zengyun, ZHU Man, CHANG Fang'e, DANG Bo. EFFECTS OF RE ON THE SOLIDIFICAIION CHARACTERISTICS OF Al-80%Si ALLOY[J]. 金属学报, 2014, 50(5): 610-618.
[12] GUO Xiong, LIN Xin, WANG Zhitai, CAO Yongqing, PENG Dongjian, HUANG Weidong. FORMATION MECHANISM OF ANOMALOUS EUTECTIC AND MICROSTRUCTURE EVOLUTION IN HIGHLY UNDERCOOLED SOLIDIFICATION OF Ni-30%Sn ALLOY[J]. 金属学报, 2013, 29(4): 475-482.
[13] HU Rui, LIU Yi, ZHANG Tiebang, KOU Hongchao, LI Jinshan. PHASE SELECTION AND THE SOLIDIFICATION CHARACTERISTICS OF TiAl BASE ALLOYS IN THE NONEQUILIBRIUM SOLIDIFICATION[J]. 金属学报, 2013, 49(11): 1295-1302.
[14] CHANG Fang'e ZHAO Zhiwei ZHU Man LI Na FANG Wen DONG Guangzhi JIAN Zengyun. SOLIDIFICATION BEHAVIORS OF HIGHLY UNDERCOOLED Ni-21.4%Si EUTECTIC ALLOY[J]. 金属学报, 2012, 48(7): 875-881.
[15] MU Danning YANG Changlin WEI Xiaowei LIU Feng. RESEARCH ON GRAIN REFINEMENT IN BULK UNDERCOOLED Fe–Co BASE ALLOYS[J]. 金属学报, 2012, 48(12): 1409-1414.
No Suggested Reading articles found!