Acta Metall Sin  1992, Vol. 28 Issue (12): 15-17    DOI:
Current Issue | Archive | Adv Search |
IN SITU OBSERVATION OF THERMAL FATIGUE CRACK GROWTH IN 3Cr2W8V STEEL
LIU Jianhong; HE Shiyu; YAO Mei (Harbin Institute of Technology)
Cite this article: 

LIU Jianhong; HE Shiyu; YAO Mei (Harbin Institute of Technology). IN SITU OBSERVATION OF THERMAL FATIGUE CRACK GROWTH IN 3Cr2W8V STEEL. Acta Metall Sin, 1992, 28(12): 15-17.

Download:  PDF(721KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  The growing process of thermal fatigue cracking in 3Cr2W8V steel was observed under desk SEM fitted with self-made minisized device for thermal fatigue test. Before growing of thermal fatigue crack, the main crack tip reveals to blunt firstly, and some holes and uncontinuous microcracks occur in front of it. The growth is developed by bridging of main crack together with holes and microcracks.
Key words:  3Cr2W8V steel      thermal fatigue      crack growth      in situ observation     
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Collect articles（）
Articles by authors

URL: 

https://www.ams.org.cn/EN/     OR     https://www.ams.org.cn/EN/Y1992/V28/I12/15

1 刘剑虹,冯晓曾,张德福,安徽工学院学报,1988;2,45
2 何晋瑞主编,金属高温疲劳,科学出版社,1988;262/
[1] QI Zhao, WANG Bin, ZHANG Peng, LIU Rui, ZHANG Zhenjun, ZHANG Zhefeng. Effects of Stress Ratio on the Fatigue Crack Growth Rate Under Steady State of Selective Laser Melted TC4 Alloy with Defects[J]. 金属学报, 2023, 59(10): 1411-1418.
[2] LI Xifeng, LI Tianle, AN Dayong, WU Huiping, CHEN Jieshi, CHEN Jun. Research Progress of Titanium Alloys and Their Diffusion Bonding Fatigue Characteristics[J]. 金属学报, 2022, 58(4): 473-485.
[3] WANG Li,HE Yufeng,SHEN Jian,ZHENG Wei,LOU Langhong,ZHANG Jian. Effect of Secondary Orientation on Oxidation Anisotropy Around the Holes of Single Crystal Superalloy During Thermal Fatigue Tests[J]. 金属学报, 2019, 55(11): 1417-1426.
[4] Guangping ZHANG, Honglei CHEN, Xuemei LUO, Bin ZHANG. Progress in Thermal Fatigue of Micro/Nano-ScaleMetal Conductors[J]. 金属学报, 2018, 54(3): 357-366.
[5] Chao XU, Qiliang NAI, Zhihao YAO, He JIANG, Jianxin DONG. Grain Boundary Oxidation Effect of GH4738 Superalloy on Fatigue Crack Growth[J]. 金属学报, 2017, 53(11): 1453-1460.
[6] Qiliang NAI,Jianxin DONG,Maicang ZHANG,Zhihao YAO. INFLUENCE OF MULTI-MICROSTRUCTURE INTERACTION ON FATIGUE CRACK GROWTH RATE OF GH4738 ALLOY[J]. 金属学报, 2016, 52(2): 151-160.
[7] Zhisheng WANG, Xiang CHEN, Yanxiang LI, Huawei ZHANG, Yuan LIU. EFFECTS OF B ON HIGH TEMPERATURE MECHA-NICAL PROPERTIES AND THERMAL FATIGUE BEHAVIOR OF COPPER DIE-CASTING DIE STEEL[J]. 金属学报, 2015, 51(5): 519-526.
[8] PU Sheng, WANG Li, XIE Guang, DING Xianfei, LOU Langhong, FENG Qiang. EFFECT OF NOTCH ORIENTATION AND LOCAL RECRYSTALLIZATION ON THERMAL FATIGUE PROPERTIES OF A DIREC- TIONALLY SOLIDIFIED Co-BASED SUPERALLOY[J]. 金属学报, 2015, 51(4): 449-457.
[9] Li WANG,Zhongjiao ZHOU,Shaohua ZHANG,Xiangdong JIANG,Langhong LOU,Jian ZHANG. CRACK INITIATION AND PROPAGATION AROUND HOLES OF Ni-BASED SINGLE CRYSTAL SUPERALLOY DURING THERMAL FATIGUE CYCLE[J]. 金属学报, 2015, 51(10): 1273-1278.
[10] YU Long, SONG Xiping, ZHANG Min, LI Hongliang, JIAO Zehui, YU Huichen. CRACK INITIATION AND PROPAGATION OF HIGH Nb-CONTAINING TiAl ALLOY IN FATIGUE-CREEP INTERACTION[J]. 金属学报, 2014, 50(10): 1253-1259.
[11] ZHANG Litao,WANG Jianqiu. STRESS CORROSION CRACK PROPAGATION BEHAVIOR OF DOMESTIC FORGED NUCLEAR GRADE 316L STAINLESS STEEL IN HIGH TEMPERATURE AND HIGH PRESSURE WATER[J]. 金属学报, 2013, 49(8): 911-916.
[12] LIU Guanglei, SI Naichao, SUN Shaochun, ZHANG Zhijian,WU Qinfang. THERMAL FATIGUE CRACK INITIATION ANDPROPAGATION OF MULTIELEMENTAl-7.5Si-4Cu ALLOY[J]. 金属学报, 2013, 49(3): 303-310.
[13] YANG Jian, DONG Jianxin, ZHANG Maicang. HIGH TEMPERATURE FATIGUE CRACK GROWTH BEHAVIOR OF A NOVEL POWDER METALLURGY SUPERALLOY FGH98[J]. 金属学报, 2013, 49(1): 71-80.
[14] XIAO Xuan XU Hui QIN Xuezhi GUO Yongan GUO Jianting ZHOU Lanzhang. THERMAL FATIGUE BEHAVIORS OF THREE CAST NICKEL BASE SUPERALLOYS[J]. 金属学报, 2011, 47(9): 1129-1134.
[15] HU Zhiyong YANG Chengwei JIANG Min YANG Guangwei WANG Wanjun WANG Xinhua . IN SITU OBSERVATION OF INTRAGRANULAR ACICULAR FERRITE NUCLEATED ON COMPLEX TITANIUM–CONTAINING INCLUSIONS IN TITANIUM DEOXIDIZED STEEL[J]. 金属学报, 2011, 47(8): 971-977.
No Suggested Reading articles found!

Copyright © 2017 Acta Metallurgica Sinica, All Rights Reserved.
Editorial Office: Acta Metallurgica Sinica, 72 Wenhua Rd., Shenyang 110016, China
Tel: +86- 024-23971286, Fax: +86-024-23843760 　E-mail: jsxb@imr.ac.cn
Powered by Beijing Magtech