热-力-电多场作用下钛合金构筑界面的结合机制

doi:10.11900/0412.1961.2025.00419

金属学报 DOI: 10.11900/0412.1961.2025.00419

本期目录 | 过刊浏览

王丰^1,2,3, 宋佳龙^1,2, 李阔³, 赵龙哲³, 钱东升^1,2

1 湖北隆中实验室襄阳 441022

2 武汉理工大学高温轻合金及应用技术全国重点实验室武汉 430070

3 中国科学院金属研究所沈阳 110016

Bonding Mechanism of the Addition Forging Interface of Titanium Alloy Under Thermal-Force-Electrical Multi-Field Coupling

WANG Feng ^1,2,3, SONG Jialong ^1,2, LI Kuo ³, ZHAO Longzhe ³, QIAN Dongsheng ^1,2

1 Hubei Longzhong Laboratory, Xiangyang 441022, China

2 State Key Laboratory of Light Superalloy, Wuhan 430070, China

3 Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

引用本文:

王丰, 宋佳龙, 李阔, 赵龙哲, 钱东升. 热-力-电多场作用下钛合金构筑界面的结合机制[J]. 金属学报, DOI: 10.11900/0412.1961.2025.00419.

全文: PDF(5976 KB)

摘要:

钛合金是航空航天领域重要结构材料，大型钛合金均质化制坯是航空航天装备制造领域面临的重要课题。本论文在热-力场构筑成形制坯工艺基础上，提出了钛合金热-力-电多场构筑成形新工艺。系统探究了热-力-电多场作用对TC4钛合金构筑界面结构演化、愈合效果及力学性能的影响。通过光学显微镜（OM）、扫描电子显微镜（SEM）、电子背散射衍射（EBSD）、单向拉伸等实验手段研究了不同电流加载下构筑界面的组织特征和力学性能，揭示了热-力-电多场作用对构筑界面愈合效果的影响机制。研究结果表明：在界面构筑过程引入适当电流（24A）可促进界面再结晶、界面氧原子扩散并降低界面内应力，从而显著促进构筑界面愈合效果，提升界面结合强度和剪切强度；而大电流（48A）下基体材料明显软化，基体材料与氧化物之间变形不协调，导致界面仍然存在大量孔洞和未分解氧化物。研究结果证实了热-力-电多场作用下界面愈合的提升效果，为大型钛合金均质化制坯提供了创新思路。

关键词 ：关键词：构筑成形, 钛合金, 热-力-电多场, 界面愈合, 力学性能。

Abstract：itanium alloy is an important structural material in the aerospace field, and the preparation of large-scale homogenized titanium alloy billets is a key issue in the manufacturing of aerospace equipment. Based on the thermo-mechanical field addition forging and forming process for billet preparation, this paper further proposes a new thermo-mechanical-electrical multi-field addition forging and forming process for titanium alloys. It systematically investigated the effects of thermo-mechanical-electrical multi-field action on the interface structure evolution, healing effect, and mechanical properties of TC4 titanium alloy addition forging interfaces. By means of experimental methods such as optical microscopy (OM), scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), and uniaxial tensile testing, the microstructural characteristics and mechanical properties of the addition forging interfaces under different current loadings were studied, and the influence mechanism of thermo-mechanical-electrical multi-field action on the healing effect of the addition forging interfaces was revealed. The research results show that introducing an appropriate current (24A) during the interface addition forging process can promote interface recrystallization, interface oxygen atom diffusion, and reduce interface internal stress, thereby significantly improving the healing effect of the addition forging interface; however, under a high current (48 A), the matrix material is obviously softened, and there is deformation incoordination between the matrix material and oxides, resulting in a large number of pores and undissolved oxides remaining at the interface. The research results confirm the improvement effect of interface healing under thermo-mechanical-electrical multi-field action, and provide an innovative idea for the preparation of large-scale homogenized titanium alloy billets.

Key words： KEYWORDS：addition forging titanium alloy thermo-force-electrical multi-field interface healing force properties.

收稿日期: 2025-12-23

基金资助:国家重点研发计划(2024YFB3714200); 湖北省自然科学基金创新研究群体项目(2025AFA014)

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王丰
	宋佳龙
	李阔
	赵龙哲
	钱东升
44.8K

链接本文:

https://www.ams.org.cn/CN/Y0/V/I/0

[1]	吴帆, 刘华辉, 边文珊, 蔡竣宇, 金士杰, 罗忠兵. TC4钛合金循环变形微观组织演化与滑移机制[J]. 金属学报, 2026, 62(6): 1082-1090.
[2]	王建峰, 许珍木, 刘战, 高转妮, 占小红. 超声振动对TC4钛合金窄间隙激光焊接组织及强化机理的影响[J]. 金属学报, 2026, 62(3): 406-420.
[3]	赵子博, 谭海兵, 张博华, 刘玉敬, 刘建荣, 郭会明, 曾卫东, 田伟, 王清江. 综述：近 α 型和 α + β 两相钛合金的微织构[J]. 金属学报, 2026, 62(2): 275-288.
[4]	谭若涵, 宋永锋, 陈超, 李丹, 成庶, 李雄兵. 增材制造钛合金等效弹性张量的细观力学建模与实验研究[J]. 金属学报, 2025, 61(9): 1438-1448.
[5]	张洺川, 徐勤思, 刘意, 蔡雨升, 牟义强, 任德春, 吉海宾, 雷家峰. 热压温度对TC4合金扩散连接区组织与性能的影响[J]. 金属学报, 2025, 61(8): 1183-1192.
[6]	范荣磊, 陈明和, 吴迪鹏, 武永. 基于晶体塑性模型预测TA32钛合金损伤及高温成形极限[J]. 金属学报, 2025, 61(8): 1293-1304.
[7]	赵焯雅, 孟令健, 林鹏, 曹晓卿. TC4钛合金跨相区连续热压缩 α 相组织演变规律及织构形成机理[J]. 金属学报, 2025, 61(5): 717-730.
[8]	戴进财, 闵小华, 辛社伟, 刘凤金. 间隙元素O对 β 型Ti-15Mo合金超低温力学性能的影响[J]. 金属学报, 2025, 61(2): 243-252.
[9]	齐敏, 王倩, 马英杰, 曹贺萌, 黄森森, 雷家峰, 杨锐. Ti6246钛合金 β → α 相变中晶界 α 相生长行为及其对微织构的影响[J]. 金属学报, 2025, 61(2): 265-277.
[10]	李丹, 宫得伦, 郝玉琳. O含量对Ti2448合金时效析出行为及力学性能的影响[J]. 金属学报, 2025, 61(12): 1790-1802.
[11]	徐玮辰, 佟向瑜, 王优强, 张斌斌, 马超群, 王秀通. 深海环境对钛合金应力腐蚀影响的研究进展[J]. 金属学报, 2025, 61(10): 1469-1484.
[12]	颜孟奇, 吴泽浩, 佟健博, 黄利军, 黄驿胜. TC18钛合金大尺寸 β 晶粒制备及典型织构对力学性能的影响[J]. 金属学报, 2025, 61(10): 1555-1566.
[13]	周牧, 王倩, 王延绪, 翟梓融, 何伦华, 李昺, 马英杰, 雷家峰, 杨锐. 焊前预处理对钛合金厚板焊接残余应力的影响[J]. 金属学报, 2024, 60(8): 1064-1078.
[14]	程坤, 陈树明, 曹烁, 刘建荣, 马英杰, 范群波, 程兴旺, 杨锐, 胡青苗. 第一性原理研究钛合金中的沉淀强化[J]. 金属学报, 2024, 60(4): 537-547.
[15]	杨杰, 黄森森, 尹慧, 翟瑞志, 马英杰, 向伟, 罗恒军, 雷家峰, 杨锐. 航空用TC21钛合金变截面模锻件的显微组织和力学性能不均匀性分析[J]. 金属学报, 2024, 60(3): 333-347.

Viewed

Full text

Abstract

Cited

Shared

Discussed