Co对Fe--B--Y--Nb块体非晶合金玻璃形成能力及软磁性能的影响

金属学报

2009, Vol. 45

Issue (2): 249-252

论文

本期目录 | 过刊浏览

Co对Fe--B--Y--Nb块体非晶合金玻璃形成能力及软磁性能的影响

吴泽宇;郭胜锋;李宁;柳林

(华中科技大学材料科学与工程学院材料成形与模具技术国家重点实验室; 武汉 430074)

INFLUENCE OF Co ON THE GLASS FORMING ABILITY AND SOFT MAGNETIC PROPERTY OF Fe–B–Y–Nb BULK AMORPHOUS ALLOY

WU Zeyu; GUO Shengfeng; LI Ning; LIU Lin

State Key Laboratory of Material Processing and Die&Mould Technology; College of Materials Science and Engineering; Huazhong University of Science and Technology; Wuhan 430074

引用本文:

吴泽宇郭胜锋李宁柳林. Co对Fe--B--Y--Nb块体非晶合金玻璃形成能力及软磁性能的影响[J]. 金属学报, 2009, 45(2): 249-252.
, , , . INFLUENCE OF Co ON THE GLASS FORMING ABILITY AND SOFT MAGNETIC PROPERTY OF Fe–B–Y–Nb BULK AMORPHOUS ALLOY[J]. Acta Metall Sin, 2009, 45(2): 249-252.

全文: PDF(714 KB)

摘要:

采用吸铸法制备了直径为2---5 mm的[(Fe_1-xCo_x)_71.2B₂₄Y_4.8]₉₆Nb₄ (x=0, 0.1, 0.2, 0.3和0.4) 合金棒. XRD测试表明, 用适量的Co替换Fe可有效提高原始
合金 (Fe_71.2B₂₄Y_4.8)₉₆Nb₄ 的玻璃形成能力, 拓宽非晶形成范围. 热分析结果显示所有的非晶合金均具有高的玻璃转变温度(T_g≥850 K) 和宽广的过冷液态区 (Δ T_x≥97 K). 此外, Co的替换明显改善了原始非晶合金的软磁性能, 其中成分为[(Fe_0.9Co_0.1)_71.2B₂₄Y_4.8]₉₆Nb₄的非晶合金的饱和磁化强度M_s达到26.6 kA/m, 矫顽力H_c仅为59 A/m.热磁实验表明, 随着Co含量的增加, 非晶合金的Curie温度不断升高, 最大值达到577 K, 与初始合金相比提高了100 K, 显著改善了原体系的热磁性能.

关键词 ：铁基非晶合金, 块体金属玻璃, Co替换, 玻璃形成能力, 软磁性能

Abstract：

[(Fe_1-xCo_x)_71.2B₂₄Y_4.8]₉₆Nb₄ (x=0, 0.1, 0.2, 0.3 and 0.4) alloy rods with 2—5 mm in diameter were prepared using commercial materials and suction casting method. XRD results show that the substitution of an appropriate amount of Co for Fe can improve effectively the glass forming ability and extend considerably the composition scope for glassy formation. DTA curves indicate that all the alloys with different Co contents exhibit a high glass transition temperature (T_g≥850 K) and wide supercooled liquid region (ΔT_x≥97 K). It is also observed that Co substitution for Fe enhances significantly the soft magnetic properties. For the [(Fe_0.9Co_0.1)_71.2B₂₄Y_4.8]₉₆Nb₄ bulk metallic glass, the saturation magnetization (M_s) has a maximum value of 26.6 kA/m, while the coercivity (H_c) is only 59 A/m. In addition, the Curie temperatures of the tested alloys increase continuously with the increase of Co content, and reaches the highest value of 577 K when x=0.4, which is about 100 K higher than that of the base alloy without Co.

Key words： Fe--based amorphous alloy bulk metallic glass Co substitution glass formingability soft magnetic property

收稿日期: 2008-08-22

ZTFLH:

TG139.8

基金资助:

高等学校博士学科点专项科研基金项目200604087069和国家自然科学基金项目50635020资助

作者简介: 吴泽宇, 男, 1984年生, 硕士生

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吴泽宇
	郭胜锋
	李宁
	柳林
44.8K

链接本文:

https://www.ams.org.cn/CN/ 或 https://www.ams.org.cn/CN/Y2009/V45/I2/249

[1] Duwez P, Lin S C H. J Appl Phys, 1967; 38: 4096
[2] Inoue A, Shinohara Y, Gook J S. Mater Trans JIM, 1995; 36: 1427
[3] Inoue A, Zhang T, Takeuchi A. Appl Phys Lett, 1997; 71: 464
[4] Inoue A, Zhang W. J Appl Phys, 1999; 85: 4491
[5] Inoue A, Shen B L. Mater Trans JIM, 2002; 43: 766
[6] Shen T D, Schwarza R B. Appl Phys Lett, 1999; 75: 49
[7] Lin C Y, Tien H Y, Chin T S. Appl Phys Lett, 2005; 86: 162501
[8] Hu Y, Pan M X, Liu L, Zhao Y H, Zhao D Q, Wang W H. Mater Lett, 2003; 57: 2698
[9] Kim D H, Park J M, Kim D H, Kim W T. J Mater Res, 2007; 22: 471
[10] Han Z, Zhang J, Li Y. Intermetallics, 2007; 15: 1447
[11] Shen B L, Inoue A, Chang C T. Appl Phys Lett, 2004; 85: 4911
[12] Park J M, Park J S, Kim D H, Kim J H, Fleury E. J Mater Res, 2006; 21: 1019
[13] Li F S, Shen B L, MakinoA, Inoue A. Appl Phys Lett, 2007; 91: 234101
[14] Greer A L. Nature, 1993; 366: 303
[15] Slater J C. J Appl Phys, 1937; 8: 385
[16] Um C Y, McHenry M E. IEEE Trans Magn, 2004; 40: 2724
[17] Egami T. Rep Prog Phys, 1984; 47: 1601
[18] He S L, He K Y, Shen B G, Zhang H W, Zhang S Y, Guo H Q. J Appl Phys, 1999; 86: 6301

[1]	杨群, 彭思旭, 卜庆周, 于海滨. 非晶态Ni₈₀P₂₀合金的玻璃转变和过冷液体性质[J]. 金属学报, 2021, 57(4): 553-558.
[2]	耿遥祥, 王英敏. 铁基非晶合金局域结构与性能关联：基于微合金化机理研究[J]. 金属学报, 2020, 56(11): 1558-1568.
[3]	赵燕春, 孙浩, 李春玲, 蒋建龙, 毛瑞鹏, 寇生中, 李春燕. 高强韧Ti-Ni基块体金属玻璃复合材料高温变形行为[J]. 金属学报, 2018, 54(12): 1818-1824.
[4]	耿遥祥,林鑫,羌建兵,王英敏,董闯. Finemet型纳米晶软磁合金的双团簇特征与成分优化[J]. 金属学报, 2017, 53(7): 833-841.
[5]	耿遥祥,张志杰,王英敏,羌建兵,董闯,汪海斌,特古斯. 高Fe含量Fe-B-Si-Hf块体非晶合金的结构-性能关联[J]. 金属学报, 2017, 53(3): 369-375.
[6]	耿遥祥,王英敏,羌建兵,董闯,汪海斌,特古斯. Fe-B-Si-Nb块体非晶合金的成分设计与优化^*[J]. 金属学报, 2016, 52(11): 1459-1466.
[7]	沈勇,徐坚. Zr_46.9Cu_45.5Al_5.6Y_2.0金属玻璃含B2-CuZr相内生复合材料的制备及其力学性能^*[J]. 金属学报, 2015, 51(11): 1407-1415.
[8]	吕宝臣刘海涛任鑫王晓亮李刚孙跃军. 高溶质浓度(伪)三元系金属玻璃原子密堆垛模型[J]. 金属学报, 2012, 48(2): 240-244.
[9]	胡强曾燮榕钱海霞谢胜辉盛洪超. 铁基块体非晶合金玻璃形成能力与特征自由体积的关系[J]. 金属学报, 2012, 48(11): 1329-1334.
[10]	覃作祥王小京张海峰王中光胡壮麒. Zr₅₅Al₁₀Ni₅Cu₃₀块体金属玻璃的摩擦焊焊接[J]. 金属学报, 2009, 45(5): 620-624.
[11]	孙亚娟魏先顺黄永江沈军. 稀土Gd掺杂对锆基块体非晶合金玻璃形成能力及力学性能的影响[J]. 金属学报, 2009, 45(2): 243-248.
[12]	徐民易军全明秀王沿东左良. Nb对非晶态Fe-Co-Nd-B合金的晶化动力学的影响[J]. 金属学报, 2009, 45(1): 91-96.
[13]	董盼; 张甲; 常新春; 侯万良; 全明秀; 王建强 . Al--Co--Y体系中富 Al区非晶相的形成与结构演化[J]. 金属学报, 2008, 44(2): 227-232 .
[14]	徐民; 孙羽; 全明秀; 王沿东; 左良 . Fe--Co--Nd--Nb--B非晶合金的形成和软磁性能[J]. 金属学报, 2007, 43(7): 699-704 .
[15]	李宏祥; Seonghoon.Yi; 张新房; 王晓东 . Fe--C--Si--B--P--Cr--Mo--Al块体非晶合金的制备与压缩性能[J]. 金属学报, 2006, 42(7): 777-780 .

Viewed

Full text

Abstract

Cited

Shared

Discussed