金属学报  1998, Vol. 34 Issue (9): 915-918

论文 本期目录 | 过刊浏览 |

微量硼对TiAl合金动态拉伸性能的影响

王瑜;林栋梁;周元鑫;夏源明;C.C.Law

上海交通大学材料科学系;教育部高温材料及高温测试开放实验室;上海;200030;上海交通大学材料科学系;教育部高温材料及高温测试开放实验室;上海;200030;中国科学技术大学近代力学系;合肥;230026;中国科学技术大学近代力学系;合肥;230026;MaterialsandMechanicsEngineering;UnitedTechnologiesCompany-Pratt&Whittney400MainStreet;EastHartford;CT06108;U.S.A.

THE EFFECT OF MINOR BORON ADDITION ON DYNAMIC TENSILE PROPERTIES OF WROUGHT Ti-47Al-2Mn-2Nb ALLOY

WANG Yu; LIN Dongliang(T. L. Lin)(Department of Materials Science; the Open Laboratory of Education Ministry for High-Temperature Materials and Test; Shanghai Jiao Tong University; Shanghai 200030)ZHOU Yuanxin; XIA Yuanming (Department of Morden Dynamics; University of Science and Technology of China; Hefei 230026)C. C. Law (Materials and Mechanics Engineering; United Technologies Company-Pratt & Whittney 400 Main Street; East Hartford; CT 06108; U. S. A.)Correspondent: LIN Dongliang; professon Tel: (021)62812544(O); (021)62835352(H);Fax: (021)62820892; E-mail: dllin@ mail. sjtu. edu. cn.

王瑜;林栋梁;周元鑫;夏源明;C.C.Law. 微量硼对TiAl合金动态拉伸性能的影响[J]. 金属学报, 1998, 34(9): 915-918.
, , , , . THE EFFECT OF MINOR BORON ADDITION ON DYNAMIC TENSILE PROPERTIES OF WROUGHT Ti-47Al-2Mn-2Nb ALLOY[J]. Acta Metall Sin, 1998, 34(9): 915-918.

摘要 参考文献 相关文章 Metrics 全文: PDF(1158 KB)   摘要: 采用自制的Hopkinson拉杆装置，研究了微量硼对形变Ti—47Al—2Mn—2Nb合金在20—1000S－1应变速率范围内的拉伸性能的影响；发现添加1．0％B（原子分数）能明显提高其动态拉伸强度，不破坏动态拉伸强度与应变速率之间的线性关系，但对其动态拉伸塑性无明显的改善作用，对动态断裂方式也无明显影响. 关键词 ： TiAl合金,  Hopkinson拉杆技术,  动态力学性能,  硼     Abstract：The effect of minor boron addition on tensile properties of wrought Ti-47Al-2Mn-2Nb alloy was investigated at strain rates from 20 to 1000s-1 , using a self-made separated Hopkinson tensile bar setup. It was found that the addition of 1.0%B (atom fraction) increases dynamic tensile strength considerably, but does not damage the linear relationship between dynamic tenisle strength and the strain rate. Meanwhile, the addition produces neither obvious improvement on dynamic tensile ductility nor noteworthy change in fracture mode. Key words： titanium aluminide    SHTB    dynamic tensile property    boron 收稿日期: 1998-09-18      服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 王瑜 林栋梁 周元鑫 夏源明 C.C.Law 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y1998/V34/I9/915 1 王瑜,林栋梁,周元鑫,夏源明,Law C C.金属学报,1998; 34: 908(Wang Y, Lin D L(Lin T L), Zhu Y X; Xia Y M, Law C C Acta Metall Sin, 1988 34: 908) 2 Larsen D E Jr, Kampe S, Christodoulou L In: Anton D L, Martin P L, Miracle D B, McMeeking R eds,Intermetallic Matrix Composites, vol. 194,Mater Res Soc Proc;Pittsburgh, PA,1990:285 3 Kim Y- W.In:Kim Y-W,WagnerR,Yamaguchi M eds,Gamma Titanium Aluminides. TMS, Warrendale, PA, 1995: 637 4 王瑜,林栋梁,Law C C.微量硼和应变速率对形变 TiAl合金室温力学性能的影响,中国有色金属学报,待发表(Wan Y,Lin D L(Li T L),Law C C.The Effects of Minor Boron Addition and Strain Rate on Room-Tempera ture Tensile Properties of TiAl Alloy, Accepted byTransaction of Nonferrous Metal Society of China. 5 王瑜,林栋梁,刘俊亮, Law C C.金属学报 1997; 33: 1021(Wang Y, Lin D L(Lin T L), Liu J L, Law C C Acta Metall Sin, 1997; 33: 1021) 6 Xia Y, Zhou Y Acta Mech Sin, 1996; 12: 243 7 Pu Z; Wu K H ScrMater, 1996; 34(1): 169 8 Larsen D J,Liu C T,Miller M K. Intermetallics, 1997;5:411 9 Nadgornyi E. Prog Mater Sci, 1988; 31: 1 [1] 刘路军, 刘政, 刘仁辉, 刘永. Nd90Al10 晶界调控对晶界扩散磁体磁性能和微观结构的影响[J]. 金属学报, 2023, 59(11): 1457-1465. [2] 李小兵, 潜坤, 舒磊, 张孟殊, 张金虎, 陈波, 刘奎. W含量对Ti-42Al-5Mn-xW合金相转变行为的影响[J]. 金属学报, 2023, 59(10): 1401-1410. [3] 刘仁慈, 王鹏, 曹如心, 倪明杰, 刘冬, 崔玉友, 杨锐. 700℃热暴露对 β 凝固 γ-TiAl合金表面组织及形貌的影响[J]. 金属学报, 2022, 58(8): 1003-1012. [4] 陈玉勇, 叶园, 孙剑飞. TiAl合金板材轧制研究现状[J]. 金属学报, 2022, 58(8): 965-978. [5] 陈伟, 章环, 牟娟, 朱正旺, 张海峰, 王沿东. 显微组织和应变速率对TC4合金动态力学性能和绝热剪切带的影响[J]. 金属学报, 2022, 58(10): 1271-1280. [6] 刘仲武, 何家毅. 钕铁硼永磁晶界扩散技术和理论发展的几个问题[J]. 金属学报, 2021, 57(9): 1155-1170. [7] 李天瑞, 刘国怀, 于少霞, 王文娟, 张风奕, 彭全义, 王昭东. 直接包套轧制铸态Ti-46Al-8Nb合金的组织特征及热变形机制[J]. 金属学报, 2020, 56(8): 1091-1102. [8] 刘先锋, 刘冬, 刘仁慈, 崔玉友, 杨锐. Ti-43.5Al-4Nb-1Mo-0.1B合金的包套热挤压组织与拉伸性能[J]. 金属学报, 2020, 56(7): 979-987. [9] 王希,刘仁慈,曹如心,贾清,崔玉友,杨锐. 冷却速率对β凝固γ-TiAl合金硼化物和室温拉伸性能的影响[J]. 金属学报, 2020, 56(2): 203-211. [10] 陈占兴,丁宏升,陈瑞润,郭景杰,傅恒志. 脉冲电流作用下TiAl合金凝固组织演变及形成机理[J]. 金属学报, 2019, 55(5): 611-618. [11] 廖依敏, 丰敏, 陈明辉, 耿哲, 刘阳, 王福会, 朱圣龙. TiAl合金表面搪瓷基复合涂层与多弧离子镀NiCrAlY涂层的抗热腐蚀行为对比研究[J]. 金属学报, 2019, 55(2): 229-237. [12] 金浩, 贾清, 刘荣华, 线全刚, 崔玉友, 徐东生, 杨锐. 籽晶制备及Ti-47Al合金PST晶体取向控制[J]. 金属学报, 2019, 55(12): 1519-1526. [13] 马秀良, 胡肖兵. 高温合金中硼化物精细结构的高空间分辨电子显微学研究[J]. 金属学报, 2018, 54(11): 1503-1524. [14] 潘宇, 路新, 刘程程, 孙健卓, 佟健博, 徐伟, 曲选辉. Sn对TiAl基合金烧结致密化与力学性能的影响[J]. 金属学报, 2018, 54(1): 93-99. [15] 李天瑞, 刘国怀, 徐莽, 牛红志, 付天亮, 王昭东, 王国栋. Ti-43Al-4Nb-1.5Mo合金包套锻造与热处理过程的微观组织及高温拉伸性能[J]. 金属学报, 2017, 53(9): 1055-1064. Viewed Full text Abstract Cited   Shared      Discussed