800H合金动态再结晶行为研究

曹宇¹,邸洪双¹,张洁岑¹,张敬奇¹,马天军²

1.东北大学轧制技术及连轧自动化国家重点实验室, 沈阳 110819
2.宝山钢铁股份有限公司特钢事业部, 上海 200940

RESEARCH ON DYNAMIC RECRYSTALLIZATION BEHAVIOR OF INCOLOY 800H

CAO Yu¹, DI Hongshuang¹, ZHANG Jiecen¹, ZHANG Jingqi¹, MA Tianjun²

1.State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819
2.Special Steel Business Unit, Baoshan Iron&Steel Co., Ltd., Shanghai 200940

引用本文:

曹宇邸洪双张洁岑张敬奇马天军. 800H合金动态再结晶行为研究[J]. 金属学报, 2012, 48(10): 1175-1185.
CAO Yu DI Hongshuang ZHANG Jiecen ZHANG Jingqi MA Tianjun. RESEARCH ON DYNAMIC RECRYSTALLIZATION BEHAVIOR OF INCOLOY 800H[J]. Acta Metall Sin, 2012, 48(10): 1175-1185.

全文: PDF(3458 KB)

摘要:

在MMS-300热模拟机上对800H合金进行了单道次压缩实验, 结合EBSD和TEM等技术, 研究了该合金在850-1100 ℃和0.01-10 s^-1变形条件下的动态再结晶行为. 结果表明, 当变形温度低于950 ℃时, 析出了大量Cr₂₃C₆和Ti(C,N)析出相, 其对动态再结晶行为产生明显的抑制作用. 建立了2段温度区间内(850-950 ℃和950-1100 ℃)800H合金的热变形本构方程; 采用lnθ-ε曲线的三次多项式拟合求解拐点的方法, 较准确地预测了800H合金动态再结晶临界应力/峰值应力和临界应变/峰值应变的比值, 并建立了临界应力、临界应变与$Z$参数的关系;800H合金在热变形过程中动态再结晶形核机制主要包括应变诱导晶界迁移、晶粒碎化以及亚晶合并形核机制.

关键词 ： 800H合金, 动态再结晶, 本构方程, 临界应变, 应变诱导晶界迁移

Abstract：

In order to optimize the hot working technology of Incoloy 800H, the dynamic recrystallization (DRX) behavior of Incoloy 800H at temperatures ranging from 850 ℃ to 1100 ℃ and strain rates from 0.01 s^-1 to 10 s^-1 was investigated by single–pass compression tests on MMS–300 thermo–mechanical simulator. The evolutions of microstructure and nucleation mechanisms of DRX were analyzed combined with the technique of EBSD and TEM. The results show that when the deformation temperature is below 950 ℃, the behavior of DRX is obviously restrained by precipitation of Cr₂₃C₆ and Ti(C,N). Therefore the hot deformation constitutive equations in two temperature intervals (from 850 ℃ to 950 ℃and from 950 ℃ to 1100 ℃) were established by regression analysis with the deformation activation energy of 465.394 kJ/mol and 427.360 kJ/mol respectively. The inflection points were determined by fitting a third order polynomial to the lnθ–ε curves, which makes the prediction for the ratios of critical stress to peak stress and critical strain to peak strain more accurately. Accordingly, the mathematical models of critical stress and critical strain vs Z parameter were deduced. The DRX nucleation mechanisms of Incoloy 800H during hot deformation mainly include strain induced grain boundary migration, grain fragmentation and subgrain coalescence.

Key words： Incoloy 800H dynamic recrystallization constitutive equation critical strain strain induced grain boundary migration

收稿日期: 2012-04-27

ZTFLH:

TG146.4

基金资助:

国家重点基础研究发展计划资助项目2011CB606306-2

作者简介: 曹宇, 男, 1986年生, 博士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	曹宇邸洪双张洁岑张敬奇马天军
44.8K

链接本文:

https://www.ams.org.cn/CN/10.3724/SP.J.1037.2012.00236 或 https://www.ams.org.cn/CN/Y2012/V48/I10/1175

[1] Tan L, Rakotojaona L, Allen T R, Nanstad R K, Busby J T. Mater Sci Eng, 2011; A528: 2755

[2] Br¨unger E, Wang X, Gottstein G. Scr Mater, 1998; 38: 1843

[3] Wang X, Br¨unger E, Gottstein G. Mater Sci Eng, 2000; A290: 180

[4] Wang X, Br¨unger E, Gottstein G. Scr Mater, 2002; 46: 875

[5] Gottstein G, Frommert M, Goerdeler M, Sch¨afer N. Mater Sci Eng, 2004; A387–389: 604

[6] Abd El–Azim M E. J Nucl Mater, 1996; 231: 146

[7] Frommert M, Gottstein G. Mater Sci Eng, 2009; A506: 101

[8] Sun C Y, Liu J R, Li R, Zhang Q D. Acta Metall Sin, 2011; 47: 191

(孙朝阳, 刘金榕, 李瑞, 张清东. 金属学报, 2011; 47: 191)

[9] McQueen H J, Ryan N D. Mater Sci Eng, 2002; A322: 43

[10] Venugopal S, Mannan S L, Rodriguez P. J Mater Sci, 2004; 39: 5557

[11] Naderi M, Durrenberger L, Bleck W. Mater Sci Eng, 2008; A478: 130

[12] McQueen H J. Mater Sci Eng, 2004; A387: 203

[13] Spigarelli S, Evangelista E, McQueen H J. Scr Mater, 2003; 49: 179

[14] Chen L Q, Zhao Y, Xu X Q, Liu X H. Acta Metall Sin, 2010; 46: 1219

(陈礼清, 赵阳, 徐香秋, 刘相华. 金属学报, 2010; 46: 1219)

[15] Momeni A, Dehghani K, Keshmiri H, Ebrahimi G R. Mater Sci Eng, 2010; A527: 1607

[16] Zhang M J, Li F G, Wang S Y, Liu C Y. Mater Sci Eng, 2010; A527: 6778

[17] Cao Y, Di H S, Ma T J, Zhang J Q. J Northeastern Univ (Nat Sci Ed), 2012; 33: 215

(曹宇, 邸洪双, 马天军, 张敬奇. 东北大学学报(自然科学版), 2012; 33: 215)

[18] Poliak E I, Jonas J J. Acta Mater, 1996; 44: 127

[19] Ryan N D, McQueen H J. Can Metall Q, 1990; 29: 150

[20] Barnett M R, Kelly G L, Hodgson P D. Scr Mater, 2000; 43: 366

[21] Gottstein G, Frommert M, Goerdeler M. Mater Sci Eng, 2004; A387–389: 604

[22] Poliak E I, Jonas J J. ISIJ Int, 2003; 43: 684

[23] Najafizadeh A, Jonas J J. ISIJ Int, 2006; 46: 1679

[24] Mirzadeh H, Najafizadeh A. Mater Des, 2010; 31: 1174

[25] McQueen H J, Yue S, Ryan N D, Fry E. J Mater Process Technol, 1995; 53: 295

[26] Hansen N, Huang X. Acta Metall, 1998; 46: 1827

[27] Yu J W, Liu X F, Xie J X. Acta Metall Sin, 2011; 47: 486

(余均武, 刘雪峰, 谢建新. 金属学报, 2011; 47: 486)

[28] Winning M. Scr Mater, 2008; 58: 86

[1]	李景仁, 谢东升, 张栋栋, 谢红波, 潘虎成, 任玉平, 秦高梧. 新型低合金化高强Mg-0.2Ce-0.2Ca合金挤压过程中的组织演变机理[J]. 金属学报, 2023, 59(8): 1087-1096.
[2]	李福林, 付锐, 白云瑞, 孟令超, 谭海兵, 钟燕, 田伟, 杜金辉, 田志凌. 初始晶粒尺寸和强化相对GH4096高温合金热变形行为和再结晶的影响[J]. 金属学报, 2023, 59(7): 855-870.
[3]	娄峰, 刘轲, 刘金学, 董含武, 李淑波, 杜文博. 轧制态Mg-xZn-0.5Er合金板材组织及室温成形性能[J]. 金属学报, 2023, 59(11): 1439-1447.
[4]	吴彩虹, 冯迪, 臧千昊, 范诗春, 张豪, 李胤樹. 喷射成形AlSiCuMg合金的热变形组织演变及再结晶行为[J]. 金属学报, 2022, 58(7): 932-942.
[5]	任少飞, 张健杨, 张新房, 孙明月, 徐斌, 崔传勇. 新型Ni-Co基高温合金塑性变形连接中界面组织演化及愈合机制[J]. 金属学报, 2022, 58(2): 129-140.
[6]	姜伟宁, 武晓龙, 杨平, 顾新福, 解清阁. 热轧硅钢表层动态再结晶区形成规律及剪切织构特征[J]. 金属学报, 2022, 58(12): 1545-1556.
[7]	倪珂, 杨银辉, 曹建春, 王刘行, 刘泽辉, 钱昊. 18.7Cr-1.0Ni-5.8Mn-0.2N节Ni型双相不锈钢的大变形热压缩软化行为[J]. 金属学报, 2021, 57(2): 224-236.
[8]	刘庆琦, 卢晔, 张翼飞, 范笑锋, 李瑞, 刘兴硕, 佟雪, 于鹏飞, 李工. Al_19.3Co₁₅Cr₁₅Ni_50.7高熵合金的热变形行为[J]. 金属学报, 2021, 57(10): 1299-1308.
[9]	赵嫚嫚, 秦森, 冯捷, 代永娟, 国栋. Al、Ni对1Cr9Al(1~3)Ni(1~7)WVNbB钢热变形行为的影响[J]. 金属学报, 2020, 56(7): 960-968.
[10]	陈文雄, 胡宝佳, 贾春妮, 郑成武, 李殿中. 热变形后Ni-30%Fe模型合金中奥氏体的亚动态软化行为[J]. 金属学报, 2020, 56(6): 874-884.
[11]	张阳, 邵建波, 陈韬, 刘楚明, 陈志永. Mg-5.6Gd-0.8Zn合金多向锻造过程中的变形机制及动态再结晶[J]. 金属学报, 2020, 56(5): 723-735.
[12]	武华健, 程仁山, 李景仁, 谢东升, 宋锴, 潘虎成, 秦高梧. Al含量对Mg-Sn-Ca合金微观组织与力学性能的影响[J]. 金属学报, 2020, 56(10): 1423-1432.
[13]	张勇, 李鑫旭, 韦康, 万志鹏, 贾崇林, 王涛, 李钊, 孙宇, 梁红艳. 850 ℃涡轮盘用新型变形高温合金GH4975挤压棒材热变形规律研究[J]. 金属学报, 2020, 56(10): 1401-1410.
[14]	李旭,杨庆波,樊祥泽,呙永林,林林,张志清. 变形参数对2195 Al-Li合金动态再结晶的影响[J]. 金属学报, 2019, 55(6): 709-719.
[15]	邓亚辉,杨银辉,曹建春,钱昊. 23Cr-2.2Ni-6.3Mn-0.26N节Ni型双相不锈钢动态再结晶行为研究[J]. 金属学报, 2019, 55(4): 445-456.

Viewed

Full text

Abstract

Cited

Shared

Discussed