OXIDATION BEHAVIOUR OF NEW COMPOSITENiAl-TYPE COATINGS MODIFIEDWITH DISPERSED Gd_2O_3 |
LI Tiefan;MA Xinqing Institute of Corrosion and Protection of Metals; Corrosion Science Laboratory; Academia Sinica; Shenyang |
|
Cite this article:
LI Tiefan;MA Xinqing Institute of Corrosion and Protection of Metals; Corrosion Science Laboratory; Academia Sinica; Shenyang. OXIDATION BEHAVIOUR OF NEW COMPOSITENiAl-TYPE COATINGS MODIFIEDWITH DISPERSED Gd_2O_3. Acta Metall Sin, 1991, 27(1): 102-107.
|
Abstract Studies were made of the influences of the nature of Gd_2O_3 and itscontent on the oxidation behaviour in air at 1100℃ of the NiAl-type compositecoatings modified with dispersed Gd_2O_3, which were prepared by co-electrodeposi-tion and diffusion aluminizing techniques. In comparison with Gd_2O_3-free coatings,the oxidation of the modified coating may be remarkably retarded and their scalesadherence to substrate may be much improved. It was revealed that some Gd_2O_3 par-ticles are still dispersed in the coatings, but other sub-microscopical Gd_2O_3 particl-es are accumulated at the coating/substrate interface just after aluminizing. Theaccumulated layer is found as the diffusion barrier. A continuous Gd_2O_3 particlelayer would be more effective to reduce the degradation and to prolong the life ofthe coatings.
|
Received: 18 January 1991
|
1 Wang Fuhui, Lou Hanyi, Bai Linxiang, Wu Weitao. Mater Sci Eng, 1989; A121: 387 2 Stringer J, Wilcox B A, Jaffee R I. Oxid Met, 1972; 5(1) : 11 3 Wood G C, Boustead J. Corros Sci, 1968; 8: 719 4 齐藤安俊,铁钢,1979;65: 747 5 Luthra K L. J Vac Sci Technol, 1985; A3: 2574L |
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|