ENTHALPIES OF MIXING FOR PbCl_2-NaCl-BaCl_2 TERNARY MOLTEN SALT MIXTURES

Acta Metall Sin

1992, Vol. 28

Issue (5): 90-92 DOI:

Current Issue | Archive | Adv Search

ENTHALPIES OF MIXING FOR PbCl_2-NaCl-BaCl_2 TERNARY MOLTEN SALT MIXTURES

YU Hualong;ZHU Jiankang;WANG Zhichang Northeast University of Technology; Shenyang Correspondent; professor; Department of Non-Ferrous Metallurgy; Northeast University of Technology; Shenyang 11006

Cite this article:

YU Hualong;ZHU Jiankang;WANG Zhichang Northeast University of Technology; Shenyang Correspondent; professor; Department of Non-Ferrous Metallurgy; Northeast University of Technology; Shenyang 11006. ENTHALPIES OF MIXING FOR PbCl_2-NaCl-BaCl_2 TERNARY MOLTEN SALT MIXTURES. Acta Metall Sin, 1992, 28(5): 90-92.

Download:

PDF(279KB)
Export: BibTeX | EndNote (RIS)

Abstract The enthalpies of mixing for the PbCl_2-NaCl-BaCl_2 ternary molten salt mix-tures have been measured along four iso-α_(PbCl_2) lines by using a SETARAM calorimeter at873 K. The results show that the molar enthalpy of mixing between iso-α(PbCl_2) liquid binarysubsystems PbCl_2-NaCl and PbCl_2-BaCl_2 is near zero, i. e., approximately fitting the partialideal solution model.

Key words: PbCl_2-NaCl-BaCl_2 molten salt enthalpy of mixing partial ideal solution model

Received: 18 May 1992

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

URL:

https://www.ams.org.cn/EN/ OR https://www.ams.org.cn/EN/Y1992/V28/I5/90

1 Sommer F. J Thermal Anal, 1988; 33: 15
2 Moser Z, Gasior W, Sommer F, Schwitzgebel G, Predel B. Metall Trans, 1986; 17B: 791
3 Kubaschewski O, Alcock C B. Metallurgical Thermochemistry. 5th ed., New York: Pergamon, 1979
4 Hino M, Kelly M G, Toguri J M. Can Metall Q, 1990; 29: 177
5 Barton J L, Bloom H. J Phys Chem, 1956; 60: 1413
6 McCarty F G, Kleppa O J. J Phys Chem, 1964; 68: 3846
7 Barin I, Knacke O. Thermochemical Properties of Inorganic Substances. Berlin: Springer Verlag, 1973
8 Hassam S, Gaune-Escard M, Bros J P, Hoch M. Metall Trans, 1988; 19A: 2075
9 Tian Y W, Yu H L, Zhang X H, Zhu J K, Wang Z C. J Phys Chem, to be submitted
10 王之昌.金属学报,1982;18:141v

[1]	Tao LIU,Jiasheng DONG,Guang XIE,Yisheng WANG,Hui LI,Zhijun LI,Xingtai ZHOU,Langhong LOU. CORROSION BEHAVIOR OF GH3535 SUPERALLOY IN FLiNaK MOLTEN SALT[J]. 金属学报, 2015, 51(9): 1059-1066.
[2]	YAN Yongde, YANG Xiaonan, ZHANG Milin, WANG Li, XUE Yun, ZHANG Zhijian. STUDY ON PREPARATION OF Al-Li-Gd ALLOYS BY ELECTROCHEMICAL CODEPOSITION FROM CHLORIDE MELTS[J]. 金属学报, 2014, 50(8): 989-994.
[3]	GONG Wenbiao, LI Renwei, LI Yupeng,SUN Daqian, WANG Wenquan. STABILIZATION AND CORROSION RESISTANCE UNDER HIGH-TEMPERATURE OF NANOSTRUCTURED CeO₂/ZrO₂-Y₂O₃ THERMAL BARRIER COATING[J]. 金属学报, 2013, 49(5): 593-598.
[4]	WANG Shulan CHEN Xiaoyun. STUDY ON THE ELECTRO–REFINING SILICON IN MOLTEN SALT CaCl2–NaCl–CaO[J]. 金属学报, 2012, 48(2): 183-186.
[5]	PENG Haijian JIN Jun LI Defu HU Jie. CORROSION BEHAVIORS OF Ni-Cr-Mo CORROSION RESISTENCE ALLOYS IN CaCl₂-CaF₂ MOLTEN SALT[J]. 金属学报, 2011, 47(9): 1195-1199.
[6]	LV Jiaxin; ZHENG Lei; ZHANG Maicang; DONG Jianxin. CORROSION BEHAVIOR OF NICKEL BASE ALLOY FGH95 IN MOLTEN NaCl–Na₂SO₄[J]. 金属学报, 2009, 45(2): 204-210.
[7]	;. Investigation on Preparation of Tb2Fe17 by Direct Electrochemical Reduction of Tb4O7-Fe2O3 Pellet in Molten Calcium Chloride[J]. 金属学报, 2008, 44(7): 859-862 .
[8]	;. EXPERIMENTAL RESEARCH OF PREPARATION OF CaB6 BY MOLTEN SALT ELECTROLYSIS METHOD[J]. 金属学报, 2008, 44(10): 1243-1246 .
[9]	. PREPARATION OF TANTALUM BY ELECTRO-DEOXIDATION IN A CACL2-NACL MELT[J]. 金属学报, 2006, 42(3): 285-289 .
[10]	ZHANG Jian(Metallurgical Engineering School; University of Science and Technology Beijing; Beijing 100083). CONSISTENCY(OR SIMILARITY) OF THERMODYNAMIC PROPERTIES OF METALLURGICAL MELTS WITH THEIR PHASE DIAGRAMS[J]. 金属学报, 1998, 34(7): 742-752.
[11]	LIU Gang;CHEN Ruiliang;LI Chonghe;CHEN Nianyi(Shanghai Institute of MetaIlurgy; Chinese Academy of Sciences; Shanghai 200050). REGULARITIES OF MUTUAL SOLUBILITY OF MOLTEN SALT-LIQUID METAL SYSTEMS[J]. 金属学报, 1997, 33(9): 939-942.
[12]	ZHANG Jian (University of Science and Technology Beijing; Beijing 100083). CALCULATING MODELS OF MASS ACTION CONCENTRATIONS FOR SEVERAL MOLTEN BINARY SALTS[J]. 金属学报, 1997, 33(5): 515-523.
[13]	GUO Naiming(Institute of Chemical Metallurgy; Chinese Academy of Sciences; Beijing 100080); GUO Jiaju(University of Science and Technology Beijing; Beijing 100083) (Manuscript received 1 995-07-2 1 ; in revised form 1 995- 1 0- 1 3). MOLTEN SALT ELECTROPLATING OF Al-Ti AND Al-Mn ALLOYS[J]. 金属学报, 1996, 32(3): 274-277.
[14]	YUAN Wenxia; MA Shulan; QIAO Hin; ZHUANG Weidong; XING Xianran;QIAO Zhiyu (University of Science and Technology Beijing; Beijing 100083)(General Institute for Non-Ferrous Metals; Beijing 100088)(Manuscript received 1995-04-28; in revised form 1995-11-05). A STUDY ON THE YCl_3-AECl_2(AE=Mg, Ca, Sr, Ba)BINARY PHASE DIAGRAMS[J]. 金属学报, 1996, 32(2): 139-143.
[15]	LIU Guankun; TONG Yexiang;HONG Huichan; CHEN Shengyang;GAN Luo(Zhongshan University; Guangzhou 510275)(Manuscript received 1995-10-23; in revised form 1996-08-25). STUDIES ON THE PREPARATION OF Dy-Cu ALLOY IN CHLORIDE MELT BY MOLTEN SALT ELECTROLYSIS[J]. 金属学报, 1996, 32(12): 1252-1257.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed