奥氏体稳定性对TRIP型双相不锈钢循环塑性行为的影响及其微观机理

doi:10.11900/0412.1961.2025.00012

金属学报 DOI: 10.11900/0412.1961.2025.00012

本期目录 | 过刊浏览

奥氏体稳定性对TRIP型双相不锈钢循环塑性行为的影响及其微观机理

李小龙^1,2,张庆玲¹,秦锐^1,3,李文玉^1,3,郝硕⁴,陈雷^1,2,金淼^1,3,蔡星周^1,5

1 燕山大学机械工程学院秦皇岛 066004

2 燕山大学国家冷轧板带装备及工艺工程技术研究中心秦皇岛 066004

3 燕山大学先进锻压成形技术与科学教育部重点实验室秦皇岛 066004

4 河北大学质量技术监督学院保定 071002

5 燕山大学起重机械关键技术国家重点实验室秦皇岛 066004

Effect of austenite stability on the cyclic plasticity behavior of TRIP-assisted duplex stainless steels and its micromechanisms

LI Xiaolong ^1,2, ZHANG Qingling ¹, QIN Rui ^1,3, LI Wenyu ^1,3, HAO Shuo ⁴, CHEN Lei ^1,2, JIN Miao ^1,3, CAI Xingzhou^1,5

1 College of Mechanical Engineering, Yanshan University, Qinhuangdao 066004, China

2 Key Laboratory of Advanced Forging & Stamping Technology and Science, Yanshan University, Qinhuangdao 066004, China

3 National Engineering Research Center for Equipment and Technology of Cold Strip Rolling, Yanshan University, Qinhuangdao 066004, China

4 School of Quality and Technical Supervision, Hebei University, Baoding 071002, China

5 State Key Laboratory of Crucial Technology of Crane Machinery, Yanshan University, Qinhuangdao 066004, China

引用本文:

李小龙张庆玲秦锐李文玉郝硕陈雷金淼. 奥氏体稳定性对TRIP型双相不锈钢循环塑性行为的影响及其微观机理[J]. 金属学报, 10.11900/0412.1961.2025.00012.

全文: PDF(4847 KB)

摘要: TRIP型双相不锈钢因其显著降低的密度以及TRIP效应带来的优异延展性和加工硬化能力，逐渐被广泛应用于新能源汽车行业。然而，钢中奥氏体稳定性的差异会影响TRIP效应，从而改变材料的循环塑性行为。本工作以两种奥氏体稳定性不同的双相不锈钢为研究对象，通过对比分析两种材料在循环加载下的力学响应特征与微观组织演变，探究奥氏体稳定性对TRIP型双相不锈钢循环塑性行为的影响，并阐明其微观机理。结果表明，随着奥氏体稳定性的降低，α'马氏体相变程度增大，且除在ε马氏体带交点处形核外，还出现了直接在ε马氏体带上形核的现象。奥氏体稳定性的降低会使材料循环软化效果减弱，二次硬化能力增强；此外，还提高了α'马氏体的相变速率和相变量，加重各相间的性能不协调与应变不连续程度，从而易于在各相界面和α'马氏体相变处萌生微裂纹，降低材料的疲劳寿命。

关键词 ： TRIP型双相不锈钢, 奥氏体稳定性, 循环塑性行为, 马氏体相变, 疲劳寿命

Abstract：TRIP-assisted duplex stainless steels (DSSs) have gradually gained widespread application in the new energy vehicle industry due to its significantly reduced density and the excellent ductility and work hardening capability induced by the TRIP effect. However, the differences in the stability of austenite in the steel can affect the TRIP effect, thereby altering the material's cyclic plasticity behavior. This study investigates two DSSs with different austenite stabilities. By comparing and analyzing the mechanical responses and microstructural evolution of these materials under cyclic loading, the influence of austenite stability on the cyclic plasticity behavior of TRIP-assisted DSSs is explored, along with the underlying microstructural mechanisms. The results indicate that with a decrease in austenite stability, the degree of α' martensitic transformation increases. In addition to nucleation at the intersections of the ε-martensite bands, nucleation is also observed directly on the ε-martensite bands. The reduction in austenite stability weakens the cyclic softening effect of the material, enhances its secondary hardening capacity, and increases the transformation rate and volume fraction of α' martensite. This leads to a higher degree of performance mismatch and strain discontinuity between the phases, making it easier for microcracks to initiate at phase interfaces and at the α' martensite transformation sites, thus reducing the material's fatigue life.

Key words： TRIP-assisted duplex stainless steel austenite stability cyclic plasticity behavior martensitic transformation fatigue life

收稿日期: 2025-01-10

基金资助:国家自然科学基金项目;国家自然科学基金项目;河北省自然科学基金项目;中央引导地方科技发展资金项目;中央引导地方科技发展资金项目;燕山大学基础研究与创新人才培养项目;燕山大学基础研究与创新人才培养项目

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李小龙
	张庆玲
	秦锐
	李文玉
	郝硕
	陈雷
	金淼
44.8K

链接本文:

https://www.ams.org.cn/CN/Y0/V/I/0

[1]	张文彬, 李小龙, 郝硕, 刘胜杰, 蔡星周, 陈雷, 金淼. TRIP型双相不锈钢Fe-19.6Cr-2Ni-2.9Mn-1.6Si的微裂纹形核及扩展[J]. 金属学报, 2025, 61(4): 608-618.
[2]	贾春妮, 刘腾远, 郑成武, 王培, 李殿中. 中锰钢奥氏体中化学界面变形行为的晶体塑性研究[J]. 金属学报, 2025, 61(2): 349-360.
[3]	王旗涛, 李艳芬, 张家榕, 李尧志, 付海阳, 李新乐, 严伟, 单以银. 聚变增殖包层用低活化9Cr-ODS钢的室温低周疲劳行为[J]. 金属学报, 2025, 61(2): 323-335.
[4]	杨谨菡, 闫海乐, 刘昊轩, 赵莹, 杨一俏, 赵骧, 左良. A₂BTi型磁性功能合金相稳定性、磁性与力学性能的第一性原理计算和实验研究[J]. 金属学报, 2024, 60(12): 1701-1709.
[5]	江河, 佴启亮, 徐超, 赵晓, 姚志浩, 董建新. 镍基高温合金疲劳裂纹急速扩展敏感温度及成因[J]. 金属学报, 2023, 59(9): 1190-1200.
[6]	姜江, 郝世杰, 姜大强, 郭方敏, 任洋, 崔立山. NiTi-Nb原位复合材料的准线性超弹性变形[J]. 金属学报, 2023, 59(11): 1419-1427.
[7]	宋文硕, 宋竹满, 罗雪梅, 张广平, 张滨. 粗糙表面高强铝合金导线疲劳寿命预测[J]. 金属学报, 2022, 58(8): 1035-1043.
[8]	李伟, 贾兴祺, 金学军. 高强韧QPT工艺的先进钢组织调控和强韧化研究进展[J]. 金属学报, 2022, 58(4): 444-456.
[9]	沈国慧, 胡斌, 杨占兵, 罗海文. 回火温度对含 δ 铁素体高铝中锰钢力学性能和显微组织的影响[J]. 金属学报, 2022, 58(2): 165-174.
[10]	原家华, 张秋红, 王金亮, 王灵禺, 王晨充, 徐伟. 磁场与晶粒尺寸协同作用对马氏体形核及变体选择的影响[J]. 金属学报, 2022, 58(12): 1570-1580.
[11]	潘庆松, 崔方, 陶乃镕, 卢磊. 纳米孪晶强化304奥氏体不锈钢的应变控制疲劳行为[J]. 金属学报, 2022, 58(1): 45-53.
[12]	王金亮, 王晨充, 黄明浩, 胡军, 徐伟. 低应变预变形对变温马氏体相变行为的影响规律及作用机制[J]. 金属学报, 2021, 57(5): 575-585.
[13]	左良, 李宗宾, 闫海乐, 杨波, 赵骧. 多晶Ni-Mn-X相变合金的织构化与功能行为[J]. 金属学报, 2021, 57(11): 1396-1415.
[14]	肖飞, 陈宏, 金学军. 形状记忆合金弹热制冷效应的研究现状[J]. 金属学报, 2021, 57(1): 29-41.
[15]	孙飞龙, 耿克, 俞峰, 罗海文. 超洁净轴承钢中夹杂物与滚动接触疲劳寿命的关系[J]. 金属学报, 2020, 56(5): 693-703.

Viewed

Full text

Abstract

Cited

Shared

Discussed