HYDROGEN EMBRITTLEMENT RESISTANCE OF AUSTENITIC ALLOYS AND ALUMINIUM ALLOYS
LI Yiyi, FAN Cungan, RONG Lijian, YAN Desheng, LI Xiuyan
Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
Download:  PDF(1076KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Hydrogen embrittlement is of the technological importance in which the hydrogen in metallic materials can cause the loss in tensile ductility, cracking or damage and degradation of other mechanical properties. The common hydrogen resistant alloys are austenitic stainless steels, precipitation-strengthened austenitic alloys, low alloy steels and aluminum alloys etc.. As austenitic alloys have high hydrogen resistance properties and their strength can be improved by precipitation strengthening, they are commonly used in hydrogen conditions. IMR had developed a series hydrogen resistant steels, such as HR-1, HR-2, HR-3, J75 and J100 as well as Al-6Mg-0.2Sc-0.15Zr hydrogen resistant aluminum alloy. These alloys posses comprehensive mechanical properties and high hydrogen resistant ability. In addition, alloy smelting, casting, forging, welding and heat treatment should be followed the laws of the preparation. It is important to control the microstructures in order to improve the performance of resistant hydrogen.
Key words:  hydrogen embrittlement      austenitic alloys      low alloy steel      Al-Mg-Sc-Zr alloy      forging deformation     
Received:  30 August 2010     
Corresponding Authors:  LI Yiyi     E-mail:  yyli@imr.ac.cn

Cite this article: 

LI Yiyi FAN Cungan RONG Lijian YAN Desheng LI Xiuyan. HYDROGEN EMBRITTLEMENT RESISTANCE OF AUSTENITIC ALLOYS AND ALUMINIUM ALLOYS. Acta Metall Sin, 2010, 46(11): 1335-1346.

URL: 

https://www.ams.org.cn/EN/10.3724/SP.J.1037.2010.00433     OR     https://www.ams.org.cn/EN/Y2010/V46/I11/1335

[1] Fan C G, Li Y Y, Zhao X J. Inside Information of Institute of Metal Research, Chinese Academy of Sciences, 1985 (范存淦, 李依依, 赵学军. 中国科学院金属研究所内部资料, 1985) [2] Li Y Y. Inside Information of Institute of Metal Research, Chinese Academy of Sciences, 1985 (李依依. 中国科学院金属研究所内部资料, 1985) [3] Xing Z S, Li Y Y, Deng Q Z. Inside Information of Institute of Metal Research, Chinese Academy of Sciences, 1988 (邢中枢, 李依依, 邓庆洲. 中国科学院金属研究所内部资料, 1988) [4] Coates D J, Mortimer B, Hendry A. Corros Sci, 1982; 22: 951 [5] Briant C L. Hydrogen Assisted Cracking of Austenitic Stainless Steels. Warrendale, PA: AIME, 1981: 527 [6] West A J, Holbrook J H. Hydrogen in Austenitic Stainless Steels: Effects of Phase Transformations and Stress State. Warrendale: AIME, 1981: 607 [7] Aerospace Structural Metals Handbooks. Michigan: Mechanical Properties Data Center, 1975: 1 [8] Schmidt A S, Verfuss F, Wicke E. J Nucl Mater, 1985; 131: 247 [9] Rozenak P, Bergman R. Mater Sci Eng, 2006; A437: 366 [10] Li X Y, Li Y Y. Hydrogen Damage in Austenitic Alloys. Beijing: Science Press, 2003: 45 (李秀艳, 李依依. 奥氏体合金的氢损伤. 北京: 科学出版社, 2003: 45) [11] Li Y Y. Inside Information of Institute of Metal Research, Chinese Academy of Sciences, 1995 (李依依. 中国科学院金属研究所内部资料, 1995) [12] Hicks P, Altstetter C. Mater Trans, 1992; 23A: 237 [13] Thompson A W, Brooks J A. Metall Mater Trans, 1975; 6: 1431 [14] Thompson A W. Metall Mater Trans, 1976; 7A: 315 [15] Rhodes C, Thompson A. Metall Mater Trans, 1977; 8A: 949 [16] Chu W Y. Hydrogen Damage and Delayed Fracture. Beijing: Metallurgical Industry Press, 1988: 10 (褚武杨. 氢损伤和滞后断裂. 北京: 冶金工业出版社, 1988: 10) [17] Li Y Y, Wang A C, Yang K. Trans Mat Res Soc Jpn, 1993; 18: 545 [18] Li X Y, Ma L M, Li Y Y. Acta Metall Sin, 2002; 38: 593 (李秀艳, 马禄铭, 李依依. 金属学报, 2002; 38: 593) [19] Wang A C, Li Y Y, Deng W, Fan C G, Li D F, Yang K, Shi C X. Chin J Mater Res, 1995; 9: 1 (王安川, 李依依, 邓 文, 范存淦, 李冬法, 杨柯, 师昌绪. 材料研究学报, 1995; 9: 1) [20] Wang A C, Fan C G, Yang K, Li Y Y. Inside Information of Institute of Metal Research, Chinese Academy of Sciences, 1993 (王安川, 范存淦, 杨柯, 李依依. 中国科学院金属研究所内部资料, 1993) [21] Liu S, Zheng H, Gui Q H, Ma A H, Yu H B, Wang L B, Yang H G. Acta Metall Sin, 2004; 40: 393 (刘 实, 郑 华, 贵全红, 马爱华, 于洪波, 王隆保, 杨洪广. 金属学报, 2004; 40: 393) [22] Zhang J, Li X Y, Rong L J, Zheng Y N, Zhu S Y. Acta Metall Sin, 2006; 42: 469) (张 建, 李秀艳, 戎利建, 郑永男, 朱升云. 金属学报, 2006; 42: 469) [23] San–Martin A, Manchester F D. The Al–H System Phase Diagram Evaluations. Section 2, 1992: 17 [24] Zhao W T, Yan D S, Rong L J. Acta Metall Sin, 2005; 41: 1150 (赵卫涛, 闫德胜, 戎利建. 金属学报, 2005; 41: 1150) [25] Du G, Deng J W, Wang Y L, Yan D S, Rong L J. Scr Mater, 2009; 61: 532 [26] Du G, Deng J W, Yan D S, Zhao M J, Rong L J. J Mater Sci Technol, 2009; 25: 749 [27] Du G, Yan D S, Rong L J. Acta Metall Sin, 2008; 44: 1209 (杜刚, 闫德胜, 戎利建. 金属学报, 2008; 44: 1209) [28] Harada Y, Dunand D C. Scr Mater, 2003; 48: 219 [29] Ferreira P J, Robertson I M, Birnbaum H K. Acta Mater, 1998; 46: 1749 [30] Tomota Y, Xia Y, Inoue K. Acta Mater, 1998; 46: 1577 [31] Ferreira P J, Robertson I M, Birnbaum H K. Acta Mater, 1999; 47: 2991 [32] Bampton C C, Jones I P, Loretto M H. Acta Metall, 1978; 26: 39 [33] Schulthess T C, Turchi P E A, Gonis A, Nieh T G. Acta Mater, 1998; 46: 2215 [34] Brooks J A, Thompson A W. Metall Trans, 1993; 24A: 1983 [35] Zhang J, Li X Y, Rong L J. Acta Metall Sin, 2006; 42: 469 (张 建, 李秀艳, 戎利建. 金属学报, 2006; 42: 469) [36] Harada Y, Dunand D C. Intermetallics, 2009; 17: 17 [37] http://www.lm.gov.cn/gb/training/2005–11/11/content 90745.htm [38] Zhang J, Li X Y, Rong L J, Liao B, Fan Y, Tan Y, Mei J. Chin J Mater Res, 2007; 21: 459 (张 建, 李秀艳, 戎利建, 廖 彬, 范英, 谭 云, 梅军. 材料研究学报, 2007; 21: 459) [39] Lu S P, Dong W C, Li D Z, Li Y Y. Compt Mater Sci, 2009; 45: 327 [40] Li D J, Lu S P, Li D Z, Li Y Y. Adv Mater Res, 2010; 97–101: 3978
[1] LIU Zhenbao,LIANG Jianxiong,SU Jie,WANG Xiaohui,SUN Yongqing,WANG Changjun,YANG Zhiyong. Research and Application Progress in Ultra-HighStrength Stainless Steel[J]. 金属学报, 2020, 56(4): 549-557.
[2] LI Jinxu,WANG Wei,ZHOU Yao,LIU Shenguang,FU Hao,WANG Zheng,KAN Bo. A Review of Research Status of Hydrogen Embrittlement for Automotive Advanced High-Strength Steels[J]. 金属学报, 2020, 56(4): 444-458.
[3] Futao DONG,Fei XUE,Yaqiang TIAN,Liansheng CHEN,Linxiu DU,Xianghua LIU. Effect of Annealing Temperature on Microstructure, Properties and Hydrogen Embrittlement of TWIP Steel[J]. 金属学报, 2019, 55(6): 792-800.
[4] Xiaoli ZHAO, Yongjian ZHANG, Chengwei SHAO, Weijun HUI, Han DONG. Hydrogen Embrittlement of Intercritically AnnealedCold-Rolled 0.1C-5Mn Steel[J]. 金属学报, 2018, 54(7): 1031-1041.
[5] Jianan ZOU, Xiaolu PANG, Kewei GAO. Crevice Corrosion of X70 and 3Cr Low Alloy Steels Under Supercritical CO2 Condition[J]. 金属学报, 2018, 54(4): 537-546.
[6] Jun SUN, Suzhi LI, Xiangdong DING, Ju LI. Hydrogenated Vacancy: Basic Properties and Its Influence on Mechanical Behaviors of Metals[J]. 金属学报, 2018, 54(11): 1683-1692.
[7] Jun YU, Deping ZHANG, Ruosheng PAN, Zehua DONG. Electrochemical Noise of Stress Corrosion Cracking of P110 Tubing Steel in Sulphur-Containing Downhole Annular Fluid[J]. 金属学报, 2018, 54(10): 1399-1407.
[8] Yunfei LU,Junhua DONG,Wei KE. EFFECTS OF SO42- ON THE CORROSION BEHAVIOR OF NiCu LOW ALLOY STEEL IN DEAERATED BICARBONATE SOLUTIONS[J]. 金属学报, 2015, 51(9): 1067-1076.
[9] Xiaolin LI,Zhaodong WANG,Xiangtao DENG,Yujia ZHANG,Chengshuai LEI,Guodong WANG. EFFECT OF FINAL TEMPERATURE AFTER ULTRA-FAST COOLING ON MICROSTRUCTURAL EVOLUTION AND PRECIPITATION BEHAVIOR OF Nb-V-Ti BEARING LOW ALLOY STEEL[J]. 金属学报, 2015, 51(7): 784-790.
[10] LU Yunfei, YANG Jingfeng, DONG Junhua, KE Wei. THE CORROSION BEHAVIOUR OF NiCu LOW ALLOY STEEL IN A DEAERATED BICARBONATE SOLUTION CONTAINING Cl- IONS[J]. 金属学报, 2015, 51(4): 440-448.
[11] WU Xinqiang, TAN Jibo, XU Song, HAN En-Hou, KE Wei. CORROSION FATIGUE MECHANISM OF NUCLEAR-GRADE LOW ALLOY STEEL IN HIGH TEMPERATURE PRESSURIZED WATER AND ITS ENVIRONMENTAL FATIGUE DESIGN MODEL[J]. 金属学报, 2015, 51(3): 298-306.
[12] Pingguang XU,Jiang YIN,Shuyan ZHANG. TENSILE DEFORMATION BEHAVIOR OF HYDROGEN CHARGED ULTRAHIGH STRENGTH STEEL STUDIED BY IN SITU NEUTRON DIFFRACTION[J]. 金属学报, 2015, 51(11): 1297-1305.
[13] Yongwei SUN,Jizhi CHEN,Jun LIU. STUDY ON HYDROGEN EMBRITTLEMENT SUSCEPTIBILITY OF 1000 MPa GRADE 0Cr16Ni5Mo STEEL[J]. 金属学报, 2015, 51(11): 1315-1324.
[14] XU Qiufa, PANG Xiaolu, LIU Quanlin, GAO Kewei. CREVICE CORROSION OF LOW ALLOY STEEL ANDCARBON STEEL IN THE SIMULATED GROUNDWATER AT 90 ℃[J]. 金属学报, 2014, 50(6): 659-666.
[15] FANG Yupei, XIE Zhenjia, SHANG Chengjia. EFFECT OF INDUCTION TEMPERING ON CARBIDE PRECIPITATION BEHAVIOR AND TOUGHNESS OF A 1000 MPa GRADE HIGH STRENGTH LOW ALLOY STEEL[J]. 金属学报, 2014, 50(12): 1413-1420.
No Suggested Reading articles found!