喷射成形大尺寸镧基块体非晶过冷液相区内的塑性变形行为

董亭义¹;杨滨^1;2;何建平¹;张勇¹

1. 北京科技大学新金属材料国家重点实验室; 北京 100083\par
2. 中国科学院国际材料物理中心; 沈阳 110016

DEFORMATION BEHAVIOR OF SPRAY–DEPOSITED La–BASED BULK AMORPHOUS ALLOY IN SUPERCOOLED LIQUID REGION

DONG Tingyi ¹; YANG Bin ^1;2; HE Jianping ¹; ZHANG Yong ¹

1. State Key Laboratory for Advanced Metals and Materials; University of Science and Technology Beijing; Beijing 100083
2. International Centre for Materials Physics; Chinese Academy of Sciences; Shenyang 110016

引用本文:

董亭义杨滨何建平张勇. 喷射成形大尺寸镧基块体非晶过冷液相区内的塑性变形行为[J]. 金属学报, 2009, 45(2): 232-236.
, , , . DEFORMATION BEHAVIOR OF SPRAY–DEPOSITED La–BASED BULK AMORPHOUS ALLOY IN SUPERCOOLED LIQUID REGION[J]. Acta Metall Sin, 2009, 45(2): 232-236.

全文: PDF(1976 KB)

摘要:

研究了喷射成形大尺寸La₆₂Al_15.7(Cu, Ni)_22.3非晶合金在过冷液相区内的塑性变形行为. 结果表明, 随加热温度的增加和应变速率的减小, 该非晶合金由非稳态变形向单一稳态变形行为转变. 当应变速率为5×10^-3 s^-1, 温度为443 K和挤压比为6.25时, 喷射成形La₆₂Al_15.7(Cu, Ni)_22.3非晶合金样品的密度由挤压前的5.723增加到挤压后的5.924 g/cm³, 达到了同成分吸铸态非晶合金密度 (6.134 g/cm³) 的96.6%. 挤压后非晶合金样品依然保持完全非晶态.

关键词 ：喷射成形, 镧基非晶合金, 挤压, 塑性变形, 过冷液相区

Abstract：

A large sized La₆₂Al_15.7(Cu, Ni)_22.3 amorphous alloy was produced by spray deposition, and its compressive deformation behavior in supercooled region was investigated. It is found that both the strain rate and test temperature significantly affect the stress–strain behavior of the amorphous alloy in the supercooled liquid region. The deformation behavior is characterized by a transformation from unsteady–state flow to steady–state flow with the decrease of strain rate or increase of heating temperature in the supercooled region. After hot extrusion at 443 K, the alloy is still amorphous and its density (5.924 g/cm³) is 96.6% of the suction-cast amorphous alloy with the same component (6.134 g/cm³) when the reduction ratio, strain rate and heating temperature are adopted as 6.25, 5×10⁻³ s⁻¹ and 443 K, respectively.

Key words： spray deposition La–based amorphous alloy hot extruding plastic deformation supercooled liquid region

收稿日期: 2008-07-25

ZTFLH:

TG139.8

基金资助:

国家自然科学基金项目 50671013和北京市自然科学基金项目2042014资助

作者简介: 董亭义, 男, 1977年生, 博士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	董亭义
	杨滨
	何建平
	张勇
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2009/V45/I2/232

[1] Dong T Y, Yang B, He J P, Zhang Y. Acta Metall Sin, 2008; 44: 652
(董亭义, 杨滨, 何建平, 张勇. 金属学报, 2008; 44: 652)
[2] Zhang Y, Tan H, Li Y. J Non–Cryst Solids, 2006; 352: 3942
[3] Jiang Q K, Zhang G Q, Chen L Y, Wu J Z, Zhang H G, Jiang J Z. J Alloys Compd, 2006; 424: 183
[4] Zhang Y, Xu W, Tan H, Li Y. Acta Mater, 2005; 53: 2607
[5] Chan K C, Chen Q, Liu L. Intermetallics, 2007; 15: 500
[6] Li J F, Cao Q P, Hu Y, Horsewell A, Jiang J Z, Zhou Y H. Mater Sci Eng, 2007; A457: 94
[7] Chu J P, Chiang C L, Wijaya H, Huang R T, Wu C W, Zhang B, Wang W H, Nieh T G. Scr Mater, 2006; 55: 227
[8] Shen J, Wang G, Sun J F, Chen D M, Xing D W, Zhou B D. Acta Metall Sin, 2004; 40: 518
(沈军, 王刚, 孙剑飞, 陈德民, 邢大伟, 周彼德. 金属学报,,2004; 40: 518)
[9] Wu S D. The Principle of Metal Superplastic Formation. Beijing: National Defense Industry Press, 1997: 9
(吴诗chun. 金属超塑性变形理论. 北京: 国防工业出版社,, 1997:9)

[1]	张海峰, 闫海乐, 方烽, 贾楠. FeMnCoCrNi高熵合金双晶微柱变形机制的分子动力学模拟[J]. 金属学报, 2023, 59(8): 1051-1064.
[2]	刘继浩, 周健, 武会宾, 马党参, 徐辉霞, 马志俊. 喷射成形M3高速钢偏析成因及凝固机理[J]. 金属学报, 2023, 59(5): 599-610.
[3]	万涛, 程钊, 卢磊. 组元占比对层状纳米孪晶Cu力学行为的影响[J]. 金属学报, 2023, 59(4): 567-576.
[4]	冯迪, 朱田, 臧千昊, 李胤樹, 范曦, 张豪. 喷射成形过共晶AlSiCuMg合金的固溶行为[J]. 金属学报, 2022, 58(9): 1129-1140.
[5]	吴彩虹, 冯迪, 臧千昊, 范诗春, 张豪, 李胤樹. 喷射成形AlSiCuMg合金的热变形组织演变及再结晶行为[J]. 金属学报, 2022, 58(7): 932-942.
[6]	刘帅帅, 侯超楠, 王恩刚, 贾鹏. Zr₆₁Cu₂₅Al₁₂Ti₂ 和Zr_52.5Cu_17.9Ni_14.6Al₁₀Ti₅ 块体非晶合金过冷液相区的塑性流变行为[J]. 金属学报, 2022, 58(6): 807-815.
[7]	郭祥如, 申俊杰. 孪生诱发软化与强化效应的Cu晶体塑性行为模拟[J]. 金属学报, 2022, 58(3): 375-384.
[8]	任少飞, 张健杨, 张新房, 孙明月, 徐斌, 崔传勇. 新型Ni-Co基高温合金塑性变形连接中界面组织演化及愈合机制[J]. 金属学报, 2022, 58(2): 129-140.
[9]	陈润, 王帅, 安琦, 张芮, 刘文齐, 黄陆军, 耿林. 热挤压与热处理对网状TiBw/TC18复合材料组织及性能的影响[J]. 金属学报, 2022, 58(11): 1478-1488.
[10]	石增敏, 梁静宇, 李箭, 王毛球, 方子帆. 板条马氏体拉伸塑性行为的原位分析[J]. 金属学报, 2021, 57(5): 595-604.
[11]	陈建军, 丁雨田, 王琨, 闫康, 马元俊, 王兴茂, 周胜名. Laves相对 GH3625合金管材热挤压过程中爆裂行为的影响[J]. 金属学报, 2021, 57(5): 641-650.
[12]	林鹏程, 庞玉华, 孙琦, 王航舵, 刘东, 张喆. 45钢块体超细晶棒材3D-SPD轧制法[J]. 金属学报, 2021, 57(5): 605-612.
[13]	曹庆平, 吕林波, 王晓东, 蒋建中. 物理气相沉积制备金属玻璃薄膜及其力学性能的样品尺寸效应[J]. 金属学报, 2021, 57(4): 473-490.
[14]	何长树, 郄默繁, 张志强, 赵骧. 轴向超声振动对搅拌摩擦焊过程中金属流动行为的影响[J]. 金属学报, 2021, 57(12): 1614-1626.
[15]	刘先锋, 刘冬, 刘仁慈, 崔玉友, 杨锐. Ti-43.5Al-4Nb-1Mo-0.1B合金的包套热挤压组织与拉伸性能[J]. 金属学报, 2020, 56(7): 979-987.

Viewed

Full text

Abstract

Cited

Shared

Discussed