金属学报  2005, Vol. 41 Issue (12): 1272-1276

论文 本期目录 | 过刊浏览 |

夹杂物对超高强度钢低周疲劳裂纹萌生及扩展影响的原位观测

王习术; 梁锋; 曾燕屏; 谢锡善

清华大学工程力学系; 北京 100084

SEM IN SITU OBSERVATIONS TO THE EFFECTS OF INCLUSIONS ON INITIATION AND PROPAGATION OF THE LOW CYCLIC FATIGUE CRACK IN SUPER STRENGTH STEEL

WANG Xishu; LIANG Feng; ZENG Yanping; XIE Xishan

Department of Engineering Mechanics; Tsinghua University; Beijing 100084

王习术; 梁锋; 曾燕屏; 谢锡善 . 夹杂物对超高强度钢低周疲劳裂纹萌生及扩展影响的原位观测[J]. 金属学报, 2005, 41(12): 1272-1276 .
, , , . SEM IN SITU OBSERVATIONS TO THE EFFECTS OF INCLUSIONS ON INITIATION AND PROPAGATION OF THE LOW CYCLIC FATIGUE CRACK IN SUPER STRENGTH STEEL[J]. Acta Metall Sin, 2005, 41(12): 1272-1276 .

摘要 参考文献 相关文章 Metrics 全文: PDF(516 KB)   摘要: 采用扫描电镜原位观测了数微米大小夹杂物对超高强度钢疲劳裂纹萌生及扩展的影 响, 并用有限元法解释了夹杂物尺寸和形状对疲劳裂纹萌生及初期扩展的影响程度, 得到了超高强度钢低周疲劳裂纹萌生与扩展特性和夹杂物对疲劳破坏的关键尺寸的 估计值. 同时, 讨论了现行实验方法对确定铁基材料裂纹扩展速率的作用. 关键词 ： 超高强度钢,  夹杂物,  疲劳裂纹萌生及扩展     Abstract：SEM in situ observations for the effects of inclusions on the fatigue crack initiation and propagation behaviors of super strength steel indicate that the inclusion size and shape affect not only on the fatigue crack initiation location but also on the crack growth behavior. At the same time, the effects of inclusions on the fatigue crack initiation are discussed by finite element method (FEM) analysis. The critical size of inclusion in low cyclic fatigue crack propagation is proposed and the influence of fatigue crack growth rate is estimated. Key words： super strength steel    inclusion    fatigue crack initiation and propagation 收稿日期: 2005-03-28      ZTFLH:  TG111.8   服务 把本文推荐给朋友 加入引用管理器 E-mail Alert RSS 作者相关文章 王习术 梁锋 曾燕屏 谢锡善 44.8K 链接本文: https://www.ams.org.cn/CN/      或      https://www.ams.org.cn/CN/Y2005/V41/I12/1272 [1] Zhou S, Murakami Y, Beretta S, Fukushima Y. Mater Sci Technol, 2002; 18: 1535 [2] Pan T, Yang Z G, Bai B Z, Fang H S. Acta Metall Sin, 2003; 39: 1037 (潘涛,杨志刚,白秉哲,方鸿生．金属学报,2003;39:1037) [3] Goto H, Miyazawa K, Tanaka T. ISIJ Int, 1995; 5: 286 [4] Shih T Y, Araki T. Trans Irons Steel Inst Jpn, 1973; 13:11 [5] Wang X S, Li Y Q. Acta Mech Solid Sin, 2003; 16: 327 [6] Zhang J M, Zhang J F, Yang Z G, Li S X, Hui W J, Weng Y Q, Acta Metall Sin, 2004; 40: 846 (张继明,张建锋,杨振国,李守新,惠卫军,翁宇庆．金属学 报,2004;40:846) [7] Yang Z G, Zhang J M, Li S X, Chu Z M, Hui W J, Weng Y Q. Acta Metall Sin, 2004; 40: 367 (杨振国,张继明,李守新．褚作明,惠卫军,翁宇庆．金属学 报,2004;40:367) [8] Hui W J, Dong H, Weng Y Q, Shi J, Nie Y H, Chu Z M, Chen Y B. Acta Metall Sin, 2004; 40: 561 (惠卫军,董瀚,翁宇庆,时捷,聂义宏,褚作明,陈蕴博． 金属学报,2004;40:561) [9] Wang X S, Zhu S Q, Kawagoishi N, Nisitani H. Acta Metall Sin (Engl Lett), 2001; 14: 271 [10] Wang X S, Kawagoishi N. J Iron Steel Res Int, 2003; 10(2): 58 [11] Wang X S, Lu X, Wang D H. Mater Sci Eng, 2004; A364: 11 [12] Wang X S, Fan J H. J Mater Sci, 2004; 39: 2617 [13] Wang X S, Xu Y, Xu X Q. J Appl Comp Mater, 2004; 11: 145 [14] Wang X S, Xu Y. J Nucl Mater, 2004; 328(2-3): 243 [15] Wang X S, Li Y Q, Yu S W. J Exp Technol, 2003; 27(2): 31 [16] Murakami Y, Endo M. Eng Fract Mech, 1983; 17: 1 [17] Wu C Z, Shih T S. Mater Trans, 2003; 44: 995 [18] Murakami Y, Endo M. Int J Fatigue, 1994; 16; 163 [19] Yates Y, Shi G, Atkinson H V, Sellars C M, Anderson C W. Fatigue Fract Eng Mater Struct, 2002; 25: 667 [20] Wang X S, Zhang L N, Xie X S. J Mater Sci Technol, in press [21] Melander A. Int J Fatigue, 1990; 12: 154 [22] Tanaka T, Mura T. J Appl Mech, 1981; 48: 97 [23] Patton E M, Santare M H. Int J Fract, 1990; 46: 71 [24] Santare M H, Keer L M. Trans ASME, 1986; 53: 3821 [1] 陈润农, 李昭东, 曹燕光, 张启富, 李晓刚. 9%Cr合金钢在含Cl－环境中的初期腐蚀行为及局部腐蚀起源[J]. 金属学报, 2023, 59(7): 926-938. [2] 张月鑫, 王举金, 杨文, 张立峰. 冷却速率对管线钢中非金属夹杂物成分演变的影响[J]. 金属学报, 2023, 59(12): 1603-1612. [3] 张开元, 董文超, 赵栋, 李世键, 陆善平. 固态相变对Fe-Co-Ni超高强度钢长臂梁构件焊接-淬火过程应力和变形的影响[J]. 金属学报, 2023, 59(12): 1633-1643. [4] 孙阳庭, 李一唯, 吴文博, 蒋益明, 李劲. Ca、Mg掺杂下夹杂物对C70S6非调质钢点蚀行为的影响[J]. 金属学报, 2022, 58(7): 895-904. [5] 刘洁, 徐乐, 史超, 杨少朋, 何肖飞, 王毛球, 时捷. 稀土Ce对非调质钢中硫化物特征及微观组织的影响[J]. 金属学报, 2022, 58(3): 365-374. [6] 朱苗勇, 邓志银. 钢精炼过程非金属夹杂物演变与控制[J]. 金属学报, 2022, 58(1): 28-44. [7] 石增敏, 梁静宇, 李箭, 王毛球, 方子帆. 板条马氏体拉伸塑性行为的原位分析[J]. 金属学报, 2021, 57(5): 595-604. [8] 唐海燕, 刘锦文, 王凯民, 肖红, 李爱武, 张家泉. 连铸中间包加热技术及其冶金功能研究进展[J]. 金属学报, 2021, 57(10): 1229-1245. [9] 周红伟, 白凤梅, 杨磊, 陈艳, 方俊飞, 张立强, 衣海龙, 何宜柱. 1100 MPa级高强钢的低周疲劳行为[J]. 金属学报, 2020, 56(7): 937-948. [10] 孙飞龙, 耿克, 俞峰, 罗海文. 超洁净轴承钢中夹杂物与滚动接触疲劳寿命的关系[J]. 金属学报, 2020, 56(5): 693-703. [11] 张新房, 闫龙格. 脉冲电流调控金属熔体中的非金属夹杂物[J]. 金属学报, 2020, 56(3): 257-277. [12] 冯业飞,周晓明,邹金文,王超渊,田高峰,宋晓俊,曾维虎. 粉末高温合金中SiO2夹杂物与基体的界面反应机理及对其变形行为的影响[J]. 金属学报, 2019, 55(11): 1437-1447. [13] 黄宇, 成国光, 谢有. 稀土Ce对钎具钢中夹杂物的改质机理研究[J]. 金属学报, 2018, 54(9): 1253-1261. [14] 马歌, 左秀荣, 洪良, 姬颖伦, 董俊媛, 王慧慧. 深海用X70管线钢焊接接头腐蚀行为研究[J]. 金属学报, 2018, 54(4): 527-536. [15] 惠亚军,潘辉,李文远,刘锟,陈斌,崔阳. 1000 MPa级Nb-Ti微合金化超高强度钢加热制度研究[J]. 金属学报, 2017, 53(2): 129-139. Viewed Full text Abstract Cited   Shared      Discussed